• Korean Chemical Engineering Research
• /
• v.48 no.1
• /
• pp.33-38
• /
• 2010

A microfluidic system has been developed using biomaterial for the measurement of cupric ion concentration. The cell-membrane-mimicking bilayer lipid membrane(BLM)-coated silver electrode was used for the sensing of cupric ion concentration. The silver-supported BLM could increase its stability. A silver-supported bilayer lipid membrane(s-BLM) was easily obtained using its self-assembling characteristics by immersing silver wire into lipid(phosphatidylcholine; PC) solution and then dipping into aqueous KCl solution. These s-BLMs were used to determine the relationship between $Cu^{2+}$ concentration and current crossing s-BLM. Their relationship showed high linearity and reproducibility. The calibration curve was constructed to express the relationship between $Cu^{2+}$ concentration and current in the $Cu^{2+}$ concentration range of 10 and $130{\mu}M$. This calibration curve was used to measure $Cu^{2+}$ concentration in an unknown sample. Microfluidic system with s-BLM was made of PDMS(polydimethyl siloxane) using typical soft photolithography and molding technique. This integrated system has various functions such as activation of the silver surface without cutting silver wire, coating of BLM on silver surface, injection of KCl buffer solution, injection of $Cu^{2+}$ sample and measurement of $Cu^{2+}$ concentration in the sample.

• Korean Journal of Crystallography
• /
• v.9 no.2
• /
• pp.85-91
• /
• 1998

고주파 마그네톤 스퍼터법을 이용하여 ZnO 박막 증착시, 증착 조건, 증착 후 표면스퍼터 및 열처리 분위기에 따른 ZnO 박막의 표면조직과 전기적 특성을 분석하였다. ZnO 박막의 면저항은 500℃에서 행한 증착후 열처리의 분위기에 따라 수 GΩ/ㅁ에서 수 KΩ/ㅁ까지 변하였다. 이들 박막의 전하운반자 농도는 1015∼1018/㎤이었으며, 이동도는 10∼40㎠Vsec이었다. 특정한 스퍼터 조직에서 박막의 표면을 스퍼터할 경우 박막 표면적이 증가하였으며, 이러한 박막의 분위기 열처리에 민감한 반응을 보였다. 증착한 박막과 증착후 열처리한 박막의 화학조성 비교를 통하여, 박막의 원자결함 유형 및 전기적 특성을 미치는 이들의 영향에 관한 고찰을 하였다.

• Proceedings of the KIEE Conference
• /
• 2005.07c
• /
• pp.1957-1959
• /
• 2005

표면이 도핑된 SOI RESURF LDMOSFET에 대해 표면 도핑의 깊이에 따른 항복전압 및 순방향 특성을 분석하였다. 표면 도핑영역의 깊이를 $0.5{\sim}2.0{\mu}m$까지 변화시켜가며 항복전압의 변화와 온-저항의 변화를 시뮬레이션 하였다. 표면 도핑영역의 깊이에 따라 항복전압은 $73V{\sim}138V$까지 변화하였으며, 온-저항도 $0.18{\sim}0.143{\Omega}/cm^2$까지 변화하였다. 항복전압은 표면 도핑 영역의 깊이가 $1.5{\mu}m$때 138V로 가장 높게 나타났으며, 동일한 에피 영역의 농도를 사용한 기존의 소자와 비교하였을 때 약 22.1%의 항복전압의 증가를 나타냈으며, 온-저항값은 약 21.8%정도 감소하였다.

• Proceedings of the Korean Society of Soil and Groundwater Environment Conference
• /
• 1999.04a
• /
• pp.94-96
• /
• 1999

충북 단양에 위치한 조일 광산에서 채취한 구리와 아연으로 오염된 광미(광산 폐기물로서 금속 추출 후 남은 찌꺼기)를 효율적으로 처리하기 위한 생물학적 용출기법(bioleaching) 에서 기본 배지 조성(9K medium)을 변화시켜 미생물의 표면 특성을 측정하고 미생물 표면 특성이 용출 효율에 미치는 영향을 관찰하였다. 인을 첨가하지 않았을 때 소수성 값은 62.5％, 질소원 농도가 45mM일 때의 소수성 값은 66.7%로 미생물 표면 특성이 가장 소수성인 특성을 가지고 있었으며, 구리와 아연의 용출 효율도 가장 높게 나타나는 상관 관계를 나타냈다. 또한 광미에 부착된 미생물의 양을 측정해 본 결과, 미생물 표면 특성이 소수성일수록 광미에 부착된 미생물의 양도 많다는 것을 알 수 있었다.

