• Proceedings of the Korean Institute of Surface Engineering Conference
• /
• 2001.11a
• /
• pp.24-25
• /
• 2001

• Journal of the Korea institute for structural maintenance and inspection
• /
• v.23 no.6
• /
• pp.18-25
• /
• 2019

The cracks occurred during service life of concrete structure should be considered in durability design, because of the concrete's material property which is weak in tensile strength. In this study, the fly ash concrete mixtures considering 2 levels of strength is designed and outdoor exposure tests are conducted for those concrete specimens. The exposure environment is set to a splash zone, and in order to evaluate the effect of crack width on the behavior of chloride diffusion, the crack width of up to 1.0 mm is generated at intervals of 0.1 mm at each concrete mixture. After that, apparent chloride diffusion coefficient and surface chloride contents are deducted considering 3 levels of exposure periods(180 days, 365 days, 730 days). The diffusion coefficients of two types of mixture increase with the increase of crack width, and the diffusion coefficients decrease with the increase of exposure periods. In addition, the effect of the crack width on the diffusion coefficient is reduced as the exposure periods increase, which is attributed to the extra hydrate by chloride ion reducing the diffusivity of concrete. The behavior of the surface chloride contents does not significantly change by the increase in crack width, compared to the behavior of apparent chloride diffusion coefficient. Also, In the high strength FA concrete mixture, the surface chloride contents are 78.9 % ~ 90.7 % than the normal FA strength concrete mixture. Thus, Surface chloride contents have correlation with the strength of concrete.

• Transactions of the Korean Society of Mechanical Engineers A
• /
• v.40 no.7
• /
• pp.637-646
• /
• 2016

This study is to investigate the influence of hydrogen attack and UNSM on fatigue behaviors of the Inconel 718 alloy. The decrease of the fatigue life between the untreated and the hydrogen attacked material is 10-20%. The fatigue lives of hydrogen attacked specimen decreased without a fatigue limit, similar to those of nonferrous materials. Due to hydrogen embrittlement, about 80% of the surface cracks were smaller than the average grain size of $13{\mu}m$. Many small surface cracks caused by the embrittling effect of hydrogen attack were initiated at the grain boundaries and surface scratches. Cracks were irregularly distributed, grew, and then coalesced through tearing, leading to a reduction of fatigue life. Results revealed that the fatigue lives of UNSM-treated specimens were longer than those of the untreated specimens.

• Composites Research
• /
• v.22 no.4
• /
• pp.33-40
• /
• 2009

Fiber orientation effects on the impact surface fracture of the glass plates coated with the glass fiber/epoxy lamina layer were investigated using a small-diameter steel-ball impact experiment. Four kinds of materials were used: soda-lime glass plates, unidirectional glass fiber/epoxy layer(one ply, two plies)-coated, crossed glass tiber/epoxy layer (two plies)-coated glass plates. The maximum stress and absorbed fracture energy were measured on the back surface of glass plates during the impact. With increasing impact velocity, various surface cracks such as ring, cone, radial and lateral cracks appeared near the impacted site of glass plates. Cracks in the plate drastically diminished by glass fiber coating. The tiber orientation guided the directions of delamination and plastic deformation zones between the tiber layer and the glass plate. Impact surface-fracture indices expressed in terms of the maximum stress and absorbed energy could be used as an effective evaluation parameter of the surface resistance.

• Journal of the Korean Society for Nondestructive Testing
• /
• v.21 no.1
• /
• pp.32-38
• /
• 2001

Although the ultrasonic method has been developed and used widely in the fields, it has been used only for measuring the defect size and thickness loss. In this study, the relationship between surface wave attenuation through micro-crack growth and variation of velocity under repeated cyclic loading has been investigated. The specimens are adopted from 2.25Cr-1Mo steel, which is used for power plant and pipeline system, and have dimensions of $200{\times}40{\times}4mm$. The results of ultrasonic test with a 5MHz transducer show that surface wave velocity gradually decreases from the point of 60% of fatigue life and the crack length of 2mm with the increasing fatigue cycles. From the results of this study, it is found that the technique using the ultrasonic velocity change is one of very useful methods to evaluate the fatigue life nondestructively.

