• Journal of the Korea Academia-Industrial cooperation Society
• /
• v.3 no.3
• /
• pp.216-220
• /
• 2002

In this study, edible coatings for ‘Niikata’ pears have been applied in order to provide an alternative way to control and extend market quality and shelf life during cold storage. Fruit treated with edible coatings had better effects on maintaining some quality features such as fresh weight, firmness and SSC content than non-coated fruits. However, non-coated fruits in terms of overall quality were better evaluated than fruit with edible film. It may be caused by various factors such as film thickness effect oil emulsion on fruit skin, unknown reactions between the fruit skin and functional groups in the chitosan structure and so on.

• Proceedings of the Korean Society of Dyers and Finishers Conference
• /
• 2011.03a
• /
• pp.60-60
• /
• 2011

막구조는 근래에 와서 대공간 구조 및 지붕구조에 가장 보편적으로 사용되는 경량 인장 구조물로 각광받고 있다. 구조용 막재는 풍하중 및 설하중에 충분히 감당할 수 있도록 강도와 내구성을 가지고 있어야 한다. 일반적으로 막구조 재는 PVC코팅 폴리에스터막, 실리콘코팅 유리섬유막, PTFE코팅 유리섬유막이 있다. 제직되는 원단의 크기가 한정되어 있기 때문에 재단 후 접착하여 제작한다. 이 때문에 이음부분이 나 재단부분에 코팅으로 인한 접착이 어려워 고온고압으로 접착을 한다. 이 연구에서는 실리콘코팅 유리섬유막의 접착시 어려움을 보완하기 위해 저온 Plasma를 이용한 처리법으로 방전에 의해 Plasma를 발생시켜 50w, 100w 출력으로 10분, 20분간 처리하여 그 결과를 접촉각과 SEM 관찰을 통해 표면처리를 관찰하였다. Plasma 처리로 인해 실리콘 표면층에 균열이 발생하고 표면이 갈라짐을 확인할 수 있었다. 접촉각측정 결과 Plasma 출력과 시간의 증가함에 따라 접촉각은 감소하였다. 실리콘코팅 원단에 저온 Plasma 처리한 후 표면 특성을 분석하고 원단을 접착을 시켜 박리 강도를 측정함으로써 막구조 원단의 접착력 향상에 대한 연구를 진행하였다. KS K 0533 접착포의 박리 강도 시험방법으로 실리콘코팅 원단의 박리 강도를 측정한 결과 플라즈마 처리 원단이 플라즈마 미처리 원단보다 박리 강도가 향상된 것을 확인할 수 있었다. 저온 Plasma 처리 시간이 증가할수록 표면의 젖음성을 향상시켜 접촉각을 낮추었다. 이는 곧 표면에너지의 증가를 뜻하는 것으로 접착력을 증가시켜 실리콘코팅 원단의 접착성을 시킴으로써 강한 강도와 내구성을 갖춘 막구조물의 개발에 기대되고 있다.

• Korean Journal of Optics and Photonics
• /
• v.17 no.5
• /
• pp.480-486
• /
• 2006

Generally, IR cut-off filters for mobile phone is coated on the glass substrate at high temperature(above $300^{\circ}C$). In this work, we prepared IR cut-off filters on the poly(methyl methacrylate)(PMMA) substrates at low temperature(about $70^{\circ}C$ ). using the $CeO_2\;and\;SiO_2$ coatings by physical vapor deposition. The surface energies of coated and uncoated PMMA, and adhesive properties of IR cut-off filters coatings were examined using contact angle measurements. We demonstrate the improve of mobile phone optical system using these results.

• Journal of the Korean Society of Marine Environment & Safety
• /
• v.23 no.4
• /
• pp.407-414
• /
• 2017

In this study, a performance evaluation was conducted using a SUS 304 plate applied to low-temperature co-fired coating as a replacement for titanium plates. As a result of computational fluid dynamic analysis, the SUS 304 plate, applied to low-temperature co-fired coating, showed better heat transfer performance than a titanium plate, for 100 micron thickness coating. The result of the experiments using an actual heat exchanger revealed that a coated SUS 304 plate showed better heat transfer performance than a titanium plate. Furthermore, as the degree of corrosion and scale formation of the plate was confirmed through an overhaul inspection, the corrosion resistance of a coated SUS 304 plate was found to be almost the same as that of a titanium plate, and the inhibition effect of scale formation by sea water was better with a coated SUS 304 plate.

• Journal of the Korean Applied Science and Technology
• /
• v.35 no.1
• /
• pp.80-88
• /
• 2018

In this study, we prepared hybrid composites by using low temperature sol-gel process for transparent and hard coating film. The hybrid composites consist of $ZrO_2/TiO_2/organosilane$, of which organosilane was introduced 3-(trimethoxysilyl)propyl methacrylate due to the role of a photocurable ceramic material for low temperature process. The ceramic composites with various composition ratios were coated on a polycarbonate substrate using a sol-gel process of low temperature process, and characterized optical and mechanical properties of coated thin film. The transparencies of coated thin films were 97.5 % or more, and the pencil hardness were 9H or more. In the case of the ZTS-2-1, the nano-indentation hardness was measured at the highest value of 1.14 GPa.

• Journal of the Korean Applied Science and Technology
• /
• v.38 no.6
• /
• pp.1561-1567
• /
• 2021

In this study, we have studied synthesis of zirconia-alumina composite coating materials via a low-temperature sol-gel process. The zirconia-alumina composites were prepared by coating zirconia precursor, alumina precursor, and organosilane mixture on a polyethylene terephthalate substrate through three steps: sol-gel process, low-temperature photocuring process, and heat treatment process. The structural properties and element analysis of the composites were confirmed by FT-IR and XPS. The coated composite showed a transmittance of 96% or more in the visible light region with a wavelength of 420 nm or more and pencil hardness of 9H or more. In case of the composite of the molar ratio of zirconia and alumina of 1:4, the highest nanoindentation hardness was measured with 1.212 GPa.

