• Corrosion Science and Technology
• /
• 제15권1호
• /
• pp.18-27
• /
• 2016

In this study, the accelerated corrosion test by combined deteriorating action of salt damage and freeze-thaw was investigated. freeze-thaw cycle is one method for corrosion testing; corrosion initiation time was measured in four types of concrete samples, i.e., two samples mixed with fly ash (FA) and blast furnace slag (BS), and the other two samples having two water/cement ratio (W/C = 0.6, 0.35) without admixture (OPC60 and OPC35). The corrosion of rebar embedded in concrete occurred most quickly at the $30^{th}$ freeze-thaw cycle. Moreover, a corrosion monitoring method with a half-cell potential measurement and relative dynamic elastic modulus derived from resonant frequency measures was conducted simultaneously. The results indicated that the corrosion of rebar occurred when the relative dynamic elastic modulus was less than 60%. Therefore, dynamic elastic modulus can be used to detect corrosion of steel bar. The results of the accelerated corrosion test exhibited significant difference according to corrosion periods combined with each test condition. Consequently, the OPC60 showed the lowest corrosion resistance among the samples.

• 한국방재학회 논문집
• /
• 제9권1호
• /
• pp.15-20
• /
• 2009

해양환경 하에 건설되는 콘크리트구조물은 다양한 염해 환경에 노출되어 있으며, 이중 염소이온의 침투 및 확산으로 인한 콘크리트 중의 철근부식과 화학적 침식 등은 콘크리트구조물의 주요 성능저하 요인으로 지적되고 있다. 따라서 해수 중의 염소이온의 침투 및 확산 메커니즘을 효율적으로 평가하기 위하여 전기화학적 촉진시험으로부터 염소이온의 확산계수를 추정하였다. 또한 콘크리트의 압축강도, 투수공극량 및 염소이온의 침투깊이 등과 염소이온의 확산계수와의 상관관계를 분석하기 위하여 회귀분석을 실시하였다. 본 연구의 시험결과에 의하면, 물-시멘트비 40~60%의 범위에서 보통콘크리트의 염소이온 확산계수는 $2.5{\sim}6.6{\times}10^{-12}m^2/s$ 정도였으며, 염소이온의 확산계수와 콘크리트의 물성과의 상관관계는 선형의 상관관계가 있었다.

• 한국건설순환자원학회논문집
• /
• 제6권1호
• /
• pp.59-65
• /
• 2018

콘크리트 구조물은 다양한 환경에 노출되며, 부식환경인 해안가에서는 매립 보강재의 부식저항성 및 동결융해 저항성이 함께 평가되어야 한다. 최근 개발된 FRP Hybrid Bar는 내부에 강재가 있으며 유리섬유와 에폭시가 코팅된 보강재인데, 기존 FRP Bar보다 탄성계수가 높은 장점이 있다. 본 연구에서는 FRP Hybrid Bar에 대하여 동결융해 300 cycle 시험을 수행한 뒤, 내부식특성과 중량결손율, 및 부착특성을 평가하였다. 300 cycle 이후 2번 에폭시를 코팅한 경우에 규사의 손실이 가장 적었으며, 외관의 결함이 관측되지 않았다. 부착강도는 규사코팅에 따른 조도의 증가로 FRP Hybrid Bar의 경우 일반철근의 120 % 수준을 나타내었다. 또한 일반철근을 가진 시편의 부착력은 부식시간 3일에서는 0.86 ~ 0.89 배, 5일에서는 0.35~0.38 배로 크게 감소하였으나, 동결융해 전후의 FRP Hybrid Bar를 가진 콘크리트 공시체는 부착강도의 감소가 발생하지 않았다.

