• Journal of Welding and Joining
• /
• v.12 no.3
• /
• pp.82-89
• /
• 1994

In this paper the effect of stress ratio on the fatigue crack growth rate of aluminum alloy A5083-O was examined. The fatigue tests were carried out using CCT (center cracked tension) specimens and CT(compact tension) specimens which were subjected to 0.5 and -1.0 stress ratio respectively. The obtained results are as follows; 1) The $\DeltaK_{th}$ as the function of stress ratio R was introduced in evaluating the fatigue crack growth rate of A5083-O. 2) A new model evaluating the effect of stress ratio on the fatigue crack growth rate was developed over the region of low and high propagation rate.

• Transactions of the Korean Society of Automotive Engineers
• /
• v.10 no.2
• /
• pp.110-116
• /
• 2002

At elevated temperature, very complex precipitations occur in STS316. To investigate the effect of the precipitation on mechanical properties in SIS316, tensile tests and fatigue crack growth tests were carried out at $650^{\circ}C$ using artificially degraded materials. The material degradation was simulated by aging for up to 20000 hrs. at $750^{\circ}C$, which is equal to 179000hrs (about 20yrs) of service life at $650^{\circ}C$, after conducting solution treatment for 20 min. at $11300^{\circ}C$. The result of the hardness test and the tensile test showed that both properties are closely related to the mean free distance of carbides. Also, from the results of fracture tests at $650^{\circ}C$, ${\triangle}K_{th}$, after values were found to decrease as aging time and microstructure, as the volume fraction of $\sigma$ phase increased.

• Transactions of the Korean Society of Mechanical Engineers A
• /
• v.41 no.9
• /
• pp.853-860
• /
• 2017

To evaluate the effects of mode II on the crack initiation and propagation stages, the effects in the fatigue threshold region under a mixed-mode I+II loading state was experimentally investigated. In the case of mixed-mode I + II, during the crack initiation stage, as the loading application angle (${\theta}$) increased, cracks occurred in the lower load owing to the effects of mode II, while the crack propagation rate decreased. The effects of mode II were experimentally investigated in the crack propagation stage by means of multilevel loading direction variation. Following mixed-mode I+II ($0^{\circ}{\rightarrow}{\theta}{\rightarrow}60^{\circ}$), as the load application angle increased, the fatigue crack propagation rate decreased, as did the fatigue crack propagation rate, which occurred later. Following mixed-mode I + II in case of(${\theta}{\geq}75^{\circ}$), the fatigue crack propagation rate was found to increase, while the fatigue life decreased.