• Proceedings of the Korean Institute of Building Construction Conference
• /
• 2023.05a
• /
• pp.85-86
• /
• 2023

This study confirmed the improvement of the Composite Waterproof Method in which the sheet layer is partially attached with perforated film and the joint is FRP-treated.

• Composites Research
• /
• v.17 no.6
• /
• pp.14-21
• /
• 2004

Failure process, mode and strength of unidirectional composite single lap bonded joints were investigated experimentally with respect to bonding methods, those are, co-curing with and without adhesive and secondary bonding. The co-cured joint specimens without adhesive had the largest failure strength. Progressive failures along the adhesive layer occurred in the secondary bonded specimens. In the co-cured specimens with adhesive film which had better material strength and adhesion performance, delamination failure occurred and the joint strengths were less than those of secondary bonded specimens. Delamination failure did not occur in the secondary bonded specimens because of earlier crack growth and progressive failure in the adhesive layer. Therefore, failure strength of composite bonded Joints were not always proportionate to material strength and adhesion performance of the adhesive due to the weakness of delamination in composite materials. The effects of surface roughness, bondline thickness and fillets were also studied on secondary bonded specimens.

• Composites Research
• /
• v.26 no.2
• /
• pp.129-134
• /
• 2013

The strength of adhesive joints employed in composite structures under cryogenic environments, such as LNG tanks, is affected by thermal residual stress generated from the large temperature difference between the bonding process and the operating temperature. Aramid fibers are noted for their low coefficient of thermal expansion (CTE) and have been used to control the CTE of thermosetting resins. However, aramid composites exhibit poor adhesion between the fibers and the resin because the aramid fibers are chemically inert and contain insufficient functional groups. In this work, electrospun meta-aramid nanofiber-reinforced epoxy adhesive was fabricated to improve the interfacial bonding between the adhesive and the fibers under cryogenic temperatures. The CTE of the nanofiber-reinforced adhesives were measured, and the effect on the adhesion strength was investigated at single-lap joints under cryogenic temperatures. The fracture toughness of the adhesive joints was measured using a Double Cantilever Beam (DCB) test.

• Composites Research
• /
• v.33 no.6
• /
• pp.371-376
• /
• 2020

The adhesive strength can be improved through surface treatment. The most common method is to improve physical bonding by varying the surface conditions. This study presents the effect of laser surface treatment on the adhesive strength of CFRP. The surface roughness was patterned using a 1064 nm laser. The effects of the number of laser shots and the direction and length of the pattern on the adhesion of the CFRP/CFRP single joint were investigated through tensile tests. Tests according to ASTM D5868 were performed, and the bonding mechanism was determined by analyzing the damaged surface after a fracture. The optimized number of the laser shots and the optimized depth of the roughness should be required to increase the bonding strength on the CFRP surface. When considering the shear stress in the tensile direction, the roughness pattern in the direction of 45° that increases the length of the fracture path in the adhesive layer resulted in an increase of the adhesive strength. The surface treatment of the bonding surface using a laser is a suitable method to acquire a mechanical bonding mechanism and improve the bonding strength of the CFRP bonding joint. The study on the optimized laser process parameters is required for utilizing the benefits of laser surface processing.

• Transactions of the Korean Society of Mechanical Engineers A
• /
• v.20 no.5
• /
• pp.1543-1551
• /
• 1996

The static tensile load bearing capability of as adhesively-bonded tubular single lap jint that is calculated usign the linear mechanical properties of adhesive is usually far from the experimentally determined because the majority of the load transfer of the adhesively-bonded jointd is accomplished by the nonlinear behavior of the rubber-toughened eoxy adhesive. In this paper, both the nonlinear mechanical properties and the fabrication residual thermal stresses of adhesive were included in the calculation of the stresses of adhesively-bonded joints. The onlinear tensile properties of adhesive were approximated by an exponential form which was represented by the initial tensile modulus and ultimate tensile stength of adhesive. The stress distribution in the adhesive were calculated by applying the load obtained from the tensile tests. From the tensile tests and the stress analysis of adhesively-bonded hoints, the failure model for adhesively-bonded tubular single lap joints was proposed.

