Hydration reaction of Free-CaO is thought to be the main reason of expansion failure of slag. A lot of research institutions are conducting studies on solutions to this problem, and moreover it has been carried out how to make use of aggregates for concrete. While studies covering wide rage of blast furnace slag have been accomplished in the country, studies on steelmaking slag are insufficient. Therefore, this study aimed at analyzing basic physical properties of electric arc furnace oxidizing slag, which is the main material, and furthermore it focused on how to make use of aggregates for concrete examining chemical mechanism, which can be put to practical use. To address this issue, components of electric arc furnace oxidizing slag were analyzed with measurement of physical properties, followed by long-term strength and detailed durability analysis, which can evaluate the appropriateness of application of cement concrete. Besides the environmental conservation and recycling which can be obtained by application of industry byproducts, commercializing of electric arc furnace oxidizing slag as fine aggregates for cement concrete are expected.

• Proceedings of the Korean Institute of Resources Recycling Conference
• /
• 2001.05a
• /
• pp.409-411
• /
• 2001

(주)서울암면은 현무암, 안산암, 백운석등의 천연원료를 사용하는 기존 공정 대신에 제철소에서 발생하는 고로슬래그를 주원료로 이용하는 공정으로 암면을 제조하고 있다. 본 연구에서는 재활용율이 낮은 산업부산물인 전기로 슬래그, 폐주물사, 알루미늄 드로스 둥을 암면원료로 대체사용하는 기술을 개발하고자 하였다. 시험생산은 전기로슬래그와 석탄을 분체로 혼합한 브리켓트를 만들어, 기존원료의 많은 부분을 대체하여 큐폴라로에 장입하여 생산하였으며 폐주물사, 알루미늄 드로스 등의 첨가율도 조절하였다. 생산된 암면 제품은 한국공업규격인 KS F4701 암면 단열재 시험법에 규정된 규격을 만족하였다.

• Resources Recycling
• /
• v.28 no.2
• /
• pp.40-45
• /
• 2019

During steelmaking in EAF, recycled scraps is used as a main material, melted by arc, and electricity use as a main energy. Slag foaming is an important technology for reducing electrical energy. CO gas generated by the reaction between injection carbon and (FeO), [C] and injection {$O_2$}. CO gas generated by this reaction is collected in slag, resulted in slag foaming. In general, the carbon materials used in the EAF process is anthracite and coke. This study investigated the effects of the carbon materials used on slag foaming in the steelmaking process. As a result of this study, the slag foaming height is increased by cokes rather than anthracite, and with an increase in the amount of particles samller than $500{\mu}m$. Based on these results, the application to the operation resulted in increase of slag forming height, reduction of injection carbon, and reduction of electrical energy.

• KSCE Journal of Civil and Environmental Engineering Research
• /
• v.9 no.2
• /
• pp.55-61
• /
• 1989

This is a basic experimental research tried to use electric furnace slag as a fine aggregate for concrete. Chemical component and physical properties of electric furnace slag were studied, and expansion mechanism and aging method for stabalization of electric furnace slag were discussed. Concrete properties electric furnace slag as a fine aggregate were also studied in this paper.

• Journal of the Korean Recycled Construction Resources Institute
• /
• v.11 no.1
• /
• pp.70-78
• /
• 2023

Blast furnace slag, a by-product of the steel industry, is mostly recycled as concrete admixture, but electric arc furnace slag has not been recycled to date. In particular, since electric arc furnace slag partially contains free lime (free-CaO) in the discharge, it is necessary to review this in order to recycle f or construction materials. Recently an atomizing process which is a method of rapidly cooling electric arc furnace slag has been developed and applied. Therefore, in order to use the fine aggregate of oxidized slag from electric furnace restored by this method as an aggregate for concrete, physical damage and chemical reviewing are required. In this study, a physical and chemical review was conducted on the fine aggregate of Electric Arc Furnace Oxidizing Slag (EFOS) as a by-product of the steel manufacturing process with atomizing process. In this experimental study, EFOS was experimentally examined about whether it can be used as concrete fine aggregate. Also, we intend to provide basic data for the future use of the EFOS fine aggregate. As a result of the experimental study, it was found that the fine aggregate of the EFOS satisfied the quality standards of the fine aggregate for concrete in most items specified by Korean Standard.

• Resources Recycling
• /
• v.22 no.1
• /
• pp.36-41
• /
• 2013

LF slag is formed by EAF carryover slag and slag former(such as lime, dolomite) put into the ladle during the tapping molten metal. After LF process, continuous casting is started when molten steel is sent from ladle to tundish through bottom nozzle of ladle. Conventionally, remained molten slag and steel in ladle are poured into a slag port and they are transferred to a slag yard and then recycled. In this study, we investigated about recycling of molten LF slag residue(including Fe residue to reuse) which is made in steelmaking process. As a result, lime usage was decreased about 2.2~3.2 kg/steel-ton and also molten steel yield rate was increased about 0.3 ~ 0.5 percent point.