• Proceedings of the Korean Institute of Surface Engineering Conference
• /
• 2013.05a
• /
• pp.174-174
• /
• 2013

현재 자동차 강판 시장에서는 승객들의 안전 확보와 연비 향상을 위하여 자동차 강판의 경량화 및 고장력화가 급속히 진행되고 있다. 더불어 소비자는 더욱 아름답고 멋있는 외관을 추구하면서 정교한 디자인이 가능할 수 있도록 높은 성형성을 갖는 강판에 대한 요구도 또한 증대되고 있다. 따라서 강도와 성형성을 동시에 확보할 수 있는 DP형, TRIP형 등의 다양한 컨셉을 갖는 변태강화형 고장력강에 대한 개발 요구가 점점 심화되고 있으나 이들 고장력강의 상 제어를 위하여 첨가된 Si, Mn등의 성분들이 표면에 안정한 산화물을 형성하기 때문에 이러한 고장력강은 표면 품질이 열위한 것으로 보고 되고 있다. 따라서 기존 연구에서는 열처리중 표면으로 확산되어 올라오는 Si, Mn 산화물의 저감을 위하여 분위기 중 산소농도나 노점등을 조절하거나, 산화전처리, 선도금처리 등을 통하여 Si, Mn 의 표면 선택산화를 제어하여 도금 결함을 최소화하려는 연구가 많이 진행되고 있다. 그러나 이러한 연구들은 대부분 강판 표면에서의 산화/환원의 반응에 대한 분위기 요인을 제어하는 연구들이며 실제 Si, Mn등의 산화성 원소들이 어떠한 조건에서 어떠한 경로들을 통해서 이동하여 표면으로 올라오는지에 대한 연구는 부족한 상황이다. 따라서 본 연구에서는 산화성 원소들의 표면 확산 거동에 대한 고찰을 위하여 다양한 열처리 온도 조건을 통한 표면 도금성 경향, 합급화 경향 및 표면 분석결과를 바탕으로 확산 거동에 대한 경향을 밝히고자 하였다.

• Journal of Radiation Protection and Research
• /
• v.32 no.3
• /
• pp.97-104
• /
• 2007

The corelation between the indoor volume and the measured radon concentration has been analyzed by comparing the radon concentration and the indoor volume of apartment rooms in Jeonju City. We also measured the annual exposure dose based on the variation in indoor radon concentration over time. To do this, we took 8 larger rooms and 8 smaller rooms of apartment, respectively, as a sample. The average volume of the larger rooms and that of the smaller rooms were $31.59\;m^3$ and $16.82\;m^3$, respectively. The average radon concentration of the larger rooms and that of the smaller rooms turned out to be $71.73\;Bq/m^3$ and $108.51\;Eq/m^3$, respectively. indicating that indoor volume is in inverse proportion to the radon concentration, i.e., the bigger the ratio of the surface area/volume, the higher the indoor radon concentration. From the measurement of the variation in indoor radon concentration over time fur a single day, the average intraday radon concentration variation was found to be about $46.8\;Bq/m^3$. The highest level of concentration ($114.5\;Bq/m^3$) was measured between 8 and 10 AM and the lowest level of concentration ($67.7\;Bq/m^3$) between 2 and 4 PM. The annual exposure dose turned out to be in the range of 0.3 mSv/yr to 2.16 mSv/yr, showing that the dose in some apartments exceeded 1.3 mSv/yr, the numerical value presented by the United Nations Scientific Committee on the Effects of Atomic Radiation (UNSCEAR).

• Journal of Adhesion and Interface
• /
• v.12 no.1
• /
• pp.26-33
• /
• 2011

Phosphoric acid treatments were conducted to improve the adhesion property of polyketone film to rubber. The effects of phosphoric acid treatments were characterized by using a contact angle analyzer and a XPS (X-ray photoelectron spectroscopy). Morphological changes were observed by using a scanning electron microscope (SEM) and an atomic force microscope (AFM) as the acid treatment condition varied in concentration and time. The contact angle was found to significantly decrease with the acid treatment. According to the XPS, increased wettability was attributed to the inclusion of oxygen containing groups such as hydroxyl, carbonyl and carboxyl by acid treatments. Cracks and pores were produced on the polyketone film surface and thus, roughness increased with the acid treatment. Interfacial adhesion strength between polyketone and natural rubber was largely improved by acid treatment due to the increased wettability and roughness of the polyketone surface. However, the higher level of acid treatment caused the degradation of the polyketone surface, and thus, its interfacial adhesion consequently decreased.

