• Journal of the Korean Vacuum Society
• /
• v.21 no.5
• /
• pp.273-278
• /
• 2012

Over the last decade, the hafnium-based gate dielectric materials have been studied for many application fields. Because these materials had excellent behaviors for suppressing the quantum-mechanical tunneling through the thinner dielectric layer with higher dielectric constant (high-K) than $SiO_2$ gate oxides. Although high-K materials compensated the deterioration of electrical properties for decreasing the thickness of dielectric layer in MOSFET structure, their nano-mechanical properties of $HfO_2$ thin film features were hardly known. Thus, we examined nano-mechanical properties of the Hafnium oxide ($HfO_2$) thin film in order to optimize the gate dielectric layer. The $HfO_2$ thin films were deposited by rf magnetron sputter using hafnium (99.99%) target according to various oxygen gas flows. After deposition, the $HfO_2$ thin films were annealed after annealing at $400^{\circ}C$, $600^{\circ}C$ and $800^{\circ}C$ for 20 min in nitrogen ambient. From the results, the current density of $HfO_2$ thin film for 8 sccm oxygen gas flow became better performance with increasing annealing temperature. The nano-indenter and Weibull distribution were measured by a quantitative calculation of the thin film stress. The $HfO_2$ thin film after annealing at $400^{\circ}C$ had tensile stress. However, the $HfO_2$ thin film with increasing the annealing temperature up to $800^{\circ}C$ had changed compressive stress. This could be due to the nanocrystal of the $HfO_2$ thin film. In particular, the $HfO_2$ thin film after annealing at $400^{\circ}C$ had lower tensile stress, such as 5.35 GPa for the oxygen gas flow of 4 sccm and 5.54 GPa for the oxygen gas flow of 8 sccm. While the $HfO_2$ thin film after annealing at $800^{\circ}C$ had increased the stress value, such as 9.09 GPa for the oxygen gas flow of 4 sccm and 8.17 GPa for the oxygen gas flow of 8 sccm. From these results, the temperature dependence of stress state of $HfO_2$ thin films were understood.

• Journal of the Korean Vacuum Society
• /
• v.16 no.5
• /
• pp.359-365
• /
• 2007

In this paper we present a bottom-gate type of zinc oxide (ZnO) and Gallium (Ga) doped zinc oxide (GZO) based thin film transistors (TFTs) through applying a radio frequency (RF) magnetron sputtering method at room temperature. The gate leakage current can be reduced up to several ph by applying $SiO_2$ thermally grown instead of using new gate oxide materials. The root mean square (RMS) values of the ZnO and GZO film surface were measured as 1.07 nm and 1.65 nm, respectively. Also, the transmittances of the ZnO and GZO film were more than 80% and 75%, respectively, and they were changed as their film thickness. The ZnO and GZO film had a wurtzite structure that was arranged well as a (002) orientation. The ZnO TFT had a threshold voltage of 2.5 V, a field effect mobility of $0.027\;cm^2/(V{\cdot}s)$, a on/off ratio of $10^4$, a gate voltage swing of 17 V/decade and it operated in a enhancement mode. In case of the GZO TFT, it operated in a depletion mode with a threshold voltage of -3.4 V, a field effect mobility of $0.023\;cm^2/(V{\cdot}s)$, a on/off ratio of $2{\times}10^4$ and a gate voltage swing of 3.3 V/decade. We successfully demonstrated that the TFTs with the enhancement and depletion mode type can be fabricated by using pure ZnO and 1wt% Ga-doped ZnO.