• Transactions of the Korean Society of Mechanical Engineers A
• /
• v.31 no.8
• /
• pp.870-879
• /
• 2007

In this study, various damage modes in bending unimorph piezoelectric composite actuators with a thin sandwiched PZT plate during bending fracture tests have been evaluated by monitoring acoustic emission (AE) signals in terms of waveform and peak frequency as well as AE parameters. Three kinds of actuator specimens consisting of woven fabric fiber skin layers and a PZT ceramic core layer are loaded with a roller and an AE activity from the specimen is monitored during the entire loading using an AE transducer mounted on the specimen. AE characteristics from a monolithic PZT ceramic with a thickness of $250{\mu}m$ are examined first in order to distinguish different AE signals from various possible damage modes in piezoelectric composite actuators. Post-failure observations and stress analyses in the respective layers of the specimens are conducted to identify particular features in the acoustic emission signal that correspond to specific types of damage modes. As a result, the signal classification based on waveform and peak frequency analyses successfully describes the failure process of the bending piezoelectric composite actuator exhibiting diverse failure mechanisms. Furthermore, it is elucidated that when the PZT ceramic embedded actuators are loaded mechanical bending loads, the failure process of actuator specimens with different lay-up configurations is almost same irrespective of their lay-up configurations.

• Proceedings of the Korean Society for Noise and Vibration Engineering Conference
• /
• 2011.04a
• /
• pp.572-577
• /
• 2011

The acoustic emission (AE) technique is a well-known non-destructive test technique, both in research and for industrial applications. It is mainly used to monitor the onset of cracking processes in materials and components. Predicting and preventing the crack phenomenon has attracted the attention of many researchers and has continued to provide a large incentive for the use of condition monitoring techniques to detect the earliest stages of cracks. In this research, goal is in grasping features of AE signal caused by crack growth. The envelope analysis with discrete wavelet transform (DWT) is used to find the characteristic of AE signal. To estimate feature of divided into three by crack length, the time waveform and the power spectrum were generated by the raw signals and the transferred signal processed by envelope analysis with DWT.

• Journal of Power System Engineering
• /
• v.14 no.6
• /
• pp.41-46
• /
• 2010

Acoustic emission (AE) technique is a well-known non-destructive test technique. Fatigue crack growth test was performed using SM53C to check up the AE signal occurred by crack growth, so AE system was used to detect the crack signal. Features calculated by the AE signals were analyzed to evaluate the steps divided the crack growth into three. The steps, initiation, growth and breaking, were separated by velocity of the crack growth. Time waveform and power spectrum were created by the AE signal of each one of the steps and compared. In the feature domains, it was found that AE values changed rapidly as the velocity of the crack increasing.

• Journal of the Korean Society for Precision Engineering
• /
• v.11 no.4
• /
• pp.69-76
• /
• 1994

AE(Acoustic Emission) signal is correlated to workpiece material, cutting conditions and tool geometry during metal cutting. The relationship between AE signal and cutting parameters can be obtained by theoretical model and experiments. The value of CR(Count Rate) is nearly constant in stable cutting, but when the chatter vibration occours, the value of CR is rapidly increased due to the vibration deformation zone. By experimental signal processing of AE, it is more effective than by RMS(Root Mean Square) measurement to detect the threshold of chatter vibration by CR measurement.

• Journal of the Korean Institute of Gas
• /
• v.8 no.3 s.24
• /
• pp.1-7
• /
• 2004

The polyethylene pipe can use semi-permanent because of the high corrosion resistance with chemical stability. In addition to, there is the merit that is an easy to establish and to maintain. However, as the reason that it is simply degraded when the polyethylene pipe was exposed to the outside, mainly it is used to lay under the ground with low-pressure gas transportation pipe. In this study, the nondestructive evaluation method was used to maintain the integrity of the polyethylene pipe. We simulated the various defects on the polyethylene pipes, and then the AE signal occurred according to the impact test of steel ball was evaluated by the acoustic emission method. From the results, the waveform and dominant frequency could be distinguishing from the defect shapes of polyethylene pipe. Especially, in the case of notch defect, the AE signals occur different by the angle and depth of the notch.

