• Journal of the Korea institute for structural maintenance and inspection
• /
• v.25 no.6
• /
• pp.169-176
• /
• 2021

In this study, pull-out tests were conducted at room temperature, 150 ℃ and 250 ℃ to evaluate the residual bond strength of carbon fiber reinforcement polymer, CFRP after elevated temperature and deformed steel rebar of D10 and D13 were also evaluated after the high temperature heating for comparison. As a result of the experiment, the bond strength of the CFRP after 150 ℃ and 250 ℃ decreased by 9.94 % and 41 %, respectively. On the other hand, after thermal heating, both the steel rebar of D10 and D13 had a lower rate of reduction in bond strength than that of the CFRP. Also slip at the maximum bond strength also decreased after the heating for both the CFRP and the rebars. Through it, the correlation between the bond strength and the slip reduction due to thermal heating was confirmed and bond slip models were presented. Finally the experimental result was evaluated as relative bond strength to identify the residual bond performance of the CFRP and the rebar after the heating was confirmed by comparing with the existing test result of the bond strength after elevated temperature.

• Journal of the Korean Recycled Construction Resources Institute
• /
• v.9 no.4
• /
• pp.569-577
• /
• 2021

CFRP(Carbon Fiber Reinforced Plastic) can maintain the same strength even if the diameter is reduced by about one - third, and the weight is about one - twentieth of that of the deformed reinforcing bars that have been used in the construction industry. In particular, it is resistant to corrosion, which is the weakest part of reinf orcing bars, and there is no concern that it will deteriorate over time, It is light and durable, so transportation costs are low and it is convenient for high-rise buildings. This paper experimentally clarifies the adhesive properties of CFRP and clarifies its behavior. That is, bond strength test was conducted with the directness of CFRP and the strength of concrete as experimental variables, and the bond mechanism was clarified experimentally. Furthermore, based on the experimental results, we constructed the bond stress-slip-strain relationship of CFRP compared to the existing deformed reinforcing bars.

• Journal of the Korean Society for Nondestructive Testing
• /
• v.27 no.2
• /
• pp.115-123
• /
• 2007

For investigating self-diagnosis applicability, a method based on monitoring the changes in the electrical resistance of carbon fiber reinforced concrete has been tested. Then after examining change in the value of electrical resistance at each flexural weight-stage of carbon fiber in CFGFRP (carbon fiber and glass fiber reinforcing plastic) with new type rib and carbon sheet for concrete reinforcing, the correlations of electrical resistance and load as a function of strain, deflection were analyzed. As the results, it is clarified that when carbon fiber rod, rib and sheet fracture, the electrical resistance of it increase largely, and specially in case of CFGFRP, afterwards glass fiber tows can be resist the load due to the presence of the hybrid (carbon and glass) reinforced fiber. Therefore, it can be recognized that reinforcing bar and new type rib of CFGFRP and sheet of CF could be applied for self-diagnosis of fracture in reinforced FRP concrete.

• Journal of the Korea Concrete Institute
• /
• v.18 no.3 s.93
• /
• pp.439-445
• /
• 2006

For investigating self-diagnosis applicability, a method based on monitoring the changes in the electrical resistance of hybrid FRP(having electrical property) reinforced concrete has been tested. Then after examining change in the value of electrical resistance of carbon fiber in CFRP(non-hybrid type), CFGFRP and CFAFRP(hybrid type) before and after the occurrence of cracks and fracture in non-hybrid and hybrid FRP reinforced concrete at each flexural weight-stage, the correlations of each factors(the changes in electrical resistance and load as a function of strain, deflection) were analyzed. As the results, it is clarified that when the carbon fiber tows fracture, the electrical resistance of it increase largely, and afterwards hybrid FRP composites can be resist the load due to the presence of the reinforced fiber, for example, glass fiber or aramid fiber tows. Therefore, it can be recognized that hybrid FRP(including carbon fiber) reinforcing bar could be applied for self-diagnosis of fracture in reinforced FRP concrete fracture.

