In this study, a liquid crystal (LC) cell was manufactured for smart window applications, such as blinds, and a system for controlling the light transmission rate was developed. The threshold voltage of the LC cell was 1.325 V and when the transmission rate was 10%, the voltage showed 2.370 V, indicating that the LC cell manufactured is driven at low voltage. The LC cell also operated reliably after being heated for 10 min at 80℃. with a response time of less than 30ms. The operation system designed the applied voltage of the LC cell with a interval of about 0.5 V from 0.15 V to 3.53 V and confirmed that the light transmission rate of the LC varies depending on the actual applied voltage. These results suggest that LC cells are likely to be smart window applications.

• Proceedings of the Korean Vacuum Society Conference
• /
• 2012.08a
• /
• pp.290-290
• /
• 2012

본 실험에서는 RF magnetron sputtering법과 evaporator법을 이용하여 다층박막 OMO구조를 $30{\times}30mm$ 유리기판 위에 제작하였다. Oxide층은 Sputter장비를 이용 IGZO막을 제작하였으며, Metal 층은 evaporator장비를 이용 Ag 막을 제작하였다. 변수로는 Oxide층의 시간에 따른 특성 변화를 연구하였다. 소결된 타겟으로는 In:Ga:ZnO를 각각 1:1:1 mol%의 조성비로 혼합하여 이용하였으며, Ag는 99.999%의 순도를 가진다. Oxide층의 RF sputter 공정 조건으로는 초기압력 $3.0{\times}10^{-6}$ Torr 이하로 하였으며, 증착 압력 $2.0{\times}10^{-2}$ Torr, Rf power 30 W, Ar gas 50 sccm으로 고정 시켰으며, 변수로는 5, 7, 9, 11분은 시간 차이를 두어 증착을 하였다. Metal층의 Evaporator 공정조건으로는 $5.0{\times}10^{-6}$ Torr이하, 전압은 0.3 V, Thickness moniter로 두께를 확인해가며 증착하였으며, $100{\AA}$으로 고정시켰다. 분석결과로는 XRD 측정 결과 35도 부근에서 Ag 피크가 관찰되었다. IGZO막 하나일때 90% 이상의 평균 투과율을 보였으며, 3층의 구조가 모두 증착됐을때의 투과도는 가시광영역에서 평균 80% 이상의 투과율을 보였으며, 500 nm부터 투과율이 떨어지기 시작해 800 nm부근에서는 평균 투과율이 30%까지 떨어져 Metal층인 Ag가 하나의 layer로 잘 증착이 된것을 보여주며, 플라즈몬효과를 보여줌을 알수있다. AFM측정 결과 평균 거칠기는 1.2 nm 정도의 거칠기를 확인했다. 홀 측정결과 전기적 특성은 발견되지 않았다.

• Proceedings of the Korean Vacuum Society Conference
• /
• 2014.02a
• /
• pp.340.1-340.1
• /
• 2014

본 실험에서는 Ag두께 변화에 따른 투과율과 Energy bandgap의 변화를 알아보기 위해 RF Sputter장비와 Evaporator장비를 사용하여 IGZO, ZnO, AZO OMO 구조로 Low-e 코팅된 Glass를 제작하였다. $3cm{\times}3cm$의 Corning1737 유리기판에 RF Sputtering 방식으로 Oxide layer를 증착 하였고 Evaporator장비로는 Metal layer인 Ag막을 증착하였다. Oxide layer 증착 시 RF Sputter장비의 조건은 $3.0{\times}10^{-6}Torr$이하로 하였으며, 증착압력은 $6.0{\times}10^{-3}Torr$, 증착온도는 실온으로 고정하였다. Metal layer 증착 시 Evaporator장비의 조건은 $5.0{\times}10^{-6}Torr$이하, 전압은 0.3 V, Rotate 2 rpm으로 고정하였다. 실험 변수로는 Ag 두께를 5,7,9,11,13 nm로 변화를 주어 실험을 진행하였다. 투과도 측정 장비를 사용하여 각 샘플을 측정한 결과 IGZO의 경우 가시광영역의 평균 투과율이 80% 이상이며 Ag두께가 5nm일 때부터 자외선 영역의 빛을 차단하여 low-e 특성을 나타내었다. 이는 산화물인 IGZO가 결정질인 AZO, ZnO 보다 낮은 표면거칠기를 가지기 때문이다. Ag 두께에 따른 각 물질의 Optical energy bandgap 분석결과 Ag 두께가 증가할수록 IGZO는 4.65~4.5 eV, AZO는 4.6~4.4 eV, ZnO는 4.55~4.45 eV로 Energy bandgap은 감소하였다. AFM장비를 이용하여 각 샘플의 표면 Roughness 측정 결과 Ag 두께가 증가할수록 표면거칠기도 증가하는 경향을 나타내었다.

