• Journal of the Korean Ceramic Society
• /
• v.40 no.7
• /
• pp.662-666
• /
• 2003

Hertzian cyclic fatigue properties of the alumina-glass dental ceramics were evaluated in exact in vitro environment at contact loads from 200 N to 1000 N and up to 10$\^$6/ cycles to investigate the indentation damage and strength degradation. At 200 N, no strength degradation and crack generation was observed up to 10$\^$6/ contact cycles. As load increased from 200 N to 1000 N, the drastic reduction in strength was found when the damage transition from ring to radial crack occurred. The extent of strength degradation was more pronounced in vitro environments probably due to chemical reaction of artificial saliva with glass phase through radial cracks introduced during large numbers of contacts.

• Proceedings of the Korean Society of Tribologists and Lubrication Engineers Conference
• /
• 1999.06a
• /
• pp.61-66
• /
• 1999

반복 응력 상태 아래서 알루미나 세라믹의 피로 표면손상 누적현상이 분석되었다. 연속 미끄럼 접촉 시에 발생하는 응력 상태를 재현하기 위해서 동시에 작용하는 수직-수평 반복 압축하중 기법이 사용되었다. 알루미나 구와 평판의 접촉면에서 알루미나 미세 결정의 피로 파손에 의한 마모 입자 형성 기구가 관찰되었고, 반복하중의 횟수와 수직-수평 하중비가 커질수록 마모량은 증가하였다. 반복 접촉하중에 의한 표면손상 누적이 접촉 수직 변위 측정으로 정량화 되었다. 두 접촉 구조물의 강성 (하중-변위 선도의 기울기) 변화가 두 재질의 탄성계수의 변화로 표현되었다.

• Proceedings of the Korean Society of Propulsion Engineers Conference
• /
• 2000.04a
• /
• pp.35-35
• /
• 2000

터빈의 핵심구동부품은 손상이 누적되어 파괴에 이를 경우 치명적인 결과를 야기할 수 있기 때문에, 부품사용조건에서의 소성변형과 이에 따른 손상 누적을 정확히 예측하고 평가함으로써 균열생성 시점을 정확히 파악하여야 할 필요가 있다. 현재 터빈디스크와 같이 고온 고응력에서 사용되고 있는 소재부품의 수명은 궁극적으로 크리프변형과 피로시험의 공동작용으로 결정되며, 재료특성모델링 시험에 있어서도 dwell time 피로시험을 통해 dwell time 효과를 점검하고 점소성 재료변형에 근거하여 피로에 의한 변형 현상을 설명할 수 있다.

• Proceedings of the Korean Institute of Industrial Safety Conference
• /
• 2000.06a
• /
• pp.215-222
• /
• 2000

반복하중을 받는 대부분의 토목구조물은 정적하중보다 훨씬 낮은 하중에서 파괴가 발생하는 경우가 있는데 이러한 현상을 피로라고 하며, 특히 강교량을 구성하는 부재중에서 2차 부재에 해당되는 덮개판, 수평보강재, 수직보강재, 거셋트 등의 용접부에서는 여러 원인으로 인해서 피로손상이 발생하게 되어 결국에는 구조물의 성능에 크게 영향을 미치게 된다. (중략)

• Proceedings of the Korean Society of Precision Engineering Conference
• /
• 1992.10a
• /
• pp.316-320
• /
• 1992

기계나 구조물등의 부재는 비금속 개재 물이나 가공과 같은 자연 결함과 함께 볼트구멍이나 기름구멍등의 인공 결함들을 가지고 있다. 이러한 인공 결함들은 초기 결함으로서 작용을 하여 반복되는 낮은 응력을 받을 경우 응력 집중원이 되고, 피로파괴의 원인이 된다. 이런 기계구조물에 대한 안전성 보장을 위하여, 금속재료의 제조 및 가공 공정상의 질적 개선과 함께 최적 설계가 강조되고 피로파괴 현상에 대한 많은 연구가 요구되고 있다.

