• Transactions of the Korean Society of Mechanical Engineers A
• /
• v.24 no.7 s.178
• /
• pp.1771-1778
• /
• 2000

The purpose of this study is to investigate the thermal embrittlement and the mechanical properties of 2.25Cr-1Mo steel aged at high temperature for the extended periods. Original, aged artificiall y and used material were tested to obtain the tensile strength, hardness and impact absorbed energy. Tensile strength, hardness and impact absorbed energy decreased with the increasing aging time. The carbide morphology with the thermal embrittlement was found to contribute to the mechanical property change by X-Ray diffraction method.

• Proceedings of the Korean Society of Precision Engineering Conference
• /
• 2004.05a
• /
• pp.116-116
• /
• 2004

편마비 환자의 보행운동 개선을 위한 보조기구로 족부보장구(Ankle Foot Orthosis, A.F.O.)가 활용되고 있다 족부보장구는 Fig. 1에 제시한 바와 같이 보행특성상 무수히 반복되는 충격과 굽힘하중을 받는다. 따라서 족부보장구용 재료는 피로특성이 우수한 탄소섬유 강화재(Carbon Fiber Reinforced Plastic, 이하 CFRP)를 주로 사용한다. 그러나 CFRP의 상용재인 프리프레그(prepreg)는 강한 이방성의 단방향 섬유이므로 섬유방향과 하중작용방향의 관계에 매우 민감하다.(중략)

• Proceedings of the Korean Nuclear Society Conference
• /
• 1995.05a
• /
• pp.1014-1020
• /
• 1995

고온구조물은 고온에서의 운전상태에 따라 복잡한 하중이력을 경험하게 됨으로써 상온에서 발생하는 손상 기구와는 달리 온도 의존성을 가질 뿐만 아니라, 상온에서 볼 수 없는 크립-피로의 상호작용에 의한 손상현상이 나타나게 된다. 따라서 고온 구조물의 건전성 평가를 위한 비탄성 해석을 신뢰성 있게 수행하기 위해서는 구조물의 비선형 거동을 비교적 정확히 예측할 수 있는 통합 구성방정식의 개발 및 적용과 온도에 따른 재료의 물성치 확보가 필수적이다. 본 연구에서는 통합 점소성 모델인 수정된 Chaboche 모델에 대해서 내연적 시간 적분법을 적용하여 ABAQUS의 UMAT으로 구현하였고, 개발된 프로그램을 이용하여 INCONEL 718을 사용한 단순 인장해석, 반복 소성 특성해석 및 크립 해석을 수행하여 프로그램의 신뢰성을 평가하였다. 또한 원공이 있는 평판에 대한 예제해석을 수행함으로써 개발된 프로그램이 고온구조물의 건전성 평가를 위한 비탄성 해석에 적절하게 적용될 수 있음을 확인하였다.

• Journal of Welding and Joining
• /
• v.31 no.2
• /
• pp.43-48
• /
• 2013

This paper Investigated the characteristics of residual stress in weld is composed of typical specimens, are investigated by using three dimensional thermal elasto-plastic FEM analysis. Numerically calculated residual stresses in the gas welds were then compared with experimental results obtained by the hole-drilling method. Using the stress amplitude (${\sigma}a$)R at the hot spot point of gas weld, the relations obtained as the fatigue test results for typical specimens having various dimensions and shapes were systematically rearranged to obtain the (${\sigma}a$)R-Nf relationship. It was found that more systematic and accurate evaluation of the fatigue strength of plug- and ring-type gas-welded joints can be achieved by using (${\sigma}a$)R.

• Journal of Ocean Engineering and Technology
• /
• v.13 no.2 s.32
• /
• pp.83-89
• /
• 1999

In this paper an experimental study on the development of the shielded metal are welding(SMAW) optimization technique for the dissimilar materials SS41 and STS304 of Auto-Lifting Magnet core plate was carried out. It was confirmed that the optimum welding heat input range was 37.5 to 45 kj/cm by considering on the strength and fatigue life of the welded joints more than 100% joint efficiency. And the quantitative relationship empirical wquation between the strength toughness adn fatigue life and the weld heat input was obtained.

