• Polymer(Korea)
• /
• v.32 no.4
• /
• pp.353-358
• /
• 2008

Maleated ethylene-propylene-diene terpolymer (MEPDM) was prepared from solution polymerization of EPDM and maleic anhydride. MEPDM-grafted-poly (dimethylsiloxane) (PDMS) copolymer (MEPDM-g-PDMS) was prepared from copolymerization of MEPDM with $\alpha$,$\omega$-hydroxyl group terminated PDMS. The MEPDM-g-PDMS was compounded with HDPE and 4-ethoxybenzoic acid modified MWCNT at $180^{\circ}C$ and positive temperature coefficient (PCT) behavior of the MWCNT composite was investigated. Surface modification of MWCNT enabled it to be more uniformly dispersed in polymer matrix and decreased aggregation of particles. Electrical resistivity of the composite was abruptly increased at melting temperature and PTC intensity of 2.3 was obtained at 15% loading of surface modified CNT.

• Polymer(Korea)
• /
• v.27 no.6
• /
• pp.589-595
• /
• 2003

Unsaturated polyester (UP) nanocomposite with montmorillonite (MMT) which contains different types of organic modifiers far nano-filler have been prepared to investigate the effect of chemical structure of organic modifiers and mixing time of all components on properties of products. It was found that the morphology and various physical properties of UP/MMT nanocomposites were influenced by properties of organic modifiers of MMTs. It was also confirmed that the content of MMT does not significantly affect properties of UP/MMT nanocomposites.

• Polymer(Korea)
• /
• v.30 no.6
• /
• pp.532-537
• /
• 2006

In order to successfully meet the environmental and recycling problems, natural polymer and their derivatives are recognized as a promising biodegradable material. In this study, the biodegradable composites of cellulose diacetate and starch were prepared, and their physical and thermal properties were investigated. For the melting processing, triacetine was added as a plasticizer into the composites. The processability of cellulose diacetate was further enhanced by increasing the amount of starch in the composites. The tensile stress and Young's modulus were decreased and elongation was increased with increasing the amount of starch in them. A $T_g$ value was decreased with increasing the amount of starch in the composites. Also, the morphology of the composites were observed with the SEM.

• Polymer(Korea)
• /
• v.34 no.2
• /
• pp.144-149
• /
• 2010

Ag/polystyrene(PS) nanocomposites were prepared by in situ reduction of silver 2-ethylhexylcarbamate (Ag-CB) complex and follwing radical polymerization only by heating at 110 $^{\circ}C$. In contrast to this conventional heating method, the microwave irradiation afforded well-dispersed silver nanoparticles(NPs) in styrene monomer without polymerization. The synthesis of Ag NPs proceeded uniformly throughout the reaction vessel only under microwave irradiation, completing the reaction simultaneously in the whole reaction solution. Successive polymerization of the monomer containing the resultant NPs has successfully produced a hybrid of the silver NPs dispersed in PS matrix. Ag/PS (0.1/100) nanocomposites were prepared successfully by melt-mixing process using Ag/PS(4.0/100) as a master-batch. UV-VIS spectroscopy, TEM, and X-ray diffraction techniques were used to investigate the process of formation of Ag/PS nanocomposites.

• Composites Research
• /
• v.12 no.3
• /
• pp.84-90
• /
• 1999

High alumina cement(HAC) and polyvinyl alcohol(PVA) based macro-defect-free(MDF) cement composites were reinforced using short carbon fibers, 3mm in length, 1-4% in weight fraction and insoluble polymers such as polyurethane, epoxy, phenol resin, in order to increase mechanical properties and water stability. The specimens were manufactured by the low heat-press(warmpress) method. In addition, the interface and the cross-linking reaction of cement and polymers was also studied by the SEM and TEM. Flexural strength of HAC/PVA based MDF cementitious composites was proportionally decreased with increasing fiber contents due to the undensified structure around fibers. The flexural strength of insoluble polymer added specimen was decreased with increasing fiber contents, while water stability was dramatically improved. Epoxy resin added specimen showed the highest strength with increasing fiber contents, compared with other specimens. The water stability of fiber content 4% added specimen immersed in water presented about 95%, 87% at 3 and 7 days immersed in water, respectively. The interfacial adhesive strength of fiber-matrix was very much improved due to cross linking reaction of polymer and metal ions of cement. Tensile strength of insoluble polymers added composites as linearly increased with increasing the fiber contents. The epoxy resin added specimen also showed highest tensile strength. The 4% fiber added specimen presented 30~80% higher strength than controlled specimen.

