• Journal of Dental Rehabilitation and Applied Science
• /
• v.25 no.3
• /
• pp.225-235
• /
• 2009

A common procedure of restoration of endodonticlly treated tooth with fiber-reinforced post is followed by core build-up after post cementation. However, this technique is complex and time-consuming. The aim of this study was to compare fracture strength of premolar, restored with various methods of core fabrications on fiber-reinforced posts and casting metal restoration. Forty five freshly extracted human mandibular premolars were obtained and devided into 5 groups acconding to the type of post and methods of core build-up. In Group A, D.T. $Light-post^{(R)}$ were cemented with $DUO-LINK^{TM}$ and then $LIGHT-CORE^{TM}$ was used for core restoration. In Group B, D.T. $Light-post^{(R)}$ and $DUO-LINK^{TM}$ were used for cementing in the postspace, and $DUO-LINK^{TM}$ was used again for core restoration. In Group C, $Light-post^{(R)}$ bonding and the core build-up were performed simultaneously by using $DUO-LINK^{TM}$. In Group D, $LuxaPost^{(R)}$ was bonded by using $LuxaCore^{(R)}-Dual$. Again, $LuxaCore^{(R)}-Dual$ was used for core restoration. In Group E, $LuxaPost^{(R)}$ bonding and the core build-up were performed simultaneously by using $LuxaCore^{(R)}-Dual$. Axial reduction was formed parallelly as possible and 45 degree bevel was made at buccal occlusal surface. Crowns were fabricated and cemented. Each tooth was embedded in self-curing acrylic resin to the level of 2mm below the CEJ. Specimens were fixed on universal testing machin such that the axis of the tooth was at 45 degree inclination to the horizontal plane, and compressive force was applied at a crosshead speed of 1mm/min until failure occurred. The mean fracture strength was the highest in group A followed by descending order in group B, D, E and C. However, there were no statistically significant differences between groups with regard to the fracture strength. The type of the post or build-up methods of the core does not seem to influence the fracture strength.

• Journal of Adhesion and Interface
• /
• v.22 no.4
• /
• pp.118-127
• /
• 2021

In this study, the mechanical properties of vulcanized rubber were evaluated through compounding by controlling filler content to improve the mechanical properties of NBR rubber. Aramid and glass fibers with excellent heat resistance were used as fillers, and ceramics were additionally used in anticipation of a complementary effect, and as for the ceramic materials, needle-shaped and plate-shaped ceramics were used. Each filler was used in an amount of 5.0, 10.0, 15.0, and 20.0 phr in order to investigate the basic properties according to the amount of filler. To confirm the complementary effect through ceramic application, each 10.0 phr fiber and ceramic were mixed with 1:1 ratio to evaluate mechanical properties. As a result, it was confirmed that the decreasing ratio of tensile strength after heat aging was small in the order of aramid fiber, acicular ceramic, glass fiber, and plate ceramic in the case of applying the filler alone. In addition, the mechanical characteristics of vulcanized rubber using composite filler based on fibers and ceramics were evaluated, and it was confirmed that the composite filler had a complementary effect on thermal aging.

• Composites Research
• /
• v.20 no.6
• /
• pp.1-7
• /
• 2007

Expanded graphite/carbon fiber hybrid conductive polymer composites were fabricated by the preform molding technique. The conductive fillers were mechanically mixed with a phenol resin to provide an electrical property to composites. The conductive filler loading was fixed at 60wt.% to accomplish a high electrical conductivity. Expanded graphites were excellent in forming a conductive networking by direct contacts between them while it was hard to get the high flexural strength over 40MPa with using only expanded graphite and phenol resin. In this study, carbon fibers were added in composites to compensate the weakened flexural strength. The effect of carbon fibers on the mechanical and electrical properties was examined according to the weight ratio of carbon fiber. As the carbon fiber ratio increased, the flexural strength increased until the carbon fiber ratio of 24wt.%, and then decreased afterward. The electrical conductivity gradually decreased as the increase of the carbon fiber ratio. This was attributed to the non-conducting regions generated among the carbon fibers and the reduction of the direct contact areas between expanded graphites.

