• 한국건축시공학회:학술대회논문집
• /
• 한국건축시공학회 2020년도 가을 학술논문 발표대회
• /
• pp.137-138
• /
• 2020

The purpose of this study is to evaluate the absorption ratio reduction of recycled coarse aggregate for concrete coated by polymer dispersions. The surface of recycled coarse aggregate is treated by polymer dispersion such as SBR and SAE with solid contents of 2%, 5% and 10%. From the test results, The minimum absorption ratio of the coated recycled coarse aggregate is 1.60 times smaller than that of uncoated recycle coarse aggregate. It is apparent that the absorption ratio of recycled coarse aggregate is much more improved by surface coating with polymer dispersions.

• 한국건축시공학회지
• /
• 제3권4호
• /
• pp.103-109
• /
• 2003

Reinforced concrete structures under sever conditions such as marine structures, bridges and structural constructed with aggregated(dredged front sea). can be deteriorated from corrosion of the reinforcing bars. The purpose of this study is to evaluate the corrosion reflectance of coated steel using polymer dispersion and polymer cement slurry. Polymer dispersion and polymer cement slurry with various polymer types were coated to the surface of bars and steel plate, and tested for accelerated corrosion tests. Tests include adhesion in tension, bending test, chloride ion spray, penetration of NaCl 10％ solution and carbonation. From the test results, the corrosive resistance of steel is considerably improved by using polymer dispersion and polymer cement flurry at surface of steel. The difference of the corrosive resistance is hardly recognized according to types of polymer dispersion. The coated steel using polymer dispersion and polymer foment slurry will be improved to a great extent compared to those of plain steel when increasing content of chloride ion in cement concrete.

• 한국건축시공학회지
• /
• 제16권2호
• /
• pp.97-105
• /
• 2016

최근 국내에서는 노후화된 도심지 도로 등을 신속하게 보수하기 위하여 초속경 콘크리트-폴리머 복합체를 사용하는 사례가 증가하고 있다. 그러나, 초속경 콘크리트-폴리머 복합체의 주재료로 사용되는 초속경시멘트와 폴리머의 높은 가격과 큰 환경부하로 보다 경제적이고 친환경적인 재료의 개발이 요구된다. 이에 본 연구에서는 제강슬래그를 재활용하여 환경부하가 작은 CAC 및 GC를 초속경시멘트에 일부 치환한 초속경 콘크리트-폴리머 복합체의 특성을 폴리머 종류별로 검토함으로써 초속경시멘트의 대체재로서 CAC 및 GC의 활용가능 여부와 초속경 콘크리트-폴리머 복합체의 성능향상 가능성을 검토하였다. 그 결과 CAC 및 GC를 초속경시멘트에 일부 치환한 경우의 압축강도, 인장강도, 휨강도, 접착강도 및 탄성계수는 초기재령인 3시간에서는 기존보다 명확히 높은 값을 보였고, 그 이후의 재령에서는 거의 동등한 수준의 값을 보였다. 폴리머 디스퍼션 종류에 따라서는 BPD를 사용한 경우가 강도측면에서는 전반적으로 우수하였지만, 탄성계수는 동등한 수준을 보였다. 이상의 결과로부터 초속경 콘크리트-폴리머 복합체 제조용 시멘트로서 CAC 및 GC의 일부 대체사용이 가능하고, 폴리머 디스퍼션으로 BPD를 사용 시 초속경 콘크리트-폴리머 복합체의 성능향상도 가능한 것으로 나타났다.

• 한국건축시공학회지
• /
• 제9권5호
• /
• pp.71-77
• /
• 2009

시멘트 혼화용 폴리머 디스퍼션은 시멘트 모르타르 및 콘크리트 내부에서 폴리머 필림을 형성하여 각종 역학적성 질 및 내구성을 향상시킨다. 본 연구는 3종류의 폴리머 디스퍼션을 폴리머 시멘트비 0, 5, 10, 20%로 변환한 폴리머 시멘트 모르타르를 제작, 투수시험을 실시하여 투수성능을 실험하였으며, 더욱이 폴리머 시멘트 슬러리를 폴리머 시멘트 모르타르 표면에 도포하여 방수성능의 개선효과를 평가하였다. 또한 보통시멘트 콘크리트 표면에 폴리머 시멘트 슬러리를 도포하여 시멘트 콘크리트와 폴리머 시멘트 슬러리의 건조수축을 측정하였다. 그리고 기본적인 역학적 성상인 휨강도와 압축강도를 측정하여 보통 시멘트 모르타르와 비교 검토하였다. 연구결과, 폴리머 시멘트 모르타르는 보통 시멘트 모르타르에 비해 방수성능과 강도가 크게 개선되었으며, 폴리머 시멘트 슬러리의 건조수축은 시멘트 콘크리트에 비해 4-5배 크게 나타났다. 또한 향후 건조수축에 따른 접착성능의 영향성에 대한 연구가 진행되어야 할 것이다.

