• Journal of the Korean Ceramic Society
• /
• v.39 no.2
• /
• pp.171-177
• /
• 2002

In this study, the vertical aligned carbon nanotubes was synthesized by DC bias-assisted Inductively Coupled Plasma Hot-Filament Chemical Vapor Deposition (ICPHFCVD). The substrate used CNTs growth was Ni(300 ${\AA}$)/Cr(200 ${\AA}$)-deposited one on glass by RF magnetron sputtering. R-F, DC bias and filament power during the growth process were 150 W, 80 W, 7∼8 A, respectively. The grown CNTs showed hollow structure and multi-wall CNTs. The top of grown CNT was found to Ni-tip that the CNT end showed to metaltip. The graphitization and field emission properties of grown was better than grown CNTs by ICPCVD. The turn-on voltage of CNT grown by DC bias-assisted ICPHFCVD showed about 3 V/${\mu}m$.

• New Physics: Sae Mulli
• /
• v.68 no.11
• /
• pp.1203-1207
• /
• 2018

In this study, silica nanowires were formed using silicon oxide films with different oxygen contents, and their microstructure and physical properties were compared with those of silica nanowires formed using Si wafers. The silicon oxide films were fabricated by using a plasma-enhanced chemical vapor deposition method. Silica nanowires were formed by thermally annealing silicon oxide films coated with nickel films as a catalyst. In the case of silicon oxide films having an oxygen content of approximately 50 at.% or less, the formation mechanism, microstructure, and physical properties of the nanowires were not substantially different from those of the silicon wafer. In particular, the uniformity of the thickness showed better behavior in the silicon oxide films. These results imply that silicon oxide films can be used as an alternative for fabricating high-quality silica nanowires at low cost.

• Proceedings of the Korean Vacuum Society Conference
• /
• 2011.02a
• /
• pp.57-58
• /
• 2011

III-V족 화합물 반도체의 일종인 InSb는 77 K에서 0.23 eV의 작은 밴드 갭을 가지며 높은 전하 이동도를 가지고 있기 때문에 대기권에서 전자파 흡수가 일어나지 않는 3~5 ${\mu}m$범위의 장파장 적외선 감지가 가능하여 중적외선 감지 소자로 이용되고 있다. 하지만 InSb는 밴드 갭이 매우 작기 때문에, 소자 제작시 누설전류에 의한 소자 특성의 저하가 문제시 되고 있다. 또한 다른 화합물 반도체에 비해 녹는점이 낮고, 휘발성이 강한 5족 원소인 Sb의 승화로 기판의 화학양론적 조성비(stoichiometry)가 변하기 쉬워, 계면특성 저하의 원인이 된다. 따라서 우수한 특성을 가지는 적외선 소자의 구현을 위해서, 저온에서 계면 특성이 우수한 고품질의 절연막 증착 연구가 필수적이다. 본 연구에서는 InSb 기판 위에 $SiO_2$, $Si_3N_4$의 절연막 형성시 증착온도의 변화에 따른 계면 트랩 밀도를 분석하였다. $SiO_2$, $Si_3N_4$ 절연막은 플라즈마 화학 기상 증착법(PECVD)을 이용하여 n형 InSb 기판 위에 증착하였으며, 증착온도를 $120^{\circ}C$부터 $240^{\circ}C$까지 변화시켰다. Metal oxide semiconductor(MOS) 구조 제작을 통하여, 커패시턴스-전압(C-V)분석을 진행하였으며, 절연막과 InSb 사이의 계면 트랩 밀도를 Terman method를 이용하여 계산하였다[1]. 또한, $SiO_2$와 $Si_3N_4$의 XPS 분석과 TOF-SIMS 분석을 통하여 계면 트랩 밀도의 원인을 밝혀 보았다. $120{\sim}240^{\circ}C$ 온도 범위에서 계면 트랩 밀도는 $Si_3N_4$의 경우 $2.4{\sim}4.9{\times}10^{12}cm^{-2}eV^{-1}$, $SiO_2$의 경우 $7.1{\sim}7.3{\times}10^{11}cm^{-2}eV^{-1}$ 값을 나타냈고, 두 절연막 모두 증착 온도가 증가할수록 계면 트랩 밀도가 증가하는 경향을 보였다. 그러나 모든 샘플에서 $Si_3N_4$의 경우, flat band voltage가 음의 전압으로 이동한 반면, $SiO_2$의 경우, 양의 전압으로 이동하는 것을 확인할 수 있었다. 계면 트랩 밀도 증가의 원인을 확인하기 위해서, oxide를 $120^{\circ}C$, $240^{\circ}C$에서 증착시킨 샘플을 XPS 분석을 통하여 깊이에 따른 성분분석을 하였고, 그 결과, $240^{\circ}C$에서 증착된 샘플에서 계면에서 $In_2O_3$와 $Sb_2O_3$ 피크의 증가를 확인하였다. 이는 계면에서 oxide양이 증가함을 의미하며, 이렇게 생성된 oxide는 계면 트랩으로 작용하므로, 계면 특성을 저하시키는 원인으로 작용함을 알 수 있었다. Nitride 절연막을 증착시킨 샘플은 TOF-SIMS 분석을 통해, 계면에서의 성분 분석을 하였고, 그 결과, $240^{\circ}C$에서 증착된 샘플에서 In-N, Sb-N, Si-N 결합의 감소를 확인하였다. 이렇게 분해된 결합들의 dangling 결합이 늘어 계면 트랩으로 작용하므로, 계면 특성을 저하시키는 원인으로 작용함을 알 수 있었다. 최종적으로, 소자특성을 확인 하기 위하여 계면 트랩 밀도가 가장 낮게 측정된 $200^{\circ}C$ 조건에서 $SiO_2$ 절연막을 증착하여 InSb 적외선 소자를 제작하였다. 전류-전압(I-V) 분석 결과 -0.1 V에서 16 nA의 누설 전류 값을 보였으며, $2.6{\times}10^3{\Omega}cm^2$의 RoA(zero bias resistance area)를 얻을 수 있었다. 절연막 증착조건의 최적화를 통하여, InSb 적외선 소자의 특성이 개선됨을 확인할 수 있었다.

