• Journal of the Korean Society of Clothing and Textiles
• /
• v.27 no.7
• /
• pp.862-871
• /
• 2003

Kenaf has been estimated as an economic and environmentally compatible crop. This study purposed to enlarge the use of kenaf as textile materials and to develope high value-added textile fibers. Kenaf has been cultivated successfully and grown fast in Jeju. The height of kenaf stalks was about 220cm at 105 DAP and 400cm at 150 DAP, After harvesting at 105 DAP and seperating the basts from harvested kenaf stalks, decorticated kenaf basts were rotted in water at 15~$25^{\circ}C$ for biological rotting and were treated with 1%, 4% and 7% NaOH at 9$0^{\circ}C$ for chemical retting. The properties of extracted fibers were compared: such as fiber diameter. Transversal and longitudinal views, colors, crystallinities, strengths and elongations etc. The diameter of kenaf bast fibers was 15~25 ${\mu}{\textrm}{m}$. Biologically rotted kenaf bast fibers had well developed lumens which were diminished after chemical retting. The degree of crystallinities of biologically rotted kenaf bast fiber was about 92~96% showed higher than those of chemically rotting. The biologically rotted fibers were bright and had creamy color. Yelloweness increased at chemically rotted fibers. Fiber bundle strengths were from maximum 98076.9 (gf/g) to minimum 63749.5 (gf/g). Fiber bundle strengths of biologically rotted kenaf fibers appeared greater than those of chemically rotted fibers. Alkali treatments of chemical rotting could make strength lower and elongation higher. Rotting method might be one of the most importance factors affecting to final fiber properties.

• Korean Journal of Environmental Biology
• /
• v.22 no.1
• /
• pp.120-126
• /
• 2004

Kenaf plants were hydroponically grown in reactor containing toxic metals as Cd, Cu, Cr, Ni and Zn to examine the ability to take up heavy metal. The plants were fertilized using a nutrient solution, which was appropriately adjusted to optimum pH, DO and conductivity. For n hydraulic retention time of 8 days, Cr, Cd, Cu, Ni and Zn were removed up to 90.5, 80.5, 66.1%, 71.1% and 79.4%, and reduced from 2.34 to 0.54 mg $L^{-1}$, 3.37 to 1.07 mg $L^{-1}$, 4.92 to 3.19 mg $L^{-1}$, 6.31 to 4.41 mg $L^{-1}$ and 6.27 to 2.09 mg $L^{-1}$. Especially, accumulation rate of Cr, Cd, Cu, Ni and Zn in the plant were measured up to 347.32, 275.39, 157.52, 50.48 and 211.01 mg DW kg $L^{-1}d^{-1}$, respectively. We considered that Kenaf plants removed Cr, Cd and Zn more effectively than other toxic metals applied.