• Journal of the Microelectronics and Packaging Society
• /
• v.5 no.1
• /
• pp.31-38
• /
• 1998

저온소결기판용 Glass-ceramics를 제조하기 위해 LiO2-MgO-MgF2-SiO2계 조성에 서 B2O3첨가가 결정화 특성 및 물성에 미치는 영향을 고찰하였다. 145$0^{\circ}C$에서용융하여 제조 한 모유리의 핵형성 온도와 결정화 온도를 결정하기 위해 TMA와 DTA분석을 실시하였다. 결정화시킨 유리의 결정상과 미세구조를 관찰하기 위하여 XRD와 SEM관찰을 실시하였다. Water swelling을 통해 Glass-ceramics powder를 제조하였으며 제조한 powder의 평균입자 크기는 8.32$\mu$m였다.

• Transactions of the Korean Society of Mechanical Engineers B
• /
• v.22 no.12
• /
• pp.1774-1783
• /
• 1998

The transition from steady laminar to chaotic convection in a glass melting furnace specified by upper surface temperature distribution has been studied by the direct numerical analysis of the two and three-dimensional time dependent Navier-Stokes equations. The thermal instability of convection roll may take place when modified Rayleigh number($Ra_m$) is larger than $9.71{\times}10^4$. It is shown that the basic flows in a glass melting furnace are steady laminar, unsteady periodic, quasi-periodic or chaotic flow. The dimensionless time scale of unsteady period is about the viscous diffusion time, ${\tau}_d=H^2/{\nu}_0$. Through primary and secondary instability analyses the fundamental unsteady feature in a glass melting furnace is well defined as the unsteady periodic or weak chaotic flow.

• Proceedings of the Korean Nuclear Society Conference
• /
• 1997.05b
• /
• pp.319-323
• /
• 1997

석탄화력발전소의 부산물인 석탄회를 이용한 DUPIC dirty scrap waste의 유리고화체에 대한 내침출성을 분석하였다. Fly ash, SiO$_2$, NaNO$_3$, B$_2$O$_3$에 DUPIC 핵연료 제조공정으로부터 발생되는 모의 dirty scrap waste를 15 wt% ~ 30 wt% 혼합하여, 115$0^{\circ}C$ 에서 3시간 용융시킨 후 서서히 냉각시켜 얻은 유리고화체의 침출성을 온도, 침출액의 종류, 폐기물의 함량 등에 따라 평가하였다 침출실험결과 석탄회유리고화체는 양호한 내침출성을 보였다. 석탄회유리고화체의 침출율은 합성지하수, 합성해수, 증류수의 순으로 감소하였으며, 폐기물함량의 증가에 따라 증가하였다.

• Journal of the Korean Crystal Growth and Crystal Technology
• /
• v.16 no.5
• /
• pp.227-234
• /
• 2006

Microstructures of free surface and interior of glass-ceramics obtained by heat treating silicate glass specimen containing electric arc furnace dust(EAF dust) were observed. The crystallization temperature, $T_c$ of glassy specimen was measured around $850^{\circ}C$ from the result of different thermal analysis so heat treatment temperature to obtain glass-ceramic specimen was selected as $950^{\circ}C$ for 1 hr. Glass specimens containing 50 wt% dust were amorphous, while glass specimens containing 70 wt% dust showed spinel crystal peaks in XRD results. In case of glass-ceramic specimens, spinel crystalline phase was appeared with willemite, and willemite crystal peak intensity increased with increasing dust contents. The fractured surface of glass specimens containing 50 wt% dust was smooth like mirror surface, but that containing 70 wt% dust showed spinel crystals of 10 ${\mu}m$ size in glass matrix. In case of glass-ceramic specimens, ZnO crystal particles of $2{\sim}5{\mu}m$ size were produced in free surface and glassy phase, spinel and willemite crystal phases existed in interior. There were no crystals in glasses containing 50 wt% dust, while glass containing 70 wt% dust had 14 vol% crystals. Crystallinity of glass-ceramic specimens containing 50 and 70 wt% dust were 19 and 43%, respectively. When microstructures of glass and glass-ceramic specimens were observed through SEM after TCLP experiment, glass specimens showed flaking phenomenon while glass-ceramic specimens showed a slight corrosion evidence without any cracks.