• Journal of Ocean Engineering and Technology
• /
• v.23 no.6
• /
• pp.124-130
• /
• 2009

This study presents a finite element simulation of elastic waves for detecting anti-symmetric damages in an adhesively-bonded single lap joint. Plane strain elements were used for modeling adherents (aluminum) and adhesives (epoxy). Three types of damage were introduced: thickness reduction, elasticity deterioration, and voids in the adhesive layers, and two excitation and reception arrangements (ER1 and ER2) were used to investigate the detectability of the damage. The simulation showed that symmetrically located damage, such as a thickness reduction, can be detected by one excitation and one reception arrangement (ER1) and anti-symmetric damages, such as elasticity deterioration and voids, can be detected by modified two-point elastic wave excitation (ER2). Compared with the ER1 arrangement, the ER2 arrangement does not require a baseline signal for damage detection; hence, an efficient method of anti-symmetric damage detection in an adhesively-bonded single lap joint is proposed.

• Journal of Ocean Engineering and Technology
• /
• v.24 no.1
• /
• pp.172-177
• /
• 2010

This study presents an explicit dynamic analysis of an adhesively bonded single-lap joint under an impact load. The finite element software, ANSYS LS-DYNA, was used for the analysis and Von Mises stresses were obtained from the analysis. To model the adherents, solid elements were used and a rigid body was assumed for impactor modeling. Three impact heights (1 m, 5 m, and 10 m) were applied to consider different impact conditions and infinite boundary conditions were applied to the end-area of each adherent to save computational time in the analysis. In addition to investigating the stresses in the normal state, we also investigated the stresses in a damaged state (elasticity deterioration), simulated by a change in Young's modulus for 36 of the 3600 elements in the upper layer of the adhesive. The results showed that the location of damage is critical to the stress state of each layer (upper, middle, and lower).

• Journal of the Korean Wood Science and Technology
• /
• v.42 no.3
• /
• pp.301-308
• /
• 2014

Despite Korea forest take 63.7% of the nation's territory, productivity of domestic structural lumber is low. Studies of domestic small lumbers need to be improved domestic structural timber productivity. In this study, small diameter lumber and finger joint small diameter lumber took bending test to calculate MOE and MOR. MOE of small diameter lumber was $9.3kN/mm^2$ and MOE of finger joint small diameter lumber was $15.4kN/mm^2$. Allowable standard bending stress of small diameter lumber and finger joint small diameter lumber was calculated according to ASTM D 2915. Standard allowable bending stress of small diameter lumber was $12N/mm^2$ and standard allowable bending stress of finger joint small diameter lumber was $11N/mm^2$. Standard allowable bending stress of finger joint small diameter lumber should be considered to design structural beam members.

• Composites Research
• /
• v.30 no.4
• /
• pp.229-234
• /
• 2017

Generally, joints are the weakest part in the composite structures. Composite joints can be classified into adhesive joints and mechanical joints, and mechanical joints are mainly used in areas less sensitive to environmental conditions. In this paper, the failure loads of composite mechanical joints with five different stacking angles are tested and predicted. Finite element analysis of mechanical joints were performed and failure loads were predicted by the FAI(Failure Area Index) method using Tsai-Wu and Yamada-Sun failure criteria, and the predicted failure loads were compared with experimental results. From the experiment and analysis, the failure loads of the mechanical joints were decreased as the ratio of 0 degree layer was low and they could be predicted within 13.03% using the FAI method and Yamada-Sun failure criteria.

• Composites Research
• /
• v.15 no.5
• /
• pp.19-26
• /
• 2002

Real defects in composite structures were detected by using laser measuring system. Four types of real defects, that is, impact-induced delamination in a composite laminate, debond in a honeycomb structure, free-edge delamination in a composite laminate and debond in an adhesive joint, were made by applying several types of loads to the specimens. Laser measuring system such as ESPI and shearography technique were used to detect those defects. Thermal loading method, which can easily induce the surface deformation of specimen, was used to detect the defects. Experimental results show that the defects in composite structures could be easily detected by ESPI and shearography technique. Moreover, it shows that ESPI and shearography technique could be usefully applied to the detection of defects in various kinds of composite structures.