• Journal of the Korean Society for Precision Engineering
• /
• v.5 no.3
• /
• pp.71-80
• /
• 1988

This paper dealt with experimentally the effect of $N_2$ and $H_2$ gas mixtures ratio in the fatigue characteristics of SM45C on Ion-nitrided. The specimen were treated water cooling after Ion-nitriding at $500^{\circ}C$ and 5 torr. in 80% $N_2$and 50% $N_2$gas mixtures ratio in the atmosphere for 3 hrs. The hardness distribution and the depth of nitriding layer shows more increase in 80% $N_2$gas mixture ratio than 50% $N_2$. Ion-nitrided specim- en for 80% $N_2$gas mixture ratio show more increase infatigue strenght in the $>1.5{\times}10^5$ cycles region than 50% $N_2$. In the $<1.5{\times}10^5$cycles region, fatigue failure is due to cracking of the brittle nitrided case, and the propergation of the surface cracks into the core. But in the $>1.5{\times}10^5$cycles region, it is found that cracks propagate from the non-metallic inclusions in the subsurface.

• Transactions of the Korean Society of Automotive Engineers
• /
• v.18 no.6
• /
• pp.38-45
• /
• 2010

Welding structures are designed to endure its expected life. The most important factors are life. Especially on welded structure, fatigue strength is critical. So this study performed a research on Box and T shape weldment specimen to examine the influence of welding type. In this experiment, the results indicate Box shape was available in more than T shape. Fatigue tests were performed to evaluate the fatigue strength of the both as-welded and statically pre-loaded specimens by 3 point bending load. Fatigue life can be improved by using Ultrasonic Impact Treatment(UIT) effect. Ultrasonic Impact Treatment(UIT) is excellent for eliminating the tensile residual stresses and generating compressive residual stresses which elevate fatigue strength of welded structures. Also, this shows that welding part has better fatigue life and welding was performed well. In this study, to evaluate the Ultrasonic Impact Treatment(UIT) effect, for welding structure, the experiment was conducted at various levels of stress range between 100MPa and 500MPa. From the test results, it was indicated that fatigue performance was improving by Ultrasonic Impact Treatment(UIT)

• Journal of the Microelectronics and Packaging Society
• /
• v.24 no.4
• /
• pp.47-52
• /
• 2017

Recently, a great attention has been paid to the mechanical behavior of ITO (Indium Tin Oxide) film, which is widely used in current smart devices due to its excellent electrical properties and transparency. In this study, the reliability of ITO thin films on flexible substrates was investigated using bending test and bending fatigue test. According to the relative position of ITO and substrate, the experiment was conducted on both outer and inner bending conditions. Inner bending condition exhibited superior electrical stability compared to outer bending test. The electrical resistance during outer bending fatigue test significantly increased compared to that in the inner bending fatigue. The crack nucleation and propagation differs according to the stress state and they have a great influence on the electrical resistance. The crack morphologies were observed by scanning electron microscopy.

• Transactions of the Korean Society of Mechanical Engineers
• /
• v.9 no.2
• /
• pp.140-149
• /
• 1985

Fully reversed push-pull low cycle fatigue tests under strain control of trapezoid cyclic mode have been conducted in air at temperature of 550.deg. C and with frequency of 0.5 cpm on the domestic stainless steel STS 316 after solution treatment for 1 hour at 1100.deg. C. As an experimental equipment for high temperature fatigue tests, an electric servo-hydraulic fatigue machine(Instron model 1350) was used. This paper presents the effects of creep hold time and plastic strain range on push-pull high temperature low cycle fatigue life and fracture behavior. The fracture surfaces were observed by means of the scanning electron microscope. The results are as follows. (1) The fatigue life decreases with increase of the plastic strain range equal hold time and also decreases as the hold time is getting longer. (2) The frequency modified damage function can predict fatigue life by incorporating a variation of Coffin's frequency modified approach into damage function. (3) The ratios of creep damage and fatigue damage can be calculated by using he linear accumulation damage concept and the ratio of creep damage increases as the hold time is getting longer. (4) At the creep hold time of 5 minutes and the strain range of 2.0%, the fracture mode was intergranular fracture and striations were hardly observed. In this case, the intergranular cracking was originated in void type('.gamma.' type) cracking.

• Composites Research
• /
• v.32 no.1
• /
• pp.65-70
• /
• 2019

The aircraft composites wing parts are usually integrated with adhesive or fastener. These laminated composites have weak interlaminar strength, which can lead to delamination. In order to compensate the disadvantages of laminated composites, it is possible to improve the strength, durability, shock and fatigue resistance by reinforcing the fiber in the thickness direction. In addition, using a single structure near-net-shape saves the manufacturing time and the number of fasteners, thus can reduce the overall cost of the composite parts. In this study, compression test, tensile test and open-hole tensile test are carried out for three structural architecture of 3D (three-dimensional) textile preforms: orthogonal(ORT), layer-to-layer(LTL) and through-the-thickness(TTT) patterns. Among these, the orthogonal textile composite shows the highest Young's modulus and strength in tensile and compression. The notch sensitivity of the orthogonal textile composite was the smallest as compared with UD (unidirectional) and 2D (two-dimensional) fabric laminates.

