• Journal of the Korean Society of Manufacturing Technology Engineers
• /
• v.6 no.4
• /
• pp.80-88
• /
• 1997

An experimental investigation of the fatigue through crack growth behavior under simple stepped variable loading condition has been performed using Al7075-T651. Experiments were carried out by using cantilever bending type specimens, with chevron notches on a small electro-magnetic test machine. Tensile overloads have a retarding effect on the fatigue crack growth rates, therefore tensile overloads were used for the beneficial effect on the fatigue life. While in most cases compressive overloads have only a vanishing effect on crack growth rates, some experiments with single edge crack tension specimens reveal a marked growth retardation. The stress ratios used in this investigations varies from R=0.32 to 0.81, from R=0.04 to 0.76, from R=-0.15 to 0.73, and from R=-0.33 to 0.68 and the peak load for each case was not varied. The crack growth and crack closure were measured by Kikukawa's compliance method with a strain gauge mounted on the backside of each specimens. The results obtained are as follows. When the stepped variable load was applied, the smaller the stress ration was, the larger the delayed retardation of the crack growth rate was. The fatigue crack growh rate data obtained for through cracks were plotted well against the effective stress intensity factor range from 4.0 to 20.0MP{a^{SQRT}m}. It was found that the effective stress intensity factor range ratio was related well to the opening stress intensity factor, the maximum stress intensity factor, and crack length.

• Composites Research
• /
• v.18 no.2
• /
• pp.1-12
• /
• 2005

Fracture behaviors of single-edge-notched monolithic aluminum plates and glass fiber/aluminum laminates under tensile loadings have been studied using acoustic emission(AE) monitoring. AE signals from monolithic aluminum could beclassified into two different types. For glass fiber/aluminum laminates, AE signals with high amplitude and long duration were additionally confirmed on FFT frequency analysis, which corresponded to macrocrack propagation and/or delamination. AE source location determined by signal arrival time showed the zone of fracture. On the basis of the above AE analysis and fracture observation, characteristic features of fracture processes of single-edge-notched glass fiber/aluminum laminates were elucidated according to different fiber ply orientations and fiber/aluminum lay-up ratios.

• Journal of the Korean Society for Precision Engineering
• /
• v.14 no.6
• /
• pp.22-27
• /
• 1997

In general, the load which acts on the structure is almost independent of time in many locations. In this case. It is difficult to estimate the life with the service load history, because the structure is on the multi- axial and multi-point loading states. In this study, the service load of the excavator which is widely used in industry field was calculated using measured cylinder pressures and displacements. The fatigue life was estimated using the multi-axial and multi-point load counting method. Service load history of 4 pin joint which act independently each other is yielded by mult-axial and multi-point load counting method. The stress spectrum is yielded by superposition of the results of FEM stress analysis applied unit load. Palm- gren-Miner's cumulative Damage is 0.000804 for Von Mises equivalent stress sequence by one side fillet weld S-N curve. This result agress with Bench test results. As a result of this study, the fatigue life esti- mation using the multi-axial and multi-axial and multi-point load counting method is useful.

• Journal of the Korean Society for Precision Engineering
• /
• v.9 no.3
• /
• pp.140-148
• /
• 1992

The effect of mechanical, properties in the plastic zone near the crack-tip was investigated, under various controlled loading conditions, i.e., ${\Delta}K$ increasing, ${\Delta}K$ decreasing, and single overload test. For both ${\Delta}K$ decreasing test and ${\Delta}K$ increasing test with constant stress ratio, it is found that the ratio of material constant m'( ${\Delta}K$ decreasing test) to material constant m( ${\Delta}K$ increasing test) is larger than 1 for n<0.1, and it is equal to 1 for 0.10.2. A modified crack growth rate equation based on Forman's equation which applied stable region of fatigue crack propagation in ${\Delta}K$ decreasing test is proposed. Within the limit of this single overload test, an empirical relation between among the retardation ratio (Nd/ $N^{*}$), the strain hardening exponent (n) and the percent peak load (%PL) has been established.established.

