• The Science & Technology
• /
• v.11 no.6 s.109
• /
• pp.35-37
• /
• 1978

한국기계금속실험연구소 (소장: 정낙은)는 특정연구기관육성법에 따라 설립된 전문연구기관으로 중화학공업의 중추인 기계금속분야의 실험, 검사에 의하여 국산 기계금속제품의 품질 향상을 촉진시키고 적극적인 연구개발활동으로 기술혁신의 선도적 지도로 기업간의 기술격차를 극소화 하며 그 수준을 평준화함으로써 국제경쟁력을 강화하여 수출산업의 구조개편 ,자력국산화 촉진등 국가경제발전에 기여함을 목적으로 하고 있다.

• Journal of the Korea Institute of Building Construction
• /
• v.15 no.1
• /
• pp.25-33
• /
• 2015

In this study, initial crack index was evaluated by FEM analysis to find the crack propagation from hydration heat in precast concrete. As results, as the usage of hardening accelerator increased, initial compressive strength increased and setting time was shortened. Additionally, as amounts of hardening accelerators increased, the central temperature of concrete increased and the time to reach the highest temperature was shortened. It was demonstrated that the hardening accelerators accelerated the hydration reaction of cement, and caused the increase of hydration heat within the short period of time. Furthermore, the crack index for evaluating the heat level was performed by FEM. As results, there was no problem about the cracks, despite of the growth of initial high hydration heat. This is because of the increased tensile strength that is large enough to sustain the thermally induced-stress.

• The Hankook-Saengyark Bo
• /
• no.250
• /
• pp.3-3
• /
• 2002

약초생산량 기하급수적 감소추세(수급조절품목서 제외되면서 부터) - 논농업직불제 지원작목 확대(작약, 목단등 약용작물도 재배 가능) - 자생식물로 성장촉진 물질개발

• Bulletin of the Society of Naval Architects of Korea
• /
• v.3 no.1
• /
• pp.3-10
• /
• 1966

• Magazine of RCR
• /
• v.16 no.2
• /
• pp.72-73
• /
• 2021

• Proceedings of the Korea Water Resources Association Conference
• /
• 2020.06a
• /
• pp.224-224
• /
• 2020

새롭게 개발된 미생물의 부산물인 바이오 폴리머는 토양의 강도를 높이고, 식물의 생장을 촉진시킨다. 본 연구에서는 실규모 수리 실험을 수행하여 바이오 폴리머를 이용한 호안 공법의 침식 저항 성능을 평가하였다. 실험을 위하여 다수의 호안 공법 시험체를 제작하였고, 이 시험체를 실 규모 실험수로에 설치하고 수리 실험을 통해 토양 손실과 이에 따른 한계 소류력을 결정하였다. 실험에는 일반 흙을 피복한 시험체, 바이오 폴리머와 혼합한 흙을 피복한 시험체, 식생매트와 바이오 폴리머 혼합토를 결합한 시험체 등이 사용되었다. 실험결과 재료나 식생의 활착도에 따른 차이는 있었으나 바이오 폴리머를 이용한 시험체의 침식 저항 성능이 바이오 폴리머를 이용하지 않은 시험체에 비해 높게 나타나는 것은 일관되게 확인 할 수 있었다. 이러한 결과는 바이오 폴리머를 이용한 호안공법이 기존 호안 공법의 침식 저항성능을 향상 시킬 수 있음을 보여준다. 바이오 폴리머를 제방 호안 시공에 활용한다면 홍수로 인한 제방의 유실이나 파괴를 상당 부분 예방할 수 있을 것이다.

• Journal of Korean Tunnelling and Underground Space Association
• /
• v.17 no.3
• /
• pp.283-293
• /
• 2015

In order to evaluate corrosion resistance of steel fiber-reinforced concrete, accelerated chloride migration and surface resistivity tests were conducted. In addition air content of fresh concrete, compressive strength and water absorption were measured for investigating fundamental characteristics of concrete. Two different water-cement ratios(0.44, 0.5) and three steel fiber contents(0.25%, 0.5%, 1%) were considered as variables. Note that all specimens cast with same compaction work. As a results, corrosion resistance decreased as steel fiber contents increased regardless of water-cement ratio when the concrete was compacted with same amount of work done. However, for concrete with same steel fiber content, the lower water-cement ratio showed the better corrosion resistance. It is found that enhancement of fluidity and enough compaction should be done for corrosion resistance of SFRC.

• Journal of the Korea Concrete Institute
• /
• v.14 no.2
• /
• pp.148-155
• /
• 2002

This research investigates the moisture and aging effects of wastepaper fiber-cement composites. Wastepaper fibers is obtained by a dry process. Wastepaper fiber-cement composites was manufactured by the hatscheck process. The effects of moisture and aging on the performance of wastepaper fiber-cement composites were investigated through accelerated laboratory tests simulating the effects of moisture sensitivity and wet-dry cycles as well as freeze-thaw cycles and long-term drying. They were shown to possess acceptable moisture and aging performance compared with virgin fiber cement composites.

• Magazine of the Korea Concrete Institute
• /
• v.9 no.3
• /
• pp.189-197
• /
• 1997

This paper describes an experimental study on the seawater resistance of steel fiber reinforced concrete. The test methods adopted for this study are divided into long-term immersion test and acceleration test by wetting and drying. Tests were carried out to evaluate the procedures which were measured for nine months about reduction in dynamic modulus, length change and compressive strength. Resistance indicators are the water-cement ratio, the content of steel fiber, the content of fly ash, the immersion water(artificial seawater or freshwater) and the types of curing. The seawater resistance of the appropriate additions of steel fiber and fly ash have apparently increased.

• Applied Chemistry for Engineering
• /
• v.28 no.1
• /
• pp.35-41
• /
• 2017

Materials exposed to outside will deteriorate due to various weathering factors such as sunlight, heat, temperature, humidity and so on. Therefore, predicting speed of degradation and life time is a very important issue. This research uses retro-reflective sheets with white and green which are most commonly used colors to conduct the outdoor exposure test and acceleration test of xenon arc in Arizona state in the United States, Chennai in India, Sanary in France and Seosan in Korea to measure the reflective performance of retro-reflection. The accelerated factor was obtained by using regression analysis through reflective values obtained from the acceleration test of xenon arc from Seosan area. Also, by using solar uv program, the accelerated factor of various climate regions were obtained and it was confirmed that the accelerated factor of Senary was 1.04, Arizona 1.82, Chennai 1.92 times higher than that of Seosan.