• Journal of the Korean Wood Science and Technology
• /
• v.36 no.4
• /
• pp.19-25
• /
• 2008

This study was carried out to investigate the bending strength properties of the unreinforced glulam beams and the GFRP laminated glulam beams according to the volume ratio of GFRP. The 7-layer glulam beams ($10cm(b){\times}14cm(h){\times}180cm(l)$) were manufactured, using Larch (Larix kaempferi Carr.) laminae ($2cm(h){\times}10cm(b){\times}360cm(l)$), which were dried to the moisture content of 8% and specific gravity of 0.54. GPRP of 0.1 and 0.3 cm was reinforced between the outmost layer of bottom and next layer. When the glulam beams were reinforced with GFRP at the volume ratio of 0.7% and 2.1%, respectively, the bending strength was increased by 12% and 28%, respectively, in the reinforced beams than in control glulam beams. Also, the GFRP reinforced layer of the glulam beams with GFRP laminations blocked the progression of rupture, and the unbroken part held about 90% of the bending strength. In the results of glue joints test, the block shear strength is higher than $7.1N/mm^2$, the standard of KS F3021, and in the result of delamination, the adhesive strength is good as the water soaking and boiling delamination was less than 5%.

• Journal of the Korea institute for structural maintenance and inspection
• /
• v.18 no.1
• /
• pp.119-127
• /
• 2014

The application of sulfur polymer emulsion (SPE) as an acrylate substitute for semi-rigid pavement grout was evaluated, and the performance improvement by employing PVA fibers were also evaluated. The result indicated that the filling ratio of semi-rigid pavement material decreased as the fiber content increased, but it was measured to be 92~94% in every mixing condition, which satisfies the target performance, 90%. The maximum Marshall stability value of semi-rigid pavement material was measured to be 25.4 kN, which is about 4.7 times higher than the Korean Standard required for semi-rigid pavement material, 5.0 kN. The dynamic stability evaluation of semi-rigid pavement material indicated that the resistance to deformation from the wheel tracking test was improved by an SPE substitution, and in every mixing condition, the deformation converged to a constant value after 45 minutes with the same dynamic stability of 31,500 times/mm. The strain at the flexural failure was about 0.53%, which shows superior rigidity to asphalt pavements. The examination of abrasion resistance and impact resistance showed that the loss ratio was 9.8~6.0% in every mixing condition, which indicates a good abrasion resistance. Also, when fiber content ratio was 0.3%, the impact resistance was 2.82 times higher compared to plain (i.e., when fibers were not added). In the limited range of this study, an SPE substitution ratio of 30% was found to be an optimal level considering the mechanical and durability performance. In addition, it is thought that semi-rigid pavement material with superior performance could be manufactured if fiber content ratio up to 0.3% is applied depending on the purpose of use.

• Journal of the Korea institute for structural maintenance and inspection
• /
• v.22 no.1
• /
• pp.6-12
• /
• 2018

Recently, The use of the curtain wall method is increasing in construction. The curtain wall construction is widely applied to the exterior wall of the building for shortening construction period and economical efficiency. However, the replacement of deterioration of the weather resistance and structural behavior of the sealing material connecting the curtain wall method and the glass frame is necessary for introduction of the stable curtain wall method and quality improvement in accordance with KS F 4910 standard. In this study, the elastic restoring force test was performed in the external environment. In this study, the deterioration of the sealant was evaluated for structural sealants. In Korea, studies on the variable displacement behavior of structural sealants are lacked. In this study, the reproduced results in laboratory conditions are compared with the deteriorating conditions exposed to the external environment, and they are reflected in the design of sealing materials in the future. According to the results of the study, it was confirmed that the existing structure sealant meets the quality standard of KS F 4910, but in the conditions performed in this study, adhesion failure of the specimen and cracking of the surface occurred. Especially, in the weather resistance test, it is necessary to evaluate the long-term durability performance of the structural sealant used in the curtain wall method by checking the insoluble state of all the test pieces. Therefore, in order to apply a conventional structural sealant to the site, it is necessary to introduce another durability performance evaluation.

