• Transactions of Materials Processing
• /
• v.29 no.3
• /
• pp.151-156
• /
• 2020

In general, the cause of slab cracking during heat treatment has been analyzed with focus on processing conditions. However, in the present work, the cause of cracking is analyzed based on the microstructural evolution during heat treatment. The microstructural analysis indicates that the structure of the slab consists of three main regions as the top, quarter, and center parts. The tensile properties are investigated in each region of the slab in the temperature range from 25 to 350 ℃. Results demonstrate that the cracking is mainly attributed to the thermal stress and specific morphology of the microstructure. It is proposed that the cracking during the heat treatment is related to the presence of inclusion at the ferrite phase which is located at the boundary of pearlite grains.

• Journal of Advanced Marine Engineering and Technology
• /
• v.18 no.3
• /
• pp.63-67
• /
• 1994

A main property for fiber reinforced thermoplastic composite material in compression molding is the flow of fibers. This flow is so effective a long direction of acting force that this study examined for the inclined angel of 30$^{\circ}$, 45$^{\circ}$ and 6$^{\circ}$. Below the near softing temperature of plastic, the fiber has been fractured at a point so that the fiber strength is smaller then the local hydrostatic stress in the mold. It has been found that the position of fracture is changing accrding to the incling angle. In case of the above softing temperature, the larger the inclined is, the farther the flow of fiber move. Also the plastic flow has been progresed with the cicular are type.

• Journal of Welding and Joining
• /
• v.12 no.3
• /
• pp.90-100
• /
• 1994

In this study the fatigue crack growth behavior was investigated for the surface cracks in aluminum alloy A5083-O plate and its weldment. Several kinds of specimens were tested at room temperature. The Eccentric specimens(E1.0, E2.5) subjected to combined stresses(tension+bending) were tested and the welded specimens with weld toes(TOE1, TOE2) were tested in order to verify the method to consider the stress concentration such as weld toe. It was ascertained that the surface crack growth property in the weld toe could be predicted by the corrected Pang's equation proposed in this study.

• Transactions of the Korean Society of Mechanical Engineers
• /
• v.17 no.10
• /
• pp.2518-2534
• /
• 1993

Fracture behavior of carbon/epoxy laminates under pin loading is studied experimentally and analytically. Effects of ratios of specimen width to hole diameter and edge distance to hole diameter on bearing strength are investigated. Characteristic length of the laminates obtained using HK model has good agreement with the experimental data. The larger hole size induced, the lower bearing strength is measured under pin loading . The bearing strength and failure mode could be predicted using HK model and Zhangs analytical solution of stress distribution around a pin loaded hole. Chamis' prediction method of bearing strength is also considered to predict failure mode and bearing strength. A modification of Chamis' method is made using the factor of rupturc. The predicted bearing strength by the modified method is reasonably close to the experimental data.

• Proceedings of the Membrane Society of Korea Conference
• /
• 1997.04b
• /
• pp.19-20
• /
• 1997

균일한 용액이 비용매의 첨가로 인해서 열역학적으로 불안정해지면 용액은 다른 조성을 가진 2개의 액상으로 분리되어서 $\Delta Gm$을 낮추게 된다. Liquid-liquid phase separation에는 nucleation and growth와 spinodal decomposition의 2가지 경로가 있다. 본 실험에서 사용된 고분자는 폴리술폰 (Udel P-3500)이며, 용매로는 NMP와 THF를 사용하였다. Flory-huggins 이론으로부터 유도된 식들과 computer simulation을 통해서 여러 조건에 따른 binodal line, spinodal line, critical 조성 등을 구하고 이를 실험치와 비교해서 interaction parameter들을 추정하였다. 10,15,20,25,30 wt%의 Polysulfone 용액을 제조한 후 유리판 위에 casting 하고, 조성이 각기 다른 침전조에 침전시켜 막을 얻고 상온에서 건조시킨 후 일부를 액체 질소에 급랭시켜 파단면과 표면을 SEM을 이용하여 관찰하였고 일부는 Instron을 이용하여 기계적 물성을 관찰하였다.

• Journal of Korean Society of Steel Construction
• /
• v.27 no.6
• /
• pp.513-523
• /
• 2015

In steel moment frames constructed of H-shapes, strong-axis moment connections should be used for maximum structural efficiency if possible. And most of cyclic seismic testing, domestic and international, has been conducted for strong-axis moment connections and cyclic test data for weak-axis connections is quite limited. However, when perpendicular moment frames meet, weak-axis moment connections are also needed at the intersecting locations. Especially, both strong- and weak-axis moment connections have been frequently used in domestic practice. In this study, cyclic seismic performance of RBS (reduced beam section) weak-axis welded moment connections was experimentally investigated. Test specimens, designed according to the procedure proposed by Gilton and Uang (2002), performed well and developed an excellent plastic rotation capacity of 0.03 rad or higher, although a simplified sizing procedure for attaching the beam web to the shear plate in the form of C-shaped fillet weld was used. The test results of this study showed that the sharp corner of C-shaped fillet weld tends to be the origin of crack propagation due to stress concentration there and needs to be trimmed for the better weld shape. Different from strong-axis moment connections, due to the presence of weld access hole, a kind of CJP butt joint is formed between the beam flange and the horizontal continuity plate in weak-axis moment connections. When weld access hole is large, this butt joint can experience cyclic local buckling and subsequent low cycle fatigue fracture as observed in this testing program. Thus the size of web access hole at the butt joint should be minimized if possible. The recommended seismic detailing such as stickout, trimming, and thicker continuity plate for construction tolerance should be followed for design and fabrication of weak-axis welded moment connections.

