• Proceedings of the KSME Conference
• /
• 2001.06c
• /
• pp.251-256
• /
• 2001

Deformation analysis of injection molded articles whose geometry is considered as the assembly of the thin flat plates has been conducted. For the in-mold analysis, thermo-viscoelastic stress calculation of rheologically simple amorphous polymer and in-mold deformation calculation considering the in-plane mold constraint has been done. Free volume theory has been used for the non-equilibrium density state by the fast cooling. At ejection, the redistribution of stress together with instantaneous deformation has been considered. During out-of-mold cooling after ejection, thermoelastic model based on the effective temperature has been adopted for the calculation of deformation. Two typical mold geometries are used to test the numerical simulation.

• Korean Journal of Materials Research
• /
• v.6 no.9
• /
• pp.878-884
• /
• 1996

본 연구는 가스압소결 질화규소의 혼합모드에 있어서 파괴거동을 실온 및 100$0^{\circ}C$에서 조사하였다. 실험은 누프압흔을 도입한 시험편을 사용하여 소둔처리에 의해 잔류응력을 제거하고, 4점굽힘법을 이용하였다. 실험결과, 종래 제창되고 있는 파괴기준과 일치하지 않고, 그래서 새롭게 4차관수의 근사식을 제안하였다.

• Journal of the Korean Society of Safety
• /
• v.12 no.2
• /
• pp.27-36
• /
• 1997

This paper evaluates the static and fatigue bending strengths of CFRP (carbon fiber reinforced plastic) laminates subjected to hygrothermals. The specimens which had different stacking composition, orthotropic and quasi-isotropic laminated plates, were prepared for this experiment. A steel ball launched by the air gun collides against CFRP laminates to generate impact damages, and the 3-point fatigue bending test is carried out by using the impacted laminates to investigate the influence of hygrothermals on the effect on the residual bending fatigue strength of CFRP laminates.

• Journal of the Society of Naval Architects of Korea
• /
• v.33 no.3
• /
• pp.22-34
• /
• 1996

Regarding the plate bending process by line heating method, in this study a simplified numerical analysis is performed for a beam model to predict its residual deformation and stress distribution. Using the modified strip theory and beam finite element method, a PC-based simulation program is developed for a thermo-elastic-plastic beam. The plate bending problem can be approximately replaced by a beam model using distributed springs to account for the effect of adjacent strips. The spring constants are chosen as the best fit with experiments. In this paper, it is assumed that the temperature distribution is already given and the temperature-dependent material properties are considered. To verify the simulation program, the results using present numerical algorithm are compared with other published experimental results and similar numerical studies. The comparison shows good agreement. The present PC-based computer program also shows good efficiency in computing time.

• Transactions of the Korean Society of Mechanical Engineers A
• /
• v.22 no.1
• /
• pp.238-246
• /
• 1998

Surface residual stresses as well as wall thickness and ovality changes after U-bending process on UNS N06690 row-1 heat exchanger tubes, were estimated. Surface residual stresses were measured by Hole Drilling Method(HDM), calculating the stresses from relieved strains of 3 rosette strain gages. After bending of the tubes, dimensional tolerances for wall thickness and ovality were satisfied with ASTM requirements. Residual stresses at the extrados were introduced with compressive stress(-) by bending operations, and its maximum value reached-319 MPa in axial direction at ${\phi}=0^{\circ}$ in position. Tensile residual stresses(+) of ${\sigma}_zz=45$ MPa,${\sigma}_zz=25$ MPa were introduced in the intrados surface at position of ${\phi}=0^{\circ}$ Maximum tensile residual stress of 170 MPa was detected on the flank side at position of ,${\phi}=95^{\circ}$i.e., at apex region. It appeared that higher stress gradients were generated at the irregular transition regions. In the trend of residual stress changes with U-bend position, the extrados is related with the changes of ovality and the intrados is related with the changes of wall thickness.

• Transactions of the Korean Society of Mechanical Engineers A
• /
• v.24 no.2 s.173
• /
• pp.279-289
• /
• 2000

Residual stress induced in U-bending and tube-to-tubesheet joint processes of PWR's row-1 heat exchanger tube was measured by X-ray method and Hole-Drilling Method(HDM). Compressive residual stresses(-) at the extrados surface were induced in U-bending, and its maximum value reached -319 MPa in axial direction at the position of $\psi$ = $0^{\circ}$. Tensile residual stresses(+) of $\sigma_{zz}$ = 45 MPa and $\sigma_{\theta\theta}$ = 25 MPa were introduced in the intrados surface at the position of $\psi$ = $0^{\circ}$. Maximum tensile residual stress of 170 MPa was measured at the flank side at the position of $\psi$ = $90^{\circ}$, i.e., at apex region. It was observed that higher stress gradient was generated at the irregular transition regions (ITR). The trend of residual stress induced by U bending process of the tubes was found to be related with the change of ovality. The residual stress induced by the explosive joint method was found to be lower than that by the mechanical roll method. The gradient of residual stress along the expanded tube was highest at the transition region (TR), and the residual stress in circumferential direction was found to be higher than the residual stress in axial direction.