• Proceedings of the Korean Institute of Electrical and Electronic Material Engineers Conference
• /
• 2007.11a
• /
• pp.333-334
• /
• 2007

Diamond-like carbon (DLC)박막은 높은 경도, 화학적 안정성, 높은 광 투과성을 가지고 있어, 공구강, 광학렌즈 및 플라스틱의 보호 코팅을 위해 응용되어진다. 본 연구에는 DLC 박막은 Silicon을 기반으로 하는 태양전지 반사 반지막으로 응용을 위해, 13.56 MHz RF 플라즈마 화학기상 증착 (RF-PECVD)법을 통해 합성되었다. DLC 합성 시 RF power는 150 W, 메탄 (CH4)가스의 유량은 6%~10% 조절되었다. 합성되어진 DLC 박막의 광학적 특성은 UV spectrometry, Ellipsometry를 사용하여 분석되었고, 경도는 Nano-indenter를 사용하여 측정되었다. 측정 결과 투과도와 굴절률 등의 광학적 특성은 탄소 조성비가 6%정도에서 가장 좋은 결과 값을 얻었으나, 물리적 특성인 경도는 탄소 조성비가 높을수록 증가하는 경향을 보였으며, Si기판과의 접착력은 32N 이상의 높은 값을 나타내었다. 결과로써, DLC 박막은 합성시 적절한 탄소 조성비를 통해 silicon을 기반으로 하는 태양전지 반사방지막으로 응용할 수 있다.

• Journal of the Microelectronics and Packaging Society
• /
• v.27 no.3
• /
• pp.77-81
• /
• 2020

Commercialization of flexible OLED displays, such as rollable and foldable displays, has attracted tremendous interest in next-generation display markets. However, during bending deformation, cracking and delamination of thin films in the flexible display panels are the critical bottleneck for the commercialization. Therefore, measuring mechanical properties of the fragile thin films in the flexible display panels is essential to prevent mechanical failures of the devices. In this study, tensile properties of the metal and ceramic nano-thin films were quantitatively measured by using a direct tensile testing method on the water surface. Elastic modulus, tensile strength, and elongation of the sputtered Mo, MoTi thin films, and PECVD deposited SiN_x thin films were successfully measured. As a result, the tensile properties were varied depending on the deposition conditions and the film thickness. The measured tensile property values can be applied to stress analysis modeling for mechanically robust flexible displays.

• Korean Journal of Materials Research
• /
• v.23 no.1
• /
• pp.47-52
• /
• 2013

Graphene has been synthesized on 100- and 300-nm-thick Ni/$SiO_2$/Si substrates with $CH_4$ gas (1 SCCM) diluted in mixed gases of 10% $H_2$ and 90% Ar (99 SCCM) at $900^{\circ}C$ by using inductively-coupled plasma chemical vapor deposition (ICP-CVD). The film morphology of 100-nm-thick Ni changed to islands on $SiO_2$/Si substrate after heat treatment at $900^{\circ}C$ for 2 min because of grain growth, whereas 300-nm-thick Ni still maintained a film morphology. Interestingly, suspended graphene was formed among Ni islands on 100-nm-thick Ni/$SiO_2$/Si substrate for the very short growth of 1 sec. In addition, the size of the graphene domains was much larger than that of Ni grains of 300-nm-thick Ni/$SiO_2$/Si substrate. These results suggest that graphene growth is strongly governed by the direct formation of graphene on the Ni surface due to reactive carbon radicals highly activated by ICP, rather than to well-known carbon precipitation from carbon-containing Ni. The D peak intensity of the Raman spectrum of graphene on 300-nm-thick Ni/$SiO_2$/Si was negligible, suggesting that high-quality graphene was formed. The 2D to G peak intensity ratio and the full-width at half maximum of the 2D peak were approximately 2.6 and $47cm^{-1}$, respectively. The several-layer graphene showed a low sheet resistance value of $718{\Omega}/sq$ and a high light transmittance of 87% at 550 nm.