• Journal of the Korean Society for Nondestructive Testing
• /
• v.31 no.1
• /
• pp.53-61
• /
• 2011

Edge notched A16061-T6 aluminum was repaired with a GFRP composite patch as a function of the number of stacking, Damage progress of specimen for tension load has been monitored by acoustic emission(AE), AE energy rate, hit rate, amplitude, waveform and 1st peak frequency distribution were analyzed. Fracture processes were classified into Al cracking, Fiber breakage, Resin cracking and Delamination. Displacement of a specimen can be divided into Region I, II and ill according to acoustic emission characteristics. Region II where the patch itself was actually fractured was focused on to clarify the AE characteristics difference for the number of stacking.

• Journal of the Korean Society for Nondestructive Testing
• /
• v.22 no.5
• /
• pp.539-544
• /
• 2002

The purpose of this study is to examine the change of full width half maximum(FWHM) and residual stress during fatigue process in S45C Steel, by X-ray diffraction. For S45C Steel, the relationship between the change in fatigue damage of the specimen and the FWHM, and residual stress of X-ray diffraction profiles during the fatigue processes has been investigated. The FWHM decreases in the early period of fatigue cycle. The change of FWHM is associated with cyclic work hardening. The change of the FWHM is not significant in $10{\sim}20%$ of ratio of fatigue life. The residual stress is changed with fatigue cycle increasing during the fatigue pro process.

• Journal of the Korea Academia-Industrial cooperation Society
• /
• v.11 no.5
• /
• pp.1785-1790
• /
• 2010

To study the vortex induced vibrations the wind tunnel and the two story shear building were designed and built. The wind tunnel was designed to generate the wind speed up to 24 m/s, and the building was designed to have the two lowest natural frequencies within the range of the vortex frequencies generated by the wind tunnel. The resonance behaviors by the locking-on phenomena were observed during the wind tunnel tests of the shear building with the cylinder attached. From the locking-on phenomena observed it is found that the effects of the amplitudes and the frequencies of the cylinders should be considered on the forces generated by the vortex shedding.

• Transactions of the Korean Society of Mechanical Engineers
• /
• v.10 no.2
• /
• pp.208-214
• /
• 1986

To establish the evaluation of the fatigue crack growth behavior in 5083-O aluminum alloy, constant load-amplitude fatigue crack growth tests were carried out under the small scale yielding conditions. Crack length and closure of this material were measured by the compliance method using a clip-on gage. The main results obtained as follows: The fatigue crack growth rate against stress intensity factor range .DELTA.K exhibits the trilinear form with two transitions at the growth rate 5.5*10$^{-6}$ and 5.5*10$^{-5}$ mm/cycle, in the so-caled Region II. The trilinear form appears still in the plot of growth rate versus effective stress intensity factor range .DELTA. $K_{eff}$. Stress ratio R affects the relationship of crack growth rates versus .DELTA.K but does not affect the reation of crack growth rate versus .DELTA. $K_{eff}$. The experimental results indicate that the effective stress intensity range ratio U depends on the maximum stress intensity factor $K_{max}$, but not on the stress ratio R.o R.R.

• Transactions of the Korean Society of Mechanical Engineers
• /
• v.14 no.3
• /
• pp.554-570
• /
• 1990

he rolling contact behaviors between a smooth ball and a flat rough surface under dynamic load are intricately affected by many factors, such as the diameter of a ball, normal load and the roughness of a flat surface etc. Accordingly, the experimental study is done to find them on the base of elastic hysteresis loss as theoretical approach is very difficult. The experimental apparatus composed of damped-free vibration system is used. This paper investigates the damping characteristics on the rolling contact area through rolling friction force and logarithmic decrement versus displacement obtained in accordance with the variations of those factors, and presents a new experimental method to find out contact width using the relations of logarithmic decrement and rolling friction force with displacement.

• Composites Research
• /
• v.17 no.2
• /
• pp.28-33
• /
• 2004

Failure detection in a cross-ply laminated composite beam under tensile loading were performed using a fiber Bragg grating (FBG) sensor. A Passive Mach-Zehnder interferometric demodulator was proposed to enhance sensitivity and bandwidth. The proposed FBG sensor system without active device such as a phase modulator is very simple in configuration, easy to implement and enables the measurement of high-frequency vibration with low strain amplitude such as impact or failure signal. Failure signals detected by a FBG sensor had offset value corresponding to the strain shift with vibration at a maximum frequency of several hundreds of kilohertz. at the instant of transverse crack propagation in the 90 degree layer of composite beam.