• Proceedings of the KSME Conference
• /
• 2004.04a
• /
• pp.302-307
• /
• 2004

This paper reviewed characteristics of fatigue crack behavior observed by changing various shapes of initial crack and magnitudes of loading in compact tension shear(CTS) specimen subjected to shear loading. In the high-loading condition, fatigue crack under shear loading propagated branching from the pre-crack tip. Meanwhile, the secondary fatigue crack in the low-loading condition which was created in the notch root due to friction on the pre-crack face grew to a main crack. Influenced by the mode II loading condition, fatigue crack propagation retardation appeared in the initial propagation region due to the reduction of crack driving force and friction on crack face. In both cases, however, fatigue cracks grew in tensile mode type. Propagation path of fatigue crack under the shear loading was 70 degree angle from the initial crack regardless of its shape and load magnitude.

• Journal of Industrial Technology
• /
• v.11
• /
• pp.135-143
• /
• 1991

The fatigue tension tests were performed by use of the specimens without and with a hole, 1/4 crack and 1/2 crack, made of SS41 and S45C steel round bars. Followings were these results. It was shown that in the base metal and the specimen with a hole the fatigue strength of the high strength steel bars was lower than that of the low strength steel bars under the low stress range. It was shown that the fatigue strength of the specimen with a hole was nearly same as that of the base metal, but the fatigue strength of the specimens with the crack was much lower than that of the base metal. It was shown that the fatigue strength of the specimens with the crack was much lower than that of the other specimens under the high stress range.

• Proceedings of the Korean Society of Propulsion Engineers Conference
• /
• 1998.04a
• /
• pp.8-8
• /
• 1998

Alloy 718은 Fe을 다량 함유하고 있어 가격이 저렴하고 엔진 작동조건에서 내열강도, 내환경성 등이 우수하여, 터빈디스크, 터빈샤프트, 터빈실, 압축기 블레이드 등에 다양하게 이용되고 있다. 이 합금은 고온에서 반복응력을 받는 부위에 대부분 사용되기 때문에 고온인장, 저주기 피로측정 등의 기계적 성질이 동시에 요구되며, 이들 특성은 단조공정변수 및 후열처리 등에 의해 크게 바뀌게 된다. 본 연구에서는 Alloy 718을 이용하여 가스터빈 디스크 제조할 경우 공정변수로서 단조온도, 변형속도 등에 의한 조직이 변화와 이에 따른 기계적 특성의 변화를 다루었다. 특히 이 합금에서 결정립크기는 고온 기계적 성질을 결정하는 중요한 변수로 작용하는데, 2단계 단조공정시 재결정에 의한 조직의 변화를 전산모사 방법에 의해 해석하고 그 결과를 조직 관찰을 통해 검증하였다.

• Journal of the korean Society of Automotive Engineers
• /
• v.12 no.2
• /
• pp.43-50
• /
• 1990

The fatigue growth behavior of surface cracks cannot be adequately predicted solely by stress intensity factor analysis. This is caused by different plastic deformation due to variations in the stress field triaxiality along the crack tip. Therefore, a new model which accounts for the crack closure phenomenon is proposed in this paper to predict the fatigue crack growth patterns for surface cracks. Fatigue tests were performed to develop the new model for the prediction and to assess the accuracy of the analysis. The predicted crack growth behavior for PMMA and Aluminum alloy 7075-T6 materials agreed well with the experimental data.

• Proceedings of the Korean Society of Propulsion Engineers Conference
• /
• 1999.04a
• /
• pp.30-30
• /
• 1999

샌드위치 복합재는 단일 부재의 금속재나 복합재에 비해 높은 비강성과 비강도를 얻을 수 있을 뿐 아니라 면재와 코아를 적절하게 조합하면 우수한 피로특성, 단열성, 흡음성 등을 얻을 수 있기 때문에 항공기, 철도차량, 선박, 냉동컨테이너, 건축재 등에 널리 활용되고 있다. 대부분의 샌드위치 복합재는 면재와 코아를 일차 또는 이차 선착을 통해 제작하기 때문에 운용 중 샌드위치 복합재에 가해질 수 있는 충격하중 등으로 인해 면재와 코아 사이의 층간분리, 면재의 인장파괴, 코아의 압축파괴, 코아의 진단파괴 등과 같은 손상이 생길 우려가 있다. 최근에는 샌드위치 복합재가 갖는 이러한 문제점들을 해결하기 위한 방편으로 코아의 양면에 부착된 면재들을 코아의 두께방향으로 스티칭함으로써 서로 일체형으로 결합시킨 형태인 스티칭된 샌드위치 복합재의 개발이 시도되고 있다.