• Journal of the Korea Concrete Institute
• /
• v.21 no.3
• /
• pp.367-375
• /
• 2009

Recently, more focus is shift to imbalances in aggregate market supply and demand and an exhaustion of natural resources. In this situation, Electric arc furnace oxidizing slag (EAF slag) has high application possibility as aggregate for concrete due to similar property with general aggregate. However, it is inherent the problem which causes pop-out by free-CaO contained in slag In this study, we've got the plan to assure the chemical stability of EAF slag, and then experimentally tested the mechanical performance and durability for the fine aggregate used EAF slag. On this test result, we suggest the application plan. At the result of this study, it shows that EAF slag would reduce the surface defect such as pop-out due to natural aging for the fixed hour and adjustment the grain size of EAF slag. And mechanical performance and durability according to the replacement rate of concrete service, were revealed more than equal or equal compare to general aggregate. Hereafter, quality control must precede not to impede the beauty of concrete surface as assure the safety for aging and processing. And, to establish the environmental resource recycling system for by-products of steel, it should be made development of various application and guideline of quality control for the EAF slag aggregate. Moreover, it must be constantly studied all kind of engineering performance and durability for related to this study.

• Journal of the Korea institute for structural maintenance and inspection
• /
• v.18 no.3
• /
• pp.133-142
• /
• 2014

Recently, more focus is shift to imbalances in aggregate market supply and demand and an exhaustion of natural resources. In this situation, Electric arc furnace oxidizing slag (EAF Slag) has high application possibility as aggregate for concrete due to similar property with general aggregate. In this study, We've got the plan to assure the chemical stability of EAF Slag, and then experimentally tested the mechanical performance and durability for the fine aggregate used EAF Slag. On this test result, we suggest the application plan. At the result of this study, it shows that EAF slag would reduce the surface defect such as pop-out due to natural aging for the fixed hour and adjustment the grain size of EAF Slag. And mechanical performance and durability according to the replacement rate of concrete service, were revealed more than equal or equal compare to general aggregate. Hereafter, quality control must precede not to impede the beauty of concrete surface as assure the safety for aging and processing. And, to establish the environmental resource recycling system for by-products of steel, it should be made development of various application and guideline of quality control for the EAF slag aggregate. Moreover, it must be constantly studied all kind of engineering performance and durability for related to this study.

• Resources Recycling
• /
• v.19 no.6
• /
• pp.93-101
• /
• 2010

In this study, we have studied hydration properties and compressive strength of the electric arc furnace reduction slag as a cement admixture. The reduction slag is mainly consisted of 17.1% of f-CaO and rapid curing clinker minerals, 37.1% of $C_{11}A_7CaF_2$, and 21.0% of $C_3A$. When the substitution rate of the slag on OPC was 30%, the initial setting time and final setting time has been shortened from 305 min. and 425 min. to 10min. and 30min. When the substitution rate of the slag on OPC was 7%, the compressive strength of mixed cement mortars has been increased than that of OPC during all period. When the substitution rate of the slag on OPC was over 20%, the compressive strength of mortars has been reduced than that of OPC at initial and final compressive strength. As a result of hydration properties of reduction slag, $C_{11}A_7CaF_2$ transfer to $C_3AH_6$ but as the substitution rate of slag on OPC increases, increased f-CaO and the metastable hydrates $C_4AH_{13}$ increased. Therefore, we should control the substitution rate of the slag on OPC was under 7% in order to use EAF reduction slag as a cement admixture.

• Journal of the Korea Concrete Institute
• /
• v.14 no.4
• /
• pp.597-607
• /
• 2002

Electric arc furnace and converter slag are produced by about 6 millions tons in Korea at 2000 year. But compared with blast furnace slag, those are utilized only in unvalued material like landfill and road construction. There are unstable materials, like free CaO, in electric arc furnace and converter slag at steel-manufacturing process. This might cause volume expansion in concrete, if electric arc furnace and converter slag aggregates were used in concrete. This expansion may reach to crack or collapse of concrete. It is therefore settled by standard specification for concrete that electric arc furnace and converter slag aggregates have not to use in concrete. First of all, volume stability and stabilized process should be solved in electric arc furnace and converter slag aggregate to use in concrete. In this study, 6 types of aging are evaluated for effects of stabilization to reduce the expansion of electric arc furnace and converter slag. h converter slag aggregate, these types of aging are not good for volume stability for concrete aggregate, and even if converter slag aggregate is treated with aging, concrete with it has some problems that strength is reduced with curing days. But in electric arc furnace slag aggregate treated with hotwater and steam aging, the expansion of electric arc furnace slag aggregate is reduced about two times than that of converter slag aggregate, and electric arc furnace slag aggregate concrete has good results in strength compared with control concrete using crushed stone.