• The Transactions of the Korean Institute of Electrical Engineers C
• /
• v.52 no.2
• /
• pp.61-66
• /
• 2003

The electromagnetic properties and thermal behavior of Mn-Zn ferrite cores used for the blocking filter in he Power Line Communication(PLC) application were investigated as the function of additives. The highest density and permeability of 4.98 g/㎤) and 8,221 respectively were obtained to the specimen with composition of MnO 24 mol%, ZnO 25 mol% and Fe$_2$O$_3$ 51 mol% added MnO$_3$ 400 ppm, SiO$_2$ 100 ppm and CaO 200 ppm since the uniform grains were organized and the microstructures were compacted through reduction of pores. The permeability was increased up to 13,904 as temperature of specimen increased to 11$0^{\circ}C$, however, it was decreased precipitously under 100 over 11$0^{\circ}C$. The exothermic behavior was observed in the frequency range from 1 kHz to 1 MHz that the maximum temperature of specimens became 102$^{\circ}C$ at 1 MHz. In the consequence, the Mn-Zn ferrite core developed by this research will maintain the stable electromagnetic properties since the temperature of ferrite core rose to 93$^{\circ}C$ in the range of 10 kHz to 450 kHz bandwidth qualified for PLC.

• 연구논문집
• /
• s.34
• /
• pp.121-129
• /
• 2004

The influence of powder size and ball-milling time on the magnetic properties of $Fe_{73}Si_{16}B_7Nb_3Cu_1$ nanocrystalline alloy powder was investigated. Flake-shaped powders were produced by pulverizing the ribbons annealed at $550^\circC$ for 1 hour. The powders were classified and consolidated into core shapes at a pressure of 18ton/$cm^2$. The initial permeability at 100kHz of the inductor core produced using $53-75\mum$ powders showed the highest value although its consolidated density showed the lowest one. The reason for the result is due to the cracking of the particles larger than $75\mum$ during the consolidation process. The ball-milling of powders for 2-4 hours improved the consolidation density and the initial permeability of the cores. The intrinsic coercivity of the powder decreased as well, resulting from the stress relief of the powder by a short-time milling.

• The Research Journal of the Costume Culture
• /
• v.23 no.6
• /
• pp.1061-1081
• /
• 2015

Recently, there has been an increase in wellbeing marketing, which focuses on increasing consumer life satisfaction or consumers' sense of subjective wellbeing. Numerous studies have been conducted to identify which aspects contribute to consumer life satisfaction. In order to provide additional insights into consumer life satisfaction, this study aimed to identify the relationships among social psychological variables (consciousness of social face, social interaction anxiety, and career anxiety), shopping confidence, and life satisfaction. Shopping confidence in this study relates to confidence for clothing/accessories. It was hypothesized that social psychological variables influence life satisfaction not only directly but also indirectly through shopping confidence. Data were gathered by surveying university students in Seoul, using convenience sampling. Two hundred eighty six questionnaires were used in the statistical analysis. Factor analysis of consciousness of social face revealed two factors, 'desire to gain face' and 'fear of losing face'. Factor analysis of social interaction anxiety, shopping confidence, and life satisfaction revealed that these variables were uni-dimensional. Test of the hypothesized path showed that all social psychological variables influenced life satisfaction indirectly through shopping confidence, whereas 'fear of losing face' of consciousness of social face and career anxiety influenced life satisfaction directly. The results give marketers some understanding of their consumers' life satisfaction in relation to consciousness of social face, social interaction anxiety, career anxiety, and shopping confidence.

• Proceedings of the Korean Institute of Electrical and Electronic Material Engineers Conference
• /
• 2002.04a
• /
• pp.64-67
• /
• 2002

The Physical and magnetic properties such as microstructure, permeability and power loss of Ni-Zn ferrite with composition of $Ni_{0.8}Zn_{0.2}Fe_2O_4$, were investigated as the function of $Bi_2O_3$ and CaO contents. The power loss increased in proportion to the amount of $Bi_2O_3$ up to 0.3 wt% but it decreased over than 0.3 wt% addition. The highest permeability of 134 was obtained to the specimen added 1.0 wt% $Bi_2O_3$ since $Bi_2O_3$ contents were strongly dominant to grain growth and size than that of CaO. $Bi_2O_3$ liquid phase created during sintering process promoted sintering and grain growth so that grain size and permeability increased compared to that of the specimens which were sintered with free-additive and CaO. Also, lots of pores existed in the specimen which was added $Bi_2O_3$ wt% with the biggest grain size.

