• Journal of Welding and Joining
• /
• 제30권6호
• /
• pp.98-105
• /
• 2012

The focus of this investigation is to evaluate the effect of joining parameter on the microstructure and mechanical properties of welds produced by friction stir lap welding. The dissimilar Al alloys, KS5J32 and AA6K31, were joined by friction stir lap welding technique under several welding conditions, and KS5J32 alloy was placed on the top of AA6K31 alloy. The tool rotation speeds were 1000, 1250, and 1500rpm, and the welding speeds were 100, 300, 500, 700mm/min, respectively. The results showed that two shapes of nugget, such as onion ring and irregular vortex type, were observed with various revolutionary pitch. In all welding conditions, fracture occurred at the soften region of bottom sheet(AA6K31) and the strengths were 64~78% of those of base metal. Fractured positions were classified into three types : HAZ, triple point, void depending on the revolutionary pitch. The actual thickness of specimen at the fractured location was decreased with decreasing heat input. A linear relationship exists between the effective thickness of fractured position and peak load.

• Journal of Welding and Joining
• /
• 제29권2호
• /
• pp.72-79
• /
• 2011

The scope of this investigation is to evaluate the effect of joining parameters on the microstructural features and mechanical properties of dissimilar aluminum alloys, 1mm-thickness fixing AA6K31 at the top position and fixing AA5J32 at the bottom position. The friction stir lap welds were studied under various welding conditions, rotation speed of 1000, 1250, 1500rpm and welding speed of 100, 300, 500, 700mm/min, respectively. Mechanical test has been investigated in terms of tensile shear test and hardness test. The results showed that three type nugget shapes such as onion ring, zigzag type, hooking with the void, have been observed with revolutionary pitch. All welding conditions fractured at the HAZ of top plate, A6K31 and also the strength compare with base metal of lap joints were low efficiency, 52~63%. The thickness of fractured position was decreased with the lower heat input conditions. The relationships were excellent due to linear between the effective thickness of fractured position and peak load. The fractured position was the interface between joint area and not joint area. Also the strength efficiency compared with base metal was lower than decreasing rate of thickness because the hardness was decreased at fractured position due to softened material.

• 대한금속재료학회지
• /
• 제48권6호
• /
• pp.533-542
• /
• 2010

The specific motivation for joining an Al alloy and Zn-coated steel arises from the need to save fuel consumption by weight reduction and to enhance the durability of vehicle structures in the automobile industry. In this study, the lap joining A6K31 Al alloy (top) and SGARC340 Zn-coated steel (bottom) sheets with a thickness of 1.0 mm and 0.8 mm, respectively, was carried out using the friction stir weld (FSW) technique. The probe of a tool did not contact the surface of the lower Zn-coated steel sheet. The friction stir welding was carried out at rotation speeds of 1500 rpm and travel speeds of 80~200 mm/min. The effects of tool geometry and welding speed on the mechanical properties and the structure of a joint were investigated. The tensile properties for the joints welded with a larger tool were better than those for the joints done with a smaller tool. A good correlation between the tensile load and area of the welded region were observed. The bond strength using a larger tool (M4 and M3) decreased with an increase in welding speed. Most fractures occurred along the interface between the Zn-coated steel and the Al alloy. However, in certain conditions with a lower welding speed, fractures occurred at the A6K31 Al alloy.