• Journal of the Korea Institute of Building Construction
• /
• v.9 no.5
• /
• pp.71-77
• /
• 2009

In a range of forms, such as latex, water-soluble polymer, liquid resin, and monomer, polymer dispersions have been widely used in the construction industry as cement modifiers because of their excellent properties, such as acid-resistance, water-proofness, and good ductility in mortar and concrete. Polymer cement slurry (polymer-modified slurry) is made of cement and polymer dispersions, with a high polymer-cement ratio of 50% or more. The purpose of this study is to evaluate the water permeability and drying shrinkage of polymer cement mortar (polymer-modified mortar) and cement concrete coated by polymer cement slurry. The polymer cement mortar and cement concrete are prepared with various polymer types, polymer-cement ratios and curing methods, and are tested for water permeability, drying shrinkage and strength. The test results showed thatthe weight of permeable water of polymer cement mortar decreases with an increase in the polymer-cement ratio, reaching a minimum at the polymer-cement ratio of 20%. In particular, the weight of permeable water of St/BA-modified mortar with a polymer-cement ratio of 20% coated with St/BA-modified slurry is about 1/55 that of unmodified mortar. The EVA- and St/BA-modified slurries coated on cement concrete have about 4 or 5 times higher drying shrinkage compared to cement concrete. The strength of polymer cement mortars tends to increase with a higher polymer-cement ratio, and is considerably higher than that of unmodified mortar. It is thus concluded that polymer cement mortars coated by polymer cement slurry are effective for industrial application, and have superior properties such as waterproofness and strengths, compared with conventional cement mortar.

• Polymer(Korea)
• /
• v.37 no.3
• /
• pp.255-261
• /
• 2013

This paper introduced a new preparation method of a composite rubber by mixing BR (butadiene rubber) and CIIR (chloro-isobutyl rubber) for the purpose of improving frictional property of BR. Since BR has high abrasion and low frictional properties, its frictional property needs to be enhanced in order to be used as an outsole of a sport shoe. Such enhancement was difficult to achieve by simple blending of CIIR. In here, CIIR was added into BR matrix after CIIR was pre-crosslinked for a time period, and both high frictional and high abrasion resistance properties were achieved. Our experiments showed that the composite rubber blend of 60% of BR and 40% of pre-crosslinked CIIR had desired BR's frictional and abrasion resistance properties for sport shoes.

• Polymer(Korea)
• /
• v.28 no.2
• /
• pp.185-193
• /
• 2004

Elastomeric nanocomposites were prepared by employing zinc dimethacrylate into an acrylonitrile-butadiene rubber, and their network structures, mechanical properties, and fracture morphologies were investigated according to the adding methods and contents of zinc dimethacrylate. The total crosslink density increased with increasing the zinc dimethacrylate level, due to increased ionic bonds. Both the tensile strength and tear strength increased with increasing zinc dimethacrylate loadings, and then decreased after reaching a maximum value. It was found that the tear strength and crack resistance were greatly affected by the mixing method of zinc dimethacrylate. The in-situ nanocomposites, where zinc dimethacrylate particles were formed by the reaction of zinc oxide and methacrylic acid, showed much improved tear strength and crack resistance compared to those of the nanocomposites based on the direct mixing of zinc dimetacrylate powders. This was because of the finer zinc dimethacrylate particles and improved dispersion of the in-situ nanocomposites.

• Polymer(Korea)
• /
• v.37 no.2
• /
• pp.225-231
• /
• 2013

Poly(vinyl alcohol) (PVA) hybrid films containing 5 wt% pristine clay mineral were synthesized in the water solution. The various PVA hybrid films were synthesized from structurally different pristine clays: saponite (SPT), montmorillonite (MMT), hectorite (SWN), hydrophilic bentonite (PGV), and mica (Mica). The thermo-optical properties and morphologies of the PVA hybrid films were evaluated with various pristine clays. The nanostructure of the hybrid films was observed using transmission electron microscopy, which showed that the clay layers were well dispersed into the matrix polymer, although some clusters or agglomerated particles were also detected. The addition of pristine clay was more effective with regard to improving the thermal properties and gas barrier characteristics, whereas the optical transparency of the PVA hybrid films deteriorated with pristine clay.

• Polymer(Korea)
• /
• v.37 no.5
• /
• pp.579-586
• /
• 2013

Poly(vinyl alcohol)(PVA) nanocomposite films containing various saponite (SPT) clay contents were synthesized using a solution intercalation method. The thermal property, morphology, optical transparency, and gas permeability of the PVA nanocomposite films with various SPT contents in the range of 0 to 10 wt% were examined. PVA nanocomposite film containing 5 wt% SPT showed excellent thermal and gas barrier property. The hybrid films containing 5 wt% SPT were equibiaxially stretched with stretching ratios ranging from 150 to 250%. The clay dispersion, optical transparency, and gas permeability were also examined as a function of equibiaxial stretching ratio. The PVA nanocomposite films with various equibiaxial stretching ratios showed excellent optical transparency and barrier to oxygen permeability.