• Journal of the Korea Concrete Institute
• /
• v.24 no.5
• /
• pp.509-516
• /
• 2012

The aims of this research is to develop a fire resistant admixture to enhance high-pressured pumping of high-strength concrete (HSC) with a compressive strength of 60~80 MPa. Generally, the efficiency of HSC high-pressured pumping is dramatically reduced due to entanglement of short fibers added to prevent fire spalling. Therefore, the fire resistant admixture that can facilitate pumping of fire resistant HSC is urgently needed presently. The fire resistant HSC mix is comprised of Polypropylene fiber, Nylon fiber and Polymer powder. The test results showed that the slump-flow was improved by approximately 70% of the HSC without fire resistant admixture. However, the air void content was increased slightly due to the addition. The standard design compressive strength at 28-days was satisfied, while its flexural strength was similar to the concrete without the admixture. Since the flexural strength was 12~15% of its compressive strength, the general trend of flexural to compressive strength ratio in normal concrete was maintained. Even though its elastic modulus was decreased by adding the admixture, the study results showed that the concrete can be used for construction since all of the test results exceeded the code requirements.

• Journal of the Korean Ceramic Society
• /
• v.41 no.3
• /
• pp.235-242
• /
• 2004

Si, NH$_4$Cl, NaN$_3$, NaCl, $N_2$ were used as raw materials for preparation of $\alpha$-Si$_3$N$_4$ powder. NH$_4$Cl and NaN$_3$ were used as additives, and NaCl was used as a diluent. Initial $N_2$ gas pressure in the SHS reactor was 60 atm. In preparation of $\alpha$-Si$_3$N$_4$, the reactivity and the properties of the products were examined with the various kinds of additives and the content of diluent. At first, the optimum reaction system for the preparation of $\alpha$-Si$_3$N$_4$ is examined and then the optimum composition was examined in the optimum reaction system. The optimum reaction system was Si-$N_2$-additive(NH$_4$Cl+NaN$_3$)-diluent(NaCl) and the optimum composition was 38 wt%Si+50 wt%(NH$_4$Cl+NaN$_3$)+12 wt%NaCl. The maximum fraction of $\alpha$-phase of Si$_3$N$_4$ produced in this condition was 96.5 wt% and the shape of the $\alpha$-Si$_3$N$_4$ produced in this condition was an irregular fiber with a length of 10 ${\mu}{\textrm}{m}$ and a diameter of 1 ${\mu}{\textrm}{m}$.

• Journal of the Korean Ceramic Society
• /
• v.40 no.12
• /
• pp.1202-1207
• /
• 2003

Using a recently developed Hybric Plasma-Particle Accelerating Impact Deposition (HP-PAID) process, synthesis of nanostructured silicon coatings has been investigated by injecting vapor-phase TEOS (tetraethosysilane, (C$_2$H$\_$5/O)$_4$Si) into an Ar hybrid plasma. The plasma jet with reactants was expanded through nozzle into a deposition chamber, with the pressure dropping from 700 to 10 torr. Ultrafine particles accelerated in the free jet downstream of the nozzle, deposited by an inertial impaction onto a temperature controlled substrate. By using this process, nanostructured amorphous silicon coatings with grain size smaller than 10 nm could be synthesized. These samples were annealed in an Ar and crystallized at 900$^{\circ}C$ for 30 min. TEM analysis showed that the annealed coatings were also composed of nanoparticles smaller than 10 nm, which showed a good consistency that the average grain size of 7 nm was also estimated from a peak shift of 2.39 cm$\^$-1/ and Full Width at Half Maximum (FWHM) 5.92 cm$\^$-1/ of Raman analysis. The noteworthy is that a strong PL peak at 398 nm was also obtained for this sample, which indicates that the deposited coatings also contained 3∼4 nm nanostructured grains.