• 콘크리트학회논문집
• /
• 제20권5호
• /
• pp.635-642
• /
• 2008

건설구조물에서 보통철근의 부식을 방지하기 위하여 에폭시 도장 철근이 널리 사용되고 있다. 그러나 에폭시 도장철근은 성능과 코스트 면에서 불리하며, 특히 취성적이고, 부착성 및 현장 가공성 등의 취약점 때문에 현장에서 사용상의 제약을 받고 있다. 본 연구는 에폭시 도장 철근을 대체할 수 있는 도장재료로서 유기계 폴리머와 시멘트의 무기계를 혼합한 하이브리드 (hybrid)형 폴리머 시멘트 슬러리를 개발하기 위한 것으로서, 특히 인장특성과 접착성에 관한 연구이다. 폴리머 시멘트 슬러리는 4종류의 폴리머 디스퍼션과 혼화재로서 플라이애쉬와 실리카퓸을 혼입하여 제작되었으며, 도장두께, 인장특성, 접착성 및 내굴곡성 시험을 실시하였다. 연구결과, 폴리머 시멘트 슬러리의 점도는 폴리머 디스퍼션의 종류에 따라 크게 영향을 받았으며, 플라이애쉬를 혼입함에 따라 약간 감소하였다. 또한 폴리머-결합재비 100%에서 폴리머 시멘트 슬러리의 적정 도장두께가 확보되었으며, 도장두께는 물-결합재비와 폴리머-결합재비에 의해 다양화 할 수 있었다. 철근의 도장을 위한 적정 도장 두께는 부착강도, 접착성 및 내굴곡성을 고려할 때, 보통 $150{\sim}250{\pm}50{\mu}m$ 범위였다. 본 연구에서 폴리머 시멘트 슬러리의 인장특성 및 접착성, 그리고 도장강의 내굴곡성은 양호하게 평가되어, 향후 에폭시 도장철근을 대체할 수 있는 재료로 사용가능성을 확인하였다.

• 한국건축시공학회지
• /
• 제5권4호
• /
• pp.115-120
• /
• 2005

In recent years, polymer-modified mortars using polymer dispersions have been widely used as finish and repair materials in the construction industry because of their excellent properties compares to those of ordinary cement mortar. Especially, the adhesion improvement of ordinary cement mortar and concrete has attracted a great deal of attention from researchers, and several unique and simply applicable techniques for the adhesion improvement have been developed. The purpose of this study is to evaluate the abrasion resistance of polymer-modified mortar according various curing methods. The polymer-modified mortar are prepared with various polymer-cement ratios, and are subjected to three curing methods such as dry rure, standard cure and freezing and thawing cure after two curing methods, and then tested for abrasion. From the test results, the polymer-modified mortars with various polymer-cement ratios have some superior abrasion resistance compared with plain mortar. The abrasion resistance of polymer-modified mortars increase with an increase in the polymer-cement ratio, and is better under water cure than any other curing methods. It is concluded that the abrasion resistance of cement mortar is markedly improved by modifying of polymer dispersion.

• 콘크리트학회지
• /
• 제8권5호
• /
• pp.135-143
• /
• 1996

콘크리트 및 모르터중의 수분의 확산 거동은 탄성계수, 크리프, 건축수축 등의 역학적 성질에 큰 영향을 미친다. 일반적으로 건조과정에서 폴리머 시멘트 콘크리트와 모르터의 수분의 증발에 의한 중량감소는 내부의 폴리머 필름형성에 의한 보수효과로 보통 시멘트 콘크리트 및 모르터에 비해 월등히 적다. 본 연구는 폴리머 시멘트 모르터 내부의 수분의 확산 과정을 확인하기 위하여 3종류의 폴리머디스퍼션과 에폭시 수지를 사용한 폴리머 시멘트 모르터를 제조하여 건조조건에 따른 수분의 확산 정도를 확산계수로 평가하였다. 실험결과, 폴리머 시멘트 모르터의 수분확산은 보통 시멘트 모르터에 비하여 아주 적었으며 폴리머 시멘트비에 따라 감소하였다.