• 헤리티지:역사와 과학
• /
• 제56권2호
• /
• pp.148-169
• /
• 2023

하엽은 짙은 녹색을 띠는 전통 안료 중 하나로 알려져 있지만 색상, 원료물질, 제법 등에 대해서 명확히 규명되지 않은 상태이다. 다만, 단청, 괘불, 회화 등 채색문화유산의 안료 분석연구를 통해 밝혀진 하엽 안료의 입자형태나 구성광물 등을 볼 때 염 부식으로 제조된 동록 안료로 보인다. 따라서 하엽 안료를 복원하기 위해 고문헌 기록을 바탕으로 동록 안료의 제조방법을 연구하였다. 고문헌 기록에서 확인되는 동록 안료의 제조방법은 동분말과 부식제를 혼합한 후 습한 조건에서 방치하여 부식시키는 자연 부식방법이다. 이를 바탕으로 보다 효율적으로 동분말을 부식시키기 위해 부식시험기를 이용한 인공부식을 도입하였고, 부식제 혼합비율, 부식 기간에 따른 부식생성물의 상태를 분석하여 적정 혼합비율과 부식 기간을 선정하였다. 또한, 잔류 부식제를 제거하기 위한 염 제거 공정과 안료 채색 시 채도를 높이기 위한 정제공정을 추가하여 동록 안료의 제조방법을 체계적으로 정립하였다. 정립된 방법으로 제조된 동록 안료는 청록 혹은 녹색의 색상을 나타냈다. 안료 입자는 표면이 다공성으로 타원형 형태의 작은 입자들이 뭉쳐져 있는 형태를 보였다. 주요 구성원소는 구리(Cu)와 염소(Cl)이고, 구성광물은 녹염동광[atacamite, Cu2Cl(OH)3]으로 동정되었다. 제조된 동록 안료의 안정성 평가를 위해 촉진내후성 시험을 진행한 결과, 열화가 진행됨에 따라 녹색도가 일부 감소하고 황색도가 증가하는 색변화 경향을 보였다. 따라서 열화 전 동록 안료의 색도는 고단청의 하엽 안료와 비교할 때 황색도가 낮은 편이었으나 열화 후에는 황색도가 크게 증가하여 고단청의 하엽 안료와 유사한 색도 범위를 갖는 것으로 나타났다. 결과적으로 제조된 동록 안료는 입자형태나 구성광물뿐만 아니라 색상에서도 고단청의 하엽 안료를 구현하여 재현성이 높은 것으로 확인되었다.

• Corrosion Science and Technology
• /
• 제13권6호
• /
• pp.214-223
• /
• 2014

Interest in the durability assessment and structural performance has increased according to an increase of concrete structures in salt damage environment recent years. Reliable way ensuring the most accelerated corrosion test is a method of performing the rebar corrosion monitoring as exposed directly to the marine test site exposure. However, long-term exposure test has a disadvantage because of a long period of time. Therefore, many studies on reinforced concrete in salt damage environments have been developed as alternatives to replace this. However, accelerated corrosion test is appropriate to evaluate the critical chlorine concentration in the short term, but only accelerated test method, is not easy to get correct answer. Accuracy of correlation acceleration test depends on the period of the degree of exposure environments. Therefore, in this study, depending on the concrete mix material, by the test was performed on the basis of the composite degradation of the salt damage, and investigate the difference of corrosion initiation time of the rebar, and indoor corrosion time of the structure, of the marine environment of the actual environments were inuestigated. The correlation coefficient was derived in the experiment. Long-term exposure test was actually conducted in consideration of the exposure conditions submerged zone, splash zone and tidal zone. The accelerated corrosion tests were carried out by immersion conditions, and by the combined deterioration due to the carbonation and accelerated corrosion due to wet and dry condition.

• 한국콘크리트학회:학술대회논문집
• /
• 한국콘크리트학회 2008년도 춘계 학술발표회 제20권1호
• /
• pp.973-976
• /
• 2008

염해환경에 건설되는 콘크리트 구조물은 염소이온과 같은 유해이온이 외부로부터 콘크리트 중으로 침투, 확산하여 철근을 부식시킴으로써 구조물의 내구성을 크게 저하시키기 때문에 구조물의 내구성 평가 또는 설계시 중요한 고려사항이 된다. 현재 설계에서 사용되는 확산계수는 각 나라마다 제시된 근거가 다르므로, 직접 비교 검토하는 것이 곤란할 뿐만 아니라 동일 환경조건에서 동일 배합의 콘크리트에 대한 수명예측 결과가 크게 상이한 결과를 초래하게 된다. 본 연구는 염해환경하 콘크리트의 염해 내구성능 품질관리를 적용하기 위해서 현장에서 적용할 수 외국에서 규격화된 시험방법들을 비교 검토하고 이들 시험 방법 가운데 품질관리에 적합한 시험방법을 선정하여 재령별 확산 특성과 침지 시험 결과를 비교하여 분석하였다. 슬래그 미분말을 혼입한 콘크리트의 경우 침지시험(NT Build 443)과 촉진시험(NT Build 492)의 상관성을 분석한다면, 이들 토대로 콘크리트 배합의 품질관리 기준 확산계수를 도출할 수 있을 것으로 판단된다.