• Journal of the Korea institute for structural maintenance and inspection
• /
• v.19 no.4
• /
• pp.92-100
• /
• 2015

The aim of this study is to evaluate the fracture characteristics of ductile fiber reinforced cement based composites with 1.5 volume ratio of polyvinyl alcohol and steel fiber by high velocity impact of steel projectile. We used gunpowder impact facility to evaluate the fracture characteristics of ductile fiber reinforced cement based composites by collision of steel projectile, and the impact velocity was from about 150 to 1,000m/s. The results of evaluation on the fracture characteristics of ductile fiber reinforced cement based composites were penetration grade, which is the kinetic energy more than three times of no-fiber reinforced specimen (Plain). In addition, ductile fiber reinforced cement based composites did not occurred critical damage other than the debris. In the case of mass loss, Plain specimen was proportional to kinetic energy of steel projectile, while ductile fiber reinforced cement based composites was not significantly affected by kinetic energy of steel projectile. In particular, this tendency had a close relationship with the fracture characteristics of back side of specimens, and the scabbing inhibiting efficiency of PVA specimen was higher than S specimen. In the results of verifying relationship between front and back side calculated by local damage, scabbing occurred at the region close to the back side in the ductile fiber reinforced cement based composites unlike Plain specimen. Thus, in this study, we examined principal fracture behaviors of ductile fiber reinforced cement based composites under collision of steel projectile, and verified that impact resistance performance was improved as compared to Plain specimen.

• Applied Chemistry for Engineering
• /
• v.25 no.3
• /
• pp.318-323
• /
• 2014

In order to analyze the effect of maleic anhydride (MAH) content and styrene monomer (SM)/MAH mole ratio on reactive extrusion of maleic anhydride grafted random polypropylenes (MAH-g-rPP), MAH-g-rPPs were prepared by using a twin screw extruder. MAH contents were 0.5, 1.0, 3.0, and 5.0 phr and SM/initiator mole ratio was 0.0, 1.0, and 2.0. Dicumyl peroxide (DCP) was used as an initiator. The graft degree of MAH was confirmed by the existence of carbonyl group (C = O) stretching peak at $1700cm^{-1}$ from FT-IR spectrum. The degree of graft reaction increased up to 3.0 phr MAH and showed the optimum value at 1.0 SM/MAH mole ratio from the area ratio of C = O and C-H stretching peak. Thermal and crystallization properties of MAH-g-rPP and PP/MAH-g-rPP/pulp composites were investigated by DSC, TGA, XRD, and POM. There was a decrease in non-isothermal crystallization temperature of PP/MAH-g-PP/pulp composites. Based on tensile properties and SEM pictures for the fractured surface of PP/MAH-g-PP/pulp composites, MAH content of 1.0 wt% and SM/MAH mole ratio of 1.0 were the optimum formulation as the compatibilizer. The rheological properties of the composites were measured by dynamic Rheometer to compare the processability of the composites with and without compatibilizer. The power law index showed slightly low value at the composites with compatibilizer.

• Korean Journal of Food Science and Technology
• /
• v.30 no.4
• /
• pp.823-826
• /
• 1998

It has been reported that alginic acid hydrolysate retains antimicrobial activity but the enzyme which hydrolyze alginic acid is not developed for industrial use. The authors developed chemical method for hydrolyzing alginic acid. For preparing alginic acid hydrolysate, equal quantity of alginic acid and ascorbic acid were added to water. Then the solution was heated at $121^{\circ}C$ for $20{\sim}30{\;}minutes$. The 4% solution of alginic acid hydrolysate was revealed relative viscosity 1.05, pH 3.2 and opaque whitish-yellow color. By addition of this hydrolysate to nutrient broth with the concentration of 0.1%, the growth of Bacillus sp. isolated from fish meat paste products was inhibited. The fish meat paste products containing 0.3% alginic acid hydrolysate prepared were prolonged their shelf life by 1 day stored at $30^{\circ}C$, 2 days at $20^{\circ}C$ and 4 days at $15^{\circ}C$.

