• Proceedings of the Korea Concrete Institute Conference
• /
• 2008.04a
• /
• pp.741-744
• /
• 2008

There are two ways to reduce cement content for a given quality level(strength, workability etc.) in concrete. First, reducing the required paste volume by varying the shape or the grading of aggregates. Secondly, holding the paste volume constant while replacing cement volume with mineral admixtures or mineral fillers. And It will also be proved that the required minimum paste volume is independent of the paste composition, provided the paste composition is in a reasonable range. In this study, therefore, we have an object to determine the required minimum paste volume for a given workability level. For this purpose, we tried the following experiments: vary the paste volume for the three different grading of aggregates and determine the minimum paste volume to achieve a certain level of workability with high-range water reducing admixture.

• Journal of the Korean Recycled Construction Resources Institute
• /
• v.10 no.4
• /
• pp.489-497
• /
• 2022

In this study, the fluidity, mechanical properties and microstructure of cement pastes with carbon nanotube (CNT) were experimentally investigated. The 6 types of cement paste mixes with different PCE:CNT and w/b had been manufactured, and several tests including flow, compressive strength, absorption and water porosity were performed on cement pastes with or without CNT.Additionally, microstructural observations such as x-ray diffraction (XRD) and scanning electron microscopy (SEM) were carried out to examine hydrates formed in cement paste with CNT. As a result, it was found that the performance of cement pastes with CNT was better compared to that of control cement paste (OPC) due to both of hydration acceleration effect and filling effect. Furthermore, the SEM images clearly showed that CNT can bridge cracks formed in cement matrix. Conclusively, it is believed that the CNT, if mixed appropriately, could be an option as nono-materials to improve performance of concrete structures.

• Journal of the Korea Concrete Institute
• /
• v.27 no.5
• /
• pp.511-519
• /
• 2015

Methods such table flow, slump and outflow time have used to be as a main evaluation criteria regards to fluidity of concrete. Since those methods mentioned above have some inaccuracies which are up to its condition of test. Studies that evaluate fluidity applying the rheology has increased its portion in this field. Meanwhile, demands for AAS binder have been increased in accordance with its demand for this market, studies for rheology of AAS binder are little though. Therefore, this paper mainly deals a rheological peculiarity of AAS binder according to its condition of W/B ratio and alkali activators. The fluidity of AAS paste was evaluated with the index of table flow and outflow time. And shear stress following its shear rate was analyzed through rheological test. Rheological parameters were deduced through this rheological test of Bingham model and analyzed its interrelation with fluidity test. As the final outcome, it proposed the interrelation among table flow, yield stress, viscosity and outflow time. In basis of this study, we would like to suggest a reference for mixing AAS mortars and concretes.

• Journal of the Korean Recycled Construction Resources Institute
• /
• v.4 no.2
• /
• pp.90-96
• /
• 2009

The high rising building construction makes increasing the requirement of high strength concrete. Especially, the workability analysis is related with dispersion of admixture such as SF for improving strength and FA, BS for reducing construction cost and improving durability of Ultra High Strength Concrete which has over 100 MPa of compressive strength is very important. Precisely, decreases dispersion because of lumping situation of each admixture and it causes the workability of admixture is decreased. Therefore, the workability of cement paste is tested for analyze effects of pre-mixed cement for solving those problems with it to this research. The summary of the results are like below. First of all, OBS is increasing workability more than OFS. This result causes that the glassy surface of BS in the OBS is increasing workability and the absorption of admixture of FA in the OFS is decreasing workability. In the case of mixing methods, pre-mixing method is increasing workability more than normal one. This result shows that the normal mixing method is bad dispersion of binders. The other side, the pre-mixing method is good. Furthermore, depending on the mixing time, according to the increasing mixing time such as 30, 60, and 120 seconds, the dispersion of binders and workability turns better.