• Journal of Industrial Technology
• /
• v.8
• /
• pp.39-46
• /
• 1988

탄소강 평활재 및 미소결함재를 사용하여, 미소 정류크랙의 크랙 개폐구거동의 상세한 관찰과 초기결함을 상정한 미소 원공과의 상호 한계크기의 비교 검토를 통하여, 다음과 같은 결론을 얻었다. 평활재의 정규크랙은, 피로과정중에 압축잔류응역이 크랙선단의 개구를 억제하는 것에 의하여 정류하게 되고, 그 크기는 평활재의 피로한도를 저하시키지 않은 미소 원공의 한계크기와 거의 일치하여, 두 경우가 역학적으로 거의 등가함을 시사해 주고 있다.

• Bulletin of the Society of Naval Architects of Korea
• /
• v.30 no.1
• /
• pp.49-55
• /
• 1993

구조물의 피로파괴 현상과 이에 대한 제어기술의 현황을 선형파괴역학적 접근방법을 중심으로 간략히 정리하였다. 현재까지의 연구결과들이 결집되므로써 피로파괴 제어기술 분야의 기초기술은 거의 정립된 단계에 이른 것으로 보여진다. 그러나 구조물의 사용환경은 고응력, 고온 또는 초저온 등으로 더욱 가혹해지는 경향이 있고 고장력강과 복합재료 등 신소재의 사용범위 확대에 의한 경량화 구조설계의 실현, 그리고 생산성 향상을 위한 용접구조물의 보편화 등에 따라 파괴역학의 적용분야는 점차 확대되고 있으며 이를 뒷받침하기 위한 기초 및 응용연구의 필요성도 더 커지고 있다.

• Transactions of the Korean Society of Mechanical Engineers A
• /
• v.34 no.3
• /
• pp.315-321
• /
• 2010

Co-cured single lap joints under cyclic tensile loads fail initially at the tip of the interface corner between the two adherents. The failure mechanism is complex because it is related to corrosion fatigue. Corrosion behavior at the interface affects the failure of the joints because corrosion deteriorates fatigue resistance. In this study, we clarified the cause of interfacial corrosion in co-cured single lap joints under cyclic tensile loads. The failure mechanism was also analyzed by observing the failed surfaces of specimens and the stress distribution along the interface. The surface roughness at the interface and the stacking sequence of the composite adherent were examined to investigate their effects on failure of the joint.

• Transactions of the Korean Society of Mechanical Engineers A
• /
• v.36 no.9
• /
• pp.1103-1108
• /
• 2012

A main steam pipe system is a branch pipe that connects a boiler with a turbine. Water hammering analysis is very important for limiting the damage caused to pipe systems by operation conditions. Water hammering created by an unsteady flow in pipeline systems can cause excessive change in pressure, vibration, and noise. The main steam pipe structure should be designed to safely maintain the pressure pulsation and several vibrations under operation environments. This study evaluated the structural integrity of a main steam pipe during suspended and normal operation by using the ASME fatigue life methodology and finite element analysis. In the analysis, water hammering was used for transient analysis. The calculated alternating stress and fatigue stress were compared with the applicable limits of ASME fatigue life. All the evaluation results satisfied the requirements of the ASME fatigue life.

• Journal of Korean Society of Steel Construction
• /
• v.22 no.3
• /
• pp.209-218
• /
• 2010

The fatigue phenomenon, which is induced by stress accumulation due to the repeated loading of vehicles in the long term, is one of the main factors of the span of life of a steel bridge. In this paper, the effects of traffic properties on the fatigue life of ordinary short- and medium-span steel plate girder bridges that are exposed to relatively large dynamic effects are investigated. From the analysis, it was known that the fatigue life of the bridge becomes shorter with increasing traffic volume and number of large vehicles, and is affected by the weights of the vehicles. Based on the analysis results, a new parameter that can represent the traffic property that affects the fatigue life of the subject bridge is suggested, and the validity of the parameter is confirmed.