• Journal of the Korean Wood Science and Technology
• /
• v.43 no.6
• /
• pp.868-875
• /
• 2015

In order to replace existing slit type steel plate on the wooden structure joint, the FRP-reinforced laminated plates were produced. Four types of FRP-reinforced laminated plates were produced according to the type of reinforcement and adhesive, and before applying to the joint, the adhesion performance test according to KSF 3021 and KSF 2160 and the Compact Tension (CT) type fracture toughness test specified in ASTM D5045-99 were carried out. As a result of adhesion performance test, all GFRP textile, GFRP sheet, and GFRP Textile-Sheet type FRP-reinforced laminated plates satisfied the requirement of soaking delamination percentage with smaller than 5% based on KS standard. However, aramid type specimen satisfied the standard as the soaking delamination percentage of 4.8% but it did not satisfied the standard as the water proof soaking delamination percentage of 70%. As a result of fracture toughness test, the volume ratio of reinforcement to timber became 23% so that the strength of FRP-reinforced laminated plates increased by two to four times in comparison to the control specimen. It was confirmed that the GFRP Textile-Sheet type specimen was most resistant to the fracture most since the ratio of stress intensity factor compared with that of the control increased to 61% owing to the parallel arrangement of glass fiber to the load. As a result of tensile shear strength test using FRP-reinforced laminated plates and nonmetal dowels, it is about 12% lower than metal connectors.

• Journal of the Korea Academia-Industrial cooperation Society
• /
• v.21 no.1
• /
• pp.129-137
• /
• 2020

In designing a high strength bolted beam splice using steel for building structures, it is necessary to present the appropriate steel grade selection criteria for how to determine the cover plate steel grade. This study examined the difference in tensile behavior according to the steel grades through static tensile tests simulating the beam member high strength bolt joints flange. For this purpose, the specimens were designed and fabricated with the main variables, such as the thickness, steel grade and the strength of flange and cover plate, which are expected to affect the splice strength and behavior. The tensile test results for a total of 48 specimens showed that the tensile-load capacity exceeded the design tensile strength applied with a nominal strength of steel in all specimens. When the design strength of the cover plate exceeded 1.25 times that of the flange plate, the flange plate governed the behavior of splice. The change in maximum tensile load due to the change in flange steel grade is not very large, but there is a difference in deformation. The test results confirmed that the steel grade and thickness of the cover plate were the main factors affecting the beam splice behavior.

• Journal of Korean Society of Steel Construction
• /
• v.12 no.2 s.45
• /
• pp.111-122
• /
• 2000

In this study, A series of fatigue tests have been performed on the fillet welded joints of cover plates in steel plate girders in order to quantitatively assess the fatigue characteristics according to the shapes of cover plates. From the results of fatigue tests, it has been shown that the fatigue strengths were slightly different according to their shapes, but satisfied the fatigue design curves in Korea and other countries. Also, from the results of beachmark tests, it has been confirmed that the points of fatigue crack initiation were closely related to the shapes of weld bead toes, and fatigue cracks simultaneously initiated from several points in weld bead toes have been grown as semi-elliptical surface cracks, and these cracks have been coalesced each other, and grown as through thickness cracks, and finally reached to fracture. Besides, from the results of fracture mechanics approaches, stress gradient factors were the most dominant factors among crack correction factors obtained from the existing equations and finite element analysis, and the fatigue life on fillet welded joints of cover plates could be estimated using the relations between fatigue crack growth rate and stress intensity factor range obtained from finite element analysis.

• Composites Research
• /
• v.26 no.2
• /
• pp.141-145
• /
• 2013

The mode II interlaminar fracture toughness was evaluated for CFRP laminates with different types of nonwoven tissues and the source of increased mode II interlaminar fracture toughness was examined by SEM analysis in this paper. The interlaminar fracture toughness in mode II is obtained by an end notched flexure test. The experiment is performed using three types of non-woven tissues: 8 $g/m^2$ of carbon tissue, 10 $g/m^2$ of glass tissue, and 8 $g/m^2$ of polyester tissue. On the basis of the specimen with no non-woven tissue, interlaminar fracture toughness on mode II at specimens inserted with non-woven carbon and glass tissues and polyester tissues increases as much as 166.5% and 137.1% and 157.4% respectively. The results show that mode II interlaminar fracture toughness of CFRP laminates inserted with nonwoven tissues increased due to the fiber bridging, fiber breakage, and hackle etc. by SEM analysis.