• Journal of Nuclear Fuel Cycle and Waste Technology(JNFCWT)
• /
• v.8 no.3
• /
• pp.247-260
• /
• 2010

The developement of a HLW disposal canister is under way in KAERI using Cold Spray Coating technique. To estimate corrosion behavior of a cold sprayed copper, a creivice corrosion test was conducted at Southwest Research Institute(SWRI) in the United State. For the measurement of repassivation potential needed for crevice corrosion, three methods such as (1) ASTM G61-86 : Cyclic Potentiodynamic Polarization Measurements, (2) Potentiodynamic Polarization plus intermediate Potentiostatic Hold method, and (3) ASTM G192-08 (THE method) : Potentiodynamic- Galvanostatic-Potentiostatic Method, were introduced in this report. In the crevice corrosion test, the occurrence of corrosion at crevice area was optically determined and the repassivation potentials were checked for three kind of copper specimens in a simulated KURT underground water, using a crevice former dictated in ASTM G61-86. The applied electrochemical test techniques were cyclic polarization, potentiostatic polarization, and electrochemical impedance spectroscopy. As a result of crevice corrosion tests, every copper specimens including cold sprayed one did not show any corrosion figure on crevice areas. And the open-cell voltage, at which corrosion reaction initiates, was influenced by the purity of copper, but not their manufacturing method in this experiment. Therefore, it was convinced that there is no crevice corrosion for the cold sprayed copper in KURT underground environment.

• Journal of the Microelectronics and Packaging Society
• /
• v.22 no.3
• /
• pp.25-30
• /
• 2015

SAC-coated Cu specimens were fabricated by novel pad finish process using a phenomenon that metal nanoparticles less than 20 nm in diameter melted at a temperature lower than the melting point of bulk metal, and their wettabilities were evaluated. The thickness of SAC305 layer coated at low temperature of $160^{\circ}C$ using SAC305 ink was extremely thin as the level of several nanometers. It was analyzed by Auger electron spectroscopy that $Cu_6Sn_5$ intermetallic layer with a thickness of 10~100 nm and $Cu_3Sn$ intermetallic layer with a thickness of 50~150 nm were sequentially formed under the SAC305 coating layer. The thickness of formed intermetallic layers was thicker in electroplated Cu than rolled Cu, which attributed to improved surface roughness in the electroplated Cu. The improved surface roughness induces the contact, melting, and reaction of a larger number of SAC305 nanoparticles per the unit area of Cu specimen. In the wetting angle test using SAC305 solder balls, the Cu coated with SAC305 through the low temperature process presented evidently low wetting angles than those in non-coated Cu, indicating that only a few nanometer-thick SAC305 coating layer on Cu could also cause the enhancement of wettability.

• Proceedings of the Korean Vacuum Society Conference
• /
• 2010.02a
• /
• pp.263-263
• /
• 2010

투명도전막(indium tin oxide; ITO)은 투명하면서도 전기 전도도가 높기 때문에, 액정표시소자(LCD; Liquid Crystal Display), 전자발광소자(ELD; Electroluminescent Display) 및 전자 크로믹 소자(Electrochromic Display)를 포함하는 평판형 표시 소자(FPD; Flat Panel Display)와 태양전지 등에 이용되고 있다. 낮은 비저항과 높은 투과율의 ITO 박막은 $300^{\circ}C$ 이상의 고온에서 코팅해야 하는 것으로 알려져 있다. 그러나 최근 플라스틱과 같은 연성 소자가 전자부품에 널리 이용되면서 ITO를 저온에서 증착해야할 필요성이 대두되고 있다. 본 연구에서는 ITO를 플라스틱에 적용하기 위한 저온 코팅 공정 및 시편의 전 후처리공정을 개발하여 박막의 특성을 알아보고자 한다. 실험에 사용된 기판은 고투과율의 고분자(polyethylene terephthalate; PET) 필름이며 $5\;{\times}\;10\;cm^2$의 크기로 절단하여 알코올로 초음파 세척을 실시하였고, 진공 용기에 장입한 후 펄스전원을 이용하여 3분간 in-situ 청정을 실시하였다. ITO 코팅은 마그네트론 스퍼터링을 이용하였으며, 코팅시간, 전처리, 후처리, 기판온도, 산소유량 등 코팅 조건에 따른 박막의 특성을 조사하였다. ITO 박막의 코팅 조건에 따른 박막의 결정구조 분석은 x-선 회절(x-ray diffraction; XRD)을 이용하였고, 박막의 표면형상과 두께 보정 및 단면의 미세조직과 결정 성장 여부 등은 투과전자 현미경(transmission electron microscope; TEM)을 이용하여 분석하였다. 또한 ITO 박막의 면저항과 분광특성은 four-point Probe (CMP-100MP, Advanced Instrument Technology), spectrophotometer (UV-1601, SHIMADZU)를 이용하여 측정하였다. ITO 박막의 광학특성 분석 결과 전광선 투과율은 두께에 따라 변화 하였지만, 색차와 Haze 값은 증착 조건에 따라 큰 차이는 보이지 않았다. 그리고 박막의 결정화에 영향을 주는 가장 중요한 인자는 기판온도이지만, 기판온도를 높이지 못할 경우 비평형 마그네트론(unbalanced-magnetron; UBM)에 의해서 플라즈마 밀도를 높이는 방법으로 유사한 효과를 얻을 수 있음을 확인하였다.

• Ceramist
• /
• v.12 no.6
• /
• pp.7-12
• /
• 2009