• The Journal of Korean Academy of Prosthodontics
• /
• v.34 no.4
• /
• pp.791-799
• /
• 1996

The purpose of this study was to compare the shear bond strength of adhesion bridge by various resin cements. One hundred and foully 1st premolars were used. The teeth were cut below 2mm from CEJ and the coronal portions were used. The coronal portions were embeded with the acrylic resin and trimmed with sic paper until the flat plane with ${\phi}$ 4mm above acrylic resin sticks in height 5mm were casted with nonprecious metal and the using surfaces were treated with sic paper from #200 to #1200 and polished with alminum oxide paste. And then, the using surfaces were sandblasted and treated with the electrochemical etching. The teeth were divided into three groups of fourty two each. In group I, teeth and specimens were cemented with Panavia 21 In group II, teeth and specimens were cemented with Superbond In group I, teeth and specimens were cemented with All-Bond & composite resin cement Each group was subdivided into three subgroups according to the storage period ; one-day storage, fifteen-day storage, and thirty-day storage. The special jig was made. Then, the specimen and jig were mounted to Instron Universal Testing Machine and the failure were measured. The results were as follows. 1. There was statisfically significant difference between the failure loads of group I and group II and III after one day storage(P<0.01), 2. There was statisfically significant difference between the failure loads of group II and group I and III and between group I and group III at fifteen day storage(P<0.01). 3. There was statisfically significant difference between the failure loads of group I and II and group III after thirty day storage(P<0.01). 4. There was statisfically significant difference between the failure loads of one day storage and fifteen and thirty days storages in group III (P<0.01).

• Clean Technology
• /
• v.21 no.1
• /
• pp.76-82
• /
• 2015

Volatile organic compounds (VOC) free adhesives have been interested by many scientists and engineers due to environmental regulations and the safety of industrial workers. In this work, a series of composites composed with bisphenol A epoxy resin used as solvent, dicyandiamide, and promoter were prepared to investigate the most appropriate molar ratio for steel-steel adhesion. The cured test specimen of each composite were measured with universal testing machine (UTM) to figure out mechanical properties such as tensile strength, Young’s modulus, and elongation. Furthermore, the lap shear strength of the specimen was tested with UTM while impact resistance was measured with Izod impact tester. The composite whose molar ratio of epoxy resin to curing agent is 1 : 0.9 (sample 3), showed better tensile strength, coefficient of elastic modulus, elongation, and impact strength than other composites did. The highest tanδ from dynamic mechanical analysis (DMA) was observed from sample 2 (epoxy resin: dicy = 1 : 0.7) while sample 3 showed slightly lower tanδ than that of 2. The morphology of the fracture surface of the cured composites from SEM showed that the number of subtle lines on the surface caused by impact increase as the contents of amine curing agent accrete. Furthermore, the viscosity change of sample 5 (epoxy resin: dicy = 1 : 1.3) was observed to confirm its storage stability.

• Journal of the Korean Wood Science and Technology
• /
• v.49 no.4
• /
• pp.336-359
• /
• 2021

In this study, hybrid CLT research and development trends were analyzed to improve the low rolling shear strength of CLT, a large wooden panel used in high-rise wooden buildings. Through this, basic data that can be used in research and development directions for localization of CLT were prepared. As a way to improve the low rolling shear strength, the use of hardwood lamina, the change of the lamina arrangement angle, and the use of structural composite materials are mainly used. Rolling shear strength and shear modulus of hardwood lamina are more than twice as high as softwood lamina. It confirmed that hardwoods can be used and unused species can be used. Rolling shear strength 1.5 times, shear modulus 8.3 times, bending stiffness 4.1 times improved according to the change of the layer arrangement angle, and the CLT strength was confirmed by reducing the layer arrangement angle. Structural wood-based materials have been improved by up to 1.35 times MOR, 1.5 times MOE, and 1.59 times rolling shear strength when used as laminas. Block shear strength between the layer materials was also secured by 7.0 N/mm², which is the standard for block shear strength. Through the results of previous studies, it was confirmed that the strength performance was improved when a structural wood based materials having a flexural performance of MOE 7.0 GPa and MOR 40.0 MPa or more was used. This was determined based on the strength of layered materials in structural wood-based materials. The optimal method for improving rolling shear strength is judged to be the most advantageous application of structural wood based materials with strength values according to existing specifications. However, additional research is needed on the orientation of CLT lamina arrangement according to the fiber arrangement of structural wood-based materials, and the block shear strength between lamina materials.

