• Journal of Dental Rehabilitation and Applied Science
• /
• v.28 no.1
• /
• pp.57-66
• /
• 2012

The purpose of this study was to evaluate the relation between intentionally induced internal stress and cyclic fatigue failure of ProTaper Universal. ProTaper Universal (Dentsply Maillefer) S1, S2, F1, F2, F3, F4 and F5 (25 mm length) were used in this study. To give the internal stress, the ProTaper Universal were put into the .02 taper Endo-Training-Bloc (Dentsply Maillefer) until auto-stop by torque controlled motor. The rotation speed was 300 rpm and torque value was 1.0 Ncm. ProTaper Universal were grouped by the induced number of internal stress and randomly distributed among one control group and three experimental groups (n=10). The four groups were Stress 0 (control), Stress 1, Stress 2 and Stress 3. These instruments were rotated until separation. For cyclic fatigue measurement, inclined plane was used and time for separation was recorded. It was statistically analyzed using two-way ANOVA and Duncan post-hoc test at 95% confidential level. In all ProTaper Universal, there was statistically significant decrease on time for separation in Stress 3. In F2 and F3, there were statistically significant difference between control group and all experimental groups. And in F4 and F5, Stress 2 and 3 groups showed significantly lower cyclic fatigue resistance from Stress 0 group. In the limitation of this study, cyclic fatigue failure of ProTaper Universal is influenced by accumulated internal stress.

• Restorative Dentistry and Endodontics
• /
• v.32 no.2
• /
• pp.130-137
• /
• 2007

This in vitro study examined the effect of surface defects on cutting blades on the extent of the cyclic fatigue fracture of HEROShaper Ni-Ti rotary files using fractographic analysis of the fractured surfaces. A total of 45 HEROShaper (MicroMega) Ni-Ti rotary flies with a #30/.04 taper were divided into three groups of 15 each. Group 1 contained new HEROShapers without any surface defects. Group 2 contained HEROShapers with manufacturing defects such as metal rollover and machining marks. Croup 3 contained HEROShapers that had been clinically used for the canal preparation of 4-6 molars A fatigue-testing device was designed to allow cyclic tension and compressive stress on the tip of the instrument whilst maintaining similar conditions to those experienced in a clinic. The level of fatigue fracture time was measured using a computer connected the system. Statistical analysis was performed using a Tukey's test. Scanning electron microscopy (SEM) was used for fractographic analysis of the fractured surfaces. The fatigue fracture time between groups 1 and 2, and between groups 1 and 3 was significantly different (p<0.05) but there was no significant difference between groups 2 and 3 (p>0.05). A low magnification SEM views show brittle fracture as the main initial failure mode At higher magnification, the brittle fracture region showed clusters of fatigue striations and a large number of secondary cracks. These fractures typically led to a central region of catastrophic ductile failure. Qualitatively, the ductile fracture region was characterized by the formation of microvoids and dimpling. The fractured surfaces of the HEROShapers in groups 2 and 3 were always associated with pre-existing surface defects. Typically, the fractured surface in the brittle fracture region showed evidence of cleavage (transgranular) facets across the grains, as well as intergranular facets along the grain boundaries. These results show that surface defects on cutting blades of Ni-Ti rotary files might be the preferred sites for the origin of fatigue fracture under experimental conditions. Furthermore this work demonstrates the utility of fractography in evaluating the failure of Ni-Ti rotary flies.

• Restorative Dentistry and Endodontics
• /
• v.31 no.3
• /
• pp.161-168
• /
• 2006

During root canal preparation procedures, the potential for instrument separation is always present. Files, a lentulo, a Gates-Glidden (GG) bur or any manufactured obstruction can be left behind in the canal Nickel-titanium (NiTi) rotary files are in common usage in these days. Despite their undeniable advantages, there is a potential risk of separation within the canals. It is very rapid, unpredictable, and creates a great deal of stress for the practitioner. When an endodontic instrument separates, the best option is to remove it. Ultrasonic instruments and microscopes have improved the success rate for removing separated instruments. But It is difficult and not always possible. Therefore prevention is the key. In this case report, several management methods of separated file in the canal are presented.

• Restorative Dentistry and Endodontics
• /
• v.31 no.2
• /
• pp.96-102
• /
• 2006

There are various factors affecting the fracture of NiTi rotary files. This study was performed to evaluate the effect of cross sectional area, pecking motion and pecking distance on the cyclic fatigue fracture of different NiTi files. Five different NiTi $files-Profile^{(R)}$ (Maillefer, Ballaigue, Switzerland), $ProTaper^{TM}$(Maillefer, Ballaigue, Switzerland), $K3^{(R)}$ (SybronEndo. Orange, CA) , Hero $642^{(R)}$ (Micro-mega, Besancon, France), Hero $Shaper^{(R)}$ (Micro-mega, Besancon, France)-were used. Each file was embedded in temporary resin, sectioned horizontally and observed with scanning electron microscope. The ratio of cross-sectional area to the circumscribed circle was calculated. Special device was fabricated to simulate the cyclic fatigue fracture of NiTi file in the curved canal,. On this device, NiTi files were rotated (300rpm) with different pecking distances (3 mm or 6 mm) and with different motions (static motion or dynamic pecking motion) . Time until fracture occurs was measured. The results demonstrated that cross-sectional area didn't have any effect on the time of file fracture. Among the files, $Profile^{(R)}$ took the longest time to be fractured. Between the pecking motions, dynamic motion took the longer time to be fractured than static motion. There was no significant difference between the pecking distances with dynamic motion, however with static motion, the longer time was taken at 3mm distance. In this study, we could suggest that dynamic pecking motion would lengthen the time for NiTi file to be fractured from cyclic fatigue.

