• Korean Journal of Fisheries and Aquatic Sciences
• /
• v.32 no.4
• /
• pp.395-398
• /
• 1999

Chitin was isolated from red snow crab (Chinonecetes japonicus) and deacetylated by boiling alkaline solution to produce chitosan. The physical properties of chitosan solution and its film properties was examined, As the molecular weights of chitosan was increased from 297Kpa to 319Kpa, the tensile strength, degree of elongation and water permeability of chitosan film were increased. As the degree of deacetylation of chitosan was increased, the tensile strength, the degree of elongation and water permeability of chitosan film were increased. As the concentration of chitosan solution was increased, the degree of elongation and water permeability of film were increased, whereas the tensile strength of film was decreased, As the pH of chitosan solution was increased, the tensile strength and water permeability of film were decreased, whereas the degree of elongation of film was increased.

• Proceedings of the Korean Society for Agricultural Machinery Conference
• /
• 2017.04a
• /
• pp.130-130
• /
• 2017

비닐하우스의 골조를 구성하는 파이프는 부식을 방지할 목적으로 아연도강관을 사용한다. 그러나 시간이 지남에 따라 아연도금량 감소와 여러 외부 환경인자 등에 의하여 부식이나 침식이 진행되어, 외관상 녹이 생기고 강도와 연신율 등이 감소하게 된다. 이는 비닐하우스 전체의 내구성을 저하시키는 요인으로 작용하게 되는데, 이를 평가하기 위한 방법이나 기준은 미비한 실정이다. 이에 본 연구에서는 농업시설의 내구성을 평가하기 위한 방법의 하나로 각기 다른 경과년수를 갖는 비닐하우스로부터 채취한 서까래 파이프의 인장 시험을 실시하였다. 인장 시험에 사용된 서까래 파이프는 (구)시설원예시험장에 설치되어 있는 비닐하우스에서 경과년별로 채취하였으며, 지중매설부와 지상노출부로 구분하여 시편을 제작하였다. 인장 실험 결과 서까래 파이프의 경과년이 오래될수록 시편의 인장 강도는 작아지는 경향을 보이고 있으나, 파단연신율은 경과년과 연관성을 찾아보기 어려운 것으로 나타났다. 그리고 동일한 경과년을 갖는 서까래 파이프 시편에서 지중매설부의 인장 강도와 파단연신율이 지상노출부에 비해 대체로 작게 측정되었으며, 경과년이 증가할수록 인장 강도의 감소폭이 커지는 경향을 보이는 것으로 나타났다.

• Proceedings of the Korean Nuclear Society Conference
• /
• 1995.05a
• /
• pp.729-734
• /
• 1995

원자력용 316L강에 질소를 첨가한 경우의 고온 인장성질을 조사하였다. 온도가 증가하면 인장강도는 감소하다가 온도범위가 30$0^{\circ}C$~50$0^{\circ}C$에서는 일정한 값을 나타낸 후 급격한 감소를 나타내었고 연신율은 감소하다가 40$0^{\circ}C$에서 최소값을 나타낸 후 다시 증가하는 경향을 나타내었다. 질소를 첨가하면 인장강도증가와 함께 연신율도 증가하였다. 동적변형시효 온도구간에서 변형속도변화에 따른 인장강도 및 연신율의 변화는 매우 작다. 동적변형시효를 위한 활성화에너지를 구해본 결과 동적변형시효를 일으키는 원소는 Cr이다. 질소를 첨가하면 동적변형시효가 발생되는 온도가 고온 쪽으로 이동되었는데 이것은 질소가 Cr과의 상호작용에 의해 Cr의 확산속도를 낮추기 때문이다. 가공경화지수는 동적변형시효와 회복의 영향으로 40$0^{\circ}C$에서 최대값을 나타내었으며 이 온도는 연신율이 최소값을 나타내는 온도와 인장강도가 일정하게되는 온도와 일치하므로 강도강화기구는 동적변형시효로 판명되었다.

• Journal of Bio-Environment Control
• /
• v.5 no.1
• /
• pp.34-42
• /
• 1996

This study was conducted to investigate the physical and optical properties of polypropylene and polyester thermal curtains, in which tensile strength, heat reservance and light transmission of two different materials were measured. The results from this study are as follows. 1. The tensile weight of different materials were ranged from 3.4kg to 13.4kg, according to the thickness of materials, but that no difference in the tensile strength was appeared between the two materials. The Elongation of polypropylene materials and the tensile weight and strength of polyester materials were greater than any other materials. 2. The light transmittances of two materials were ranged from 50.3% to 81.7 %, light transmittances in polypropylene were higher by 20-30%,than those in polyester. 3. The heat reservances of two materials were ranged from 18.2% to 41.2%, in which polypropylene showed better performance than polyester. 4. From the results of the test, the polypropylene thermal material was better in elongation, heat reservances and light transmittances, but polyester thermal material was better in tensile strength and light isolation than the other material.