• Journal of the Korean Crystal Growth and Crystal Technology
• /
• v.24 no.3
• /
• pp.120-126
• /
• 2014

Translucent green colored opal glass was fabricated to substitute polycarbonate diffuser of LED lighting in order to solve the durability problem. Batch materials of green colored opal glass with the composition of calcium phosphate for opacifier and iron oxide for colorant were made and melted at $1550^{\circ}C$. As the results, translucent green colored opal glass was obtaind, which had excellent optical properties compare with nomal color glass for the diffuser of LED lighting, with no dazzling from direct light by high haze value over 90 % and low parallel transmittance value about 1 %. Therefore, it is concluded that this translucent green colored opal glass can be used for the glass diffuser materials of LED lighting with high heat resistance and high durability to substitute polycarbonate diffuser.

• Journal of the Korean Ceramic Society
• /
• v.38 no.12
• /
• pp.1137-1143
• /
• 2001

In this study, glass-ceramics containing cordierite(2MgO$.$2Al$_2$O$_3$5SiO$_2$) as a major crystalline phase was prepared from MAS (MgO-Al$_2$O$_3$-SiO$_2$) glass system for the application to reflector. Glasses prepared with addition of TiO$_2$as a nucleating agent were crystallized by two-step heat treatment of nucleation and crystal growth. Then nucleation and crystal growth behavior were investigated and the influence of heat treatment schedule on the nature of crystal phases and the diffuse reflectance spectrum was investigated. As a result, cordierite and rutile were precipitated as a major crystalline phases for the glass-ceramics with the nucleation at 750$^{\circ}C$ for 3 hours and then crystallization at 1100$^{\circ}C$ for 5 hours, and this glass-ceramics showed the reflectance over 90% in 570∼2500nm specturm region.

• Journal of the Korean Ceramic Society
• /
• v.40 no.7
• /
• pp.662-666
• /
• 2003

Hertzian cyclic fatigue properties of the alumina-glass dental ceramics were evaluated in exact in vitro environment at contact loads from 200 N to 1000 N and up to 10$\^$6/ cycles to investigate the indentation damage and strength degradation. At 200 N, no strength degradation and crack generation was observed up to 10$\^$6/ contact cycles. As load increased from 200 N to 1000 N, the drastic reduction in strength was found when the damage transition from ring to radial crack occurred. The extent of strength degradation was more pronounced in vitro environments probably due to chemical reaction of artificial saliva with glass phase through radial cracks introduced during large numbers of contacts.

• Proceedings of the Materials Research Society of Korea Conference
• /
• 2010.05a
• /
• pp.50.1-50.1
• /
• 2010