• Restorative Dentistry and Endodontics
• /
• v.35 no.4
• /
• pp.257-266
• /
• 2010

The purpose of this study was to determine the effect of post types and sizes on fracture resistance in immature tooth model with various restorative techniques. Bovine incisors were sectioned 8 mm above and 12 mm below the cementoenamel junction to simulate immature tooth model. To compare various post-and-core restorations, canals were restored with gutta-percha and resin core, or reinforced dentin wall with dual-cured resin composite, followed by placement of D.T. LIGHT-POST, ParaPost XT, and various sizes of EverStick Post individually. All of specimens were stored in the distilled water for 72 hours and underwent 6,000 thermal cycles. After simulation of periodontal ligament structure with polyether impression material, compressive load was applied at 45 degrees to the long axis of the specimen until fracture was occurred. Experimental groups reinforced with post and composite resin were shown significantly higher fracture strength than gutta-percha group without post placement (p < 0.05). Most specimens fractured limited to cervical third of roots. Post types did not influence on fracture resistance and fracture level significantly when cement space was filled with dual-cured resin composite. In addition, no statistically significant differences were seen between customized and standardized glass fiber posts, which cement spaces were filled with resin cement or composite resin individually. Therefore, root reinforcement procedures as above in immature teeth improved fracture resistance regardless of post types and sizes.

• Restorative Dentistry and Endodontics
• /
• v.33 no.1
• /
• pp.54-65
• /
• 2008

The purpose of this study was to determine the effect of sodium hypochlorite and steam autoclaving on the cyclic fatigue of nickel-titanium endodontic files. Two types of files with a .06 taper and #30 were used, $K3^{(R)}$ (SybronEndo, Glendora, California, USA) and Hero $642^{(R)}$(Micro-Mega, BesanCon, France). The files were divided into 6 experimental groups containing 10 files each group depending the soaking time in 6% sodium hypochlorite solution and number of cycles of steam autoclave. After sterilization, a cyclic fatigue test was performed on each file, and the fracture time was recorded in seconds. The control group underwent the cyclic fatigue test only. After the test, the surface characteristics of the files were observed using scanning electron microscopy (SEM). All groups containing the Hero 64~ files showed a similar cyclic fatigue fracture time. However, the cyclic fatigue fracture time with the $K3^{(R)}$ files was significantly shorter in groups which were treated with sodium hypochlorite than in the control group (P < 0.05), SEM revealed both Hero $642^{(R)}$ and $K3^{(R)}$ files to have significant corrosion on the file surface in groups treated with sodium hypochlorite, compared with the sharp and regular blades of the control group. $K3^{(R)}$ files showed more corrosion than the Hero $642^{(R)}$ files. Bluntness of the blades of the $K3^{(R)}$ file was observed in groups treated with steam autoclave. Although there was no obvious destruction on the surface of steam autoclaved Hero $642^{(R)}$ files, slight bluntness was observed. Sterilizing with a steam autoclave is much less destructive to $K3^{(R)}$ files than sodium hypochlorite. The longer time exposed to sodium hypochlorite, the more destructive pattern was shown on the blades of the files. Therefore, when using sodium hypochlorite solution, the exposure time should be as short as possible in order to prevent corrosion and increase the cyclic fatigue fracture time.

• Restorative Dentistry and Endodontics
• /
• v.34 no.5
• /
• pp.424-429
• /
• 2009

This study aimed to assess the influence of different cross-sectional area on the cyclic fatigue fracture of Ni-Ti rotary files using a fatigue tester incorporating cyclical axial movement. Six brands of Ni-Ti rotary files (ISO 30 size with. 04 taper) of 10 each were tested: Alpha system (KOMET), HeroShaper (MicroMega), K3 (SybronEndo), Mtwo (VDW), NRT (Mani), and ProFile (Dentsply). A fatigue-tester (Denbotix) was designed to allow cyclic tension and compressive stress on the tip of the instrument. Each file was mounted on a torque controlled motor (Aseptico) using a 1:20 reduction contra-angle and was rotated at 300 rpm with a continuous, 6 mm axial oscillating motion inside an artificial steel canal. The canal had a $60^{\circ}$ angle and a 5 mm radius of curvature. Instrument fracture was visually detected and the time until fracture was recorded by a digital stop watch. The data were analyzed statistically. Fractographic analysis of all fractured surfaces was performed to determine the fracture modes using a scanning electron microscope. Cross-sectional area at 3 mm from the tip of 3 unused Ni-Ti instruments for each group was calculated using Image-Pro Plus (Imagej 1.34n, NIH). Results showed that NRT and ProFile had significantly longer time to fracture compared to the other groups (p < .05). The cross-sectional area was not significantly associated with fatigue resistance. Fractographycally, all fractured surfaces demonstrated a combination of ductile and brittle fracture. In conclusion, there was no significant relationship between fatigue resistance and the cross-sectional area of Ni-Ti instruments under experimental conditions.

