• Korean Journal of Materials Research
• /
• v.10 no.7
• /
• pp.505-514
• /
• 2000

The carburizing behavior and fatigue properties of the plasma carburized low carbon Cr-Mo steel(0.176C-1.014Cr-0.387Mo) have been investigated. The effective case depth in plasma carburized steel increased up to 50% in comparison with that of gas carburizing, and this case depth increased with the increasing surface carbon content. With increasing time in plasma carburizing, the surface carbon content increased but its increasing rate decreased. Fatigue properties were studied in terms of microstructure, case depth, retained austenite and residual stress near the surface. The fatigue limit of the plasma carburized steel was higher than that of gas carburized one. The initiation of microcracks and initial crack propagation were retarded due to a relatively little surface and internal oxidation layer in plasma carburized steel. Fractography showed the crack initiated at the surface, and transgranular fracture at surface layer was more predominant in plasma carburized steel compared to that of gas carburized steel.

• Journal of the Korea Academia-Industrial cooperation Society
• /
• v.21 no.10
• /
• pp.386-392
• /
• 2020

The self-weight of the 3D printing concrete increases with increasing printing height. Therefore, the lower layer must be hardened within a suitable time to secure continuous printing performance. In particular, the hardening speed of concrete is slow in the winter season when the temperature was low. Hence, the early strength of 3D printing concrete requires improvement. In domestic and international literature, cases of increasing the early strength of concrete using inorganic chemical additives, such as amine-based, nitrate-based, sodium-based, and calcium-based, have been reported. In this study, early strength improvement-type additive samples (amine-based, nitrate-based, sodium-based) were prepared, and their performance was evaluated. When using a nitrate-based additive, the early strength was increased significantly in a 10 ℃ environment. In addition, it was possible to secure a higher early strength than the existing 3D printing concrete mixed at 20 ℃.

• Polymer(Korea)
• /
• v.37 no.1
• /
• pp.41-46
• /
• 2013

The glass transition temperature ($T_g$) and conversion (${\alpha}$) were measured for a diglycidyl ether of bisphenol A (DGEBA) epoxy/aromatic amine system incorporated with an organic-inorganic hybrid molecule, polyhedral oligomeric silsesquioxane (POSS). Samples isothermally cured at varying cure temperatures and times were analyzed by differential scanning calorimetry (DSC). $T_g$ vs. ln (time) data at an arbitrary reference were superposed by time-temperature shifts for the kinetically controlled reaction, and the shift factors were used to calculate an Arrhenius activation energy. Influence of POSS was investigated from $T_g$ vs. ${\alpha}$ data, which in turn were fitted with DiBenedetto equation.

• Restorative Dentistry and Endodontics
• /
• v.28 no.4
• /
• pp.295-302
• /
• 2003

본 연구에서는 인산 칼슘 근관 봉함재 [Apatite Root Sealer (ARS) Type I, II, III]의 세포독성을 혼합후의 시간 경과에 따라서 다른 4계열의 근관 봉함재 (Pulp Canal Sealer EWT, AH Plus, Sealapex, Ketac Endo)와 비교하여 평가하였다. 근관 봉함재를 혼합한 후 1시간, 8시간, 24시간, 48시간, 1주, 2주,4주의 기간동안 배양액을 이용하여 추출액을 얻었다. L929 쥐섬유아세포를 24시간동안 각 시간군에서 얻은 추출액과 함께 배양한 후 dimethylthiazol diphenyltetrazolium (MTT) assay와 neutral red (NR) assay를 이용하여 세포독성(%)을 평가하였다. 실험 결과 ARS Type I, II, III는 전 시간군에 걸쳐 낮은 세포독성을 보였고 (23.65-0.55%) 특히 경화 초기에 다른 계열의 근관 봉함재보다 유의성 있게 낮은 세포독성을 나타내었다. ARS Type I, II, III간의 세포독성은 각 시간군에서 유의성 있는 차이를 보이지 않았다. AH Plus와 Ketac Endo는 초기에 높은 세포독성을 보였으나 AH Plus는 8시간 이후에, Ketac Endo는 24시간 이후에 독성이 급격히 감소하여 ARS와 유의성 있는 차이를 보이지 않았다. Pulp Canal Sealer EWT와 Sealapex는 4주까지 지속적인 세포독성을 나타내었다. 그리고 MTT assay와 NR assay를 이용하여 얻은 각 근관봉함재의 세포독성은 시간 경과에 따라서 비슷한 변화 양상을 나타내었다. 인산 칼슘 근관 봉함재는 생체적합성이 우수한 재료로써 앞으로 지속적인 개발과 평가가 필요할 것으로 사료된다.

