• Journal of the Korean Society for Aeronautical & Space Sciences
• /
• v.47 no.4
• /
• pp.256-265
• /
• 2019

In this paper, the progressive damage of an orthogonal grid shell fabricated with plain weave fabric CFRP under bending load was investigated. The orthogonal grids were cured with the bottom composite shell. Progressive damage analysis of an orthogonal grid shell under bending was performed using nonlinear finite element method with Hashin-Rotem failure criterion and Matzenmiller-Lubliner-Taylor(MLT) model. In addition, the three - point bending test for the structure was carried out and the test results were compared with the analysis results. The comparison results of the strain and displacement agreed well. The damage area estimated by the progressive damage analysis were compared with the visual inspection and ultrasonic non-destructive inspection.

• Composites Research
• /
• v.35 no.4
• /
• pp.269-276
• /
• 2022

In this paper, a composite stiffened panel was fabricated using a three-dimensional weaving method that can reduce the risk of delamination, and mechanical properties such as buckling load and natural frequency were investigated. The preform of the stringer and skin of the stiffened panel were fabricated in one piece using T800 grade carbon fiber and then, resin (EP2400) was injected into the preform. The compression test and natural frequency measurement were performed for the stiffened panel, and the results were compared with the finite element analyses. In order to compare the performance of 3D weaving structures, the stiffened panels with the same configuration were fabricated using UD and 2D plain weave (fabric) prepregs. Compared to the tested buckling load of the 3D woven panel, the buckling loads of the stiffened panels of UD prepreg and 2D plain weave exhibited +20% and -3% differences, respectively. From this study, it was confirmed that the buckling load of the stiffened panel manufactured by 3D weaving method was lower than that of the UD prepreg panel, but showed a slightly higher value than that of the 2D plain weave panel.

• Composites Research
• /
• v.20 no.5
• /
• pp.26-33
• /
• 2007

Pull-out and shear strengths of insert Joints of sandwich structure were investigated by experiment. Specimens were prepared by cocuring of nomex honeycomb core and carbon-epoxy composite face using an adhesive FM73. A total of 75 specimens with 10 different types depending on the core height and density, face thickness, and loading direction were tested. In the test under pull-out loading, although both the core height and density affect the failure loads, the effect of cell density is more serious. Dominant factor fur failure loads of the joints under shear loading is face thickness and the effect of core height is negligible. In the joint with same dimension, failure loads vary depending on the potted area of the core, particularly in the pull-out test.