• Journal of the Korean Applied Science and Technology
• /
• v.31 no.2
• /
• pp.231-237
• /
• 2014

The supercritical fluids (SCFs) have been widely used for material synthesis and processing due to their remarkable properties including low viscosity, high diffusivity and low surface tension. Carbon dioxide is one of the suitable solvents in SCFs processes in terms of its advantages such as easy processibility (with low critical temperature and pressure), inexpensive, nonflammable, nontoxic, and readily available. However, it has generally low solubility for high molecular weight polymers with the exception of fluoropolymers and siloxane polymers. Therefore, hydrocarbon solvents and hydrochlorofluorocarbons have been used for various SCFs process by its high solubility for high molecular weight polymers. In this report, a PMMA/clay nanocomposites were fabricated by using supercritical fluid process. The $Na^+$-MMT(montmorillonites)was modified by a fluorinated surfactant which is able to enhance compatibility with the chlorodifluoromethane(HCFC-22) and thus, improve dispersability of the clay in the polymer matrix. The PMMA/fluorinated surfactant modified clay nanocomposite shows enhanced mechanical and thermal properties which characterized by X-raydiffraction(XRD), Thermo gravimetric analysis(TGA), Dynamic mechanical analysis (DMA) and Transmission electron microscopy (TEM).

• Journal of the Korean Society for Aeronautical & Space Sciences
• /
• v.47 no.11
• /
• pp.753-760
• /
• 2019

Sparkjet actuator, also known as plasma synthetic jet actuator, which is a kind of active flow control actuator is considered as being high possibility for the supersonic flow control due to ejecting stronger jet compared to the other active flow control actuators. Sparkjet actuator generates high temperature and high pressure flow inside the cavity by using arc plasma and leads momentum by ejecting such flow through orifice or nozzle. In this research, numerical calculation of sparkjet actuator with respect to the location of electrodes which exists inside the cavity is conducted and the change of the performance of sparkjet actuator is suggested. As the location of electrodes goes closer to the bottom of the cavity, impulse is increased and the average pressure inside the cavity maintains higher. When the location of electrode is 25% and 75% of the entire cavity height, impulse is 2.515 μN·s and 2.057 μN·s, respectively. Each impulse is changed by about 9.92% and -10.09% compared to when the location of electrodes is 50% of the entire cavity height.

• Transactions of the Korean Society of Mechanical Engineers B
• /
• v.40 no.4
• /
• pp.213-220
• /
• 2016

The objective of this study is to investigate the cooling performance of an air-conditioning system for a special purpose vehicle under tropical and severe weather conditions. In order to evaluate and compare the cooling performances, the dual refrigeration cycle using R-134a was tested on a special purpose vehicle with various refrigerant charge amounts and indoor temperatures. The cycle was tested considering indoor cooling speed and compression ratio (discharge pressure), and was optimized at the refrigerant charge amount of 1.5 kg and outdoor temperature of $40.0^{\circ}C$. The time to reach indoor temperature of $15.0^{\circ}C$ increased by 86.5% and 38.1%, at the indoor temperatures from $25.0^{\circ}C$ to $32.5^{\circ}C$ and from $32.5^{\circ}C$ to $40.0^{\circ}C$, respectively. In addition, with the increase in indoor temperature from $25.0^{\circ}C$ to $40.0^{\circ}C$, the cooling capacity increased by 7.3%, from 19.1 kW to 20.5 kW, but decreased by 7.0% from 4.67 to 5.1.

• Journal of Korea Water Resources Association
• /
• v.41 no.8
• /
• pp.761-772
• /
• 2008

The object of this study is to develop the model that solves the numerically difficult problems in hydraulic engineering and to demonstrate the applicability of this model by means of various test examples, such as, verification in the gradually varied unsteady condition, three steady flow problems with the change of bottom slope with exact solution, and frictional bed with analytical solution. The governing equation of this model is the integral form of the Saint-Venant equation satisfying the conservation laws, and finite volume method with the Riemann solver is used. The evaluation of the mass and momentum flux with the HLL Riemann approximate solver is executed. MUSCL-Hancock scheme is used to achieve the second order accuracy in space and time. This study introduce the new and simple technique to discretize the source terms of gravity and hydrostatic pressure force due to longitudinal width variation for the balance of quantity between nonlinear flux and source terms. The results show that the developed model's implementation is accurate, robust and highly stable in various flow conditions with source terms, and this model is reliable for one-dimensional applications in hydraulic engineering.