• Journal of the Korea Concrete Institute
• /
• v.13 no.5
• /
• pp.447-456
• /
• 2001

Many investigators have tried to represent the nonlinear behavior of stress-strain relationship of concrete using mathematical curves. Most of empirical expressions for stress-strain relationship, however, have focused on old age concrete, and were not able to represent well the behavior of concrete at an early age. Where wide understanding on the behavior of concrete from early age to old age is very important in evaluating the durability and service life of concrete structures. In this paper, effect of 5 different strength levels and ages of from 12 hours to 28 days on compressive stress-strain relationship was observed experimentally and analytically. Tests were carried out on $\phi$100${\times}$200mm cylindrical specimens water-cured at 20${\pm}$3$^{\circ}C$. An analytical expression of stress-stain relationship with strength and age was developed using regression analyses on experimental results. For the verification of the proposed model, the model was compared with present and existing experimental data and some existing models. The analysis shows that the proposed model predicts well experimental data and describes well effect of strength and age on stress-strain relationship.

• Composites Research
• /
• v.22 no.6
• /
• pp.39-44
• /
• 2009

The effect of exposure times on the aging characteristics of carbon fiber/epoxy composite ring specimen was evaluated using an accelerating aging tester. Combined exposure conditions, such as temperature, moisture, and ultraviolet, were applied up to 3000 hours. Tensile properties and flexural properties including the effect of curvature were evaluated on the specimens subject to various exposure times through a material testing system. Their aging surfaces were observed through a scanning electron microscope. According to the results, tensile modulus was little affected by the exposure times. However, tensile strength, at the early stage of the exposure times, increased due to physical aging and curing reaction, but tensile strength slightly decreased due to degradation as the exposure times increased. The flexural modulus and flexural strength increased at the early stage of the exposure times, but slightly decreased as the exposure times increased. Aging surfaces of the specimens examined using the scanning electron microscope revealed a different morphology in various exposure times and provided useful information for identifying the degradation in mechanical properties of the composite subject to various exposure times.

• Elastomers and Composites
• /
• v.40 no.3
• /
• pp.196-203
• /
• 2005

In this work, the engine oil resistant evaluation and breakdown analysis of room temperature vulcanizing silicone adhesives were performed through the surface properties, thermal stabilities, adhesive strength, and morphology measurements. As a result, the permeation of engine oil into adhesive specimens was carried out from surface to center in the specimens. And the oil content in the adhesive specimens was increased and the Si-O-Si bond of the adhesives was decomposed with increasing the aging time. The TGA results indicated that the thermal degradation was mainly occurred at under and surfaces of the specimens. The tensile strength, elongation, and adhesive strength of the adhesives were significantly decreased after the engine oil resistant tests, which could be attributed to the initial lose of adhesive properties resulting from the engine oil absorption and thermal aging. And the failure mode of the adhesive specimens was changed from cohesive failure to interfacial failure.