• Journal of Dental Rehabilitation and Applied Science
• /
• v.40 no.1
• /
• pp.24-30
• /
• 2024

Complicated crown fractures of maxillary anterior teeth caused by trauma in adolescence can cause functional and aesthetic problems. For crown fractures with pulp exposure, various restorative methods can be considered depending on the amount of remaining tooth structure. Direct resin restorations are the most traditional and effective method, but they are likely to discolor and break over time. Fixed prosthesis have a high possibility of re-restoration due to marginal disharmony due to tooth movement during the growth period, and restorations using post which are mainly performed for extensive crown fractures increase the risk of root perforation and root fracture. However, endocrown is an integrated structure that gains retention force from the pulp space, enabling effective reconstruction from a biomechanical perspective and providing advantages in restoring function and aesthetics. Therefore, endocrown can be considered as a restoration method for complicated crown fractures caused by trauma in adolescence.

• Journal of the korean academy of Pediatric Dentistry
• /
• v.36 no.1
• /
• pp.126-132
• /
• 2009

Injuries of permanent teeth by trauma occur frequently in childhood and adolescence. Crown fractures are as frequent as 25-76% and especially maxillary incisors are prone to fractures. There have been numerous efforts to achieve both aesthetically and functionally satisfying restoration. When a mature tooth is fractured, porcelain crown or laminate veneer could be a choice of prosthodontic treatment. However, in a case of immature permanent incisor fracture, prosthodontic treatment is more complicated due to the immaturity of the tooth. Moreover, if endodontic treatment is accompanied with the prosthodontic treatment, the treatment period is prolonged. In the past, restoration using an orthodontic band, a ready-made crown, or glass ionomer cement did not exhibit esthetically satisfying result. As restorational materials have been improved, now more esthetic restoration is possible by reattaching fractured fragments or light-curing composite resin restoration. We reports cases of patients with fractured maxillary incisors and their successful treatment results through reattachment of fractured fragments and composite resin restoration.

• The korean journal of orthodontics
• /
• v.28 no.6 s.71
• /
• pp.955-974
• /
• 1998

The purpose of the present study was to seek bracket-adhesive combinations which have adequate bond strength with no enamel and bracket fracture. The shear bond strengths were measured, the sites of failure and the enamel damage were investigated and the peripheral sealing and adaptation between enamel surface, bonding adhesive and bracket were evaluated. 240 noncarious human premolars were divided into twenty four groups of ten teeth. Shear bond strengths of each group were determined in an universal testing machine after two days passed and the debonded specimens were inspected to determine the predominant bond failure sites. To evaluate peripheral sealing and adaption between enamel surface, adhesive and bracket, each specimen was cut longitudinally into two halves which included the midsection of the bracket, adhesive and enamel and exmined in scanning electron microscope. Six different types of brackets were bonded to the tooth with four different type of adhesives. Six different types of brackets were Image, Plastic, Crystaline, Fascination, Transcend 2000 and metal bracket and four different adhesives were No-mix, Light-Bond, OrthoLC and Superbond C&B. From this study, it may be concluded that (1) The mean shear bond strength varied from a high of 36.58 Kg (410.07 Kg/$cm^2$) with the Fascination-Light Bond combination group to a low of 8.93 Kg (75.51 Kg/$cm^2$) with theImage-OrthoLC combination group. When using OrthoLC as adhesive, the mean shear bond strength was significantly lower than that of other combination groups, (2) Regardless of adhesives, the mean shear bond strength of Fascination brackets was relatively high whereas Plastic and Image brackets had low shear bonding strength. The shear bond strength of Crystaline bracket and Transcend 2m was relatively equal to or lower than that of metal bracket, (3) There was a correlation between bond strength, enamel damage and bracket fracture. As the shear bond strength was increased, the rate of enamel damage and bracket fracture were increased, (4) The combination groups that use OrthoLC as adhesive were debonded in shear stress without enamel fracture and bracket fracture, whereas the combination groups that use Superbond C&B as adhesive experienced a relative high enamel fracture rate and bracket fracture rate, (5) Peripheral sealing and adaptation between enamel-adhesive-bracket were relatively good when using Light-Bond or No-mix as adhesive. Regardless of adhesives, adaptation between bracket-adhesive were relatively good in Ceramic brackets, (6) The combination groups which had adequate bonding strength with no enamel and bracket fracture were Crystaline-No mix, Crystaline-Light Bond, Crystaline-OrthoLC, metal-No mix, metal-Light Bond and metal-OrthoLC combination groups.