• Journal of the Korea institute for structural maintenance and inspection
• /
• v.21 no.6
• /
• pp.178-184
• /
• 2017

This study was aimed to investigate the tensile behaviors of PE(Polyethylene) fiber-reinforced highly ductile cementitious composites with different combinations of micro silica sand and normal sand(river sand) with maximum particle size of 4.75 mm. Flow test result indicated the increase of flowability with higher replacement ratio of river sand. There was no noticeable difference in the mean compressive strength with different replacement ratio of river sand, but the variation in the compressive strength increased as higher amount of river sand was adopted for the replacement. The difference in the uniaxial tensile strength was negligible, but the tensile strain capacity was significantly influenced by the replacement ratio of river sand. It is thought that increased density of multiple cracks induced improved tensile strain capacity when higher percentage of river sand was adopted for fine aggregate. The deviation in the strain capacity increased as the replacement ratio of river sand was higher, as in the compressive strength. This study presented the feasibility of using normal sand instead of micro silica sand for highly ductile cementitious composites with equivalent or better uniaxial tensile performance, even though it might increase the deviation in the performance.

• Proceedings of the Materials Research Society of Korea Conference
• /
• 2003.11a
• /
• pp.213-213
• /
• 2003

고온 및 고압의 가혹한 방사선 분위기에서 사용되는 핵연료 피복관은 중성자 조사 및 수소화합물의 생성 등으로 인하여 기계적 성질이 저하된다. 따라서 조사된 핵연료 피복관의 손상기준 확립과 안전성 해석을 위해서는 연성 및 강도 등 기계적 특성을 정확히 이해하여야 할 필요가 있다. 핵연료 피복관의 종 및 횡 방향 인장특성 평가를 위하여 개발된 기존의 다양한 시험법들을 비교하고, 핫셀시험에 적합한 인장시험법을 개발하였다. 피복관의 종방향 인장시편은 튜브시편 또는 게이지부 내에서 균일한 변형률 분포를 얻도록 설계된 도그본 튜브시편(그림 1)을 사용한다. 피복관의 횡방향 인장시험에 사용되는 링시편(그림 2)은 게이지부 내에서 균일한 단축 원환변형율 분포 또는 평면변형율 조건을 나타내도록 설계한다. 연소 또는 조사된 피복관으로부터 시편을 제작하기 위해서는 핫셀 내에서 작업 이 가능한 방전가공기(그림 3)를 사용한다. 피복관의 종방향 인장시험용그립(grip)은 핀-부하형이며, 횡방향 인장시험의 경우는 시험 동안 시편의 곡률이 일정하게 유지 되도록 그립의 형상 및 치수를 결정한다(그림 4). 피복관의 종 및 횡방향 강도와 변형 등 기계적 특성을 평가하기 위한 응력-변형율 곡선은 시험기의 복합 강성(K)을 고려하여 결정한다. 이상과 같이 검토된 인장시험법은 피복관의 안전성 해석(safety analysis)과 관련 규정(regulatory)에서 사용되는 피복관 손상기준(fuel damage criteria)의 개선에 필수적인 자료를 제공한다.

• Journal of Korean Association for Spatial Structures
• /
• v.10 no.1
• /
• pp.51-58
• /
• 2010

ETFE is the abbreviation of Ethylen Tetra Fluoro Etylene, a sort of colorless and transparent granules. The advantage ETFE film has daylight transmission and chemical the resistance and The thickness of ETFE film is used to from $50{\mu}m$ to $300{\mu}m$ and tensile strength of ETFE film changes from 40MPa to 60MPa and the tensile strain at break can get to about 300-400%. In this paper, ETFE film carried out the tensile proprieties, such as the tensile strain at break, the tensile strength are examined.