• Applied Chemistry for Engineering
• /
• v.9 no.4
• /
• pp.579-584
• /
• 1998

Polymer dispersed liquid crystal(PDLC) composite films were made by polymerization induced phase separation method using UV-curing to investigate the effect of fabrication conditions, such as photoinitiator concentration, film thickness, polymerization temperature, and electric field during polymerization, etc., on the electro-optic properties. As the amount of photoinitiator increased, the driving voltage of PDLC device increased due to the increase of small-size liquid crystal phases. This was considered as the results from the increased interfacial area between liquid crystal (LC) and polymer matrix, since LC molecules at the interfacial regions were relatively difficult to response for the applied electric field. When the higher molecular weight oligomer (PTDA-1000) was used as matrix, the initial transmittance was observed to be relatively higher than that for the lower molecular weight oligomer (PTDA-250). Saturation transmittance for PTDA-1000 was observed at relatively lower voltage than that for PTDA-250, of which transmittance was not saturated even at 60 V. As polymerization temperature increased, the initial transmittance of resulting PDLC film increased due to the larger LC droplets formation and the more matched refractive index between LC and matrix than those cases for the lower polymerization temperature. Though driving voltage decreased for the thinner film, it was considered that optimum thickness of the film should be maintained to get some practical contrast, which is the ratio of off- and on-state transmittance. Furthermore, electro-optic properties such as initial transmittance, driving voltage, and response time were observed to be considerably affected by application of external field during polymerization.

• Journal of Yeungnam Medical Science
• /
• v.18 no.2
• /
• pp.215-225
• /
• 2001

Background: There are many evidences that inflammation is an important determinant of the development of atherosclerosis and one of the systemic markers of inflammation, C-reactive protein(CRP), is associated with extent of coronary artery disease and risk of coronary events. We assessed the time response of CRP response after coronary angioplasty and it's influence on the clinical restenosis in angina patients. Materials and Methods: Patients included 36 angina patients undergoing single vessel angioplasty. Levels of CRP were measured before and 12, 24, 48, and 72 hours after angioplasty. Clinical restenosis was assessed at 6 months after procedure. Results: Baseline CRP level was $0.30{\pm}0.01$ mg/dL in stable and $0.46{\pm}0.28$ mg/dL in unstable angina patients(p<0.05). After angioplasty, CRP level was increased with peak at 24 hour and persisted to 72 hours after angioplasty. At 24 hour after angioplasty, the magnitude of CRP change was $0.32{\pm}0.31$ mg/dL in stable and $0.79{\pm}0.73$ mg/dL in unstable angina patient(p<0.05). The change of CRP level was not associated with troponin-T after angioplasty. In unstable angina patients, clinical restenosis was developed in 8% of patients with low baseline CRP levels and in 50% of those with high baseline CRP levels more than 0.6 mg/dL(p<0.05). Conclusion: In unstable angina patients, inflammatory response is more increased than stable angina patients, and increased inflammatory response effects on the restenosis after coronary angioplasty.

• Proceedings of the Korean Institute of Electrical and Electronic Material Engineers Conference
• /
• 2004.07a
• /
• pp.82-85
• /
• 2004

Colloidal Silica(CS) HSA/2327과 methyltrimethoxysilane(MTMS), 1034A와 tetramethoxysilane(TMOS)/MTMS 간의 졸겔 반응조건이 코팅도막의 특성에 미치는 영향을 조사하기 위하여 CS종류, CS 대비 TMOS/MTMS의 함량비, 반응시간 등을 달리하여 졸을 합성하고, 합성된 졸을 slide glass에 코팅한 후 $300^{\circ}C$에서 경화시킨 도막의 특성들을 조사하였다. HSA/2327/MTMS에 의한 졸로부터 제조된 코팅도막은 졸 반응시간 의존성이 거의 없으며 반응초기부터 접촉각이 상당히 안정되어 있고 특히 낮은 MTMS 함량을 가진 졸들이 더욱 안정된 표면물성을 보였다. 1034A/TMOS/MTMS에 의해서 제조된 코팅도막은 적절한 소수성의 형성과 표면조도의 향상과 더불어 안정된 접촉각 양상을 나타내었다. 표면거칠기는 HSA/2327 혼합 CS계에 의해서는 반응시간이 길고 MTMS 함량이 높아질 때 비교적 표면조도가 나빠지는데 반응시간과 더불어 약간씩 증가하는 경향을 보였다. 1034A CS계에서는 반응시간과 MTMS 함량의 조건에 영향을 받지 않고 표면조도와 균질성이 우수하였다.