• Journal of the Korean Society for Aeronautical & Space Sciences
• /
• 제49권10호
• /
• pp.813-820
• /
• 2021

In this study, a low-velocity impact test was performed to obtain the dynamic properties of solid propellants. The dynamic behavior of the solid propellant was examined by measuring the force and displacement of the impactor during the low-velocity impact test. The bending displacement was calculated by compensating for the local displacement caused by the low-velocity impact test in the form of three point bending and the shear displacement caused by using a short and thick solid propellant specimen. Stress and strain were calculated using compensated displacements and measured force, and dynamic properties of solid propellants were obtained from the stress-strain curve and compared with static bending test. The dynamic properties of solid propellant under the low-velocity impact loading at various operating temperature conditions such as room temperature(20 ℃), high temperature(63 ℃), and low temperature(-32 ℃) were compared and investigated.

• Composites Research
• /
• 제18권3호
• /
• pp.7-13
• /
• 2005

This paper presents a study on the low velocity impact response of the woven fabric laminates for the hybrid composite bodyshell of a tilting railway vehicle. In this study, the low velocity impact tests for the three laminates with size of $100mm\times100mm$ were conducted at three impact energy levels of 2.4J, 2.7J and 4.2J. Based on the tests, the impact force, the absorbed energy and the damaged area were investigated according to the different energy levels and the stacking sequences. The damage area was evaluated by the visual inspection and the C-scan device. The test results show that the absorbed energy of [fill]8 laminate is highest whereas (fill2/warp2)s is lowest. The [fill]8 laminate has the largest damage area because of the highest impact energy absorption.

• Composites Research
• /
• 제20권4호
• /
• pp.42-50
• /
• 2007

This paper describes the results of experiments and numerical simulation studies on the low-velocity impact damage of two different sandwich composite panels for application to bodyshell and floor structure of the BIMODAL tram vehicle. Square test samples of 100mm sides were subjected to low-velocity impact loading using an instrumented testing machine at four impact energy levels. Part of this work presented is focused on the finite element analysis of low-velocity impact response onto a sandwich composite panels. It is based on the application of explicit finite element (FE) analysis codes LS-DYNA 3D to study the impact response of sandwich structures under low-velocity impact conditions. Material testing was conducted to determine the input parameters for the metallic and composite material model, and the effective equivalent damage model for the orthotropic honeycomb materials. Numerical and experimental results showed a good agreement for damage area and the depth of indentation of sandwich composite panels created by the impact loading.

• Journal of the Korean Society for Aeronautical & Space Sciences
• /
• 제32권7호
• /
• pp.51-59
• /
• 2004

An experimental procedure to identify failure modes of impact damage using sensor signals and to analyze their general features is examined. A series of low-velocity impact tests from low energy to damage-induced high energy were performed on the instrumented drop weight impact tester to monitor the stress wave signals due to failure modes such as matrix cracking, delamination, and fiber breakage. The wavelet transform(WT) and Short Time Fourier Transform(STFT) are used to decompose the piezoelectric sensor signals in this study. The extent of the damage in each case was examined by means of a conventional ultrasonic C-scan. The PVDF sensor signals are shown to carry important information regarding the nature of the impact process that can be extracted from the careful signal processing and analysis.

• Composites Research
• /
• 제26권2호
• /
• pp.116-122
• /
• 2013

In this study, impact behavior of aluminium and glass-fiber structure is studied under low impact velocity. Compression test is carried out to investigate the compressive strength of the specimens. The degree of damage is observed using microscopy and compared with the experimental analysis data. The maximum load capacity, impact strength and elastic energy of glass-fiber honeycomb sandwich panel are more than the aluminium honeycomb sandwich panel.

• Composites Research
• /
• 제35권6호
• /
• pp.469-476
• /
• 2022

In this paper, the microwave absorbing characteristics after the impact of the radar-absorbing structure (RAS) consisting of periodic pattern sheet (PPS) and glass fiber-reinforced plastic (GFRP) were experimentally investigated. The fabricated RAS effectively absorbed the microwave in the X-band (8.2-12.4 GHz). In order to induce the damage to the RAS, a low-velocity impact test with various impact energy of 15, 40, and 60 J was conducted. Afterward, the impact damage was observed by using visual inspection, non-destructive test, and image processing method. Moreover, the absorbing performance of intact and damaged RAS was measured by the free-space measurement system. The experiment results revealed that the delamination damage from the impact energy of 15 J did not considerably affect the microwave absorbing performance of the RAS. However, fiber breakage and penetration damage with a relatively large damaged area were occuured when the impact energy was increased up to 40 J and 60 J, and these failures significantly degraded the microwave absorbing characteristics of the RAS.