• Proceedings of the Korean Society of Precision Engineering Conference
• /
• 2004.05a
• /
• pp.88-88
• /
• 2004

내압을 받는 압력관의 파괴는 원주방향의 응력이 주된 요인이므로, 압력관의 안전성을 평가를 위해서는 원주방향의 인장특성을 아는 것이 필요하다. 소형 압력관의 인장특성을 평가할 때, 정확한 원주방향의 인장특성을 알기 위해서는 관으로 가공된 후의 재료로 시험해야 하지만, 부피의 제약으로 인하여 원주방향으로의 표준 인장시험편을 제작하지 못하므로 가공하기 전의 재료의 물성치를 사용하고 있다. 이를 개선하고자 원주방향의 인장특성을 평가하기 위한 방법의 하나로 링 시험법(ring test)이 있다.(중략)

• Proceedings of the Materials Research Society of Korea Conference
• /
• 2010.05a
• /
• pp.39.1-39.1
• /
• 2010

겨울철 혹한지방에서의 차량운행 또는 여름철 혹서지방에서의 장시간 차량 운행시 차체를 구성하고 있는 강판에는 약 $-50^{\circ}C{\sim}150^{\circ}C$의 온도환경에 처하게 된다. 따라서 이러한 저온 고온 환경하에서 차체 충돌상품성 예측 및 충돌안전 설계를 위해 온도에 따른 차체 강판의 기계적 물성평가가 요구된다. 이를 위해 본 연구에서는 자동차용 충돌부재에 주로 쓰이는 HS440MPa, HS590MPa급 냉연 고장력 강판에 대해 $-60^{\circ}C{\sim}200^{\circ}C$의 온도범위로 저온 고온 인장시험을 수행 하였다. 각각의 인장시험 결과로부터 온도 별 항복강도, 인장강도, 연신율, 가공경화지수 등 기계적 물성 변화를 평가하였다. 저온 고온 인장시험은 ZWICK Z250 만능재료시험기를 사용하였고 KS5호 규격의 인장시편을 사용하였으며, 시편에 충분한 온도를 가하기 위하여 목표온도 도달 후 20분간 유지한 뒤 인장시험을 수행하였다. 인장시험결과 HS440MPa, HS590MPa급 두 강종 모두 온도가 낮아질수록 강도 및 연신율 등이 증가하였고, 온도가 증가할수록 강도 및 연신율 등 기계적 물성이 저하 되었다. 즉, 우리가 주로 평가해왔던 상온($25^{\circ}C$)에 비해 저온 고온 환경하에서는 강판의 기계적 물성 변화가 큰 것을 알 수 있다. 따라서 혹한 또는 혹서 지방 등 온도차이가 큰 운행환경하에서의 차체 강도 및 충돌안전성 확보를 위해 온도에 따른 강판의 정확한 물성평가가 필요하고 차체 설계시 온도에 따른 강도변화를 충분히 고려하여야 한다.

• Magazine of the Korea Concrete Institute
• /
• v.5 no.3
• /
• pp.187-194
• /
• 1993

본 논문에서는 유리섬유의 적층수, 유리섬유의 배향각도에 대한 유리섬유 강화 플라스틱(Glass Fiber Reinforced Plastics ; GFRP)의 인장거동 변화를 고찰하고, 이들의 상관관계를 규명하기 위하여 일련의 GFRP 시험체에 대하여 인장실험을 수행하였다. 시험체는 폭12.5mm, 길이 60mm크기로 일정하게 제작하였으며, 시험체에 대하여 인장실험을 수행하였다. 시험체 제작시 유리섬유로 적층수는 14, 22, 30층, 유리섬유의 배향각도는 0$^{\circ}$, 30$^{\circ}$, 45$^{\circ}$로 하였다. 인장실험시 각 시험체의 파괴양상, 극한하중 및 하중변화에 대한 인장변형율을 조사하였고, 이들 결과를 토대로 유리섬유의 적층수와 배향각도에 따른 GFRP의 극한하중, 응력-변형율 선도 및 탄성계수 등을 비교 분석하였다. 한편 본 논문에서는 유리섬유의 적층수, 직경 변화에 따른 GFRP관의 파괴거동을 고찰하기 위하여 4점 재하법에 의한 GFRP관의 휨파괴실험을 수행하였다. 실험에 사용된 시험체는 길이 1200mm로 하였으며, 유리섬유의 적층수를 30, 35, 40층, 관의 직경을 50, 100, 150mm로 하였다. 파괴실험시 각 시험체의 하중변화에 대한 휨 변형율, 중앙점 처짐량 및 항복하중을 측정하였고, 이들 결과를 토대로 유리섬유으 적층수와 관의 직경에 따라 GFRP관의 항복하중 및 파괴에너지를 비교 분석 하였으며, 항복시 파괴에너지를 추정할 수 있는 제안식을 유도하였다.