• Composites Research
• /
• v.36 no.5
• /
• pp.342-348
• /
• 2023

There has been increasing demand for real-time monitoring of body and ambient temperatures using wearable devices. Graphene-based thermistors have been developed for high-performance flexible temperature sensors. In this study, the temperature coefficient of resistance (TCR) of monolayer graphene was controlled by coating polyethylenimine (PEI) on graphene surfaces to enhance its temperature-sensing performances. Monolayer graphene grown by chemical vapor deposition (CVD) was wet-transferred onto a target substrate. To facilitate the interfacial doping by PEI, the hydrophobic graphene surface was altered to be hydrophilic by oxygen plasma treatments while minimizing defect generation. The effect of PEI doping on graphene was confirmed using a back-gated field-effect transistor (FET). The CVD-grown monolayer graphene coated with PEI exhibited an improved TCR of -0.49(±0.03) %/K in a temperature range of 30~50℃.

• Proceedings of the Korean Vacuum Society Conference
• /
• 2010.02a
• /
• pp.123-123
• /
• 2010

3족 질화물계 물질은 발광다이오드와 같은 광전자소자적용에 있어서 매우 우수한물 질이다.일반적으로, GaN 에피 성장에 있어서 저온 중간층을 삽입한 2 단계 성장 방법은 낮은 결함밀도와 균일한 표면을 얻기 위해 도입된 기술이다. 특히 AlN 중간층은 GaN 중간층과 비교하였을 때 결정성뿐만 아니라 높은 온도에서의 열적안정성, GaN 기반의 자외선 검출기서의빛 흡수 감소 등의 장점을 가지고 있다. 또한 패턴 사파이어 기판위 GaN 에피 성장은 측면성장 효과를 통해 결함 밀도 감소와 광 추출 효율을 향상시키는 것으로 알려져 있다.또한 열응력으로 인한 기판의 휨 현상은 박막성장중 기판의 온도 분포를 불균일하게 만드는 원인이 되며 이는 결국 박막 조성 및 결정성의 열화를 유도하게 되고 최종적으로 소자특성을 떨어 뜨리는 원인이 되는데 AlN 중간층의 도입으로 이것을 완화시킬 수 있는 효과가 있다. 하지만, AlN 중간층이 패턴된 기판 위에 성장시킨 GaN 에피층에 미치는 영향은 명확하지 않다. 본 연구팀은 일반적인 c-plane 사파이어 기판과 플라즈마 건식 에칭을 통한 렌즈 모양의 패턴된 사파이어 기판을 이용해서 AlN 중간층과 GaN 에피층을 유기금속 화학기상증착법으로 성장하였다. 특히, 렌즈 모양의 패턴된 사파이어 기판은 패턴 모양과 패턴 밀도가 성장에 미치는 영향을 연구하기 위해 두가지 패턴의 사파이어 기판을 이용하였다. AlN 중간층 두께를 조절함으로써 최적화된 GaN 에피층을 90분까지 4단계로 시간 변화를 주어 성장 양상을 관찰한 결과, GaN 에피박막의 성장은 패턴 기판의 trench 부분에서 시작하여 기판의 패턴부분을 덮는 측면 성장을 보이고있다. 또한 TEM과 CL을 통해 GaN 에피박막의 관통 전위를 분석해 본 결과 측면 성장과정에서 성장 방향을 따라 옆으로 휘게 됨으로 표면까지 도달하는 결정결함의 수가 획기적으로 줄어드는 것을 확인함으로써 고품질의 GaN 에피층을 성장시킬 수 있었다. 그리고 패턴밀도가 높고 모양이 볼록할수록 측면 성장 효과로 인한 결정성 향상과 난반사 증가를 통한 임계각 증가로 광추출 효율이 향상 되는 것을 확인할 수 있었다. 이러한 결과를 바탕으로 최적화된 AlN 중간층을 이용하여 패턴 기판위에서 고품질의 GaN 에피층을 성장시킬 수 있었다.

• Journal of the Korean Vacuum Society
• /
• v.20 no.1
• /
• pp.42-49
• /
• 2011

We deposited $SiN_x$ thin films by using PECVD technique at $200^{\circ}C$ with various flow ratios of the $SiH_4/N_2$ gases. The photoluminescence measurements revealed that the maximum emission wavelength shifted to long wavelength as the ratio increased, however, positions of the several peak wavelengths, such as 1.9, 2.2, 2.4, and 3.1 eV, were independent on the ratio. Changes of the photoluminescence spectra were measured in the $N_{2}-$, $H_{2}-$, and $O_2$-annealed films. The luminescence intensities increased after the annealing process. In particular, the maximum emission wavelength shifted to short wavelength after $H_{2}-$ or $O_2$-annealing. But there were still several peaks on the spectra of all annealed films, several peak positions remained to be unchanged after the annealing. As for the light emission mechanism, we have considered the defect states of the Si- and N- dangling bonds in the $SiN_x$ energy gap, so that the energy transitions from/to the conduction/valence bands and the defect states in the gap were attributed to the light emission in the $SiN_x$ films. The experimental results point to the possibility of a Si-based light emission materials for flexible Si-based electro-optic devices.