• Magazine of the Korea Concrete Institute
• /
• v.10 no.6
• /
• pp.281-289
• /
• 1998

This study has been performed to test the flowability and filling ability of high flowing concrete as well as distribution of aggregate and pore of core specimen, heat of hydration, compressive strength and core strength of concrete. In addition, the resistance to chloride ion penetration and chemical solutionof concrete was tested in order to evaluate the resistance to sea water of concrete and its application of high flowing concrete using blended low heat cement in the field of Seohae Grand Bridge. The properties of high flowing concrete with blended low heat cement were compared with ordinary 25-240-15 concrete using Type V cement. As the results of this study, the flowability and filling ability of high flowing concrete with blended low heat cement is satisfied without vibration. Though the cement content of high flowing concrete with blended low heat cement was 400kg/m$^2$, the rising temperature of it was relatively lower than that of the ordinary 25-240-15 concrete with Type V cement. Also, the compressive of high flowing concrete with blended low heat cement is similar to that of the ordinary 25-240-15 concrete with Type V cement.

• Magazine of the Korea Concrete Institute
• /
• v.7 no.4
• /
• pp.119-128
• /
• 1995

This paper summarizes experimental results for studying feasibility and structural behavior of' a half slab which is getting popularity in recent building construction in favour of the savings in manpower, coats, and construction period. 17 specimens were tested to investigate and analyze the flexural strength of precast concrete slab, half slab, and half slab-wall joint. The primary variables of the testing program were: thickness of precast concrete slab, truss mesh shape, and type of loadings. Test results show that the flexural strength of precast concrete slab in reverse loading is lower than the design strength, but the flexural strength of precast concrete slab, half slab and half slab-wall joint in direct loading is higher than the design srength. No horizontal cracks were found in the connection between insitu concrete and precast concrete slab. The flexural strength of half slab and half slab-wall joint was the same as that of reinforced concrete members. This study concludes that there will not be any structural problem in using a half slab reinforced by truss mesh if props spacing of 2.0m-2.5m, cleanness, and rough finishing between precast concrete and insitu concrete slab are kept.

• Journal of Korean Association for Spatial Structures
• /
• v.6 no.3 s.21
• /
• pp.69-76
• /
• 2006

Concrete Filled Steel Tube (CFT) system is advantageous because it increases the load-carrying capacity without increasing the size of column. However CFT system has many benefits, it is not applied to field generally because of its heavyweight and difficulty of concrete filling method. As a solution to these problems, we proposed concrete filled steel tube column with hollow made by factory-manufactured PC method. The hollow concrete filled steel tube system is expected to obtain the high strength and high capacity of deformation despite it is a lightweight. This study deals with mechanical properties, strength and deformation, of hollow concrete filled steel tube subjected to axial load. 9 specimens were tested to examine mechanical properties closely, and the following results were obtained: All specimens basically showed higher initial rigidity and maximum strength with increased concrete filling rate. And most specimens showed almost linear behavior until around 80% of maximum strength regardless of filling rate, it is estimated that the elastic range is up to a half of the maximum strength which is the yield strength level.

• Proceedings of the Korea Concrete Institute Conference
• /
• 2008.04a
• /
• pp.413-416
• /
• 2008

The concrete used most in construction materials. There is an overcrowded iron dimensions use of the concrete at time of the other concrete theory on the reinforcing rod back which did congestion and compares it with this, and there are more few dimensions of the aggregate than concrete, and quantity of aggregate passage is superior in mortar than concrete. If a volume rate of the aggregate writes mortar than concrete against this, therefore, unit amount increases, and quantity of paste increases and quantity of dry shrinkage than increase concrete. However, I let I regulate lay priest distribution of the aggregate, and the results rates increase and reduce unit amount and decrease quantity of dry shrinkage, and separation resistance and the gap passage characteristics are judged because it can be it in a substitute document of very superior concrete. I came to carry out the study that I watched to let I was useful a little more and do the improvement repair of a become building wall body, a basement pillar and repair reinforcement of the assistant in the reinforcing rod back, the old age when I made congestion here. I regulated lay priest distribution of the aggregate in the study and regulated substitution rate of the aggregate (40%, 50%, 60%) and divided W/C 30%, 40% standards and produced mortar and I compared quantity of air by this, slump, compression robbery and showed it this time.