• Proceedings of the Korean Vacuum Society Conference
• /
• 2010.08a
• /
• pp.123-123
• /
• 2010

투명전극 물질인 ITO는 가시광선 영역에서 높은 투과율과 낮은 전기저항을 나타내어 OLED, PDP, LCD등 다양한 분야에서 널리 사용되는 물질이다. 하지만 차세대 조명으로 개발이 확대되고 있는 OLED 조명 등 더 많은 분야에 적용하기 위해서는 많은 개선점이 필요하다. 특히 픽셀 구조가 아닌 OLED 조명의 경우 ITO의 저항에 의해 전압 강하가 발생하여 휘도 불균일, 발열 등의 문제가 발생할 수 있다. 이 때문에 보다 우수한 전기적인 특성과 높은 투과율을 갖는 투명전극이 필요하다. 현재 이러한 문제점을 개선하기 위해 ITO 박막 내부에 얇은 금속 층을 삽입하여 다층 박막으로 증착하는 연구가 활발히 진행되고 있다. 본 연구에서는 기존의 투명 전극인 ITO 대신 ITO 중간에 Ag를 삽입한 3층 박막인 ITO/Ag/ITO와 5층 박막인 ITO/Ag/ITO/Ag/ITO를 투명 전극으로 대체하였을 때 수반되는 전기적, 광학적 특성을 알아보고자 한다. 또한 열처리 조건을 다르게 하여 열처리에 따른 다층 박막의 특성 변화도 비교해보았다. In-line 형태의 RF-DC sputter를 이용하여 다층박막을 증착시킨 후 Oven과 Vacuum Oven에 열처리를 하여 특성을 알아보았다. 전기적 특성을 알아보기 위해 4-point probe를 이용하여 비저항을 측정하였고, UV-VLS spectrometer를 이용하여 투과율을 측정하였다. 또한, Atomic force microscopy(AFM)을 이용하여 표면 형상을 측정하였다.

• Korean Journal of Optics and Photonics
• /
• v.5 no.3
• /
• pp.411-417
• /
• 1994

The electro-optic polarization transmission characteristics of a liquid crystal (LC) cell is represented by a rotational transformation on the Poincare sphere, and its characteristic parameters, the angle and the axis of the rotation, are experimentally determined with respect to the voltage applied to the LC cell. From the experimental data obtained, we determine driving voltage for the LC cell to give the rotation angle near $180^{\circ}$ of the rotation for the change of the state of the LC cell from non-select to select state, which is a necessary condition for the realization of maximally bright images. The directions of the transmission axes of the polarizer and the analyzer which form a liquid crystal display panel together with the LC cell, are determined from the general characteristics of the rotaional transformation of the LC cell. cell.

• Proceedings of the Korean Vacuum Society Conference
• /
• 1999.07a
• /
• pp.158-158
• /
• 1999

NiO 박막은 전자비임증착법과 RF-스퍼터링법으로 제작하여 박막의 성능을 평가하였다. NiO 박막의 성능평가를 위한 착색과 탈색은 전기적 착색셀을 제작하여 순환전압전류법으로 KOH 전해질 내에서 반복수행하였으며 성능이 퇴화된 박막의 투과율은 가시광선 분광기로 측정하였다. XPS에 의한 분석결과 막의 낱알 내부보다 낱알 표면에 많은 산소가 포함될수 있음을 알 수 있었다. KOH 전해질 속에서 사이클이 반복 수행된 막의 표면 낱알의 형태는 변하였으며, 3$\times$10-4mbar에서 제작된 시료가 막의 안정성이 좋았다. 제작 방법에 다라 막에 주입 및 추출되는 전하밀도와 투과율의 차이가 나타났고, 니켈 산화물 박막의 성능평가를 하기 위해 착색효율을 계산하였다. 기판물질인 IT(indium tin oxide)의 전기적 착색성과 전해질이 전기적 착색성에 미치는 영향에 대해서도 논의되었다.

• Journal of the Korean Institute of Electrical and Electronic Material Engineers
• /
• v.14 no.6
• /
• pp.487-490
• /
• 2001

Residual DC voltage of the in-plane switching (IPS)-liquid crystal display(LCD) by voltage-transmittance (V-T) hysteresis method was studied. Several IPS-LCD which have different concentrations of cynao LCs and different resistivities of fluorine LCs were fabricated. We found that the residual DC voltage of the IPS-LCD was decreasing with increasing concentration of cyano LCs and increasing with decreasing specific resistivity of fluorine LC materials. The residual DC voltage property can be improved by low molecular weight and high polarity of cyano LC.

• Proceedings of the Korean Institute of Electrical and Electronic Material Engineers Conference
• /
• 2001.07a
• /
• pp.656-659
• /
• 2001

We investigated the residual DC in the in-plane switching (IPS)-liquid crystal display(LCD) by voltage-transmittance (V-T) hysteresis method. Several IPS-LCD which have different concentrations of cynao LCs and different resistivities of fluorine LCs were fabricated. We found that the residual DC voltage of the IPS-LCD was decreasing with increasing concentration of cyano LCs and increasing with decreasing specific resistivity of fluorine LC materials. The residual DC voltage property can be improved by low molecular weight and high polarity of cyano LC.

• Journal of the Korean Institute of Electrical and Electronic Material Engineers
• /
• v.13 no.10
• /
• pp.883-886
• /
• 2000

We have developed a novel vertical-alignment(VA) - 1/6$\pi$ mode that provides a wide viewing angle for nematic liquid crystal (NLC) with negative dielectric anisotropy on a homeotropic polyimide (PI) surfaces. Good voltage-transmittance curves were achieved with the new VA - 1/6$\pi$ cell model without a negative compensation film. The viewing angle of a new VA -1/6$\pi$ cell without a negative compensation film was wider than that of a conventional VA cell. Finally, the wide viewing angle using the new VA-1/6$\pi$ cell mode can be achieved.

• Proceedings of the Korean Institute of Electrical and Electronic Material Engineers Conference
• /
• 2000.11a
• /
• pp.515-518
• /
• 2000

We studied the viewing angle characteristics of a negative dielectric anisotropy nematic liquid crystal (NLC) using the new vertical-alignment (VA)-1/6 cell on a rubbed polyimide (PI) surface. Good voltage-transmittance (V-T)characteristics using the new VA-1/6 cell without a negative compensation film were obtained. The iso-viewing angle characteristics using the new VA-1/6 cell without the negative compensation film can be achieved.