• 한국콘크리트학회:학술대회논문집
• /
• 한국콘크리트학회 2006년도 춘계 학술발표회 논문집(II)
• /
• pp.69-72
• /
• 2006

Recently sewage facilities mainly consisted of concrete structures are being deteriorated seriously by biodeterioration originated from sulfur-oxidizing bacteria. To prevent biochemical corrosion of the sewage concrete, antibiotics which prevent growth of sulfur-oxidizing bacteria were developed. Existing methods to evaluate properties of biochemical corrosion of concrete examine the antimicrobial performance and resistance to sulfuric acid separately, but don't complexly. So, in this study, new method to test properties of biochemical corrosion of concrete complexly is suggested.

• Corrosion Science and Technology
• /
• 제8권2호
• /
• pp.53-61
• /
• 2009

본 연구에서는 강교 도장재료로 사용될 수 있는 에폭시 하도 도료를 도포한 시험편을 촉진시험을 통해 열화시킨 후 도막의 외관 평가 및 EIS에 의한 평가를 실시하고, 그 2가지 방법에 대한 비교 분석을 실시하였다. 화상처리 기법에 의해 구한 총 열화 면적율과 열화도 평점 산정 결과를 상호 비교해 본 결과 녹이 발생한 경우가 그렇지 않은 경우보다 열화도 평점이 높게 나타났다. 이는 강교 도장의 열화도 평가 기준에서 단위 열화 면적율당 부여하는 열화도 평점이 박리의 경우보다 녹의 경우가 더 크기 때문이다. 열화 면적율과 EIS 측정 데이터를 비교해 본 결과 녹의 면적율 약 0.1% 이상, 블리스터링의 면적율 약 3% 이상만 되어도 도막의 임피던스는 약 $10^4{\Omega}{\cdot}cm^2$ 혹은 그 이하로 크게 저하되었다. 2개의 시험편을 제외한 모든 시험편에 대해 전하전달저항(charge transfer resistance, $R_{ct}$)과 이중층 정전용량(double layer capacitance, $C_{dl}$) 값이 나타났으며, 이 결과로부터 이들 시험편들은 도막과 강재 계면에 수분이 축적되어 부식이 진행되고 있음을 알 수 있었다. 열화도 평점과 EIS 측정결과를 상호 비교해 본 결과 저주파수(10 mHz)에서의 임피던스 값이 $10^6{\Omega}{\cdot}cm^2$ 이하로 떨어진 경우는 모두 열화도 평점이 10점 이상으로 나타났으며, NORSOK cyclic test 과정에 의해 열화시킨 경우 열화도 평점이 높지 않음에도 불구하고 임피던스는 가장 낮게 나타났다. 이것은 도장계와 열화조건이 주 시험편과 다르기 때문인 것으로 판단되며, 열화조건이 더 가혹하거나 복합적일 경우 외관 상태에 비해 도막의 저항이 더 크게 저하될 가능성이 있다고 생각된다.

• 한국건축시공학회지
• /
• 제15권2호
• /
• pp.143-151
• /
• 2015

실환경에서는 비래염분 뿐만 아니라 자외선, 산성비, 산업공해 부유 물질 등의 여러 가지 복합 열화요소에 노출되어 있어 강재가 발청(發錆)하는 임계 비래염분량을 찾기에 어려움이 있다. 본 연구에서는 비래염분 시뮬레이터를 사용하여 인위적으로 비래염분 부착량을 조절하였으며 강재 마감별 5종을 대상으로 부식촉진 시험을 실시하였다. 그 결과 NC, UC, RLC-1, SS201에 각각 0.58~0.73, 7.89~8.46, 57.95~69.48, $80.73{\sim}89.35mg/dm^2$의 비래염분량을 부착시켰을 때 발청하는 것을 확인할 수 있었으며, 발청 후 부식속도는 각각 1.60, 0.36, 0.97, 0.17로 NC가 가장 빠른 부식속도를 가지는 것으로 평가 되었다.

• 보존과학회지
• /
• 제34권6호
• /
• pp.503-515
• /
• 2018

원주 법천사지 지광국사탑의 1957년 수리 복원에 사용된 모르타르의 손상정도를 평가하고 제거 필요성에 대한 객관적인 데이터를 제공하기 위해 콘크리트 분야에서 사용되는 반전위측정방법을 적용하였다. 철근이 사용된 옥개석 모르타르와 실내 실험체의 촉진부식시험 후 반전위 측정값에 대한 다중회귀분석 결과, 부식량과 피복두께에 따른 HCP 값의 결정계수는 0.86이상의 높은 상관식이 도출되었다. ASTM C876기준에 따르면 옥개석의 습윤상태 측정값 - 431~-663 mV는 철근의 부식손상 확률이 90%이상이기 때문에 손상된 모르타르를 제거한 후 신석재를 사용한 복원이 필요한 것으로 판단된다.