• 산업기술연구
• /
• 제8권
• /
• pp.39-46
• /
• 1988

탄소강 평활재 및 미소결함재를 사용하여, 미소 정류크랙의 크랙 개폐구거동의 상세한 관찰과 초기결함을 상정한 미소 원공과의 상호 한계크기의 비교 검토를 통하여, 다음과 같은 결론을 얻었다. 평활재의 정규크랙은, 피로과정중에 압축잔류응역이 크랙선단의 개구를 억제하는 것에 의하여 정류하게 되고, 그 크기는 평활재의 피로한도를 저하시키지 않은 미소 원공의 한계크기와 거의 일치하여, 두 경우가 역학적으로 거의 등가함을 시사해 주고 있다.

• 한국해양공학회지
• /
• 제3권2호
• /
• pp.601-601
• /
• 1989

The behavior of fatigue was studied by using low carbon steel bar with microhole(artificial small defect) under the condition of rotary bending stress which is made artificially at smooth surface and round notch root. The results obtained can be summerized; The behavior of non-propagating cracks which are produced at both tips of small defect occurred to dissymmetry, and it is found to be double size of small defect. For the range of l>lc, threshold stress intensity is constant. However, for the range of l

• 한국해양공학회지
• /
• 제3권2호
• /
• pp.101-107
• /
• 1989

The behavior of fatigue was studied by using low carbon steel bar with microhole(artificial small defect) under the condition of rotary bending stress which is made artificially at smooth surface and round notch root. The results obtained can be summerized; The behavior of non-propagating cracks which are produced at both tips of small defect occurred to dissymmetry, and it is found to be double size of small defect. For the range of l>lc, threshold stress intensity is constant. However, for the range of l

• 산업기술연구
• /
• 제30권B호
• /
• pp.17-23
• /
• 2010

Since the propagation of a short fatigue crack is directly related to the large crack which causes the fracture of bulk specimen, the detailed study on the propagation of the short crack is essential to prevent the fatigue fracture. However, a number of recent studies have demonstrated that the short crack can grow at a low applied stress level which are predicted from the threshold condition of large crack. In present study, the threshold condition for the propagation of short fatigue crack is examined with respect to the micro-structure and cyclic loading history. Specimens employed in this study were decarburized eutectoid steels which have various decarburized ferrite volume fraction. Rotating bending fatigue test was carried out on these specimens with the special emphasis on the "critical non-propagating crack length" It is found that the reduction of the endurance limit of their particular micro-structures can be due to the increase of the length of critical non-propagating crack, and the quantitative relationship between the threshold stress ${\sigma}_{wo}$ and the critical non-propagating crack length $L_c$ can be written as ${\sigma}_{wo}{^m}{\cdot}L_c=C$ where m,C is constant. Further experiments were carried out on cyclic loading history on the length of critical non-propagating crack. It shown that the length of critical non-propagating crack is closely related to cyclic loading history.

• 산업기술연구
• /
• 제21권A호
• /
• pp.17-26
• /
• 2001

The fatigue strength of SM55C has significantly decreased by 83% compared with atmosphere where distilled exists due to strong erosive action of acid fog. The reason is inferred in a way that strong acid erosive material such as acid fog act and give rise to multi-site crack on the surface. Several fatigue clacks occurred under the acid fog repeat the process of division and unification on the surface and form a long non-propagating crack throughout the circumference of experimented steel. However, in the depth, many parts do not show much trace of unification, and the depth is not as big as the one of normal crack shape. 10% of $CaCl_2$ causes strong erosive reaction to material. Then eventually make the life of fatigue shooter. On the other hand, 20% of $CaCl_2$ beings about oxidized material organic crack closing due to weak erosive reaction.

• 대한기계학회논문집
• /
• 제19권2호
• /
• pp.402-407
• /
• 1995

The effects of room temperature and strain aging treatment are discussed on the critical condition for the onset of growth of non-propagating cracks on 0.15% C low carbon steel, with special emphasis on the length of the critical non-propagating crack and on the crack opening displacement(COD) at the crack tip. It is found from the experimental analysis that room temperature and strain aging of a fatigue pre-cracked specimen introduced the closure of a crack tip of the pre-crack and the reduction of crack opening displacement at the wake of crack, together with an improvement in crack growth resistance of the microstructure. This may cause an increase in the endurance limit of the specimen, through the enhancement of effective stress for the onset of growth of the critical non-propagating crack.

• 대한기계학회논문집
• /
• 제12권3호
• /
• pp.505-512
• /
• 1988

본 연구에서는 상술한 $\boxDr$한계정유길이$\boxUl$를 찾아내는 것을 주요수단으로 하여, 그 전파 하한계응력으로서의 피로한도와의 관계를 정량적으로 검토하고, 미소크랙전파 거동이 미시조직 또는 피로부하이력등에 민감함을 감안하여, 이들 인자가 미소크랙 전 파의 하한계조건에 미치는 영향에 관하여 검토하기로 하였다.