• Proceedings of the Korean Institute of Electrical and Electronic Material Engineers Conference
• /
• 2002.04a
• /
• pp.68-71
• /
• 2002

The electromagnetic properties and thermal behavior of ferrite cores used in the blocking filter for PLC were investigated as a function of additives. The highest density of 4.98 $g/cm^2$ and permeability of 8221 were obtained to the specimen added $MoO_3$ 400 ppm, $SiO_2$ 100 ppm and CaO 200 ppm since the microstructures were compacted through reduction of pores in the specimen. The permeability was increased up to 13094 at $110^{\circ}C$ with increasing temperature of specimen, however, it was decreased precipitously to under 100 over $110^{\circ}C$. The exothermic behavior was observed that the temperature of specimens became $102^{\circ}C$ at 1MHz. In the consequence, the ferrite core developed by this research will maintain the stable electromagnetic properties since the temperature of ferrite core rose to $93^{\circ}C$ in the range of 10kHz to 450kHz bandwidth qualified for PLC.

• Proceedings of the Korean Institute of Information and Commucation Sciences Conference
• /
• 2001.10a
• /
• pp.652-655
• /
• 2001

Power transformers are increasingly becoming more significant in the advancement of electronic equipment. A high-performance, low-cost core material is necessary in order th come up with power transformers in the smallest and lightest scale possible and with low power requirements. In this study, we added V$_2$O$_{5}$ and CaCo$_3$to Mn-Zn ferrite to produce a high-performance low-cost core material. The compositions used were MnO : ZnO : Fe$_2$O$_3$= 37 : 11 : 52 mol%. The materials were sintered at 125$0^{\circ}C$ for three hours. Initial permeability was measured at 0.1MHz. At 200mT, power loss was measured by changing the temperature at 25KHz, 50KHz, 100KHz. When we added 0.lwt% and 0.1%wt% of V$_2$O$_{5}$와 CaCo$_3$, respectively we obtained 405 405KW/㎥ at 200mT, 100KHz, 6$0^{\circ}C$. We tan reduce eddy current loss as a primary loss of high frequency by adding a small amount of V$_2$O$_{5}$와 CaCo$_3$. This reduces power loss in the power transformersormers

• Proceedings of the Korean Institute of Electrical and Electronic Material Engineers Conference
• /
• 2003.05a
• /
• pp.96-100
• /
• 2003

평면형 자심재료용으로 응용하기 위한 Mn-Zn 페라이트에서 저손실 조성의 전자기적 특성과 분위기 조건에 따른 특성변화를 관찰하였다. $Fe_{2}O_{3}$ : MnO : ZnO 의 물비가 53 : 36 : 11 일 때, 가장 우수한 특성을 나타내었으며, $SiO_{2}$와 CaO는 입계 저항층 형성을 통한 손실은 감소시키고, 이로 인해 성능지수는 증가하여 100kHz ~ 200kHz 범위에서 최대값을 나타내어 전자기적 효율이 극대화되었다. 산소분압의 제어는 승온과정부터 산소분압을 제어시켜주어야만 Zn-loss 현상의 증가와 $Fe^{2+}$이온 농도의 감소 및 $Fe^{2+}-Fe^{3+}$ 이온간의 호핑(hoping)현상 등에 의한 손실을 최소화 할 수 있으며, 높은 투자율을 얻을 수 있었다. 그리고 소결 또는 냉각 중 평형 산소분압이 유지되지 못하면 다량의 결함이 출현하게 되고, 특히 $600^{\circ}C$이하에서 스피넬 상의 분해-산화반응이 일어나면서 미세구조 상에 결함으로 남게 되어 전자기적 특성이 저하되었다.

