• Transactions of the Korean Society of Mechanical Engineers A
• /
• v.28 no.4
• /
• pp.333-342
• /
• 2004

Tensile and low cycle fatigue (LCF) tests on prior cold worked 316L stainless steel were carried out at various temperatures from room temperature to 650$^{\circ}C$. At all test temperatures, cold worked material showed the tendency of higher strength and lower ductility compared with those of solution treated material. The embrittlement of material occurred in the temperature region from 300$^{\circ}C$ to 600$^{\circ}C$ due to dynamic strain aging. Following initial cyclic hardening for a few cycles, cycling softening was observed to dominate until failure occurred during LCF deformation, and the cyclic softening behavior strongly depended on temperature and strain amplitude. Non-Masing behavior was observed at all test temperatures and hysteresis energy curve method was employed to describe the stress-strain hysteresis loops at half$.$life. The prediction shows a good agreement with the experimental results.

• Journal of Advanced Marine Engineering and Technology
• /
• v.18 no.3
• /
• pp.52-62
• /
• 1994

기계나 구조물 파괴의 대부분은 노치부를 기점으로 하여 발생하기 때문에 첨단복합재료를 노지부 재로서 안전하면서도 경제적으로 사용하기 위해서는 각종 조건하에 있어서 강도특성을 명확히 하는 것은 대단히 중요하다. 본 연구에서는 노치를 갖는 복합재료를 이용하여 각종조건하에서 강도특성평가실험을 행하였으 며, 얻어진 결과를 종합하면 다음과 같다. (1) 첨단복합재료 노치재는 試驗片의 幾可學的 形狀과는 관계없이 노치반경 p만에 의해 결정되는 최대탄성응력 $\sigma_{max}$일정의 條件下에서 破t짧된다. (2) 破斷時 최소단면에서의 공칭응력 $\sigma_{c}$와 응력집중계수 $K_{t}$와의 관계에 있어서,$\sigma_{c}$의 값이 $K_{t}$의 증대와 더불어 떨어지고 있는 부분과, $K_{t}$와 관계없이 거의 일정하게 되고 있는 부분으로 나누어지는 現象은 노치재의 回轉굽힘 또는 인장압축파열에서 보여지는 현상과 外觀上 對應하고 있다. 즉, 정적파괴와 피로파괴는 파괴의 양상이 비슷하다 (3) PEN수지단체의 경우, 피로균열발생은 점발생적 피로균열이 최대탄성응력에 의해 지배되며, 노치에 만감하며,균열전파수명은전수명에 비해 상당히 짧다. (4) 단탄소섬유강화복합재료의 경우, 피로균열은 섬유端에 응력이 집중하기 때문에 일반적으로 섬유端에서 아주 빠른 시기에 발생하지만, 섬유가 피로균열진전에 대해 방해물로 작용하기때문에 아주 천천히 전파한다. (5) 短탄소鐵維는 피로균열발생에 대해서는 負의 강화작용 전수명의 극히 초기단계에 피로균열 발생을, 피로균열전파에 대해서는 正의 강화작용을 한다. (6) 단탄소섬유를 PEN에 강화함으로 인해 정적강도 보다 피로강도에 더 큰 강화효과를 초래했으며, 선형노치역학의 개녀은 첨단 복합재료의 강도평가에 대단히 유효했다.

• Journal of Korean Society of Steel Construction
• /
• v.21 no.1
• /
• pp.55-62
• /
• 2009

Blast cleaning has been applied in steel bridges for cleaning forged surface and increasing adhesive property of applied coating systems. Blasting is the operation of cleaning or preparing a surface by forcible propelling a stream of abrasive metals against it. Blast cleaning may improve surface geometry and induce compressive residual stress, and eventually may increase fatigue life of weld joints. In this paper, fatigue tests were carried out on three types of non-load-carrying fillet welded cruciform joints, as-welded joints, blast-treated joints, and stress-relieved joints after blasting, in order to investigate effect of blast cleaning on fatigue behavior of the weld joints. By Blast cleaning, the weld toe radius was increased by 29% and compressive residual stress was induced near weld toes. Blast cleaning increased fatigue life and fatigue endurance limit of the weld joints. When the applied stress ranges decreased, the increment in fatigue life became larger. About a 150% increase in fatigue limit could be realized by using blast cleaning.

• Transactions of the Korean Society of Mechanical Engineers A
• /
• v.35 no.10
• /
• pp.1243-1248
• /
• 2011

Internal defects are a major concern in the casting process because they have a significant influence on the strength and fatigue life of casting products. In general, they cause stress concentration and can be a starting point of cracks. Therefore, it is important to understand the effects of internal defects on mechanical properties such as fatigue life. In this study, fatigue experiments on tensile specimens with internal defects were performed. The internal defects in the casting product were scanned by an industrial CT scanner, and its shape was simplified by ellipsoidal primitives for the structural and fatigue analysis. The analysis results were compared with experimental results for casting products with internal defects. It was demonstrated that it is possible to consider internal defects of casting products in stress and fatigue analysis. The proposed method provides a tool for the prediction of the fatigue life of casting products and the investigation of the effects of internal defects on mechanical performance.