• The Journal of Korean Academy of Prosthodontics
• /
• v.52 no.1
• /
• pp.1-8
• /
• 2014

Purpose: The purpose of this study is to evaluate the effect of applying Silano-pen to feldspathic porcelain and zirconia on shear bond strength with composite resin. Materials and methods: Feldspathic porcelain and zirconia specimens were produced into 30 per each 2 mm thick and 12 mm in diameter and their surface was made smooth and even and then embedded in acrylic resin. The specimens were divided into each Group F (Feldspathic porcelain) and Group Z (Zirconia), (1) Hydrofluoric acid etching and silane (F1 & Z1), (2) Silano-pen and silane (F2 & Z2), (3) Hydrofluoric acid etching and Silano-pen, silane (F3 & Z3). After surface conditioning, substrate surfaces of the specimen were examined by SEM. Composite resin cylinders (2 mm high, 3 mm in diameter)were bonded to specimen and shear bond strength between ceramic and composite resin was measured by using universal testing machine. The measured values were statistically analyzed by using two way ANOVA and Tukey's multiple comparison test (${\alpha}=.05$). Results: In the scanning electron micrograph of the treated ceramic surface, Group F2 and F3 appeared the high roughness and Group Z3 appeared the highest density of silica particle. In Feldspathic porcelain, the result of measuring shear bond strength showed that Group F3 was measured to be highest and Group F1 was measured to be lowest but there was no statistical significance among Groups. In zirconia, Group Z3 was measured to be highest and Group Z1 was measured to be lowest and there was statistical significance among Groups (P<.05). Conclusion: In zirconia, applying hydrofluoric acid etching and then Silano-pen and silane is effective for composite resin adhesion.

• Journal of the Korean GEO-environmental Society
• /
• v.12 no.12
• /
• pp.79-88
• /
• 2011

Adfreeze bond strength develops upon freezing of pore water within soil and at foundation surface. It has been reported that various factors like temperature, soil type, and pile surface roughness affect adfreeze bond strength. Especially, pile surface roughness has been considered as a primary factor to design pile foundation in frozen ground. It has usually been estimated with fixed correction factors for pile materials. However, even if the pile foundation material is the same, the surface roughness could vary depending on the production circumstances. In this study, laboratory test was carried out to quantitatively analyze the effects of surface roughness on the adfreeze bond strength, and fractal dimension was used as a measure for surface roughness. Test results showed that adfreeze bond strength increased with decreasing temperature, increasing vertical stress and surface roughness. The adfreeze bond strength varies sensitively with surface roughness in the early freezing section of $-2^{\circ}C$, but its sensitivity decreased in the temperature ranging between $-2^{\circ}C$ to $-5^{\circ}C$. The results conclude that the roughness highly affects the frictional resistance of pile surface in frozen ground; however, the roughness does not affect considerably when the temperature drops below about $-2^{\circ}C$.

• Journal of Conservation Science
• /
• v.26 no.2
• /
• pp.183-190
• /
• 2010

We fabricated urethane material based on properties of reversible and unfading for antic-ceramics restoration. This material with low viscosity was made hardness control possible that user want. And it have very strong adhesion and shear strength properties and is shown the best properties for pigment filling, anti-contractibility, coloring as like epoxy system materials. Particularly, the yellowing and ir-reversibility problem in epoxy restoration material were finally solved. So, there is guarantee in the eternity and stabilization of restoration for antic-celamics. And in order to show the reversible state of the restoration, we successfully dissolve this urethane materials in solvent after perfect restoring subsequently.

• The korean journal of orthodontics
• /
• v.24 no.2
• /
• pp.433-445
• /
• 1994

Bonding of brackets is one of the essential factors for successful orthodontic treatment' so bond strength of orthodontic adhesives are very important. The purposes of this research were to compare shear bond strength of various orthodontic adhesives and to evaluate failure sites. One-hundred twenty extracted human first premolars were prepared for bonding and premolar brackets were bonded to prepared enamel surfaces with Super C Ortho, Mono-$Lok^2$, Transbond, and Super C Ortho after applying Fluorobond. After bonding of brackets, teeth specimens were divided into 3 groups. In group 1 specimens were stored at humidor $37^{\circ}C$ in 1 hour, in group 2 specimens were stored at humidor $37^{\circ}C$ in 24 hours, thermocycled 10 times and in group 3 specimens were stored at humidor $37^{\circ}C$ in 24 hours, thermocycled 1800 times. Then the universal testing machine Instron 6022, Instron Co., U.S.A. was used to test the shear bond strength of brackets to enamel. After debonding, brackets and enamel surfaces were examined under stereoscopic microscope to determine the failure sites The results were as follows : 1. Shear bond strength was significantly highest of using Super C Ortho after applying Fluorobond and Super C Ortho In group 1, was highest of using Super C Ortho in group 2, and was highest of using Mono-$Lok^2$ in group 3. 2. According to time and temperature change, in using Super C Ortho the group 2 had significantly highest strength and group 3 had lowest strength, in using Mono-$Lok^2$ the group 2 and had higher strength than group 1 and in using Super C Ortho after applying Fluorobond shear bond strength decreased constantly, 3. The failure sites were tooth-resin interface in Super C Ortho after applying Fluorobond, Mono $Lok^2$ and Transbond and were at almost same ratio bracket base-resin interface and tooth-resin interface in Super C Orth.