• Proceedings of the Korean Vacuum Society Conference
• /
• 2014.02a
• /
• pp.274-274
• /
• 2014

금속칼코게나이드 화합물중 하나인 $MoS_2$는 초저 마찰계수의 금속성 윤활제로 널리 사용되고 있으며 흑연과 비슷한 판상 구조를 지니고 있어 기계적 박리법을 통한 그래핀의 발견 이후 2차원 박막 합성법에 대한 활발한 연구가 진행되고 있다. 최근 다양한 응용이 진행 중인 그래핀의 경우 높은 전자이동도, 기계적 강도, 유연성, 열전도도 등 뛰어난 물리적 특성을 지니고 있으나 zero-bandgap으로 인한 낮은 on/off ratio는 thin film transistor (TFT), 논리회로(logic circuit) 등 반도체 소자 응용에 한계가 있다. 하지만 $MoS_2$는 벌크상태에서 약 1.2 eV의 indirect band-gap을 지닌 반면 단일층의 경우 1.8 eV의 direct-bandgap을 나타내고 있다. 또한 단일층 $MoS_2$를 이용하여 $HfO_2/MoS_2/SiO_2$ 구조의 트랜지스터를 제작하였을 때 $200cm^2/v^{-1}s^{-1}$의 높은 mobility와 $10^8$ 이상의 on/off ratio 나타낸다는 연구가 보고되어 있어 박막형 트랜지스터 응용을 위한 신소재로 주목을 받고 있다. 한편 2차원 $MoS_2$ 박막을 합성하기 위한 대표적인 방법인 기계적 박리법의 경우 고품질의 단일층 $MoS_2$ 성장이 가능하지만 대면적 합성에 한계를 지니고 있으며 화학기상증착법(CVD)의 경우 공정 gas의 분해를 위한 높은 온도가 요구되므로 박막형 투명 트랜지스터 응용을 위한 플라스틱 기판으로의 in-situ 성장이 어렵기 때문에 이를 보완할 수 있는 $MoS_2$ 박막 합성 공정 개발이 필요하다. 특히 Plasma enhanced chemical vapor deposition (PECVD) 방법은 공정 gas가 전기적 에너지로 분해되어 chamber 내부에서 cold-plasma 형태로 존 재하기 때문에 박막의 저온성장 및 대면적 합성이 가능하며 고진공을 바탕으로 합성 중 발생하는 오염 요소를 효과적으로 제어할 수 있다. 본 연구에서는PECVD를 이용하여 plasma power, 공정압력, 공정 gas의 유량 등 다양한 공정 변수를 조절함으로써 저온, 저압 조건하에서의 $MoS_2$ 박막 성장 가능성을 확인하였으며 전구체로는 Mo 금속과 $H_2S$ gas를 사용하였다. 또한 향후 flexible 소자 응용을 위한 플라스틱 기판의 녹는점을 고려하여 공정 온도는 $300^{\circ}C$ 이하로 설정하였으며 합성된 $MoS_2$ 박막의 두께 및 화학적 구성은 Raman spectroscopy를 이용하여 확인 하였다. 공정온도 $200^{\circ}C$와 $150^{\circ}C$에서 성장한 $MoS_2$ 박막의 Raman peak의 경우 상대적으로 낮은 공정온도로 인하여 Mo와 H2S의 화학적 결합이 감소된 것을 관찰할 수 있었고 $300^{\circ}C$의 경우 약 $26{\sim}27cm^{-1}$의 Raman peak 간격을 통해 5~6층의 $MoS_2$ 박막이 형성 된 것을 확인할 수 있었다.

• Proceedings of the Korean Vacuum Society Conference
• /
• 2014.02a
• /
• pp.122-122
• /
• 2014