• Journal of Korean Society of Steel Construction
• /
• v.9 no.3 s.32
• /
• pp.363-375
• /
• 1997

This study encompasses the performance of static and fatigue test for the 8 large scale test specimens to clarify the fatigue behavior of coped stringer and the effect of the repair and strengthening on the damaged stringer of the floor system in steel railway bridges. For the purpose of the research, the actual stress wave for the existing bridge was measured, the basic stress range frequency histogram was made and the equivalent stress range was calculated. Using the result from the equivalent stress range made by adjusting the stress range, the static and fatigue test was carried out by identifying the previous rehabilitation and after. As the result of the static tests, it was revealed that the level of local stress under the S1 specimen test of the real equivalent stress range was similar to tensile strength of the test material, and it was consistent with the requirement of the initiation condition of the fatigue crack. Through the various rehabilitation methods to the damaged specimens, the effects of the repair and reinforcement were analyzed. According to the results of the repair of effect, bolting the high tension bolt over the stop hole was confirmed to be more adequate method than drilling only stop hole to delay the fatigue crack growth. Futhermore, in case of the stringer subjected by bending moment, the reinforcement over the upper flange side was determined to be a useful strengthening method, and the reinforcement to the web of the stringer was not appropriate to accomodate as a adequate strengthening method. Also it was confirmed that the category of the fatigue design for the coped stringer met with the category E specified on the fatigue design criteria of the Highway Standard Specification in Korea.

• KSCE Journal of Civil and Environmental Engineering Research
• /
• v.33 no.3
• /
• pp.1153-1163
• /
• 2013

Bonded concrete overlay is a favorable maintenance method since the material properties are similar to existing concrete pavements. In addition, bonded concrete overlay has advantage of structural performance based on being bonded together, both for the overlay layer and the existing pavement which perform as one monolithic layer. Therefore, it is important to have a suitable bond strength criteria for long term performance of bonded concrete overlay. This study aimed to investigate the affecting of bond strength on various bond characteristics, and to compare the bond strength between direct tensile test and indirect tensile test due to various conditions such as overlay materials, compressive and flexure strength of existing pavement, and deterioration status of existing pavement. As a result of this study, bond strength occurred by both of direct and indirect tensile test due to monotonic load is highly correlated such as coefficient of determination of 0.75 and P-value of 0.002. However, bond strength by indirect tensile test was relatively higher than bond strength by direct tensile test. It was known that correlation between direct and indirect tensile test was possible to use the characteristics analysis of bond fatigue behavior based on bond strength due to cyclic load which can simulate real field behavior of bonded concrete overlay.

• Proceedings of the Korean Society for Technology of Plasticity Conference
• /
• 2007.10a
• /
• pp.334-337
• /
• 2007

Austenitic stainless steel is used as high temperature components such as gas turbine blade and disk because of its good thermal resistance. In the present investigation, tensile and low cycle fatigue(LCF) behavior of stainless steel for turbine disks was studied at wide temperature range $20^{\circ}C\;{\sim}\;750^{\circ}C$. In the tensile tests, it was shown that elastic modulus, yield strength, ultimate tensile strength decreased when temperature increased. The effect on fatigue failure of the parameters such as plastic strain amplitude, stress amplitude and plastic strain energy density was also investigated. Coffin-Manson and Morrow models were used to adjust experimental data and predict the fatigue life behavior at different mean strain values during cyclic loading of high temperature components.

• 한국기계연구소 소보
• /
• s.18
• /
• pp.169-175
• /
• 1988

The influence of mean strain on the behavior of early stage stress amplitude was investigated quantitatively in low cycle fatigue. It was obtained that the exponent of cyclic strain(n') and the coefficient of cyclic strain(C') decreased with increasing cycle numbers in compressive mean strain level. But it was the opposite in 0% mean strain and tensile mean strain level. And the cyclic yield strength ($\delta_(yc)$) was constant irrespective of mean strain or cyclic strain

• Proceedings of the Korea Concrete Institute Conference
• /
• 2008.04a
• /
• pp.333-336
• /
• 2008

CFRP tendons have been attempted in concrete structures as a substitute for steel tendons considering their many advantages such as the corrosion-resistance, light weight etc. However, the elastic behavior up to failure is likely to result in ductility problems. To overcome such problems, prestress concrete beams with partially bonded tendons have been developed and suggested. In this new system, the un-bonded part near the mid-span contributes to the improvement of ductility. And the bonded parts at both ends play a role as a safe anchorage. According to the previous research on the static behavior, the suggested method has demonstrated enough ductility and strength. However it is essential to verify the long-term safety for repetitive fatigue loads under service states. For this purpose, flexural fatigue loading tests were carried out in this research. This paper includes an experimental investigation on the static load-carrying capacities of the beams with or without fatigue tests. The results showed that the beams prestressed with partially bonded CFRP tendons possessed good fatigue capacity under the constant cyclic loads.

• Bulletin of the Society of Naval Architects of Korea
• /
• v.27 no.2
• /
• pp.47-54
• /
• 1990

In this study, the effects of gas ratio($N_2:H_2$) and treatment time on the fatigue fracture behavior, fatigue crack growth behavior and corrosion fatigue fracture behavior for the ion-nitrided SM45C steel were investigated. The results show that the fatigue limit and corrosion fatigue strength increased in porportion to $N_2$ gas and treatment time for all kinds of specimen, used in the experiment. Compare to the non-nitrided specimen, the fatigue limit and the corrosion fatigue strength increased about $24{\sim}29%$ at $10^7$ cycles in air and $32{\sim}48%$ at $10^6$ cycles in 3% NaCl aqueous solution, respectively. Similar results were derived with SM45C steel under Compression-Tension $24{\sim}29%$ at $10^6$ cycles in air and $32{\sim}48%$ either in 3% NaCl aqueous solution or in tap water, respectively. Ion-nitrided SM45C steel showed a slow fatigue crack growth rate at relatively low range of ${\Delta}K$ compared to the non-nitrided specimen. To the contrary, its rate increase at higher range of ${\Delta}K$.