• Proceedings of the Korean Institute of Building Construction Conference
• /
• 2009.05b
• /
• pp.25-28
• /
• 2009

This study investigated the results of insulation heat curing method using double layer bubble sheet in slab concrete in cold weather environment. First of all, when double bubble sheets are applied, it was shown that slab concrete was protected from early freezing by remaining between 5 and $l0^{\circ}C$ even in case outside temperature drops $-11^{\circ}C$ below zero until the 4nd day from piling. The insulation heat preservation curing method using the double bubble sheet applied in this field prevented early freezing owing to stable curing temperature management, deterring concrete strength development delay at low temperature, and obtained the needed strength. Also, it was proven that the method is highly effective and economic for cold weather concrete quality maintenance through curing cost reduction like construction period shortening and labor cost reduction, etc by reducing the process of temporary equipment installation and disassembling.

• Journal of the Architectural Institute of Korea Structure & Construction
• /
• v.34 no.5
• /
• pp.27-34
• /
• 2018

Concrete placed under hot weather condition suffers from larger slump loss, rapid moisture evaporation due to high air temperature. Proper measures for material, transportation and curing should be taken to prevent the quality deterioration of the concrete under hot weather condition. In Korea, Although the period of hot weather concrete in Korea occupies only 2 months, there are a lot of quality problems including plastic, drying shrinkage and cold joint. Therefore, the objective of this paper is to investigate and compare the temperature history and crack occurrence of the concrete, which was placed in the actual apartment house construction field under hot weather condition, in response to the application of surface covered curing blankets including PE film, single layer clear bubble sheet, white colored bubble sheet and aluminum metalized bubble sheet. Test results indicated that the application of white colored bubble sheet and aluminum metalized bubble sheet showed most favorable results in terms of reduction in temperature rise and crack occurrence as well as easiness in handling. But, due to light reflection by aluminum metalized bubble sheet, it is believed that white colored bubble sheet is preferable.

• Proceedings of the Korean Institute of Building Construction Conference
• /
• 2022.04a
• /
• pp.239-240
• /
• 2022

In winter, low outdoor temperature can casue reduction of concrete strength. Therefore, thermal protection is required when curing concrete in winter to maintain a certain level or higher surface temperature. Accordingly, in domestic construction sites, a curing method in which surrounds casting areas by tents and operates hot air blowers are widely applied. However, local low-temperature areas may occur due to airtightness of the curing tents. If additional heat is supplied to prevent occurrence of local low-temperature areas, energy consumption increases. Therefore in this study, a plan for improvement method of concrete curing was considered and the performance was evaluated through numerical analysis. A plan to improve the airtightness of the wall opening was applied, but the analysis showed that if only a part of the curing area is shielded, the temperature of the unshielded area decreases,making it inappropriate to improve curing performance.

• Journal of the Korean Recycled Construction Resources Institute
• /
• v.6 no.2
• /
• pp.89-96
• /
• 2011

In this study, increasing the range of replacement rate of FA with concrete properties were analyzed to provide basic data of FA replacement 0-40 % and curing temperature $5-35^{\circ}C$ range. As a result of the increased fluidity in proportion to the increase in FA, but decreased air. Setting time delayed at replacement rate increases and low temperature, simple insulation temperature history of the FA up to 40 % replacement rate increases the maximum temperature was low $8^{\circ}C$, the highest temperature reaching time delay of 13 hours. FA replacement up stream of the curing temperature, compressive strength compared to the higher plane, it was found that improved strength development. In carbonation tests with increasing the replacement ratio of FA carbonation depth was increased. Therefore, continued research on carbonation measures was to be necessary.

• Journal of Korean Society of Coastal and Ocean Engineers
• /
• v.15 no.2
• /
• pp.71-79
• /
• 2003

The estimation functions were proposed for calculating diffusion coefficient, chloride binding, and evaporable water. The program estimating chloride ion penetration was developed on the basis of these functions and the effects of humidity, curing temperature, water-cement ratio, and $C_3$A on chloride penetration were analyzed. The relative humidity increases the depth of chloride ion penetration and the trend becomes greater with aging. On the contrary, the influence of curing temperature on chloride ion penetration decreases with aging. By the way, the rise of $C_3$A in cement increases total chloride concentration on the surface as the bound chloride concentration increases but it decreases total chloride concentration on the inner part as the diffusion velocity of free chloride decreases. The fall of water-cement ratio decreases the chloride penetration depth rapidly. Therefore, the reduction of water-cement ratio may be the most effective method for reducing of the steel corrosion by chloride penetration.

