• Korean Journal of Materials Research
• /
• v.10 no.4
• /
• pp.305-311
• /
• 2000

Applicability of crack arrest load measured from the Charpy V-notch impact test has been investigated to predict the fracture toughness of nuclear reactor pressure vessel (RPV) steels (ASME SA508 Cl.3). The temperature dependence of the crack arrest load was well described by the type of exponential function characterized by an index temperature at which the crack arrest load is 2kN. The specific index temperature, which also well correlated with $T_{NDT}\;and\;T_{41J}$ is expected to be representative index temperature characterizing the crack arrest fracture toughness of RPV steels. Also, the crack arrest load correlated well with the stable crack length measured from the fracture surface. From the measurements of the crack arrest load and the stable crack length, the lower bound fracture toughness, $K_{Ia}$ of RPV steels could be predicted with sufficient accuracy.

• Korean Journal of Materials Research
• /
• v.11 no.3
• /
• pp.171-177
• /
• 2001

The thermal and mechanical properties of amorphous Z $r_{62-x}$N $i_{10}$C $u_{20}$A $l_{8}$ $Ti_{x}$ (x=3, 6, 9at%) alloys were investigated. The crystallization process was confirmed as amorphous longrightarrow amorphous + Z $r_2$A $l_3$+ Zr + (Ni,Ti) longrightarrow Z $r_2$Cu + Al + (Ni,Ti) for 3at%Ti, amorphous longrightarrow amorphous + Al longrightarrow $Al_2$Ti + NiZr + CuTi for 6at%Ti and amorphous longrightarrow amorphous + Zr + Al longrightarrow Zr + $Al_2$Zr + Al $Ti_3$+ CuTi for 9at%Ti. lickers hardness ( $H_{v}$ ) increased with increasing volume fraction( $V_{f}$ ) of pricipitates for all concerned compositions. Tensile fracture strength ($\sigma_{f}$ ) showed a maximum value 1219MPa at $V_{f}$ = 38% for 3at%Ti, 1203MPa at $V_{f}$ = 2% for 6at%Ti and 1350MPa at $V_{f}$ = 5% for 9at%Ti. The $\sigma_{f}$ was rapidly decreased after showing the maximum value. The $V_{f}$ corresponding to rapidly decreased $\sigma_{f}$ coincided with the $V_{f}$ transited from ductile to brittle fracture surface.ace.