• Journal of the Korean Society for Nondestructive Testing
• /
• v.20 no.4
• /
• pp.276-284
• /
• 2000

The acoustic emission (AE) behavior of reinforced concrete beams tested under flexural loading was investigated to characterize and identify the source of damage. This research was aimed at identifying the characteristic AE response associated with micro-crack development, localized crack propagation, corrosion, and debonding of the reinforcing steel. Concrete beams were prepared to isolate the damage mechanisms by using plain, notched-plain, reinforced, and corroded-reinforced specimens. The beams were tested using four-point cyclic step-loading. The AE response was analyzed to obtain key parameters such as the time history of AE events, the total number and rate of AE events, and the characteristic features of the waveform. Initial analysis of the AE signal has shown that a clear difference in the AE response is observed depending on the source of the damage. The Felicity ratio exhibited a correlation with the overall damage level, while the number of AE events during unloading can be an effective criterion to estimate the level of corrosion distress in reinforced concrete structures. Consequently, AE measurement characterization appears to provide a promising approach for estimating the level of deterioration in reinforced concrete structure.

• Journal of Ocean Engineering and Technology
• /
• v.13 no.3 s.33
• /
• pp.36-48
• /
• 1999

Fatigue life and crack retardation behavior after penetration were experimentally examined using surface pre-cracked specimens of aluminium alloy 5083. The Wheeler model retardation parameter was used successfully to predict crack growth behavior after penetration. By using a crack propagation rule, the change in crack shape after penetration can be evaluated quantitatively. Advanced, waveform-based acoustic emission (AE) techniques have been successfully used to evaluate signal characteristics obtained form fatigue crack propagation and penetratin behavior in 6061 aluminum plate with surface crack under fatigue stress. Surface defects in the structural members are apt to be origins of fatigue crack growth, which may cause serious failure of the whole structure. The nondestructive analysis on the crack growth and penetration from these defects may, therefore, be one of the most important subjects on the reliability of the leak before break (LBB) design. The goal of the present study is to determine if different sources of the AE could be identified by characteristics of the waveforms produced from the crack growth and penetration. AE signals detected in four stages were found to have different signal per stage. With analysis of waveform and power spectrum in 6061 aluminum alloys with a surface crack, it is found to be capabilities on real-time monitoring for the crack propagation and penetration behavior of various damages and defects in structural members.

• Journal of the Korean Society for Nondestructive Testing
• /
• v.31 no.5
• /
• pp.500-507
• /
• 2011

Acoustic emission(AE) signals during the polymerization shrinkage of composite resin subjected to the LED light exposure were detected through a wave guide method and a direct sensor attachment method. For PMMA, human tooth, stainless steel substrate, data of AE hits and amplitudes were compared. For the test using the wave guide, AE amplitudes decreased because of the attenuant wave. However, AE hits and 1st peak frequency distribution were not different according to the sensor attachments. Through the experiments, wave guide could be used for a nondestructive evaluation of the marginal disintegrative fracture of dental restoration.

• The Journal of the Acoustical Society of Korea
• /
• v.22 no.1
• /
• pp.61-68
• /
• 2003

The guided wave has been widely employed to characterize thin plates and layered media. The dispersion curves of phase and group velocities are essential for the quantitative application of guided waves. In the present work, a fully automated system for the measurement of backward radiation of LLW has been developed. The specimen moves in two dimensional plane as well as in angular rotation. The signals of backward radiation of LLW were measured from an elastic plate in which specific modes of Lamb wave were strongly generated. Phase velocity of the corresponding modes was determined from the incident angle. The generated Lamb waves propagated forward and backward with the leakage of energy into water. Backward radiated LLW was detected by the same transducer and its frequency components were analyzed to extract the related information to the dispersion curves. The dispersion curves of phase velocity were measured by varying the incident angle. Moving the specimen in the linear direction of LLW propagation, group velocity was determined by measuring the transit time shift in the ultrasonic waveform.

• Journal of the Korean Society for Nondestructive Testing
• /
• v.14 no.2
• /
• pp.122-131
• /
• 1994

Journal bearings in the rotating machineries are vulnerable to the contamination or the insufficient supply of lubricating oil, which is likely to be the cause of unexpected shutdown or malfunction of these systems. Various destructive and nondestructive testing methods had been used for the reduction of maintenance cost and the operational safety problems due to the accidents related to bearing damages. In this experimental approach, acoustic emission monitoring is employed to the detection of incipient failure caused by intervention of foreign particles most probable in the journal bearing systems. Experimental schedules for the intervention of foreign particles was composed to be more quantitative and systematic than last study in consideration of minimum oil film thickness and particle size. The experiment was conducted under such designed conditions as inserting alumina particles to the lubrication layer in the simulated journal bearing system. Several parameters such as AE rms level, waveform, AE energy distribution and other AE event parameters are used for analysis and characterization of damage source. The results showed that the history of damage was well correlated with the changes of AE rms level and the type of damage source signal can be verified using other informations such as waveform, distributions of AE parameters etc.