• Electrical & Electronic Materials
• /
• v.10 no.4
• /
• pp.327-333
• /
• 1997

Experiments on mechanical fatigue were conducted using the specimens which were cut from hydrogen cooled generator(rated 22kV and 50OMW) stator windings. We have investigated the aged mechanism of mica/epoxy insulation systems under air or hydrogen by both the tensile and compressive loadings. The fracture of generator stator windings is generally affected by mechanical stress. Thus, the tensile strength test were conducted. In this case, the maximum strength and strain are quite different between sound and aged specimens. It is observed that low bonded interface parts of tapes generally have lower strength than those of normal tapes which causes stress. In order to estimate the effects of cyclic load by the electromagnetic forces while the generator starts/stops, the mechanical fatigue test was also conducted. It is confirmed that the equation of expected life depends on stress amplitude and number of cycles. Though the stress amplitude and number of cycles are very tiny, the tensile fatigue of aged specimens under hydrogen atmosphere is bigger than those under air. In the case of hydrogen atmosphere, the tensile stress gives bigger effect than the compressive one.

• Transactions of the Korean Society of Mechanical Engineers A
• /
• v.35 no.8
• /
• pp.913-920
• /
• 2011

We describe the evaluation of the fatigue life and strength of a lightweight railway bogie frame made of glass fiber/epoxy 4-harness satin-woven composites. To obtain the S-N curve for the evaluation of the fatigue characteristics of the composite bogie frame, we performed a tension-compression fatigue test for composite specimens with different stacking sequences of the warp direction, fill direction, and $0^{\circ}/90^^{\circ}$ direction. We used a stress ratio (R) of -1, a frequency of 5 Hz, and an endurance limit of $10^7$. The fatigue strength of the composite bogie frame was evaluated by a Goodman diagram according to JIS E 4207. The results show that the fatigue life and strength of the lightweight composite bogie satisfy the requirements of JIS E 4207. Given its weight, its performance was better than that of a conventional metal bogie frame based on an SM490A steel material.

• Bulletin of the Society of Naval Architects of Korea
• /
• v.27 no.2
• /
• pp.47-54
• /
• 1990

In this study, the effects of gas ratio($N_2:H_2$) and treatment time on the fatigue fracture behavior, fatigue crack growth behavior and corrosion fatigue fracture behavior for the ion-nitrided SM45C steel were investigated. The results show that the fatigue limit and corrosion fatigue strength increased in porportion to $N_2$ gas and treatment time for all kinds of specimen, used in the experiment. Compare to the non-nitrided specimen, the fatigue limit and the corrosion fatigue strength increased about $24{\sim}29%$ at $10^7$ cycles in air and $32{\sim}48%$ at $10^6$ cycles in 3% NaCl aqueous solution, respectively. Similar results were derived with SM45C steel under Compression-Tension $24{\sim}29%$ at $10^6$ cycles in air and $32{\sim}48%$ either in 3% NaCl aqueous solution or in tap water, respectively. Ion-nitrided SM45C steel showed a slow fatigue crack growth rate at relatively low range of ${\Delta}K$ compared to the non-nitrided specimen. To the contrary, its rate increase at higher range of ${\Delta}K$.

• Proceedings of the Korean Society for Technology of Plasticity Conference
• /
• 2009.10a
• /
• pp.132-136
• /
• 2009

The importance and interests for saving of energy and cost in industry has been steadily grown up. Therefore, process optimization to reduce the processing step and energy is one of the most important things. The micro-alloyed steel of which post-heat-treatment is not necessary, has attractive points for high strength materials. However, for the application of non-heat-treated steel to structural parts, it is necessary to confirm the reliability of mechanical properties. In order to estimate mechanical properties. The microstructure, hardness, tensile strength, compressive strength and tensile fatigue strength of micro-alloyed steel having 900MPa tensile strength has been investigated.

• Proceedings of the Korean Society For Composite Materials Conference
• /
• 2001.05a
• /
• pp.60-64
• /
• 2001

In this paper, the tension-compression fatigue test method and the fatigue life characteristics of carbon fabric/epoxy laminate coupon are presented. To avoid the buckling during the compression, a proper design for the test coupons is essential. The critical buckling loads for the coupons are calculated by assuming the coupons as columns under two types of fixed conditions. The first is that both ends of each coupon are perfectly clamped, the second is that both ends of each coupon are simply supported. The strain-load curves are obtained by compressing the representative coupons, on each surface of which a strain gage is attached. The buckling loads obtained from the tests are all between the two calculated critical buckling loads. All the coupons are broken by the compression during the fatigue tests. It is estimated to be the reason that the fatigue load causes delamination before the eventual failure of each coupon, and sequentially the micro-buckling in the delaminated region drives each coupon into fatigue failure during the compression. The S-N curve, the fatigue life characteristics of carbon fabric/epoxy is obtained.