• Journal of the Korea institute for structural maintenance and inspection
• /
• v.24 no.3
• /
• pp.39-46
• /
• 2020

Carbonation is a deterioration which degrades structural and material performance by permitting CO₂ and corrosion of embedded steel. Service life evaluation through deterministic method is conventional, however the researches with probabilistic approach on service life considering loading and cold joint effect on carbonation have been performed very limitedly. In this study, probabilistic service life evaluation was carried out through MCS (Monte Carlo Simulation) which adopted random variables such as cover depth, CO₂ diffusion coefficient, exterior CO₂ concentration, and internal carbonatable materials. Probabilistic service life was derived by changing mean value and COV (Coefficient of variation) from 100 % to 300 % and 0.1 ~ 0.2, respectively. From the analysis, maximum reduction ratio (47.7%) and minimum reduction ratio (11.4%) of service life were obtained in cover depth and diffusion coefficient, respectively. In the loading conditions of 30~60% for compressive and tensile stress, GGBFS concrete was effective to reduce cold joint effect on carbonation. In the tensile condition, service life decreased linearly regardless of material types. Additionally service life rapidly decreased due to micro crack propagation in the all cases when 60% loading was considered in compressive condition.

• Journal of the Korea Concrete Institute
• /
• v.15 no.4
• /
• pp.606-614
• /
• 2003

The major cause of deterioration for the concrete bridge decks exposed to de-icing chemicals would be chloride-induced reinforcement corrosion. Thus, in this paper, in order to predict time to corrosion for concrete bridge decks in the urban area, chloride concentration was measured with depth from the surface. A frequency analysis on surface chloride concentration and chloride diffusion coefficient of concrete bridge deck equals 0.192, 29.828 in the scale parameter and 7.899, 1.983 in the shape parameter of gamma distribution. The average value of surface chloride concentration equals 1.5 kg/㎥ and condenses from 1 to 2 kg/㎥ in the level of probability 70%. From the probabilistic results, it is confirmed that 26mm of minimum cover depth in order to target 20 years over is calculated. The countermeasure strategy to extend the service life of concrete bridge deck exposed to de-icing chemicals would be an effective method to increase cover depth and to place high performance concrete, which could lead to reduce the chloride diffusion coefficient and distribution range.

• Journal of the Korea institute for structural maintenance and inspection
• /
• v.19 no.5
• /
• pp.45-55
• /
• 2015

Currently, extreme weather events such as super typhoon, extreme snowfall, and heat wave are frequently occurring all over the world by natural and human caused factors. After industrial growth in the 1970s, earth's temperature has risen sharply. due to greenhouse effect. Global warming can be attributed to gases emitted from using fossil fuel such as average carbon dioxide, perfluorocarbons, nitrous oxide, and methane. Especially, carbon dioxide has the highest composition of about 90%. in the fossile fuel usage emitted gas. Concrete has excellent durability as a building material climate change. However, due to various of physical and chemical environmental effect such as conditions during its curing process, the performance degradation may occur. Carbon dioxide in the atmosphere causes steel corrosion and durability decreases by lowering the alkalinity of concrete. Therefore, in this study, concrete durability performance with respect to carbonation from curing conditions change due to wind speed and sunshine exposure time. Concrete carbonation experiment are performed. using wind speed (0, 2, 4, 6) m/s and sunlight exposure time (2, 4, 6, 8) hrs. Also, performance based evaluation through the satisfaction curve based on the carbonation depth and carbonation rate test results are performed.