• Journal of Welding and Joining
• /
• v.14 no.3
• /
• pp.75-85
• /
• 1996

In this paper the influence of postweld heat treatment on mechanical properties of SMAW and FCAW stainless steel weldments was examined and the obtained results are as follows ; (1) The amount of $\delta$-ferrite formed by SMAW and FCAW process decreased with increasing holding temperature and time in post weld heat treatment(PWHT), and it was found that the reduced ferrite was transformed into sigma phase after $800^{circ}C{\times}50hr$ PWHT. This sigma phase, even though it was very small, resulted in brittleness of dissimilar weldment between carbon steel and stainless steel in bending test, however in similar weldment between stainless steel and stainless steel was not occured. (2) The chemical composition of sigma phase was measured to 28-30%Cr, 7-9%Mo, 4-6Ni in 316L weldment, and also 35-37%Cr, 0.9-1.0Mo, 6-8%Ni in 309L weldment by EDS analysis.

• Journal of Welding and Joining
• /
• v.13 no.1
• /
• pp.127-137
• /
• 1995

The possibility of new GMAW process using economic shielding gases including CO$_{2}$ gas was investigated on the effect of shielding gas on weldabilty. In the optimum welding condition using 600A power source, FCAW process showed low depositions rate, 114 g/min at 300A, but new GMAW using other mixed shielding gases exhibited high deposition rate, 208-224 g/min at 450A. TIME gas, Ar+CO$_{2}$ gas and Ar+CO$_{2}$+O$_{2}$ gas as a shielding gas were able to be used to the very high welding current(450A), moreover TIME gas and Ar+CO$_{2}$ gas showed the highest arc stability among shielding gases studied in this experiments. The weld penetration was performed by axial spray transfer mode of weld droplet. On the basis of workability, weldability and economic point of view, Ar mixture (80%Ar+20%CO$_{2}$) gas was recommended as a shielding gas for the development and application of new GMAW process. This shielding gas showed the low spatter, good weld quality, stable arc and low cost at the region of high welding current.

• Journal of Welding and Joining
• /
• v.11 no.4
• /
• pp.57-69
• /
• 1993

In the present study, the microstructure and Charpy V notch toughness of multipass $CO_2$ FCA weldment in three different heat inputs(1-3KJ/mm)were investigated. The weldments using two different domestic FCAW wires(AWS E71T-1 and E71T-5 equivalent) in C-Mn steel were chemically analysed. The following conclusions can be inferred. 1. T-1 wire Showed a stable arc transfer, less spatter and harsh, a better bead spreading and easy slag removal, whereas T-5 wire suffered from the arc stability, which tended to increase spatter and produce a more convex bead. 2.The microsturctures of the top beads of the weldments in three different heat inputs consisted of coarse-grained boundary ferrite and Widmanstatten ferrite side plate with increasing heat inputs. The modest fraction of acicular ferrite in the two wire weldments was observed in the 2KJ/mm heat input. 3.The fine-grained reheated zones of both welds consisted of a duplex microstructure of polygonal ferrite and second phases. 4. The basic flux weldment of T-5wires showed a higher Charpy impact property than that of T-1 wires because of a higher fraction of acicular ferrite in the weld microstructure.

• Journal of the Korea Academia-Industrial cooperation Society
• /
• v.6 no.2
• /
• pp.122-128
• /
• 2005

A feasibility study on the application of self?shielded flux cored arc welding to the on-site SM520 steel bridge box fabrication for express trains and high way construction instead of gas-shield flux cored arc welding was conducted in terms of weld soundness, mechanical properties, toughness and microstructures. All welded specimens made with the self?shielded FCAW process were tested by magnetic particle and ultrasonic techniques and they were found to be sound. All multipass weld specimens made with both self-shielded and gas-shielded FCAW processes showed yield and tensile strengths of $462{\sim}549\;MPa$ and $548{\sim}640\;MPa$, respectively. The impact values of Charpy V-Notch weld specimens also met with the required value of 40J at $-20^{\circ}C$. The hardness values of the top area of weldments were higher than those of the bottom area because of higher residual stresses in the near surface. It was found that welding characteristics of SM520 steel by the on-site welding conditions with self-shielded FCAW showed almost equivalent to those by gas-shielded FCAW in terms of sound welds, mechanical properties and microstructure.

• Journal of the Society of Naval Architects of Korea
• /
• v.35 no.4
• /
• pp.65-75
• /
• 1998

The $CO_2$ welding with 100% $CO_2$ gas is commonly used because of its cost and efficiency. Arc phenomena and spattering ratio of the $CO_2$ welding are influenced by various factors such as chemical compositions of welding wire, shielding gas, welding condition and welding power source etc.. Spattering ratio is predominantly influenced by the welding condition which determines a droplet transfer rode. In this study, arc phenomena and spattering ratio are investigated by using two type of FCW(titania type, semi-metal type). Then, the welding quality and optimum welding condition can be selected. From this study, the following results ware obtained; 1) In low current range(140A), FCW up to welding voltage(22V) resulted in a typical short circuit transfer, increase of spattering ratio and growth of spatter diameter. 2) In high current range(320A), the arc stability in titania FCW of a typical globular transfer is better than that of semi-metal FCW.