• Journal of the Korea institute for structural maintenance and inspection
• /
• v.16 no.3
• /
• pp.1-10
• /
• 2012

In spite of high resistant to corrosion and its strength, over the last two decades, concerns still remain about the durability of FRP materials under severe environmental and thermal exposures. In this paper, authors experimentally examine the combined degradation by thermal and chemical attacks in heterogeneous FRP rebar be made up with various fibers and resins. Five types of Carbon, Glass and Hybrid FRP rebars had manufactured by different process and surface patterns are adopted for the experiments such as weight change, interlaminar shear strength, SEM and FT-IR analysis. FRP specimens were immersed in alkaline or distilled solution up to 150 days and then thermal exposed on 60, 100, 150 and $300^{\circ}C$ for 30 minutes. From the test results, the degradation of FRP bars are influnced by the resin type and manufacturing process as well as the fiber, and ILSS of exposed FRP bar in solutions is slightly increased in initial stage and then decresed with the passing of immersed time. But, in this test, it is observed that the discrepancy of ILSS between degraded by alkaline solution and distilled water is negligible value.

• Proceedings of the Korean Society For Composite Materials Conference
• /
• 2004.04a
• /
• pp.9-12
• /
• 2004

Presented is a preliminary design concept of the carbon-glass hybrid composite rebars for the application in the construction field. A glass fiber rod with indentation is used for the core of the rebar. Carbon fibers are placed over the glass core by pultrusion. To increase the mechanical locking force and bonding surface, carbon filament windings are added in the hoop direction over the carbon face. Finite element analysis and test were conducted to evaluate the effective stiffness and strength of the rods. The results show that the effective axial stiffness of the rebar with indentation are about $50\%$ of the straight rebar.

• Journal of the Korea institute for structural maintenance and inspection
• /
• v.12 no.3
• /
• pp.93-100
• /
• 2008

The use of fiber reinforced polymer (FRP) composites is significantly growing in construction and infrastructure applications where durability under harsh environmental conditions is of great concern. In order to examine the applicability of FRP rebar as a reinforcement in flexural member, flexural tests were conducted. 12 beams with different FRP materials such as CFRP, GFRP and Hybrid FRP and reinforcement ratio were tested and analyzed in terms of failure mode, moment-deflection, flexural capacity, ductility index and sectional strain distribution. The test results were also compared with the theoretical model represented in ACI 440.1R06. Test results indicate that the flexural capacity of the beams reinforced by FRP bars can be accurately predicted using the ultimate design theory. They also show that the current ACI model for computing the deflection overestimates the actual deflection of GFRP series and underestimates the deflection of CFRP series.

• Composites Research
• /
• v.35 no.5
• /
• pp.328-333
• /
• 2022

In this study, the fabrication conditions of CFRP rebar were controlled to derive the correlation between flexural strength and pore characteristics. The fabrication conditions of CFRP rebar were adjusted for presence or absence of rib, resin temperature, and curing furnace temperature. Flexural strength and pore characteristics of fabricated CFRP rebar were analyzed. The flexural strength of CFRP rebar was changed depending on the fabrication condition, such as the presence or absence of rib, the resin temperature, and the curing furnace temperature. It was confirmed that the flexural strength of CFRP rebar was significantly lowered when the rib was not wound. As a result of Nano X-ray CT analysis, the max. pore diameter was shown in CFRP rebar prepared at a resin temperature of 60℃. According to optical microscopic analysis, the maximum porosity was 6.89% in No. 1, and the minimum porosity was 2.88% in No. 7. The correlation coefficient between porosity used optical microscopy and flexural strength was -0.64, which was higher than the correlation coefficient between porosity or pore size used Nano X-ray CT and flexural strength.

• Journal of the Korean Society of Hazard Mitigation
• /
• v.8 no.4
• /
• pp.1-8
• /
• 2008

RC beam of existing structures often encounter shear problems for various reasons. The shear failure of RC beam is sudden and brittle. Strengthening technique jacketing with external bonding of steel plates(or CFRP and CFS) with epoxy is many use to in practice. This study presents test results on strengthening shear deficient RC beams by external bonding of slit type steel plates. Test parameters are width, interval, length, thickness and angle of slit in steel plates. The purpose was to evaluate the reinforcing effects, failure modes and shear capacities for RC beams of strengthened with various slit type steel plates. The test result confirmed that all slit steel plates improved the stiffness and strength of the specimens significantly. Failure modes of SV series and SD series showed shear fractures and flexure fractures at ultimate state respectively. SD series were ductile rather than SV series.