• Proceedings of the Korean Vacuum Society Conference
• /
• 2013.02a
• /
• pp.489-489
• /
• 2013

AF 코팅은 유리나 플라스틱과 같은 기재 표면을 특수 처리하여 지문과 같은 오염물질의 부착방지와 오염물질이 부착되더라도 쉽게 제거 가능하도록 하는 기술이다. 전자, 자동차, 건축, 섬유, 철강분야 등에 활용 가능한 중요기술로 박막의 발수 발유 기능을 부여하는 표면처리 기술이고, 코팅방법에는 진공증착, 스핀코팅, 딥코팅, 플로우 코팅, 스프레이 코팅 등이 있으며, 경화 방법이나 접촉각 등의 특성이 반영된다. 터치패널 등의 지문부착방지 기술은 불소계와 비불소계 재료로 구분할 수 있지만 지문을 쉽게 지울 수 있고, 오염 방지 기능과 내구성이 있으며, 우수한 광학특성을 유지하는 것이 과제라 할 수 있다. 그리고 항균성을 부여하는 기술도 개발되고 있다. 이런 터치패널의 강화유리에 AF 코팅한 제품은 핸드폰 글래스에 처음 적용하면서부터 실생활에 도입이 시작되고 있다. 이러한 AF 코팅을 스퍼터링 법을 이용하여 증착 시켰다. 기존에는 E-beam을 이용한 증착 방식이 주를 이루었지만, 스퍼터링 법을 이용함으로써 박막의 균일화 및 대량생산이 가능해졌다. 따라서 이 연구에서는 기존의 E-beam 방식과 sputtering 공정 중 ion source에 의한 전처리의 유무에 따른 박막의 특성을 비교하였다. 내부식성, 내마모성 시험을 거친 후, 접촉각을 측정하여 알아보았으며, 박막의 건전성 및 균일성은 FE-SEM을 이용하여 관찰하였다. 실험용 장비가 아닌 실제 생산장비인 직경 1,400 파이의 장비를 이용하여 증착하였으며 염수분무 및 내마모 시험 후, 기존 접촉각의 ${\pm}5^{\circ}$ 내외임을 확인 할 수 있었고, 박막의 건전성 또한 뛰어남을 알 수 있었다.

• Proceedings of the KIEE Conference
• /
• 1993.07b
• /
• pp.581-583
• /
• 1993

One of the principal problems encountered in the use of fiber reinforced composites is to establish an active fiber surface to achieve maximum adhesion between resin and fiber surface. In order to improve the interface bonding, the surface of glass fiber should be treated with silane coupling agent in ordinary composite manufacturing processes. However, the price of the coupling agent is very high and in the treating process voids are formed, which decreasees electrical and mechanical strength. We want to develope new process that will overcome the disadvantage of the coupling agent and achieve maximum adhesion at the interface between resin and fiber by active plasma treatment on the glass fiber surface. In this study, we investigate the improvement of contact angle on the glass plate surface as the first step in developing new GFRP.

• Proceedings of the Korean Society of Precision Engineering Conference
• /
• 2005.06a
• /
• pp.1322-1325
• /
• 2005

The main objectives of this research work are to develop conductive glass fiber woven roving and carbon fiber unidirectional fabric composite materials and to determine their electromagnetic shielding effectiveness(EMSE). Epoxy is the matrix phase and glass, carbon fiber are the reinforcement phase of the composite material. Carbon black are incorporated as conductive fillers to provide the electromagnetic shielding properties of the composite material. The amount of carbon black in the composite material is varied by changing the carbon black composition, woven roving and unidirectional (fabric) structure. The EMSE of various fabric composites is measured in the frequency range from 300MHz to 800MHz. The variations of EMSE of woven roving and unidirectional composites with fabric structure, metal powder composite are described. Suitability of conductive fabric composites for electromagnetic shielding applications is also discussed.