• 콘크리트학회논문집
• /
• 제13권4호
• /
• pp.406-413
• /
• 2001

본 연구는 기존 원심력 철근콘크리트관의 성능을 향상시킬 수 있는 방법으로 관체 표면을 일정한 두께로 방식 라이닝 모르타르로 처리함으로써 보다 더 내구적인 하수관을 개발하기 위하여 실시하였다. 이를 위해 원심력 철근콘크리트관 제작 시, 동시성형이 가능하고 촉진 증기양생 조건에서도 균열이 발생되지 않는 접착강도가 큰 폴리머 시멘트 모르타르를 제조하였다. 폴리머 시멘트 모르타르를 원심력 철근콘크리트관용 라이닝 재료로 사용하기 위한 기초적 실험결과, 보통 시멘트 모르타르에 비해 역학적 성질 및 내구성이 우수하였으며, 현장적용결과, 동시성형 및 양생조건에 따라 적용될 수 있는 방법은 다양하나, 폴리머의 종류에 관계없이 폴리머 시멘트비를 20% 이하로 하며, 양생온도는 8$0^{\circ}C$이하의 양생조건을 제안할 수 있었다. 또한 현장조건이 가능하면, 2일간 기중양생(2$0^{\circ}C$)을 실시하여 폴리머 시멘트 모르타르 속의 폴리머 필름이 형성된 후, 8$0^{\circ}C$에서 양생시키는 방법이 이상적인 것으로 나타났다.

• 한국건축시공학회지
• /
• 제4권3호
• /
• pp.93-100
• /
• 2004

In recent years, it has widely been studied on the light-weight composites for the purpose of the large space and thermal insulation of building structures. The purpose of this study is to evaluate the properties of light-weight composites made by binders as cement, resin and polymer cement slurry. The concrete composites are prepared with various conditions such as polymer-cement ratio, void-filling ratio, type of resin, filler content and light-weight aggregate content, tested for thermal conductivity. From the test results, the thermal conductivity of concrete composites with the binder of cement tends to decrease with increasing polymer-cement ratio, and to increase with increasing void-filling ratio. The thermal conductivity of concrete composites with the binder of resin are markedly affected by the light-weight aggregate content, type of resin and filler content. The composites made by polymer-modified concrete and polymer cement slurry have a good thermal insulation property. From the this study, we can recommend the proper mix proportions for thermal insulation Panel or concrete. Expecially. the thermal conductivity of concrete composites made by polyurethane resin is almost the same as that of the conventional expanded polystyrene resin.

• 콘크리트학회논문집
• /
• 제20권5호
• /
• pp.653-660
• /
• 2008

본 연구는 펄라이트를 이용한 흡음재료의 흡음성능을 개선시키기 위한 최적배합에 대한 분석을 실시하였다. 결합재로서 폴리머 시멘트 슬러리와 무기질 결합재를 사용하여 흡음재료를 각종 배합조건에 따라 제작하여, 강도, 동결 융해 저항성, 그리고 흡음성능에 대하여 실험을 실시하였다. 실험 결과, 관내법에 의한 흠음재의 흠음계수는 배합에 따라 약간의 차이가 있으나 폴리머 디스퍼션을 결합재로 사용한 경우 흡음재의 감음계수 (NRC)는 $0.48{\sim}0.51$로 시멘트만 결합재로 사용한 경우에 비해 약간 크게 나타났으나, 방음벽의 환경부 고시 기준에서의 흡음재로서 감음계수 0.70에 비하면 낮은 수치이다. 그러나 잔향실법에 의한 흡음용 패널의 저주파수 영역($250\;Hz{\sim}500\;Hz$)에서 흡음계수가 $0.84{\sim}1.00$로 매우 높게 나타났으며, 고주파 영역에서도 $0.57{\sim}0.77$ 정도로 비교적 높은 흡음률을 나타내 감음계수가 0.77로 높게 나타났다. 폴리머 디스퍼션을 결합재로 사용한 흡음재는 압축강도, 휨강도 및 동결융해 저항성 등에서 방음벽 재료로서 적당한 성능을 발휘하였으며, 성능과 가격면에서 밸런스를 확보할 수 있는 배합을 도출할 수 있었다.