• Restorative Dentistry and Endodontics
• /
• v.30 no.6
• /
• pp.450-460
• /
• 2005

The aim of this study was to evaluate the effect of cavity shape, bond quality of bonding agent and volume of resin composite on shrinkage stress developed at the cavity floor. This was done by measuring the shear bond strength with respect to iris materials (cavity shape , adhesive-coated dentin as a high C-factor and Teflon-coated metal as a low C-factor), bonding agents (bond quality: $Scotchbond^{TM}$ Multi-purpose and Xeno III) and iris hole diameters (volume; 1mm or 3mm in $diameter{\times}1.5mm$ in thickness). Ninety-six molars were randomly divided into 8 groups ($2{\times}2{\times}2$ experimental setup). In order to simulate a Class I cavity, shear bond strength was measured on the flat occlusal dentin surface with irises. The iris hole was filled with Z250 restorative resin composite in a bulk-filling manner. The data was analyzed using three-way ANOVA and the Tukey test. Fracture mode analysis was also done When the cavity had high C-factor, good bond quality and large volume, the bond strength decreased significantly The volume of resin composite restricted within the well-bonded cavity walls is also be suggested to be included in the concept of C-factor, as well as the cavity shape and bond quality. Since the bond quality and volume can exaggerate the effect of cavity shape on the shrinkage stress developed at the resin-dentin bond, resin composites must be filled in a method, which minimizes the volume that can increase the C-factor.

• Journal of Adhesion and Interface
• /
• v.23 no.2
• /
• pp.44-52
• /
• 2022

Epoxy resin has the disadvantage of being easily destroyed by instantaneous impact due to its high crosslinking density despite its high glass transition temperature (T_g) and excellent properties. To compensate for this, in this study, polyol was synthesized by ring opening polymerization of propylene glycol (PPG) diamine, Jeffamine D 2000 and propylene carbonate, and urethane modified epoxy was synthesized using this. The properties of the synthesized urethane modified epoxy were confirmed by FT-IR, H-NMR. To confirm the degree of improvement in impact resistance as an adhesive, a urethane modified epoxy adhesive was prepared by mixing a digylcidyl ether bisphenol A (DGEBA) with curing agent and curing accelerator. Properties test of urethane modified epoxy were shear strength, tensile strength and impact strength. As a result, excellent results were obtained in all test when the ratio of DGEBA : urethane modified epoxy was 8:2.

• Journal of the korean academy of Pediatric Dentistry
• /
• v.37 no.3
• /
• pp.298-307
• /
• 2010

The purpose of this study was to assess the effect on oxygen inhibition layer(OIL) for the interfacial bonding between resin composite layers, including shear bond strength, fracture modes and degree of conversion. The first layer of specimen was filled with Z-250(shade A3) and was cured for 40s. The second layer of specimen was filled with same composite(shade A1) and was cured for 40s. The first layer of specimens for each group were prepared by methods as followings. Control(curing in atmospheric air), Group1(curing against Mylar strip), Group2(scrubbed with a acetone-soaked cotton), Group3(using Tescera light cup), Group4(using Tescera heat cup), Group5(stored in disti1led water for 30days at $37^{\circ}C$), Group6 (using bonding agent). The results were as follows: 1. There was no statistically significant different shear bond strength between control and group 1(p>0.05). 2. Group 2 showed significantly lower shear bond strength than control and group 1(p<0.05). 3. The observation of the fracture surface leads to the evidence that a major difference occurs in the case of control, group1 and group 3 samples which break mainly cohesively while the other groups break in majority adhesively. 4. The results of FTIR showed that the degree of conversion was the highest in group 2 and the lowest in control group(p<0.05). It can be concluded that an OIL is not necessary for bonding with composite resin. But if a reduced critical amount of the unreacted monomer is present, it was detrimental to bonding additional layers of composite. Further study, such as the quantitative analysis of the unreacted monomer are required.