• Journal of Korean Tunnelling and Underground Space Association
• /
• v.4 no.3
• /
• pp.195-205
• /
• 2002

Most tunnel damage such as cracks or leakage which exist in tunnel liner commonly, is caused by the cavities that exist behind the tunnel liner, through the tunnel safety inspections. These cavities were analysed to check if they affect the stability of tunnels. This study is on the development of the controlled low-strength and flowable filling material which an be applied to the cavity behind the tunnel lining. The backfilling material studied here is crushed sand and stone-dust which is in cake-state and is a by-product obtained in the producing process of aggregate. Varying the compound mixing ratio, laboratory tests of compression test and chemical analyses were carried out. In addition, the material was applied to an old tunnel for the performance assessment.

• Journal of the Korean Recycled Construction Resources Institute
• /
• v.4 no.3
• /
• pp.307-315
• /
• 2016

The aim of this research is analyzing the fundamental properties and autogenous shrinkage reducing performance of 70 and 100MPa grade high performance concrete including emusified refined cooking oil(ERCO) under the mock-up conditions. As a results of experiment, the mixture contained 0.5% of ERCO showed slightly decreased slump flow while the slump was increased and segregation resistance performance was improved as 2.5 of EIS. For air content, all mixtures satisfied target air content with increased unit weight and delayed setting time with ERCO addition. In the case of compressive strength, when ERCO was added 0.5%, the result of approximately 5 to 10% of increased compressive strength was observed. For the autogenous shrinkage, ERCO contributed on 20-30% of shrinkage reducing performance comparing to Plain mixture without ERCO. It is considered that capillary pore filling action of soap particles occurred by the reaction of ERCO in cement paste between fatty aicd and calcium hydroxide contributed the shrinkage reducing performance. Based on these mock-up test results, application of the high performance concrete mixture with ERCO on CFT actual structure was decided.

• International Journal of Highway Engineering
• /
• v.11 no.3
• /
• pp.41-49
• /
• 2009

Cement concrete pavement has become more common in Korean highway systems. However, as its service period increases, there are some technical problems occurs and no clear solution is available primarily due to the lack of active researches. This research, hence, aims to develop a new mix proportion that may provide better strength and durability with extended service life. Based on a variety of literature reviews, the experimental variables were determined as unit cement content, S/a ratio and W/C ratio. From the experimental works, it is recommended to increase the unit cement content up to 375kg/$m^3$, 400kg/$m^3$ and 425kg/$m^3$. The target slump and air content were set 40mm and 5%, respectively. The maximum size of coarse aggregate was decided to be 25mm because of the easiness of supply in the field. The reduction of W/C ratio was necessarily required and decreased to 0.4 which was proven not to cause any mixing problem with the increased unit cement contents along with polycarbon-based high range water reducing agent. In addition, it was known that the S/a ratio could be reduced to 0.34. The lowered S/a might be possible because of the increased cement paste and hence increased cohesiveness and workability.

• Journal of Korean Tunnelling and Underground Space Association
• /
• v.8 no.3
• /
• pp.273-287
• /
• 2006

This study investigates the failure mechanism and load-carrying capacity of a single-shell lining which has no disturbance in transfer of shear force, with respect to a conventional double-shell lining which has separation between layers of shotcrete lining and secondary concrete lining by water-proof membrane. In order to evaluate the capacity, a 2-D numerical investigation is preliminarily carried out and then real-scale loading tests with tunnel lining section specimens are performed on the condition given by the numerical investigation. In the test, a concentrated load is applied for considering a released ground load or rock wedge load. Through this study, it appears that the single-shell lining takes the load-bearing capacity 20% higher than in case of the double-shell lining. In addition, a possibility of a composite single-shell shotcrete layer composed by multiple bonded layers partly involving different contents of high-capacity additives is shown thereby leading to use of less amount of the high-capacity additives on the condition of taking a similar load-bearing capacity.