• Resources Recycling
• /
• v.21 no.5
• /
• pp.18-30
• /
• 2012

Zirconium is one of the most important material used as cladding of fuel rods in nuclear reactors because of its high dimensional stability, good corrosion resistance and especially low neutron-absorbing cross section. However, Hf free nuclear grade Zr sponge is commercially produced by only three countries including USA, France and Russia. So, Zr has been thoroughly managed as a national strategic material in Korea. Most of the zirconium is used for Korean nuclear industry as nuclear fuel cladding materials manufactured from Hf free Zr alloy raw material. Also, there are some other applications such as alloying element and detonator. In this review, zirconium production and recycling technologies have been reviewed and current industrial status was also analyzed. And recent achievements in innovative reduction technologies such as electrolytic reduction process and molten oxide electrolysis were also introduced.

• Journal of the Korean Vacuum Society
• /
• v.18 no.1
• /
• pp.30-36
• /
• 2009

The effects of $HfO_2$ film thickness on electrical, optical, and structural properties were investigated. We fabricated ITO/$HfO_2$/ITO metal-insulator- metal (MIM) capacitor using transparent conducting oxide. When $HfO_2$ film thickness increase from 50 nm to 300 nm, dielectric constant of $HfO_2$ was decreased from 20.87 to 9.72. The transparent capacitor shows an overall high performance, such as a dielectric constant about 21 by measuring the ITO/$HfO_2$/ITO capacitor structures and a low leakage current of $2.75{\times}10^{-12}\;A/cm^2$ at +5 V. Transmittance above 80% was observed in visible region.

• Journal of the Korean Vacuum Society
• /
• v.21 no.5
• /
• pp.273-278
• /
• 2012

Over the last decade, the hafnium-based gate dielectric materials have been studied for many application fields. Because these materials had excellent behaviors for suppressing the quantum-mechanical tunneling through the thinner dielectric layer with higher dielectric constant (high-K) than $SiO_2$ gate oxides. Although high-K materials compensated the deterioration of electrical properties for decreasing the thickness of dielectric layer in MOSFET structure, their nano-mechanical properties of $HfO_2$ thin film features were hardly known. Thus, we examined nano-mechanical properties of the Hafnium oxide ($HfO_2$) thin film in order to optimize the gate dielectric layer. The $HfO_2$ thin films were deposited by rf magnetron sputter using hafnium (99.99%) target according to various oxygen gas flows. After deposition, the $HfO_2$ thin films were annealed after annealing at $400^{\circ}C$, $600^{\circ}C$ and $800^{\circ}C$ for 20 min in nitrogen ambient. From the results, the current density of $HfO_2$ thin film for 8 sccm oxygen gas flow became better performance with increasing annealing temperature. The nano-indenter and Weibull distribution were measured by a quantitative calculation of the thin film stress. The $HfO_2$ thin film after annealing at $400^{\circ}C$ had tensile stress. However, the $HfO_2$ thin film with increasing the annealing temperature up to $800^{\circ}C$ had changed compressive stress. This could be due to the nanocrystal of the $HfO_2$ thin film. In particular, the $HfO_2$ thin film after annealing at $400^{\circ}C$ had lower tensile stress, such as 5.35 GPa for the oxygen gas flow of 4 sccm and 5.54 GPa for the oxygen gas flow of 8 sccm. While the $HfO_2$ thin film after annealing at $800^{\circ}C$ had increased the stress value, such as 9.09 GPa for the oxygen gas flow of 4 sccm and 8.17 GPa for the oxygen gas flow of 8 sccm. From these results, the temperature dependence of stress state of $HfO_2$ thin films were understood.