• Journal of Biomedical Engineering Research
• /
• v.22 no.6
• /
• pp.511-518
• /
• 2001

In vitro corrosion resistance of the commercially used 76.5wt.%Pd-17.6%Cu-7.2%Ga and 77.3%Pd-6.0%Ga dental Prostheses high-Palladium system alloys in cast, degassing and porcelain-firing heat treatment conditions were evaluated by the potentiodynamic polarization technique in the de-aerated 0.9%NaCl and a modified Fusayama electrolyte. From the corrosion rate experimental results, we found that there is a small difference in the corrosion resistance depending on the microstructure. However. it was so small that there is no significant problem as a dental material. The 77.3%Pd-6.0%Ga showed better corrosion resistance than the 76.5%Pd-11.6%Cu-7.2%Ga dental Prostheses high-palladium system alloys. These experimental observations in 76.5%Pd-11.6%Cu-7.2%Ga alleys are mainly due to a rapid quenching and Cu in the alloy which accelerate the eutectic reaction with a segregation and Precipitates in the microstructure. On the ocher hand, 77.3%Pd-6.0%Ga alloys, which are solid-solution matrix, show much better col·lesion resistance compared with that of 76.5%Pd-11.6%Cu-7.2%Ga alloys.

• Journal of Biomedical Engineering Research
• /
• v.20 no.4
• /
• pp.443-449
• /
• 1999

현재 시판되고 있는 치과용 76.5%Pd-11.6%Cu-7.2^%GarP 합금의 주조상태 및 임상열처리에 따른 미세조직의 변화를 X-선 회절기, 광학현미경, 시차열분석기를 이용하여 관찰하였다. 주조상태, 탈개스 및 세리믹소성처리 후 미세조직은 Pd고용체와 금속간화합물 Pd2Ga으로 구성되어 나타났고, 이들 상들은 열처리에 따라 상당한 변화를 보였다. 또한 Pd은 아르곤 분위기 내의 산소와 반응하여 산화물 형성 및 분해로 인해 질량변화곡선(TG)이 변하였고, 시차열분석(DTA)에서는 약 815$^{\circ}C$ 정도에서 Pd2Ga에 기인하는 흡열피크를 확인하였다. 이러한 실험의 결과들은 Cu가 이원계 Pd-Ga 합금의 Ga의 고용량을 낮추어 공정반응이 저 Ga 쪽으로 이동하기 때문인 것으로 설명하였다. 그러나 앞으로 보다 명확한 상변태 규명을 위해서 TEM등의 분석장비를 사용하여 체계적인 연구가 요구된다.