수중방전을 환경분야에 적용하기 위한 플라즈마 부상법이 개발되었다. 플라즈마 부상법은 물 속에서 발생시킨 플라즈마가 가지고 있는 주요특성 중 물리적 특징인 쇼크웨이브, UV조사, 버블생성 등과 화학적 특징인 OH라디칼 및 염소산화물 생성 등을 이용하여 물 속에 존재하는 용존성 및 입자성 물질을 부상분리 기법으로 제거하는 공법이다. 유기물을 제거하는 기작으로는 침전, 여과, 분해 등이 있고, 이를 구현하기 위한 공정으로 중력침강법, 부상분리법, 멤브레인법, 미생물법 등이 있다. 이 중에서 가압공기부상법은 침강법에 비해 부지면적을 적게 소모하고 처리시간이 50% 이상 감소되는 특징이 있다. 가압공기부상법은 물 속에 공기를 과포화시킨 후 노즐을 통해 재분사할 때 발생하는 압력차에 의해 미세기포가 발생함을 이용하여 유기물을 분리하는 공법이다. 그러나, 가압용 장비 및 반송수가 필요하고, 미생물분리는 불가능한 단점이 있다. 이에 본 연구에서는 미생물살균과 유기물 분리가 동시에 일어나는 플라즈마를 이용한 부상분리기법을 개발하였다. 본 연구에서는 난분해성 용존유기물인 휴믹산 100 mg/L의 플라즈마 공기부상법에 의한 제거능을 확인하였다. 용존성 휴믹산을 입자성 물질로 전환하여 플록을 형성시키고자 알루미늄설페이트(Al2(SO4) $3{\cdot}18H2O$)를 100 mg/L 주입하였고, 침출수와 같이 염도가 높은 물을 모사하고자 35 g/L의 염화나트륨을 첨가한 상태에서 방전을 실시하였다. 방전에 사용된 전원은 EESYS사에서 제작한 펄스형 고전압 전원장치를 사용하였고 최대 15 kW의 출력 중 6 kW의 전력을 인가하였다. 전극 한 개는 2 mm 텅스텐봉을 세라믹튜브로 감싼 구조로 총 사용전극은 28개이다. 전극 한 개당 대략 200 Watt의 전력이 소모되며 이 때 최대의 버블이 생성됨을 확인하였다. 전극 1개에서 생성되는 버블의 부피는 14 mL/min 로 측정되었다. 버블의 크기는 평균 70 um이고 가압공기부상법에서 최적공기크기로 제시하고 있는 40~80 um 의 버블은 약 80% 가량 생성된다. 본 연구에서 사용된 반응시스템에서의 물의 높이는 약 500 mm 이고 전체 40 L의 수조가 3개의 벽으로 분리되어 4개의 수조로 분리되었다. 각 수조는 하부에 7개의 전극을 포함하고 있다. 플라즈마 발생시 생성되는 기포는 약 1분 방전 후에 포화농도에 도달하며 방전종료 후 약 4분간 수체 내에 남아있게 된다. 이를 공정에 적용하여 1분 방전 및 4분 휴지의 순서로 플라즈마를 인가하였다. 휴믹산 용액의 유량을 2 lpm 으로 운전하였을 때 최종 처리율은 94% 이고 이때의 대장균 살균능은 99%이다.

• Polymer(Korea)
• /
• v.27 no.5
• /
• pp.458-463
• /
• 2003

The effect of ozone surface treatment of montmorillonite (MMT) was investigated in thermal stabilities of polypropylene (PP) nanocomposites. Sodium montmorillonite (Na$\^$+/-MMT) was organically modified with dodecylammonium chloride. The surface properties of MMT, including the specific surface area (S$\_$BET/), equilibrium spreading pressure ($\pi$$\_$e/), and London dispersive component (${\gamma}$s$\^$L/), were studied by the BET method with $N_2$ adsorption. Also, the thermal stabilities of the nanocomposites were investigated in DSC and TGA. As experimental results, $\pi$$\_$e/ and ${\gamma}$s$\^$L/ of the ozonized dodecylammonium chloride (DA-MK ( $O_3$)) were increased in about 1.7 and 3.5 mJ/ $m^2$, resulting from the increasing of the micropores. From the DSC results, it was found that the melting temperature and crystallization temperature of PP/DA-MK and PP/DA-MK ( $O_3$) were higher that those of pure PP. These results were explained that dodecylammonium chloride of nano-scale led to a nucleation effect for PP crystallization. Also, it was found that E$\_$t/ of the PP/DA-MK ( $O_3$) nanocomposies was increased within about 64 kJ/mol. These results were probably explained by the improvement of dispersivity of DA-MK ( $O_3$) in a PP matrix.