• Journal of the Korean Institute of Electrical and Electronic Material Engineers
• /
• v.13 no.6
• /
• pp.493-501
• /
• 2000

The microstructure and electrical properties of ZnO-Pr$_{6}$/O$_{11}$-CoO-Er$_{2}$/O$_{3}$ based varistors were investigated with Er$_{2}$/O$_{3}$ additive content of the range 0.0 to 2.0 mol%. Most of the added Er$_{2}$/O$_{3}$ were segregated at the nodal points and grain boundaries and it coexisted with Pr$_{6}$/O$_{11}$ in the bulk intergranular layer. The average grain size was decreased in the range of 7.44 to 5.62${\mu}{\textrm}{m}$ at 130$0^{\circ}C$ and 18.36 to 9.11 at 135$0^{\circ}C$ with increasing Er$_{2}$/O sub 3/ additive content. The density of ceramics was in the range 4.87 to 5.08 g/cm$^3$ at 130$0^{\circ}C$ and 5.35 to 5.62 g/cm$^3$at 135$0^{\circ}C$. At 130$0^{\circ}C$ the varistors without Er$_{2}$/O$_{3}$ exhibited 29.66 in the nonlinear exponent and 28.23 $\mu$A in the leakage current whereas the varistors with 0.5 mol% Er$_{2}$/O$_{3}$ exhibited a high nonlinearity which is 52.78 in thenonlinear exhibited and 9.75 $\mu$A in the leakage current. At 135$0^{\circ}C$ the varistors without Er$_{2}$/O$_{3}$ exhibited a very poor nonlinearity indicating 2.08 in the nonlinear exponent and 133.79 $\mu$A in the leakage current whereas the varistors with 1.0mol% Er$_{2}$/O$_{3}$ exhibited a relatively high nonlinearity which is 36.79 in the nonlinear exponent and 5.92 $\mu$A in the leakage current. Therefore Er$_{2}$/O$_{3}$ was additive which greatly improve the nonlinearity. It is believed that ZnO-0.5 mol% Pr$_{6}$/O$_{11}$-1.0 mol% CoO-0.5 mol% Er$_{2}$/O$_{3}$ based ceramicss will be usefully used as a basic composition to develop the advanced pr$_{6}$/O$_{11}$-based ZnO varistors.ristors.ristors.

• Journal of the Korean Institute of Electrical and Electronic Material Engineers
• /
• v.13 no.8
• /
• pp.667-674
• /
• 2000

The stability of ZnO-Pr$_{6}$/O$_{11}$-CoO-Er$_{2}$/O$_3$based varistors was investigated with Er$_{2}$/O$_3$additive content of the range 0.0 to 2.0 mol%. All varistors sintered at 130$0^{\circ}C$ exhibited the thermal runaway within short times even under weak d.c. stress. As a result these varistors were completely degraded. On the contrary the stability of varistors sintered at 135$0^{\circ}C$ was far better than that of 130$0^{\circ}C$. In particular the varistors added with 0.5mol% Er$_{2}$/O$_3$ which the nonlinear exponent is 34.83 and the leakage current is 7.38 $mutextrm{A}$ showed a excellent stability which the variation rate of the varistors voltage the nonlinear coefficient and the leakage current is below 1%, 2%, and 3.5% respectively even under more severe d.c. stress such as (0.80 V$_{1mA}$9$0^{\circ}C$/12h)+(0.85 V$_{1mA}$115$^{\circ}C$/12h)+(0.90 V$_{1mA}$12$0^{\circ}C$12h) Consequently it is estimated that the ZnO-0.5 mol% Pr$_{6}$/O sub 11/-1.0 mol% CoO-0.5 mol% Er$_{2}$/O sub 3/ based varistors will be used to develop the advanced Pr$_{6}$/O$_{11}$-1.0 mol% CoO-0.5 mol% Er$_{2}$/O$_{3}$ based varistors will be used to develop the advanced Pr$_{6}$/O$_{11}$-based ZnO varistors having the high performance and stability in future. future.ure. future.

• Journal of the Korean Institute of Electrical and Electronic Material Engineers
• /
• v.13 no.9
• /
• pp.735-744
• /
• 2000

The electrical procerties and stability of ZnO-Pr$_{6}$O$_{11}$-CoO-Cr$_2$O$_3$-Er$_2$O$_3$ (ZPCCE) based varistors were investigated in the Er$_2$O$_3$content range of 0.0 to 4.0 mol%. ZPCCE ceramics containing 2.0 mol% Er$_2$O$_3$ exhibited the highest density of 5.74 g/㎤ corresponding to 99.3% of theoretical density. The varistors with 0.5 mol% and 2.0 mol% Er$_2$O$_3$exhibited a relatively satisfying nonlinearity, which the nonlinear exponent is 40.50 and 47.15, respectively and the leakage current is 2.66 $mutextrm{A}$, respectively. Under more severe d.c. stress, such as (0.80 V$_{1mA}$/9$0^{\circ}C$/12h)+(0.85 V$_{1mA}$115$^{\circ}C$/12h)+(0.90 V$_{1mA}$12$0^{\circ}C$/12h)+(0.95 V$_{1mA}$1$25^{\circ}C$12h), they showed a very excellent stability, which the variation rate of the variator voltage is -0.89% and -0.15%, the variation rate of the nonlinear coefficient is -4.67% and -3.56%, and the variation rate of leakage current is -6.02% and -19.56%, respectively. It is surely bellived that ZnO-0.5 mol% Pr$_{6}$O$_{11}$-1.0 mol% CoO-0.5 mol% Cr$_2$O$_3$-x mol% Er$_2$O$_3$(x=0.5, 2.0) based varistors will be greatly contributed to develop the advanced Pr$_{6}$O$_{11}$-based ZnO varistors in future.uture. future.uture.