• Transactions of the Korean Society of Mechanical Engineers A
• /
• v.21 no.10
• /
• pp.1541-1550
• /
• 1997

Since the ceramic/metal joint material is made at a high temperature, the residual stress develops when it is cooled from bonding temperature to room temperature due to remarkable difference of thermal expansion coefficient between ceramic and metal. As residual stress at ceramic/metal joints influences the strength of joints, it is important to estimate residual stress quantitatively. In this study, it is attempted to estimate joint residual stress of Si$_3$N$_4$STS304 joints quantitatively and to compare the strength of joints. The difference of residual stress is measured when repeated thermal cycl is loaded, under the conditions of the practical use of the ceramic/metal joint. The residual stress increases at 1 cycle of thermal load but decreases in 3 cycles to 10 cycles of thermal load. And 4-point bending test is performed to examine the influence of residual stress on fracture strength. As a result, it is known that the stress of joint decreases as the number of thermal cycle increases.

• Journal of the Microelectronics and Packaging Society
• /
• v.20 no.1
• /
• pp.21-26
• /
• 2013

This study presents new analysis method to predict bending behavior of packaging substrate structure by comparing finite element method simulation and measured curvature using 3D scanner. Packaging substrate is easily bent and deflected while undergoing various processes such as curing of prepreg and copper pattern plating. We prepare specimens with various conditions and measure contours of each specimen and compute the residual stresses on deposited films using analytical solution to find the principle of bending. Core and prepreg in packaging substrate are made up of resin and bundles of fiber which exist orthogonally each other. Anisotropic material properties cause peculiar bending behavior of packaging substrate. We simulate the bending deflection with finite element method and verify the simulated deflection with measured data. The plating stress of electrodeposited copper is about 58 MPa. The curing stresses of solder resist and prepreg are about 13 MPa and 6.4 MPa respectively in room temperature.

• Resources Recycling
• /
• v.12 no.3
• /
• pp.46-53
• /
• 2003

Recycling of aluminum dross is an important issue in the secondary aluminum industries. In this study, aluminum dross generated in the domestic secondary aluminum industry was processed to use it as raw material for producing alumina refractories. Sample dross was classified according to its size. The dross smaller than 1 mm was leached with sodium hydroxide solution to extract the remained aluminum from the dross into the solution. and then aluminum hydroxide precipitate was recovered from the leach liquor. The waste residue in the leaching was washed, dried and roasted. Most remained metallic components in the residue was changed into oxide through the processes. The roasted dross was made into alumina castable refractories by mixing with aggregates and a binder. Bending strength of the tested castable specimen was over $25\;kg/\textrm{m}^2$ and compressive strength over $80\;kg/\textrm{cm}^2$, which satisfied the Korean Standard value respectively. From the results, it was suggested that this process could be applicable to recycling of aluminum dross.

• Proceedings of the Korea Committee for Ocean Resources and Engineering Conference
• /
• 2001.10a
• /
• pp.247-252
• /
• 2001

Recently the steel parts used at automobiles are required to be used under high stress more than ever before in need of the weight down. To achieve this requirement of a high strength steel, it must be necessary to decrease inclusion content and surface defect as like decarburization, surface roughness etc.. In this study, the surface conditions are measured to know the influence on fatigue properties by two cases of shot peening of two-stage shot peening and single-stage shot peening. And for this study, two kinds of spring steel (SUP7, 50CrV4) are used. This study shows the outstanding improvement of fatigue properties at the case of two-stage shot peening in the rotary bending fatigue test and this is assumed to be from on low stress condition, the 1st stage shot peening is not affected by nonmetallic inclusion under metal. it is possible that the 2nd stage shot peening increases the fatigue life and the high stress but that is affected by nonmetallic inclusion under metal. so far beeasily 50CrV4 have made high stress. But, results also show fatigue failures originated at inclusion near surface, and this inclusion type is turned out to be a alumina of high hardness.