• Proceedings of the Korean Institute of Electrical and Electronic Material Engineers Conference
• /
• 2000.05b
• /
• pp.250-253
• /
• 2000

The fiber orientation in FRP has a great effect on the strength of FRP because the strength of FRP mainly depends on the strength of fiber. Unidirectional FRP made by pultrusion method has comparatively lower compressive strength than tensile strength. Compressive strength of unidirectional FRP may be increased by filament winding layer which has tensile stress when compressive stress was loaded. In this study, compressive strength and stresses of FRP rods were simulated according to the winding orientation of glass fiber. Inner part of FRP was made unidirectionally by pultrusion method and outer part of FRP was made by filament winding method. Simulated value and real evaluated compressive strength were compared to investigate stresses which is prominent to the fracture of FRP. The shear stresses had a great effect on the strength of FRP although the stress of parallel direction of FRP was much higher.

• Journal of the Korean Society for Nondestructive Testing
• /
• v.31 no.1
• /
• pp.53-61
• /
• 2011

Edge notched A16061-T6 aluminum was repaired with a GFRP composite patch as a function of the number of stacking, Damage progress of specimen for tension load has been monitored by acoustic emission(AE), AE energy rate, hit rate, amplitude, waveform and 1st peak frequency distribution were analyzed. Fracture processes were classified into Al cracking, Fiber breakage, Resin cracking and Delamination. Displacement of a specimen can be divided into Region I, II and ill according to acoustic emission characteristics. Region II where the patch itself was actually fractured was focused on to clarify the AE characteristics difference for the number of stacking.

• Transactions of the Korean Society of Mechanical Engineers
• /
• v.16 no.9
• /
• pp.1681-1690
• /
• 1992

The effects of the stress ratio and the fiber orientation(0.deg./90.deg. and .+-.45.deg.) to the load direction on the fracture behavior of the glass/epoxy plain woven composites were studied. The tests were carried out using compact tension specimens under both static and fatigue loading. The values of $k_{a}$ obtained from the energy release rate are independent of notch depth(a/w=0.2~0.6) for the 0.deg./90.deg. specimens, but decreases with an increase in a/w for the .+-.45.deg. specimens. And $k_{q}$ has higher values than $k_{ASTM}$ has been evaluated by the ASTM E399 test procedure. It is shown in the relation between fatigue crack growth rate da/dN and stress intensity factor range .DELTA.K using modified shape correction factor that da/dN decreases with a decrease in stress ratio and is lower for .+-..deg. specimens than for 0.deg./90.deg. These phenomena can be explained by the crack deflection to the load direction.n.n.

• Journal of Korean Society of Water and Wastewater
• /
• v.34 no.2
• /
• pp.149-159
• /
• 2020

Cured-in-place-pipe(CIPP) is the most adopted trenchless application for sewer rehabilitation to extend the life of the existing sewer without compromising both direct construction and indirect social costs especially applied in the congested urban area. This technology is globally and domestically known to be the most suitable for partial and full deteriorated pipe structure rehabilitation in a sewer system. The typical design of CIPP requires a significant thickness of lining to support loading causing sewage flow interruption and increasing material cost. This paper presents development of a high strength glass fiber composite lining material for the CIPP application and structural test results. The test results exhibit that the new glass fiber composite lining material has 12 times of flexural strength, 6.2 times of flexural modulus, and 0.5 Creep Retention Factor. These test results can reduce lining design thickness 35% at minimum. Even though taking into consideration extra materials such as outer and inner films for actual field applications, the structural capacity of the composite material significantly increases and it reduces 20 percent or more line thickness as compared to the conventional CIPP. We expect that the newly developed CIPP lining material lowers material costs and minimizes flow capacity reduction, and fully replaceable to the conventional CIPP lining materials.