• Proceedings of the Korean Institute of Electrical and Electronic Material Engineers Conference
• /
• 2004.11a
• /
• pp.481-484
• /
• 2004

다중 채널 전극 위에 세포를 성장시켜 전극면을 통해 검출되는 신경 신호의 손실을 줄이고 주파수의 변형을 줄이기 위해서 전극과 전해질의 사이의 impedance를 줄이는 것이 바람직하다. 전하 이동을 증대시키기 위해서는 낮은 impedance가 요구되며 이를 위한 전극의 개선 방안으로 전극면이 증착될 기판의 표면을 거칠게 하여 결과적으로 전극면의 표면적을 넓히는 방법을 모색하였다. 기판으로 사용되는 glass(Pyrex#7740)의 구성 물질 중에서 4%를 차지하는 $N^+$ 이온을 황산 용액으로 표면 처리하여 제거함으로써 매끈한 표면을 거칠게 하여 표면적을 넓힐 수 있다. 기판으로 사용되는 glass (pyrex#7740) $1cm{\times}1cm{\times}0.05cm$를 50%, 95% 농도의 황산 용액 내에서 각각 30분, 60분 동안 상온에서 표면처리를 진행하였다. AFM을 이용하여 표면을 관찰한 결과 황산 용액 95%에서 30분간 표면 처리를 진행한 시편에서 최대 $4000{\AA}$정도의 조도를 얻었다. 이후 동일 시편에 대해 전극으로 사용될 Ti/Au를 각각 $500{\AA}/2500{\AA}$ 증착 후 사진식각 공정으로 MEA(Multi-channel electrode array)를 제작하여 impedance를 측정한 결과, 표면 처리 후 impedance가 70% 개선되었음을 측정하였다.

• Journal of the Mineralogical Society of Korea
• /
• v.17 no.2
• /
• pp.157-168
• /
• 2004

The surface chemical properties of aqueous kaolinite and halloysite were studied using a potentiometric titration experiment and a computer program FITEQL3.2. Among the surface complexation models a constant capacitance model was selected for this study. The 2 sites - 3 p $K_{a}$ s model, in which the surfaces were assumed to have tetrahedral and octahedral sites, was reasonable for the description of the experimental data. The surface charges of both minerals were negative above pH of 4. The higher the pH, the lower the proton surface charge densities of both minerals. The ≡ $SiO^{[-10]}$ site played an important role in cation adsorption in acid and neutral pH range; whereas the ≡ Al $O^{[-10]}$ site was in an alkaline pH range. The optimized intrinsic constants of kaolinite, p $K_{a2(Si)}$$^{int}$, p $K_{al(Al)}$$^{int}$ and p $K_{a2(Al)}$$^{int}$ were 4.436, 4.564, and 8.461 respectively, and those of halloysite were 7.852, 3.885, and 7.084, respectively. The total Si and Al surface sites concentrations of kaolinite were 0.215 and 0.148 mM, and those of halloysite were 0.357 and 0.246 mM. The ratio of Si and Al surface site densities ([≡SiOH]:[≡AlOH]) of both minerals was 1 : 0.69. The total surface site density of kaolinite, 3.774 sites/n $m^2$, was 1.6 times larger than that of halloysite, 2.292 sites/n $m^2$./TEX>.

• Korean Journal of Fisheries and Aquatic Sciences
• /
• v.24 no.5
• /
• pp.345-355
• /
• 1991

In order to effectively utilize the by-products of sea-food, the utilization of enzyme-modified flounder(Limanda aspera) skin gelatin as an emulsifier was investigated. In the experiment, the gelatin was extracted from the flounder skin with the heat-treatment at $60^{\circ}C$ and in pH 5.0 for 3 hrs with four volumes of distilled water and emulsifiers were enzymatically modified L-leucine alkyl esters$(L-leucine-OC_n$ : n= 2, 4, 6, 8 and 10) to the gelatin$(EMFSG-C_2,\;EMFSG-C_4,\;EMFSG-C_6,\;EMFSG-C_8,\;EMFSG-C_{10})$ for improving the functional properties such as emulsifying activity, emulsifying viscosity, whippability, electric conductivity, critical micelle concentration and interface tension, etc. Also, the functional properties of the L-leucine alkyl ester modified gelatins were compared with those of Tween-60 as reference. Molecular weights of the enzymatically modified flounder skin gelatin(EMFSG) were 20.5kDa. in $EMFSG-C_2.\;19.5 kDa.\;in\;EMFSG-C_4\;and\;16.5kDa.\;in\;EMFSG-C_6,\;EMFSG-C_8$ and $EMFSG-C_{10}$. respectively. Emulsifying activity and emulsifying viscosity in the modified gelatins were risen with increase of carbon number of the introduced L-leucine alkyl esters. Among the modified gelatins, $EMFSG-C_6$ exhibited the highest emulsifying stability and foaming stability, whereas $EMFSG-C_8$ showed the highest whippability. The electric conductivities of the all $EMFSG-C_n$ were linearly risen to critical micelle concentration(CMC) , therefore $EMFSG-C_{10}$ exhibited the lowest CMC value and interface tension, and dense particles in the microscopic observation. In conclusion, the best quality in functional properties was assured on $EMFSG-C_{10}$.