• The Journal of Engineering Research
• /
• v.8 no.1
• /
• pp.31-50
• /
• 2006

Shrinkage may cause cracking in concrete. In practice such cracking must be considered in most concrete applications because, under normal conditions, drying of the concrete is unavoidable, and when drying takes place shrinkage occurs. Cracked concrete is an inferior concrete because it is weaker, more permeable, and more susceptible to chemical attack. The development of the strength of LAC with aging depends on a few factors such as type of the cement, W/C ratio, curing conditions and periods. The higher the strength of LAC, the lower the possibility of shrinkage cracking. Hence, the strength of LAC in the hypocaust system depends to a large extent on the effect of cracking decrease of the antifoaming rate to drying shrinkage in cement.

• Proceedings of the Korea Concrete Institute Conference
• /
• 2008.11a
• /
• pp.433-436
• /
• 2008

Deterioration in the concrete structure are due to carbonation, chloride ion attack and frost attack. Therefore, concrete structure is needed to surface protection for increase durability using silicate impregnants. Thus, this study is concerned with self-cleaning and durability of silicate hydrophilic impregnants of concrete structure using lithium and potassium silicates. From the experimental test results, lithium and potassium silicates have a good properties as a carbonation resistance. Lithium and potassium silicates make good use of hydrophilic impregnants of concrete structures.

• Journal of the Korea Concrete Institute
• /
• v.25 no.1
• /
• pp.73-80
• /
• 2013

Polymer cement slurry (PCS) made from organic polymer dispersion and cement has good adhesion to steel, waterproofness and acid resistance due to being of polymer films formed in cement slurry. The purpose of this study is to evaluate the mix design conditions at early curing age of PCS-coating material effected on improvement in bond strength of coated rebar. The test pieces are prepared with two types of polymer dispersions such as St/BA and EVA, four polymer-cement ratios, two types of cement, four coating thicknesses and three curing ages, and tested for the bond strength test. From the test results, in general, bond strength of PCS-coated rebar is better than that of uncoated rebar and epoxy-coated rebar. It is also high bond strength at curing ages of 7-day or less, and coating thicknesses of $75{\mu}m$ and $100{\mu}m$. The maximum bond strength of PCS-coated rebar at curing age of 3-hour is almost same as that of curing age of 1-day and 7-day. The maximum bond strength of PCS-coated rebar with ultra high-early strength cement and St/BA at polymer-cement ratio of 80%, and coating thickness of $100{\mu}m$ is about 1.52 and 1.58 times respectively, the strength of uncoated rebar and epoxy-coated rebar. It is apparent that the curing age, coating thickness, type of polymer and cement are very important factors to improve the bond strength of PCS-coated rebar to cement concrete. We can have basic information that PCS-coated rebar with curing age at 3-hour and coating thickness of $100{\mu}m$ can replace epoxy-coated rebar.

• Proceedings of the Korea Concrete Institute Conference
• /
• 2009.05a
• /
• pp.351-352
• /
• 2009

The purpose of this study was to evaluate the characteristic of air content, slump, air void structure and strength development for concrete mixed with mineral admixture according to types of mineral admixtures and substitution ratio, temperature and condition of curing.

• Proceedings of the Korea Concrete Institute Conference
• /
• 2008.11a
• /
• pp.625-628
• /
• 2008

Size-effect correction factors of the flexural test specimens, which had controled cement concrete pavement quality, were investigated and derived to be easily used in field. We couldn't find the size-effects in this size range (10, 12, 15cm) of specimens, which were made of 32mm crushed aggregates, and the theoretical verification was presented by Bazant's equations. Finally, non-dimensional chart for size-effect correction was proposed, covering the relationship between compressive strengths and w/c ratios.