• Journal of the Korean Chemical Society
• /
• v.37 no.4
• /
• pp.416-422
• /
• 1993

As a result of adsorbing phthalocyanine (metal free, ${\alpha}\;and\;{\beta}$-Cu) on zinc oxide in aqueous solution using nonionic surfactant, all of the added dye was adsorbed and Na salt of sulfonated phthalocyanine showed the Langmuir monolayer adsorption. To analyze the effect of adsorption on zinc oxide, photovoltage was measured using surface photovoltmeter. The high photovoltaic effect was observed at intrinsic wavelength of zinc oxide and wavelength of adsorbed phthalocyanine dye. Metal free phthalocyanine, ${\alpha}$-copper phthalocyanine and ${\beta}$-copper phthalocyanine showed the highest photovoltaic effect when the percentage of coverage (${\theta}_{BET}$) for zinc oxide is about 80, while sulfonated phthalocyanine showed the highest photovoltaic effect when the percentage of coverage for zinc oxide is about 30.

• Korean Journal of Materials Research
• /
• v.10 no.1
• /
• pp.7-14
• /
• 2000

The object of this study was to improve electrophotographic photoreceptor using metal free-phthalocyanine dye sensitized system. In here a various types of metal free-phthalocyanine and polymers and hydrazone were used as charge generation material(CGM) and binder, respectively, and also the hydrazone derivative or zinc complex was used as charge transport material(CTM). It was found that $x-H_2Pc$ showed the highest sensitivity among the ${\alpha}-$, ${\beta}-$ and x- metal free-phthalocyanine($x-H_2Pc$) as CGM. The photoreceptor made by $x-H_2Pc$ and hydrazone derivative as CGM and CTM, respectively, showed the highest ratio of dark decay having 73.1% and the good sensitivity of $1.50lux{\cdot}sec$ compared to other photoreceptors.

• Electrical & Electronic Materials
• /
• v.7 no.5
• /
• pp.409-416
• /
• 1994

A double layered photoreceptor using phthalocyanine dye was made by dip-coating method. The under cutting layer(UCL) was coated with A1$\_$2/O$\_$3/ or polyamide, and the charge generation layer(CGL) was formed by .tau.-type metal-free phthalocyanine. The oxadiazole was used as a charge transport layer(CTL) and polycarbonate and poly(vinyl butyral) was employed as a host polymer. The .tau.-H$\_$2/Pc had an absorption peak around 780nm, which coincided with the emitting wavelengths of GaAlAs diode lasers. Maximum charge acceptance of CTL that gives thickness of 12.mu.m was -900V by corona charge of -6.0kV. In photo-induced discharge measurements, residual potential was less than -20V and sufficient for ordinary use, and sample films using of poly(vinyl butyral) was showed good charge retention. In printing test, drum that was employed polycarbonate as a host polymer showed the good print quality.

• Korean Journal of Materials Research
• /
• v.7 no.5
• /
• pp.403-410
• /
• 1997

본 연구는기존의 보고에서 보다 감광화효율을 더욱 향상시키기 위하여 결정형이 다른 전하발생물질 (CGM:Charge Generation Material)과 전하수송물질(CTM:Charge Transport Material)을 사용하여 감광체를 만들었고, 이들의 정전특성을 비교검토하였다. 전하발생물질로서 결정형이 다른 $\alpha$-, $\beta$-, x-형 무금속 프탈로시아닌 (H$_{2}$Pc)을 사용한 결과, x-H$_{2}$Pc를 사용한 감광체의 감도는 E$_{1}$2/의 값이 2.62 $\mu$J/$\textrm{cm}^2$로 가장 두수하게 나타났다. 전하발생층(CGL:Charge Generation Layer)에 첨가되는 CGM-CTM, CGM-CTM-ZnO로 구성된 감광체보다 전하발생층에 전하발생계만으로 구성된 감광체의 경우의 전하유지율 (80%) 및 감도(E$_{1}$2/=2.83$\mu$J/$\textrm{cm}^2$)면에서 우수함을 보여주었다. 한편 binder로서 PVB-co-PVA-co-PVA$_{c}$[poly(viny1 butyral-co-viny1 alcohol-co-viny1 acetate)]를 사용했을 때는, CGM-CTM으로 구성된 감광체보다 CGL에 CGM-CTM으로 구성된 감광체의 경우의 전하유지율(71%) 및 감도(E$_{1}$2/=2.62$\mu$J/$\textrm{cm}^2$)면에서 우수함을 보여주었다.