내열성과 내부식성, 촉매능력등이 뛰어난 백금은 자동차 배출가스 정화촉매, 유/무기화학반응의 공정 촉매, 석유화학산업에서의 촉매 등 촉매 뿐만 아니라 용융유리용 도가니, 유리 섬유용 부싱 등의 유리산업, 백금 열전대 외에도 전기/전자기기, 치과용 합금, 장신구, 항공우주,등의 많은 분야에서 폭넓게 쓰인다. 한편 낮은 기계적 특성을 개선하기 위하여 로듐 등의 백금족 원소를 첨가한 합금을 제조하여 이용하고 있지만 로듐의 공금 부족과 이에 따른 가격 상승으로 인한 대체조성의 설계가 요구되고 있다. 또한 고온의 산화분위기에 노출이 되면 산화물이 형성되고 이것이 휘발하여 중량의 손실이 생긴다고 알려져 있다. 본 연구에서는 백금 합금의 이러한 문제점의 해결방안을 제시하고자 백금족 원소를 첨가하고 첨가 원소별 산화휘발의 정도를 측정하였다. 시편은 plasma arc melting법으로 각각 Pt, Pt-20%Rh, Pt-11%Ir, Pt-10%Rh-10%Ir의 조성을 가지는 합금을 만든 후 압연을 하여 판상으로 만들었고, 이를 각각 $1000^{\circ}C$, $1200^{\circ}C$, $1400^{\circ}C$ 등에서 각각 96시간 까지 산화휘발시켜 중량손실량을 측정하였고 이를 XPS를 이용한 표면분석을 하여 산화휘발거동을 규명하였다. 그 결과 Pt-20%Rh가 가장 우수한 고온산화휘발특성을 보였으며 상대적으로 고온산화휘발특성이 좋지 않은 Pt-Ir 2원계 합금에 Rh를 첨가한 Pt-10%Rh-10%Ir 3원계 합금을 만들어 약 60% 향상된 결과를 얻을 수 있었고 이 결과를 증기압 관점에서 고찰하였다.

• Journal of the Korean Crystal Growth and Crystal Technology
• /
• v.17 no.2
• /
• pp.82-89
• /
• 2007

Glass-ceramics were fabricated by heat-treating a glass at $700^{\circ}C$/10hr which was obtained by melting a glass frit mixed with $40{\sim}80 wt%$ EAF dust at $1300^{\circ}C$/1hr. Dependence of crystal phase and bonding state change upon a compositional change and heat treatment condition were studied and the results was connected to the toxic characterization leaching procedure (TCLP) test data to investigate a chemical durability of the specimens. Increasing dust in a glass shifted the peak around $1000cm^{-1}$ to the lower frequency which was composed of two vibration peaks for the nonbridging oxygen at $960cm^{-1}$ and the bridging oxygen at $1050{\sim}1060cm^{-1}$. Also, the $B_2O_3$ structure of boroxol ring changed to a tetrhedral-, trigonal- and di-borate with dust addition. The Fe-O peaks in the glass-ceramics were observed which is consitent with XRD results of spinel formation. The surface of glass after TCLP test was severely cracked while there was no cracks on a glass-ceramics after TCLP test so the chemical durability of the glass-ceramics is superior than that of glass. The leaching concentration of Fe for the glass-ceramics containing EAF dust 80 wt% is 1/15 times lower than that of glass. The Zn leaching concentration fur the glass-ceramics containing dust < 70 wt% was higher than that of glass but its trend was reversed for the specimen of dust content > 80 wt% which could be concluded as correlated with occurrence of willemite phase.

• Journal of the Korean Crystal Growth and Crystal Technology
• /
• v.29 no.5
• /
• pp.208-214
• /
• 2019

The glass of $BaO-GeO_2-La_2O_3-ZnO$ system with a transmittance of more than 75 % at mid-wave infrared (MWIR) region in the range of $3{\mu}m$ to $5{\mu}m$ is manufactured and its property is evaluated. After selecting construction that can melt glass through flow button test, $BaO-GeO_2-La_2O_3$ system where 10 mol%, 20 mol% of ZnO were added respectively were melted at $1350^{\circ}C$ for 1 hour and $BaO-GeO_2-La_2O_3$ system of glass was manufactured. Among them, with 20 mol% of ZnO, 16 mol% BaO-56 mol% $GeO_2-8mol%$ $La_2O_3-16mol%$ ZnO system of glass was found to has less than $660^{\circ}C$ of glass transition temperature, more than 1.70 of refractive index, and more than 530 of knoop hardness. Therefore, it is concluded that glass of $BaO-GeO_2-La_2O_3-ZnO$ system of glass with 20 mol% ZnO has good melting conditions at low temperatures and excellent optical properties, thus, can be utilized for special optical materials field.