• Korean Chemical Engineering Research
• /
• v.43 no.3
• /
• pp.425-431
• /
• 2005

New type of supercapacitor using high surface area activated carbons mixed with high conductivity polypyrrole (Ppy) has been prepared in order to achieve low impedance and high energy density. Mixed carbons of BP-20 and MSP-20 were used as the active electrode material, and polypyrrole doped with 2-naphthalenesulfonic acid (2-NSA) and carbon black (Super P) as conducting agents were added to activated carbons in order to enhance good electric conductivity. Electrodes prepared with the activated electrode materials and the conducting agents were added to a solution of organic binder [P(VdF-co-HFP) / NMP]. The ratio of optimum electrode composition was 78 : 17 : 5 wt.％ of (MSP20 : BP-20=1 : 1), (Super P : Ppy=10 : 7) and P(VdF-co-HFP) respectively. The performance of unit cell with addition of 7 wt％ Ppy have shown specific capacitance of 28.02 F/g, DC-ESR of $1.34{\Omega}$, AC-ESR of $0.36{\Omega}$, specific energy of 19.87 Wh/kg and specific power of 9.77 kW/kg. With addition of Ppy, quick charge-discharge of unit cell was possible because of low ESR, low charge transfer resistance and quick reaction rate. And good stability up to 500 chargedischarge cycles were retained about 80％ of their original capacity. It was concluded that the specific capacitance originated highly from compound phenomena of the pseudocapacitance by oxidation-reduction of polypyrrole and the nonfaradaic capacitance by adsorption-desorption of activated carbons.

• Journal of the Korean Chemical Society
• /
• v.40 no.7
• /
• pp.467-473
• /
• 1996

Although a polypyrrole shows better electrical conductivity, 100∼400 ${\Omega}^{-1}cm^{-1}$, than other organic conducting polymers, its electrical conductivity will be worsen in the presence of the oxygen due to its easy oxidation. On the other hand, polythiophene shows better stability in the air while its electrcal conductivity is poor compared to the polypyrrole. We succeed to develope the mixed polymer electrode that is stable in the air and shows a good redox characteristics. The mixed polymer electrode has been prepared by the electrical polymerization of polypyrrole on the Pt electrode as 1.70 C$cm^{-2}$ and then coating with polythiophene as 0.34 C$cm^{-2}$. The polymerization rate of polythiophene was $3.89{\times}10^{-8}$ at the bare Pt electrode and $6.07{\times}10^{-8}cms^{-1}$ at the mixed polymer electrode. And the standard rate constants of each electrode were $5.16{\times}10^{-6}\;and\;3.94{\times}10^{-4} cms^{-1}$ respectively. Also, the electrocatalytic rate of the polypyrrole polymer electrode was $3.45{\times}10^{-3}cm^3mol^{-1}s^{-1}.$ We found the immobilized layer at the modified electrode acted as an electrocatalyst. Finally, this polymerization process at the Pt electrode was the electron transfer controlled, but that the mixed polymer electrode was the diffusion and charge transfer controlled.