• 한국전기전자재료학회논문지
• /
• 제11권10호
• /
• pp.842-848
• /
• 1998

The stability of paraseodymium-based zinc oxide varistor consisting of Zn-Pr-Co-Cr-Y oxide was investigated according to yttria additives under different stress conditons, such as 0.8V\ulcorner\ulcorner/373K/12h and 0.85V\ulcorner\ulcorner/393K/12h. Wholly, all varistor after the stress showed nearly symmetric and stable I-V characteristics. Particularly, in the case of 2.0mol% and 4.0mol% yttria-added varistor showing a good I-V characteristics, the varation rate of varistor voltage were less 1% and that of nonlinear coefficient were about degree of 5%, and what is remarkable, leakage current with increasing stress time during the applied stress was almost constant. It the light of these facts, it is estimated that varistor constituents having 2.0mol% and 4.0mol% yittria, respectively, will be utilized to various application fields.

• 한국전기전자재료학회:학술대회논문집
• /
• 한국전기전자재료학회 1999년도 춘계학술대회 논문집
• /
• pp.312-316
• /
• 1999

I-V characteristics of Praseodymium-based ZnO varistor doped with $Nd_2O_3$ in the range 0.0-2.0mol% sintered at 130$0^{\circ}C$ and 135$0^{\circ}C$ were investigated. In the all sides, ZnO varistors sintered at $1300^{\circ}C$ exhibited much better varistor characteristics than that at 135$0^{\circ}C$. All ZnO varistors doped with $Nd_2O_3$ sintered at $1300^{\circ}C$ exhibited good varistor characteristics but particularly ZnO varistor doped with l.Omol% $Nd_2O_3$ exhibited the best characteristics, which the nonlinear is 65.2 and the leakage current is 4.5pA. It is estimated that ZnO varistor doped with l.Omol% $Nd_2O_3$ will begin to be sufficiently used as basic composition to fabricate a good varistor.

• 한국전기전자재료학회논문지
• /
• 제18권10호
• /
• pp.896-901
• /
• 2005

The microstructure and electrical properties of praseodymium-based zinc oxide varistors were investigated at various cobalt oxide contents in the range of $0.5{\~}5.0 mol\%$. The ceramic density increased in the range of $5.25{\~}5.55 g/cm^3$ with increasing cobalt oxide content. The varistor doped with cobalt oxide of $1.0 mol\%$ exhibited the highest nonlinearity, with 66.6 in nonlinear exponent and 1.2 $\mu$A in leakage current. The donor concentration, density of interface states, and tamer height were in the range of $(1.06{\~}1.69){\times}10^{18}/cm^3$, $(3.11 {\~}3.56){\times}10^{12}/cm^2$, and 0.80${\~}$1.07 eV, respectively.