• Electrical & Electronic Materials
• /
• v.3 no.3
• /
• pp.205-214
• /
• 1990

본 논문은 저손실 Mn-Zn-Fe 페라이트 제조에 관하여 연구한 것이다. Mn-Zn-Fe 페라이트는 16mol% Xno, 31mol% MnO 및 53mol% Fe$_{2}$O$_{3}$로 조성하였으며 0.1wt% $Na_{2}$SiO$_{3}$ 0.05wt% $Na_{2}$SiO$_{3}$ 0.1%wt% CaO 0.05% SiO$_{2}$ 및 0.05wt% SiO$_{2}$ 및 0.05wt% $Na_{2}$SiO$_{3}$ 0.1% CaO 0.05wt% $Al_{2}$O$_{3}$를 미량 첨가하였다. 그리고 하소와 분쇄과정을 거친 분말은 충진성을 높이기 위하여 과립화하였다. 소결 1250, 1300 및 1350.deg.C에서 이루어졌고, 평형 산소분압은 소오킹 시 PO$_{2}$는 6%부터 시작하여 점차 감소시켰으며 900.deg.C에서 순수한 질소 분위기로 냉각시켰다. 초투자율, 손실계수 및 고유저항 등의 자기적인 특성은 1300.deg.C에서 소결했을 경우의 것이 가장 우수하였다. 즉, 초투자율은 2*$10^{3}$~$10^{3}$의 높은 값을 얻을 수 있었으며 tan.delta./.mu.i값은 100KHz~ 400KHz의 고파수대에서 9*10$_{-6}$~21*10$_{-6}$이었으며 고유저항 값은 485~680 .OMEGA.-cm의 높은 값을 나타내어 중간주파수대의 자심재료에 적합한 페라이트임을 확인하였다.

• Proceedings of the Korean Institute of Electrical and Electronic Material Engineers Conference
• /
• 2004.05b
• /
• pp.19-22
• /
• 2004

The resonant planar transformer, which had power capacity of 300 W, input voltage of 220 V, output voltage of 15 V, and switching frequency of 500 kHz, was designed and manufactured by using the planar core with large effective area and the flat copper lead frames for miniaturization and high efficiency of the switching mode power supply (SMPS). As well as, a resonant converter equipped with the above mentioned planar transformer was manufactured and electromagnetic characteristics were investigated. The numerical value of turns for 1st and 2nd winding were 12 and 2 respectively. The self inductance of 1st winding was 33.2 ${\mu}H$, very low leakage inductance of 1.27 ${\mu}H$, and the coupling factor of 0.98 were obtained at switching frequency of 300 kHz. The high efficiency of 88.21 % for the SMPS equipped with planar transformer was obtained at power capacity of 300 W.

• Proceedings of the Korean Institute of Electrical and Electronic Material Engineers Conference
• /
• 2007.11a
• /
• pp.239-240
• /
• 2007

변압기 코어소재로 사용하는 방향성 규소강판의 가공 방법에 따른 물성을 조사하기 위하여 테이프 와인딩 코어 형태, 곡률반경을 20, 30, 40mm로 하여 토로이달 형태 변압기 시료의 B-H 자성 특성을 조사하였다. 곡률반경이 40mm, 높이는 10mm의 비율에서 보자력은 0.02Oe, 포화자속밀도는 0.98, 1.85T으로 보자력(Hc)은 낮고 포화자속일도(Bs)는 제일 큰 값을 나타내었고, 국내에서 생산되고 있는 방향성 규소강판의 자속밀도값 보다 약간 크게 나타났으며, 본 연구로부터 방향성 규소강판을 이용하여 권자심 코어을 제작할 때 고려해야하는 탄성변형에 대한 중요성과 코어 소재의 가공방법이 자기적 특성에 미치는 영향을 고찰하였다. 또한 토로이달 코어형태의 변압기를 설계 제작시 높이와 곡율반경, 가공 방법에 따라 용량, 효율 등이 다르므로 사전에 소재의 물성을 면밀히 검토 후에 전기기기에 적용해야함을 재확인하였다.