• Fire Science and Engineering
• /
• v.31 no.5
• /
• pp.63-69
• /
• 2017

This study describes the development of a long-distance hose for ultra-high pressure operation, which can be used in conjunction with an ultra-high pressure pump and can be effectively applied to the fire suppression of high-rise buildings and a long, large tunnels. Also, it has phosphorescent properties, which can help to secure the withdrawal route of the fire-fighters when they are threatened by the fire. We developed an ultra-high pressure hose aiming at a pressure of 3 MPa and a flow rate of 2000 lpm and developed an ultra-high pressure fire hose that can withstand this very high pressure by using a double jacket, triple polyurethane coating and warf (Wp) of 52. In order to ensure the performance of the developed ultra-high pressure hose, its structure, appearance, leakage at high pressure, length and elongation were inspected by a certified certification agency, who also subjected it to a peeling test, friction test, breaking pressure test and free fall test. Also, it was studied in addition to the luminescent high-pressure hose for fire-fighting. In the phosphorescence test, the luminance measurement value was more than the reference value of the luminance test after 40 minutes, which confirmed that its performance was satisfactory for fire-fighting products. In the future, if such an ultra-high pressure fire hose were commercialized and applied in the field, it could contribute to securing improved fire suppression and safer exit from fires, as compared to the fire hoses currently used in the suppression of fires in skyscraper buildings and long tunnels.

• Journal of the Korea Academia-Industrial cooperation Society
• /
• v.18 no.4
• /
• pp.521-526
• /
• 2017

In the GTA welding process of Al 7075 alloy using different types of filler metals, the tensile test and micro-hardness test were conducted to evaluate the mechanical characteristics. Also, the radiographic test result showed that the weld met the criterion of level 1 in accordance with KS D 0242 for verifying the welding integrity and there were no welding defects. The tensile test result obtained using Al 7075 as a filler metal showed that the material was fractured in the weld zone. The tensile strengths of the materials using Al 7075 and ER 4043 as the filler metal were about 240MPa and 253MPa, their yield strengths were about 132MPa and 120MPa and their elongation percentages were 6.6% and 13%, respectively. The micro-hardness value of the deposited metal zone when using Al 7075 as the filler metal was Hv 132. However, the micro-hardness of the material using ER4043 as the filler metal was about 24% lower than that using Al 7075. When the chemical composition of the filler metal is the same as that of the material itself, fracture can occur in the deposited metal zone. Therefore, it is not desirable to use the same material as the filler metal for the welding of Al 7075 alloy. Moreover, the use of Al-Si based ER 4043 as a filler metal is more desirable than using the same material as a filler metal for welding Al 7075.

• Journal of the Computational Structural Engineering Institute of Korea
• /
• v.32 no.5
• /
• pp.333-340
• /
• 2019

Tests using a middle velocity propulsion impact machine (MVPIM) were performed to verify the impact resistance capability of sandwich concrete panels (SCP) in a modular liquefied natural gas (LNG) outer tank, and numerical models were constructed and analyzed. $2{\times}2m$ specimens with plain sectional characteristics and specimens including a joint section were used. A 51 kg missile was accelerated above 45 m/s and impacted to have the design code kinetic energy. Impact tests were performed twice according to the design code and once for the doubled impact speed. The numerical models for simulating impact behaviors were created by LS-DYNA. The external steel plate and filled concrete of the panel were modeled as solid elements, the studs as beam elements, and the steel plates as elasto-plastic material with fractures; the CSCM material model was used for concrete. The front plate deformations demonstrated good agreement with those of other tests. However the rear plate deformations were less. In the doubled speed test for the plain section specimen, the missile punctured both plates; however, the front plate was only fractured in the numerical analysis. The impact energy of the missile was transferred to the filled concrete in the numerical analysis.