• Journal of Advanced Marine Engineering and Technology
• /
• v.35 no.1
• /
• pp.75-81
• /
• 2011

Dissimilar joining of aluminum 6061-T6 alloy to aluminum 5083-O alloy was performed using friction-stir welding technique. The mechanical properties, hardness, macro- and micro-structure on dissimilar friction-stir-weld aluminium alloy were investigated. Mechanical properties of the weld mainly depend on which Al alloy is placed at the retreating sides of the rotating tool respectively during dissimilar friction-stir weld because the microstructure of stir zone was mainly composed of welded Al alloys of the retreating side. Onion ring pattern was observed like lamella structure stacked by each Al alloy in turn. It apparently results in defect-free weld zone that traverse speed was changed to 124 mm/min under conditions of tool rotation speed like 1250 rpm with 5 mm of tool's prove diameter, 4.5 mm of prove length, 20 mm of shoulder diameter, and $2^{\circ}$ of tilting angle. The 231 MPa of ultimate stress and the 121 MPa of yield point are obtained about the friction-stir-welded Al 6061-T6(AS) to Al 5083-O(RS).

• Proceedings of the KWS Conference
• /
• 2003.05a
• /
• pp.57-59
• /
• 2003

• Proceedings of the KWS Conference
• /
• 2003.11a
• /
• pp.275-277
• /
• 2003

• Proceedings of the KWS Conference
• /
• 2004.05a
• /
• pp.162-164
• /
• 2004

1991년 영국의 TWI(The Welding Institute)에서 처음 FSW(Friction Stir Welding)가 개발된 이후로 전 세계적으로 관심이 증가하여 꾸준한 연구가 계속되고 있다. FSW공정은 특수하게 설계된 용접툴(tool)을 특정한 회전수로 회전시키면서 용접하고자 하는 재료의 용접라인에 삽입하여 용접에 필요한 마찰열과 소성변형을 발생시키고, 그 후 용접라인을 따라 툴을 이동시킴으로써 용접이 이루어지는 매우 간단한 공정이다. (중략)

• Proceedings of the KWS Conference
• /
• 2002.05a
• /
• pp.109-111
• /
• 2002

• Proceedings of the KWS Conference
• /
• 2003.05a
• /
• pp.72-74
• /
• 2003

• Journal of the Korea Academia-Industrial cooperation Society
• /
• v.17 no.8
• /
• pp.706-713
• /
• 2016

In this study, the welding characteristics of friction stir welding were investigated in accordance with the tool plunge position and cooling to the base materials for the joining of dissimilar materials (A6005-AZ61). Other different welding conditions, such as the tool rotation speed and welding speed, were fixed to 500rpm-30mm/min, respectively, and welding was then carried out by placing the Mg alloy (AZ61) on the advancing side and Al alloy(A6005) on the retreating side. Welding was conducted under six different conditions. To investigate the welding characteristic, tensile test and microstructure observations using an optical microscope were carried out. As the tensile test result, the maximum strength appeared under the condition in which the tool is moved 1 mm to the Mg alloy direction and cooling to the base materials. Under the same welding conditions, the strength with cooling was approximately two times higher than that without cooling. The tool was located in each direction of 1.7 mm from the weld line. Therefore, in the excessive off-set of tool position, the welding integrity was in an extremely poor condition due to the lack of stirring. This study was confirmed by the A6005-AZ61 dissimilar friction stir welding the welding speed and the tool rotation speed. In addition, the temperature control and tool plunge position are important welding parameters.

• Proceedings of the KWS Conference
• /
• 2009.11a
• /
• pp.49-49
• /
• 2009

마찰교반접합법은 특정한 회전수로 회전하는 용접 툴을 이용하여 접합하고자 하는 피접합재의 맞댄면에 삽입시킨 후 툴을 이동시키거나 혹은 시편을 견고하게 고정시킨 장치(backing plate)가 움직여 고상 상태에서 접합이 이루어진다. 알루미늄, 마그네슘 등 비교적 융점이 낮은 저융점 재료의 재료에 처음 적용이 되어 많은 연구가 활발히 진행되었고 타 용접방법에 비해 우수한 접합특성을 나타내었다. 최근 이러한 마찰교반접합은 이러한 저융점 재료를 넘어서 스틸, 타이타늄, 니켈 등과 같은 고융점 재료 등에 대한 적용이 늘어나고 있다. 마찰교반접합을 이용하여 이러한 고융점 재료의 접합 경우 내마모성 및 내열성 등의 내구성이 갖추어진 툴과 이러한 툴을 냉각시킬 수 있는 냉각 장치 등이 필요로 하나 경제적 측면이나 접합부의 우수한 특성 등을 고려 할 때 그 적용 및 발전 가능성이 매우 높다고 볼 수 있다. 최근 무공해 연료로 각광받고 있는 액화천연가스 (LNG)의 수요가 급증함에 따라 LNG 저장탱크 소재로 널리 사용되고 있는 9% Ni강의 수요 또한 증가하고 있는 상황이다. 하지만 9% Ni 강은 극저온용 소재로 용접부의 저온인성 ($-196^{\circ}C$)이 가장 중요하기 때문에 저온인성을 확보하고자 Inconel 계나 Hastelloy계 등의 니켈 기 합금을 용접재료로 사용하고 있으나 이러한 용접재료는 가격이 매우 고가이며 또한 용접 후 용접부의 강도가 낮다는 문제가 제기되고 있다. 또한 LNG 탱크 제작시 사용되는 용접법은 GTAW, SAW 및 SMAW 이지만 국내에서는 주로 SMAW에 의존하고 있는 실정인 관계로 보다 더 경제적인 용접 프로세스의 적용 가능성이 검토되고 있는 상황이다. 본 연구에서는 마찰교반용접을 이용하여 두께 4mm의 9% Ni 강에 대해 맞대기 마찰교반접합을 실시하였다. 툴 회전 속도 및 접합 속도를 고정한 상태에서 접합을 실시 하였으며 접합 시 툴은 $Si_3N_4$로 제작된 툴을 사용하였다. 접합 후 외관상태 점검, 미세조직 관찰, 경도, 인장 강도 및 저은 충격 측정 등의 실험을 실시하였고, 이러한 결과를 이용하여 미세조직과 기계적 특성과의 관련성을 조사하였다.

• Proceedings of the KWS Conference
• /
• 2006.10a
• /
• pp.240-241
• /
• 2006

• Proceedings of the KWS Conference
• /
• 2006.05a
• /
• pp.272-273
• /
• 2006