• Journal of the Korea Institute of Building Construction
• /
• v.6 no.3 s.21
• /
• pp.75-82
• /
• 2006

This study investigates the influence of various blending factors on cement paste fluidity and find out the most effective evaluation method of cement paste flow, comparing flow test apparatuses such as ring flow(R-F), flow cone(F-C) and mini slump(M-S). A viscometer also measures the rheology coefficients to secure faithful numerical data. Firstly, series I examines cement paste, affected by several cement products and mineral admixture types in the range of W/B 40%, ordinary fluidity, and W/B 30%, high fluidity. In this series, the three types of cement product depended on companies, are randomly used and the mineral admixture, such as fly ash, blast furnace slag and silica fume, are incorporated in the cement paste, in response to the ratio of 10, 20, to 30%, respectively. In addition, series II studies various chemical admixture types, affecting the cement paste. This series is carried out with manufacturing companies and component types in the range of W/C 30%, high fluidity. For the manufacturing companies, randomly four products are used and for the component types, polycaboxylate, melamine, naphthalene and lignosulfonate type are chosen. Test results showed that in the fluidity test of cement paste considering various types of blending factors, R-F exhibited similar tendency with F-C and M-S. In the analysis of consistency curves measured by viscometer, the fluidity evaluation method using flow test apparatuses was significantly effective, except for the some of the low fluidity specimens. In conclusion of this study, R-F was the most convenient, faithful and effective fluidity evaluation method of cement paste.

• Journal of the Korea Institute of Building Construction
• /
• v.21 no.1
• /
• pp.31-39
• /
• 2021

The aim of this paper is to improve durability of cement paste by imparting hydrophobicity to the surface and sphere of cement-based materials. A cement paste mixed with a silane/siloxane-based water repellent, and the initial hydration performance, flow performance, and age-specific compressive strength were measured. In addition, the water contact angle, SEM, and XRD before and after surface polishing were measured. When 0.5% of the silane/siloxane-based water repellent was mixed into the cement paste, the compressive strength increased, but the compressive strength decreased as the mixing amount increased by 1.5% and 3.0%. When a silane/siloxane water repellent was incorporated into the cement paste, the hydrophilicity was improved and the contact angle was increased due to hydrophobicity. In addition, the contact angle after surface polishing was found to be larger than the contact angle before surface polishing.

• Applied Chemistry for Engineering
• /
• v.22 no.4
• /
• pp.423-428
• /
• 2011

Hydration characteristics of cement containing zeolite mined at Daepo in Gyeongbuk province were studied for use as a mineral admixture. The cement paste containing zeolite was characterized by the measurement of heat evolution, XRD, EDS, nitrogen adsorption and mercury intrusion porosimetry. The cement paste containing zeolite exhibited tendencies toward acceleration of paste setting and promotion of cement hydration with the increase of zeolite content. The flow of mortar containing zeolite strongly reduced with increase of zeolite content. Compressive strength of the mortar containing zeolite increased very rapidly at an early age in comparison with plain mortar. These results would be related to aluminum species escaped from zeolite particles during the alkali dealumination of zeolite by the hydration process of cement.

• Journal of the Korean Recycled Construction Resources Institute
• /
• v.5 no.4
• /
• pp.129-136
• /
• 2010

This study is to investigate experimentally the engineering characteristics of cement mortar according to the replacement method and contents of recycled aggregate powder (RP) by collecting the recycled aggregate powder with the maximum size of below 0.08 mm and 0.15 mm. then, the results of the study can be summarized as follows. The flow of flesh mortar represented a trend in decreasing while the recycled aggregate powder was substituted as it is compared with that of plain. In addition, in case of correlation between tests, it appeared that the correlation between flow and ring flow is big. In the case of the characteristics of hardened mortar, the strength showed more improvements as the RP was substituted to aggregate than the case, which is substituted to aggregate. In addition, it was verified that the results in which the RP was substituted to aggregate by 5% represented similar values to that of the plain according to the passage of age.

• Proceedings of the Korea Concrete Institute Conference
• /
• 2002.10a
• /
• pp.91-96
• /
• 2002

This study is to analyze the influence of paste flow, compaction time and compaction thickness on the fundamental properties of porous concrete. Results of this study were shown as follows; 1) As paste flow increase, compaction time according to paste flow and compaction thickness decrease. Also, though paste flow is same, as compaction thickness increase, compaction time Increase. So It must be considered that the influence of compaction time according to paste flow and compaction thickness. 2) In the range of this study, compressive strength is the highest value at paste flow 190mm. 3) Occasion of manufactured compactor in this study compaction thickness 10, 15cm is influenced heavily but compaction thickness 20cm is influenced slightly.

• Proceedings of the Korea Concrete Institute Conference
• /
• 2009.05a
• /
• pp.341-342
• /
• 2009

In this study, various tests were performed such as setting time, flow, F1exural strength and compressive strength test to evaluate the effect according to the substitution of the replacement ratio of waste concrete powder and the change of particle size