• Journal of the Korea Institute of Building Construction
• /
• v.23 no.2
• /
• pp.197-207
• /
• 2023

Concrete is a widely used material due to its excellent compressive strength and durability. However, depending on the surrounding environment and the characteristics of the materials used in the construction, various defects may occur, such as cracks on the surface and subsidence of the structure. The detects on the surface of the concrete structure occur after completion or over time. Neglecting these cracks may lead to severe structural damage, necessitating regular safety inspections. Traditional visual inspections of concrete walls are labor-intensive and expensive. This research presents a deep learning-based semantic segmentation model designed to detect cracks in concrete walls. The model addresses surface defects that arise from aging, and an image augmentation technique is employed to enhance feature extraction and generalization performance. A dataset for semantic segmentation was created by combining publicly available and self-generated datasets, and notable semantic segmentation models were evaluated and tested. The model, specifically trained for concrete wall fracture detection, achieved an extraction performance of 81.4%. Moreover, a 3% performance improvement was observed when applying the developed augmentation technique.

• Journal of the Korean Society of Fisheries and Ocean Technology
• /
• v.36 no.2
• /
• pp.147-154
• /
• 2000

실온 대기 중에서 탄소강배관(STS370)의 피로시험을 행하였다. 배관에는 외부결함을 인공적으로 상정하여, 피로균열진전 및 관통의 거동, 균열형상, 누설 및 파단수명, 균열개구변위를 실험과 이론의 양면으로부터 비교·검토하였다. 특히, 배관의 벽두께 관통후에 있어서의 응력확대계수를 평가하기 위하여 새로운 식을 제안하였다. 피로균열이 관벽을 관통하기 전에 있어서는 판모델에 의한 Newman-Raju의 응력확대계수 평가식을 이용하므로서 aspect비와 누설수명 등 관통전의 피로균열성장거동을 평가할 수 있음을 나타내었다. 또한, 피로균열이 관벽을 관통한 후에 있어서는 본 논문에서 제안한 배관모델에 의한 응력확대계수의 평가식을 이용하여 관통후의 균열형상, 파단수명 및 균열개구변위 등 관통후의 피로균열성장거동을 평가하였다.

• Transactions of the Korean Society of Mechanical Engineers
• /
• v.16 no.4
• /
• pp.819-827
• /
• 1992

Investigations of the fatigue damage of roughing mill roll and experimentally. By the computer simulation for analysing the stresses on the roll surface and experimental hot rolling, the following results were drawn : The crakcs observed on the roll surface were initiated thermally in the initial stage of the rolling and propagated by repeated thermal and bending stresses. The size of the roll surface cracks smaller than 4.87mm could avoid the occurrence of tiny scab, surface defect of hot steel strip. Since the size of surface cracks observed on the roughing mill roll was very small, the fatigue damage of roll surface was found not to be the major factor for the formation of the scab.

• Journal of the Korea Concrete Institute
• /
• v.21 no.3
• /
• pp.337-345
• /
• 2009

The purpose of this study is to investigate the shear strengthening effectiveness of the beams strengthened with near surface mounted (NSM) and external bonded (EB) CFRP strips. A total of nine concrete beams were made and tested. From this study, it was found that the shear stiffness and strength of the beams strengthened with NSM and EB strips were significantly improved compared to the control beam. Failure of the beam strengthened with NSM and EB strips was initiated by shear cracks, propagated diagonally to the adjacent epoxy grooves without crossing the epoxy and finally sudden diagonal crack connecting the point of application of load and flexural crack was occurred. For the beam strengthened combined with NSM and EB CFRP strips, the tensile strains in the NSM CFRP strips were observed in the range of 0.35% to 0.45% and strains with EB strips were measured about 0.3%.

• Proceedings of the Korean Institute of Industrial Safety Conference
• /
• 2000.11a
• /
• pp.423-428
• /
• 2000

콘크리트구조물은 비교적 경제적인 시공이 가능하며 구조물의 수명 또한 안정적인 관계로 널리 사용되어 왔다. 그러나 최근 콘크리트의 고강도화 및 설계의 최적화에 따른 부재단면의 최소화 경향, 새로운 공법의 적용 등에 따른 균열문제가 빈번하게 대두되고 있는 실정이다. 특히 다양한 토목구조물중 매스콘크리트구조물, 벽체구조물 등과 같은 종류에서의 균열문제가 자주 언급되고 있으며, 균열에 따른 심리적 불안감과 콘크리트 내구성의 저하, 궁극적으로는 구조물의 안전성에 대한 불안심리를 가증 시키고 있다.(중략)