• Journal of the Korean Society of Manufacturing Technology Engineers
• /
• v.21 no.6
• /
• pp.860-864
• /
• 2012

The contact tip is higher the wear of resistance and the longer life are demanded to GMA welding process. In this study, four different contact tips with three different compositions by two wires were evaluated their wear resistance by measuring in every one hour the area of enlarged hole at the exit side during actual wleding. Experimental results clearly showed that the Cr-containing tips strengthened by precipitation hardening have much better resistance to wear than those made by work hardening. In addition, flux cored wire is excellent abrasion resistance test results showed. Based on these results, the domestic industry, the life of the contact tip to know will be used as basic data.

• Proceedings of the Korean Institute of Surface Engineering Conference
• /
• 1998.11a
• /
• pp.19-20
• /
• 1998

오버레이용접에 의한 표면개질기술(Weld Surfacing or Hardfacing Technology)은 내식성, 내 마모성, 또는 내열성을 갖는 합금의 용접재료를 모재 표면에 균일하게 용착(오버레이:Ovedayer)시킴으로써 목적하는 재료의 표면성질을 향상시키는 표면처리의 한 방법이으로써 1922년 Stoody가 Steel Tube에 Cr합금 분말을 충진한 용접봉을 제조하여 석유시추용 회전드릴의 선단 표면을 오버 레이 용접시켜 내마모성을 획기적으로 개선시킴으로써 이루어 졌다. 초기 오버레이 용접기술은 발전설비I 제철설비I 시벤트설비, 그리고 제지설비 등 주로 설비 부품들의 표면부 내마모성을 개선시키는 방향으로 주로 연구 개발이 이루어졌으나, 기술개발의 진전으로 탈황설비 둥의 표면부 내식성 향상, 연속주조롤 표면부의 내산화성, 내열피로성, 내마모 성 향상 둥을 위해 점차 산업전반에 널리 이용되고 있으며, 설비의 고도화 및 장수명화가 요구되 면서 본 기술의 중요성 또한 점차 부각되고 있다. 그림 1은 연강의 모재 위에 셀프쉴드플럭스코어드와이어(Self-Shield Flux Cored Wire:SS-FCW, 이하 55-FCW라 기술함)를 사용하여 오버레이 용접올 하는 장면을 도식적으로 나 타낸 것이다. 모재와 전극재인 용접봉(S5-FCW) 사이에서 아크가 발생되고, 아크열에 의해서 용접 봉 및 모재 일부가 용융되면서 모재 표면에 새로운 오버레이 표면층이 형성된다. 통상 오버레이 층의 1층 두께는 2-6mm 내외이며, 단층 혹은 다충 오버레이를 자유롭게 실시한다. 오버레이층의 물성은 아크열에 의한 모재로의 용입정도에 따라 1층부에서는 모재의 영향을 크게 받지만 오버레 이충 수가 증가된 3층부에서 부터는 전적으로 용접봉의 성분에 좌우된다. 사진 1은 연강(55-41)의 모재위에 크롬탄화물이 다량 함유된 고크롬 탄화물형 내마모재가 오버 레이된 내마모 복합강판 (wear plate)의 단면 미세조직 사진으로써 모재부와 오버레이충을 함께 보여주고 있다. 모재와 오버레이 충간의 경계면은 모재 일부가 용융된 후 웅고하면서 형성됨으로 인해서 도금이나 용사층과는 달리 매우 견고하게 결합되어 있다. 따라서 계면부의 탈락이라는 문 제점은 거의 없어 심한 응력을 받는 기계구조물 및 부품에도 본 기술은 널리 적용되고 있다. 그리고 사진 1에서 알 수 있는 바와 같이 모재와는 전혀 상이한 재료를 자유로이 선택하여 표면 유효층 일부만 오버레이시키며I 주조 및 단조가 불가능한 재료까지도 표면부에 오버레이 시킴으로 서 부품 및 설비의 제조에 있어 재료비의 절감과 제품의 수명이 획기적으로 개선될 수 있다. 그리고 최근에는 도금 빛 용사 둥과 같은 표면처리를 할 경우임의 소재 표면에 도금 및 용 사에 용이한 재료를 오버레이용접시킨 후 표면처리를 함으로써 보다 고품질의 표면층을 얻기위한 시도가 이루어지고 있다. 따라서 국내, 외의 오버레이 용접기술의 적용현황 및 대표적인 적용사례, 오버레이 용접기술 및 용접재료의 개발현황 둥을 중심으로 살펴봄으로서 아직 국내에서는 널리 알려지지 않은 본 기 술의 활용을 넓이고자 한다.