• Resources Recycling
• /
• v.9 no.1
• /
• pp.63-69
• /
• 2000

Ferromanganese dust is an oxide substance of Mn. If imprities are removed and oxidation degree is controlled, the dust can be recycled for soft ferrite materials. The ferromanganese dust contained about 7 kinds of impurities, expecially about 9000 ppm of $SiO_2$ contents of the ferromanganese dust from 9000 ppm to under 500 ppm by fritting method. The $SiO_2$ in ferromanganese dust can be converted into water soluble compounds by alkali fritting and removed by water leaching. KOH and NaOH were used. The most effective conditions to get rid of $SiO_2$ from the dust are that the weight ratio of alkali to ferromanganese dust is 1.75 and fritting is run at $550^{\circ}C$ for 1 hour.

• Resources Recycling
• /
• v.21 no.3
• /
• pp.21-27
• /
• 2012

In order to make high-purity ferro-manganese from $Mn_3O_4$ dust, the application of aluminothermy process to the reduction of $Mn_3O_4$ dust was investigated in previous work. The result showed the fact that can be obtained high purity ferro-manganese which have over about 93% of manganese content and lower impurities such as C, P, S than those of KS D3712 specification. The addition of silicon powder instead of aluminum powder was investigated as reductant in the thermite reaction process of $Mn_3O_4$ dust in this work because its production cost is lower than that of aluminum powder. In case of addition of silicon powder only as reductant, the experimental result showed the unstable ignition and no thermite reaction of mixture, but in case of simultaneous addition of silicon and aluminum powders as reductant, showed the fact that can be obtained high purity ferro-manganese which have much low content of impurities such as C, P, S component.

• Resources Recycling
• /
• v.24 no.6
• /
• pp.24-30
• /
• 2015

The sulfuric acid leaching of ferromanganese dust was studied. The effect of acid concentration, reaction temperature, stirring rate, particle size and solid to liquid ratio on Mn and Fe extraction in the solution were investigated. It was found that the leaching rate of Mn and Fe increased with increasing reaction temperature and sulfuric acid concentration. Examination of data by shrinking core model suggested that the leaching rate is controlled by chemical reaction at the surface of particle. The activation energy for the leaching reaction of Mn and Fe were calculated to be 79.55 kJ/mol and 77.48 kJ/mol, respectively.

• Journal of the Korean Applied Science and Technology
• /
• v.32 no.1
• /
• pp.23-30
• /
• 2015

The properties of dust collected from electric arc furnace of ferro manganese production units was investigated, and also the metallic manganese was recovered from the dust by aluminothermy process. The ferromanganese dust collected from electric arc furnace contained about 15% of manganese oxide ($Mn_3O_4$) and 9% of carbon as the contaminant, and have a 5um of 50% median diameter and irregular particle shape. The carbon contaminant in the dust could be reduced until about 0.1~0.5% level by roasting in the air at a temperature of 600~900C for 60minutes. The recovery of manganese could not be carried out using only ferromanganese dust from electric arc furnace by aluminothermy process, but the ferromanganese which contained manganese of about 92% and iron of about 5% could be obtained from the mixture of ferromanganese dusts from electric arc furnace and converter. The best mixing condition of dust fixed at electric arc furnace dust / converter dust ratio of 1:9 and 2:8, and the mixing rato of 3:7 or more could not separated the metal and slag from the reactant after aluminothermy reaction.