• Transactions of the Korean Society of Mechanical Engineers A
• /
• 제36권11호
• /
• pp.1345-1352
• /
• 2012

This paper aims to evaluate the low-velocity impact responses and mechanical properties of balsa-wood and urethane-foam core materials and their sandwich panels, which are applied as the impact limiter of a nuclear spent fuel shipping cask. For the urethane-foam core, which is isotropic, tensile, compressive, and shear mechanical tests were conducted. For the balsa-wood core, which is orthotropic and shows different material properties in different orthogonal directions, nine mechanical properties were determined. The impact test specimens for the core material and their sandwich panel were subjected to low-velocity impact loads using an instrumented testing machine at impact energy levels of 1, 3, and 5 J. The experimental results showed that both the urethane-foam and the balsa-wood core except in the growth direction (z-direction) had a similar impact response for the energy absorbing capacity, contact force, and indentation. Furthermore, it was found that the urethane-foam core was suitable as an impact limiter material owing to its resistance to fire and low cost, and the balsa-wood core could also be strongly considered as an impact limiter material for a lightweight nuclear spent fuel shipping cask.

• Journal of the Korean Society for Aeronautical & Space Sciences
• /
• 제31권2호
• /
• pp.51-56
• /
• 2003

The piezoelectric thin film(PVDF: polyvinylidene fluoride) sensors having good dynamic sensing charachteristics can be used to monitor low vwlocit impact on composite structures. The impact response function for composite sandwich beam was derved. The impact tests at low energy without inducing damage were performed on the instrumented drop weight impact tester. The measured signals of PVDF sensors attached on the surface of the beam agreed well with the simulated signals. And the inverse technique was applied to reconstruct the impact forces from the PVDF sensor signals. Most of reconstructed impact forces showed good agreement with the measured forces. The comparison results showed that the piezoelectric thin film sensor can be used to monitor the low velocity impact on composite sandwich structures.

• Composites Research
• /
• 제16권4호
• /
• pp.66-73
• /
• 2003

The importance of understanding the response of structural composites to impact and CAI cannot be overstated to develop analytical models for impact damage and CAI strength predictions. This paper presents experimental findings observed from quasi-static lateral load tests, low velocity impact tests. CAI strength and open hole compressive strength tests using 3 mm thick composite plates($[45/-45/0/90]_{3s}$- IM7/8552). The conclusion is drawn that damage areas for both quasi-static lateral load and impact tests are similar and the curves of several drop weight impacts with varying energy levels(between 5.4 J and 18.7 J) follow the static curve well. In addition, at a given energy the peak force is in good agreement between the static and impact cases. It is identified that the failure behaviour of the specimens from the CAI strength tests was very similar to that observed in laminated plates with open holes under compression loading. The residual strengths art: in good agreement with the measured open hole compressive strengths. considering the impact damage site area, an equivalent hole. The experimental findings suggest that simple analytical models for the prediction of impact damage area and CAI strength can be developed on the basis of the failure mechanism observed from the experimental tests.

• Composites Research
• /
• 제15권5호
• /
• pp.7-13
• /
• 2002

The piezoelectric thin film sensor has good characteristics to observe the impact responses of composite structures. The capabilities for monitoring impact behavior of Gr/Ep laminates subjected to damage-induced impact using the PVDF(polyvinylidene fluoride) film sensor were examined. For a series of low-velocity impact tests from low energy to damage-induced energy, simulated sensor signals were compared with measured signals and the PVDF film sensor. Local impact damages(matrix cracking and delamination) were found at three impact tests, but the measured signals agreed well with the simulated sensor signals based on the linear relationship between the impact forces and the PVDF film sensor signals. And the inverse technique was applied to reconstruct the impact forces using the PVDF film sensor signals. Most of reconstructed impact forces had good agreement with the measured forces. The comparison results showed that the local damage due. to low-velocity impact didn't disturb the global impact responses of composite laminates and the reconstruction of impact forces from PVDF sensor signals wasn't affected by the local damage.